High solid content CO_(2)-based cationic waterborne polyurethanes(CWPUs)were prepared using CO_(2)-polyols as soft segment and Nmethyl diethanolamine(MDEA)as hydrophilic group.The resulting stable aqueous dispersion d...High solid content CO_(2)-based cationic waterborne polyurethanes(CWPUs)were prepared using CO_(2)-polyols as soft segment and Nmethyl diethanolamine(MDEA)as hydrophilic group.The resulting stable aqueous dispersion displayed a high solid content of 52%with a low MDEA loading of 3.52 wt%.This novel structural CWPU can provide excellent adhesive strength,whose T-peel strength could reach 173.48N/5cm,20%higher than that of ester-based cationic waterborne polyurethane(87.55 N/5cm).The CO_(2)-based CWPU film showed only 2 wt%swelling percentage after 240 min immersion in water,and no change was observed during its immersion in 5 wt%sodium hydroxide solution.The tensile strength of CO_(2)-WPUs dropped slowly to 91.2%after 480 min immersion in a 5 wt%sodium hydroxide solution,whereas that of esterbased CWPUs dropped quickly to 32%after 240 min and their mechanical properties were lost after 360 min immersion.Meanwhile,the retention of the tensile strength of the CO_(2)-CWPUs was 81.5%even after 720 min immersion in 10 wt%H_(2)O_(2) solution,while it was only ca.38%for the ester-based CWPUs.These results indicated that the cationic CO_(2)-based CWPU may be promising waterborne adhesive with outstanding ageing resistance due to its synergistic effect from carbonate and ether groups of CO_(2)-polyol structure.展开更多
The microemulsion copolymerizations of acrylic acid (AA),acrylamide (AM),N-methylol acrylamide (NMA),methylmethacrylate (MMA),butyl acrylate (BA) and acrylonitrile (AN) initiated by the redox initiator ammonium persul...The microemulsion copolymerizations of acrylic acid (AA),acrylamide (AM),N-methylol acrylamide (NMA),methylmethacrylate (MMA),butyl acrylate (BA) and acrylonitrile (AN) initiated by the redox initiator ammonium persulfate (APS) and N,N,N′,N′-tetramethylethylenediamine (TMEDA) at ambient temperature were investigated.With this process high solids-content (44.0 wt%) and small (less than 50 nm) particle diameter copolymer latexes were attained.The effects of surfactants,the mechanical stabilities and application properties as an environmentally friendly self-crosslinking pigment printing binder with multifunctional groups were studied.展开更多
Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a referen...Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.展开更多
The high water content of municipal solid waste(MSW)will reduce the effciency of mechanical sorting,consequently unfavorable for beneficial utilization.In this study,a combined hydrolytic-aerobic biodrying technology ...The high water content of municipal solid waste(MSW)will reduce the effciency of mechanical sorting,consequently unfavorable for beneficial utilization.In this study,a combined hydrolytic-aerobic biodrying technology was introduced to remove water from MSW.The total water removals were proved to depend on the ventilation frequency and the temporal span in the hydrolytic stage. The ventilation frequency of 6 times/d was preferable in the hydrolytic stage.The hydrolytic span should not be prolonged more than ...展开更多
The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare th...The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.展开更多
Engineering properties of municipal solid waste （MSW） depend largely on the waste＇s initial compositionand degree of degradation. MSWs in developing countries usually have a high kitchen waste content（called HKWC ...Engineering properties of municipal solid waste （MSW） depend largely on the waste＇s initial compositionand degree of degradation. MSWs in developing countries usually have a high kitchen waste content（called HKWC MSW）. After comparing and analyzing the laboratory and field test results of physicalcomposition, hydraulic properties, gas generation and gas permeability, and mechanical properties forHKWC MSW and low kitchen waste content MSW （called LKWC MSW）, the following findings wereobtained： （1） HKWC MSW has a higher initial water content （IWC） than LKWC MSW, but the field capacitiesof decomposed HKWC and LKWC MSWs are similar; （2） the hydraulic conductivity and gaspermeability for HKWC MSW are both an order of magnitude smaller than those for LKWC MSW; （3）compared with LKWC MSW, HKWC MSW has a higher landfill gas （LFG） generation rate but a shorterduration and a lower potential capacity; （4） the primary compression feature for decomposed HKWCMSW is similar to that of decomposed LKWC MSW, but the compression induced by degradation ofHKWC MSW is greater than that of LKWC MSW; and （5） the shear strength of HKWC MSW changessignificantly with time and strain. Based on the differences of engineering properties between these twokinds of MSWs, the geo-environmental issues in HKWC MSW landfills were analyzed, including highleachate production, high leachate mounds, low LFG collection efficiency, large settlement and slopestability problem, and corresponding advice for the management and design of HKWC MSW landfills wasrecommended.展开更多
基金financially supported by the National Natural Science Foundation of China(No.32071686)。
文摘High solid content CO_(2)-based cationic waterborne polyurethanes(CWPUs)were prepared using CO_(2)-polyols as soft segment and Nmethyl diethanolamine(MDEA)as hydrophilic group.The resulting stable aqueous dispersion displayed a high solid content of 52%with a low MDEA loading of 3.52 wt%.This novel structural CWPU can provide excellent adhesive strength,whose T-peel strength could reach 173.48N/5cm,20%higher than that of ester-based cationic waterborne polyurethane(87.55 N/5cm).The CO_(2)-based CWPU film showed only 2 wt%swelling percentage after 240 min immersion in water,and no change was observed during its immersion in 5 wt%sodium hydroxide solution.The tensile strength of CO_(2)-WPUs dropped slowly to 91.2%after 480 min immersion in a 5 wt%sodium hydroxide solution,whereas that of esterbased CWPUs dropped quickly to 32%after 240 min and their mechanical properties were lost after 360 min immersion.Meanwhile,the retention of the tensile strength of the CO_(2)-CWPUs was 81.5%even after 720 min immersion in 10 wt%H_(2)O_(2) solution,while it was only ca.38%for the ester-based CWPUs.These results indicated that the cationic CO_(2)-based CWPU may be promising waterborne adhesive with outstanding ageing resistance due to its synergistic effect from carbonate and ether groups of CO_(2)-polyol structure.
文摘The microemulsion copolymerizations of acrylic acid (AA),acrylamide (AM),N-methylol acrylamide (NMA),methylmethacrylate (MMA),butyl acrylate (BA) and acrylonitrile (AN) initiated by the redox initiator ammonium persulfate (APS) and N,N,N′,N′-tetramethylethylenediamine (TMEDA) at ambient temperature were investigated.With this process high solids-content (44.0 wt%) and small (less than 50 nm) particle diameter copolymer latexes were attained.The effects of surfactants,the mechanical stabilities and application properties as an environmentally friendly self-crosslinking pigment printing binder with multifunctional groups were studied.
基金Funded by Ministry of Education (No.2006-KL-008),and Qingxin Hanerchem Chemical Technology Co,Ltd.
文摘Stable high-solids-content acrylate emulsion were obtained with a nonionic polymerizable emulsifier allyloxy nonylphenoxy poly （ethyleneoxy） （10） ether （ANPEO10）, and a conventional emulsifier OP-10 as a reference sample. 1H NMR proves that the polymerizable emulsifier ANPEO10 has been incorporated into the resulted acrylate polymers. TEM demonstrates that there are some differences in the particle morphologies. AFM proves that the polymerizable emulsifier ANPEO10 migrating to the surface of the emulsion film was much less than the conventional emulsifier OP-10. The polymerizable emulsifier ANPEO10 can enhance the adhesion with glass plate compared to the conventional emulsifier. Furthermore, with increasing amount of emulsifier, the surface free energy of the films first decreased and then increased, and the adhesion with glass plate is initially enhanced and then attenuated. The water-resistance and solvent-resistance of the films prepared by the polymerizable emulsifier ANPEO10 are superior to those prepared by the conventional emulsifier OP-10.
基金supported by the National Key Technolo-gy R&D Program(No.2006BAC06B04,2006BAC02A03)the Key Grant Project of Shanghai Committee of Science and Technology(No.06dz12308).
文摘The high water content of municipal solid waste(MSW)will reduce the effciency of mechanical sorting,consequently unfavorable for beneficial utilization.In this study,a combined hydrolytic-aerobic biodrying technology was introduced to remove water from MSW.The total water removals were proved to depend on the ventilation frequency and the temporal span in the hydrolytic stage. The ventilation frequency of 6 times/d was preferable in the hydrolytic stage.The hydrolytic span should not be prolonged more than ...
基金This work was supported by the National Natural Science Foundation of China
文摘The seeded semicontinuous emulsion multi-copolymerization of butyl acrylate (BA), 2-ethylhexyl acrylate (2EHA), methyl methacrylate (MMA), 2-hydroxyl propyl acrylate (HOPA) and acrylic acid (AA) was used to prepare the acrylic latexes with high-solid content. The effects of monomer emulsion feed rates (R(a)) and (R/E)(E) values, the ratio of emulsifier amount between the initial charge (R) and the addition monomer emulsion (E), on the polymerization reaction features, the viscosities, surface tensions,particle sizes and particle sizes distributions of latexes, T-g and the insoluble fractions of films, the 180 degrees peel strength, tack and holding power of pressure-sensitive adhesive (PSA) tapes, prepared from the latexes, were studied. Experimental study shows that the grafting and crosslinking fraction in the PSA tapes must be controlled within a suitable range to keep the balance of the 180 degrees peel strength, tack and holding power.
基金Financial support provided by the National Basic Research Program of China(973 Project)(Grant No.2012CB719806)
文摘Engineering properties of municipal solid waste （MSW） depend largely on the waste＇s initial compositionand degree of degradation. MSWs in developing countries usually have a high kitchen waste content（called HKWC MSW）. After comparing and analyzing the laboratory and field test results of physicalcomposition, hydraulic properties, gas generation and gas permeability, and mechanical properties forHKWC MSW and low kitchen waste content MSW （called LKWC MSW）, the following findings wereobtained： （1） HKWC MSW has a higher initial water content （IWC） than LKWC MSW, but the field capacitiesof decomposed HKWC and LKWC MSWs are similar; （2） the hydraulic conductivity and gaspermeability for HKWC MSW are both an order of magnitude smaller than those for LKWC MSW; （3）compared with LKWC MSW, HKWC MSW has a higher landfill gas （LFG） generation rate but a shorterduration and a lower potential capacity; （4） the primary compression feature for decomposed HKWCMSW is similar to that of decomposed LKWC MSW, but the compression induced by degradation ofHKWC MSW is greater than that of LKWC MSW; and （5） the shear strength of HKWC MSW changessignificantly with time and strain. Based on the differences of engineering properties between these twokinds of MSWs, the geo-environmental issues in HKWC MSW landfills were analyzed, including highleachate production, high leachate mounds, low LFG collection efficiency, large settlement and slopestability problem, and corresponding advice for the management and design of HKWC MSW landfills wasrecommended.