The general hot deformation process consists of two steps, hot pressing and die-upsetting in order to obtain the anisotropic NdFeB magnet. This is the first report that the high anisotropy NdFeB magnets can be fabrica...The general hot deformation process consists of two steps, hot pressing and die-upsetting in order to obtain the anisotropic NdFeB magnet. This is the first report that the high anisotropy NdFeB magnets can be fabricated by single stroke hot deforming the isotropic magnet. The magnetic properties of those materials are: coercivity iHc ～11 kOe, remanence Br ～12 kG, and the maximum energy product (BH)max ～28 MG.Oe.展开更多
In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The ...In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The shear angle and forming defects of the fabrics were measured on the hemisphere, under different blank holder forces（BHFs）. The results showed that increasing BHF could enhance the shear angle slightly, reduce the asymmetry for the deformation of the fabrics, and change the main type of the process-induced defects. Besides, compression tests were performed on the corresponding composite components. By analyzing the change of fiber volume fraction and structural parameters of the textile reinforcements, the effects of draping behavior of NCFs on the mechanical performance of the composites were studied. The results reveal that draping process has distinguishable impacts on the mechanical properties of the final components, which is closely related to the stitching pattern of the NCFs.展开更多
文摘The general hot deformation process consists of two steps, hot pressing and die-upsetting in order to obtain the anisotropic NdFeB magnet. This is the first report that the high anisotropy NdFeB magnets can be fabricated by single stroke hot deforming the isotropic magnet. The magnetic properties of those materials are: coercivity iHc ～11 kOe, remanence Br ～12 kG, and the maximum energy product (BH)max ～28 MG.Oe.
基金Funded by the National Natural Science Foundation of China(No.51203144)
文摘In order to investigate the draping behavior of non-crimp fabrics（NCFs）, two types of carbon NCFs with tricot-chain stitches or chain stitches were formed on a hemispherical mould via a stretch forming process. The shear angle and forming defects of the fabrics were measured on the hemisphere, under different blank holder forces（BHFs）. The results showed that increasing BHF could enhance the shear angle slightly, reduce the asymmetry for the deformation of the fabrics, and change the main type of the process-induced defects. Besides, compression tests were performed on the corresponding composite components. By analyzing the change of fiber volume fraction and structural parameters of the textile reinforcements, the effects of draping behavior of NCFs on the mechanical performance of the composites were studied. The results reveal that draping process has distinguishable impacts on the mechanical properties of the final components, which is closely related to the stitching pattern of the NCFs.
