The hydrogen-induced cracking （HIC） behavior of X80 pipeline steel was studied by means of electrochemical charging, hydrogen permeation tests, tension test, and scanning electron microscopy （SEM）. The experimenta...The hydrogen-induced cracking （HIC） behavior of X80 pipeline steel was studied by means of electrochemical charging, hydrogen permeation tests, tension test, and scanning electron microscopy （SEM）. The experimental results indicate that the increase of charging time and charging current density or the decrease of the solution pH value leads to an increase of the hydrogen content in X80 steel, which plays a key role in the initiation and propagation of HIC. It is found that the majority of macro-inclusions within the as-used X80 steel do not constitute a direct threat to HIC except aluminum oxides, which directly or indirectly lead to HIC. The hydrogen trap density at room temperature is estimated to be pretty high, and this is an essential reason why the steel is sensitive to HIC. After hydrogen charging, the elongation loss rate and area reduction of X80 steel decline obviously, taking a noticeable sign of hydrogen-induced plasticity damages. It is demonstrated that the losses of these plastic parameters have a linear relation to the fracture size due to hydrogen.展开更多
The corrosion behavior of C110 bushing at high temperature and high pressure with a high H2S / CO2 was studied, and a basis for the materials selection of sour gas well bushing was provided in H2S, CO2 and saline coex...The corrosion behavior of C110 bushing at high temperature and high pressure with a high H2S / CO2 was studied, and a basis for the materials selection of sour gas well bushing was provided in H2S, CO2 and saline coexisting environment. Under acidic condiction, hydrogen atoms greatly entered into the material and caused the material properties changed. Weight loss method was used to study the corrosion rate of hydrogen charging samples and original untreated samples in simulated oil field environment. PAR2273 electrochemical workstation was used to examine the electrochemical performance of samples untreated, hydrogen charging after reacting in autoclave. The corrosion product film was observed through SEM. The experimental results show that sample with hydrogen charging has a much more obvious partial corrosion and pitting corrosion than the untreated blank sample even the downhole corrosion speed of bushing is increased after being used for a period of time. Polarization curve shows the corrosion tendency is the same between sample with or without hydrogen charging and corrosion tendency is reduced by corrosion product film. A layer of dense product film formed on the surface of samples provides a certain protective effect to the matrix, but cracked holes which will accelerate partial corrosion of the sample were also observed.展开更多
Extracts of elephant grass （Penniseturn purpureum） blended with some intensifier halides like ammonium chloride （AMC） and potassium iodide （PTI） were investigated as corrosion inhibitor for mild steel. The corro...Extracts of elephant grass （Penniseturn purpureum） blended with some intensifier halides like ammonium chloride （AMC） and potassium iodide （PTI） were investigated as corrosion inhibitor for mild steel. The corrosion process was monitored in 3.5% HCI by mass loss and electrochemical techniques at 30, 40, 50, 60 and 90 ℃. Addition of AMC and PTI increased the inhibition efficiency with the highest inhibition efficiency obtained with PTI blend- ed extract. The blends behaved as mixed type inhibitors and were spontaneously adsorbed on mild steel surface in exothermic nature. Synergistic parameters of the intensifier ions revealed cooperative effect. Kinetic data treatment indicated increase in energy barrier by intensifier ions. The results demonstrate that elephant grass extract blended with halide ions can act as alternative ecofriendly inhibitor for mild steel at elevated temperatures.展开更多
基金supported by the National Natural Science Foundation of China (No.50401016)
文摘The hydrogen-induced cracking （HIC） behavior of X80 pipeline steel was studied by means of electrochemical charging, hydrogen permeation tests, tension test, and scanning electron microscopy （SEM）. The experimental results indicate that the increase of charging time and charging current density or the decrease of the solution pH value leads to an increase of the hydrogen content in X80 steel, which plays a key role in the initiation and propagation of HIC. It is found that the majority of macro-inclusions within the as-used X80 steel do not constitute a direct threat to HIC except aluminum oxides, which directly or indirectly lead to HIC. The hydrogen trap density at room temperature is estimated to be pretty high, and this is an essential reason why the steel is sensitive to HIC. After hydrogen charging, the elongation loss rate and area reduction of X80 steel decline obviously, taking a noticeable sign of hydrogen-induced plasticity damages. It is demonstrated that the losses of these plastic parameters have a linear relation to the fracture size due to hydrogen.
基金Funded by the National Natural Science Foundation of China(No. 50904050)the Basic Projects of Sichuan Province(2011JY0106)the Postdoctoral Science Foundation(20110490810)
文摘The corrosion behavior of C110 bushing at high temperature and high pressure with a high H2S / CO2 was studied, and a basis for the materials selection of sour gas well bushing was provided in H2S, CO2 and saline coexisting environment. Under acidic condiction, hydrogen atoms greatly entered into the material and caused the material properties changed. Weight loss method was used to study the corrosion rate of hydrogen charging samples and original untreated samples in simulated oil field environment. PAR2273 electrochemical workstation was used to examine the electrochemical performance of samples untreated, hydrogen charging after reacting in autoclave. The corrosion product film was observed through SEM. The experimental results show that sample with hydrogen charging has a much more obvious partial corrosion and pitting corrosion than the untreated blank sample even the downhole corrosion speed of bushing is increased after being used for a period of time. Polarization curve shows the corrosion tendency is the same between sample with or without hydrogen charging and corrosion tendency is reduced by corrosion product film. A layer of dense product film formed on the surface of samples provides a certain protective effect to the matrix, but cracked holes which will accelerate partial corrosion of the sample were also observed.
基金financial support provided by World Bank Robert S.Mc Namara Fellowship Program 2015 to carry out this research abroad
文摘Extracts of elephant grass （Penniseturn purpureum） blended with some intensifier halides like ammonium chloride （AMC） and potassium iodide （PTI） were investigated as corrosion inhibitor for mild steel. The corrosion process was monitored in 3.5% HCI by mass loss and electrochemical techniques at 30, 40, 50, 60 and 90 ℃. Addition of AMC and PTI increased the inhibition efficiency with the highest inhibition efficiency obtained with PTI blend- ed extract. The blends behaved as mixed type inhibitors and were spontaneously adsorbed on mild steel surface in exothermic nature. Synergistic parameters of the intensifier ions revealed cooperative effect. Kinetic data treatment indicated increase in energy barrier by intensifier ions. The results demonstrate that elephant grass extract blended with halide ions can act as alternative ecofriendly inhibitor for mild steel at elevated temperatures.