The effect of glass network modifier R2O （R=Li, Na, K） on upconversion luminescence in Er3＋/yb3＋ co-doped NaYF4 oxyfluoride glass-ceramics was investigated. NaYF4 nanocrystals with different sizes were studied und...The effect of glass network modifier R2O （R=Li, Na, K） on upconversion luminescence in Er3＋/yb3＋ co-doped NaYF4 oxyfluoride glass-ceramics was investigated. NaYF4 nanocrystals with different sizes were studied under glass network modifier alkali mental oxide. The nanocrystals size in NaYF4 of Li2O modified samples was 11 nm, whereas in the Na20 and K2O modified sample, the crystal size was 25 and 43 nm, respectively. It was found that red, yellow and green upconversions were observed in SAL, SAN, SAK glass ceramics. The reported results would deepen the understanding of size effects on the lanthanide upcon- version in nanocrystals.展开更多
基金supported by the National Natural Science Foundation of China(61368007,61265004,51272097)the Specialized Research Fund for the Doctoral Program of Higher Education of China(20125314120018)
文摘The effect of glass network modifier R2O （R=Li, Na, K） on upconversion luminescence in Er3＋/yb3＋ co-doped NaYF4 oxyfluoride glass-ceramics was investigated. NaYF4 nanocrystals with different sizes were studied under glass network modifier alkali mental oxide. The nanocrystals size in NaYF4 of Li2O modified samples was 11 nm, whereas in the Na20 and K2O modified sample, the crystal size was 25 and 43 nm, respectively. It was found that red, yellow and green upconversions were observed in SAL, SAN, SAK glass ceramics. The reported results would deepen the understanding of size effects on the lanthanide upcon- version in nanocrystals.