NbC ceramic surface-reinforced steel matrix composites were prepared by an in-situ reaction method at different temperatures(1,050℃,1,100℃and 1,150℃)for different times(1 h,2 h and 3 h).The phase constitution,micro...NbC ceramic surface-reinforced steel matrix composites were prepared by an in-situ reaction method at different temperatures(1,050℃,1,100℃and 1,150℃)for different times(1 h,2 h and 3 h).The phase constitution,microstructure and fracture morphology of NbC ceramic surface-reinforced steel matrix composites were analyzed by XRD,SEM and EDS,and the effects of the in-situ reaction temperature and time on the mechanical properties were systematically studied.The results indicate that the NbC reinforcement layer is formed through the reaction between Nb atoms and carbon atoms diffused from the steel matrix to the Nb plate.The thickness of this reinforcement layer increases as the reaction time prolongs.Additionally,an increase in reaction temperature results in a thicker reinforcement layer,although the rate of increase gradually decreases.The relationship among the thickness of the Nb C reinforcement layer,the reaction time and temperature was established by data fitting.The optimal tensile performance is achieved at 1,100℃for 1 h,with a tensile strength of 228 MPa.It is also found that the defects between the reinforcement layer and the steel matrix are related to reaction temperature.At 1,100℃,these defects are minimal.Fracture mostly occurs in the NbC reinforced layer of the composites,and the fracture mode is characterized by typical intergranular brittle fracture.展开更多
Copper azide with high density was successfully synthesized by in-situ reaction of nanoporous copper(NPC)precursor with HN_(3) gaseous.NPC with pore size of about 529 nm has been prepared by electroless plating using ...Copper azide with high density was successfully synthesized by in-situ reaction of nanoporous copper(NPC)precursor with HN_(3) gaseous.NPC with pore size of about 529 nm has been prepared by electroless plating using polystyrene(PS)as templates.The copper shells thickness of NPC was controlled by adjusting the PS loading amount.The effects of copper shell on the morphology,structure and density of copper azide were investigated.The conversion increased from 87.12%to 95.31%when copper shell thickness decrease from 100 to 50 nm.Meanwhile,the density of copper azide prepared by 529 nm NPC for 24 h was up to 2.38 g/cm^(3).The hollow structure of this NPC was filled by swelling of copper azide which guaranteed enough filling volume for keeping the same shape as well as improving the charge density.Moreover,HNS-IV explosive was successfully initiated by copper azide with minimum charge thickness of 0.55 mm,showing that copper azide prepared has excellent initiation performance,which has more advantages in the application of miniaturized explosive systems.展开更多
The(TiNbTaZrHf)C high entropy carbide(HEC)was successfully synthesized by complete commercial transition metal powders,obtained fine sintered bulks without additives by in-situ reaction element synthesis method.(TiNbT...The(TiNbTaZrHf)C high entropy carbide(HEC)was successfully synthesized by complete commercial transition metal powders,obtained fine sintered bulks without additives by in-situ reaction element synthesis method.(TiNbTaZrHf)C bulk shows a face centered cubic rock salt structure with homogeneous single-phase FCC structure in composition and structure.The optimum sintering temperature is about 1900℃at which the best mechanical properties are obtained.The mechanical properties of(TiNbTaZrHf)C ceramic block are better than those of binary transition metal carbides,and it has obvious high entropy effect.Adding a small amount of Al as sintering additive,the mechanical properties of(TiNbTaZrHf)C ceramics continue to improve,the bending strength of the samples at each temperature is increased by at least 38%,and the highest is 486 MPa.The elastic modulus and hardness of the sample at 1900℃are also slightly increased by 4%and 14%,respectively.The above conclusions illustrate that the properties of high entropy ceramics are greatly improved by in-situ reaction sintering.展开更多
The potential of carrying out oxidative desulfurization(ODS) using oxygen as an oxidant was explored in this work. n-Octane firstly reacted with oxygen to produce hydroperoxides in-situ, which were then used as oxidan...The potential of carrying out oxidative desulfurization(ODS) using oxygen as an oxidant was explored in this work. n-Octane firstly reacted with oxygen to produce hydroperoxides in-situ, which were then used as oxidants to oxidize the dibenzothiophene(DBT) in the absence of catalysts. The hydroperoxides generated in-situ were effective in oxidizing DBT to its corresponding dibenzothiophene sulfone(DBTO_2) which was characterized by FT-IR and ~1H-NMR. The removal rate of DBT could reached 98.4% under conditions covering a temperaure of 140℃, a rection duration of 4 h, and an oxygen partial pressure of 0.4 MPa. The influences of different hydrocarbon components in diesel on DBT removal were investigated. The results showed that cyclohexane and n-dodecane had no effect on the removal of DBT, but xylene had a slight negative effect on DBT removal. A possible oxidation mechanism was proposed and the concentration of hydroperoxides in both O_2-oxidized octane and model diesel were detected.展开更多
ZL202 matrix composite reinforced by Al2 Os particles was prepared by combining in-situ reaction and casting techniques. Particles' size in the composites was from 1 to 5microns in diameter. X-ray diffraction anal...ZL202 matrix composite reinforced by Al2 Os particles was prepared by combining in-situ reaction and casting techniques. Particles' size in the composites was from 1 to 5microns in diameter. X-ray diffraction analysis verified that the reinforcing particleswere δ-Al2 O3 which belong to γ-Al2Oa series. The wetting angle between matrix andreinforcement was less than 90°. Energy spectrum analysis indicated that the reactionin bell cover pressing process took place not so completely as in flouring stir process.When the reaction was finished, the matrix was still ZL202 alloy in both processes.展开更多
Systematical experiments were done at five temperature levels: （500 ℃,） （630 ℃,） （900 ℃,） （1 000 ℃） and （1 100 ℃） to illuminate the layer structure of the multi-layered metal-intermetallic composites of...Systematical experiments were done at five temperature levels: （500 ℃,） （630 ℃,） （900 ℃,） （1 000 ℃） and （1 100 ℃） to illuminate the layer structure of the multi-layered metal-intermetallic composites of Ni-Al system that were fabricated by a previously reported simple and cost-effective method. The analysis of back scattering photos and XRD examination of specimens reveal that the look like single compound layer is composed of several different components. The primary phase produced during reaction is Ni2Al3 and there exists a like two-phase field between NiAl3 and Ni2Al3. The high temperature phases like NiAl and Ni3Al are also found at low temperature. The results indicate that the key driving force of in-situ reaction is not temperature, but the atom concentration.展开更多
A novel method was used to fabricate AIN coating on graphite substrate.This approach included two steps:firstly,the emulsion composed of BN and anhydrous ethanol was sprayed on the surface of the graphite substrate;se...A novel method was used to fabricate AIN coating on graphite substrate.This approach included two steps:firstly,the emulsion composed of BN and anhydrous ethanol was sprayed on the surface of the graphite substrate;secondly,AIN coating was formed through the in-situ reaction of Al with the sprayed BN.The reaction was investigated by thermogravimetric-differential thermal analysis(TG-DTA),and the phase composition in the synthetic process was characterized by X-ray diffraction(XRD).Scanning electronic microscopy(SEM)was used to observe the morphology,and electron probe microanalysis(EPMA)was used to observe the distribution of the elements.The experimental results show that the AIN coating is dense and bonded with graphite tightly.展开更多
As a classic in-situ reaction, the Al-TiO_(2) reaction is expected to prepare aluminum matrix composites with high thermal stability.In this study, it was found that the preparation method of ensuring sufficient react...As a classic in-situ reaction, the Al-TiO_(2) reaction is expected to prepare aluminum matrix composites with high thermal stability.In this study, it was found that the preparation method of ensuring sufficient reaction using higher temperatures in previous studies was not conducive to acquiring optimized high-temperature strength. With the increase of hot-pressing temperature and the extension of holding time, the in-situ reaction became more thorough, but the strength of the composites first increased and then decreased. Coarsening of the microstructure at high temperatures would lead to degradation of strength and controlling the in-situ reaction process by the hot-pressing parameters could optimize the mechanical properties of the composites. Strengthening mechanisms at room and high temperatures were studied, and it was found that the load-transfer and Orowan strengthening mechanisms are the main strengthening effects at room temperature, while the pinning effect of fine particles became more crucial at elevated temperatures. As a result, the coarsening of the reinforcing phases was more detrimental to the hightemperature strength. Therefore, an insufficient in-situ reaction led to more excellent mechanical properties, and the composite hot-pressed at 605℃ and held for 2 h exhibited the highest strength, which was 367 MPa at room temperature and 170 MPa at 350℃.展开更多
Thiol-ene click reaction is an intriguing strategy for preparing polymer electrolytes due to its high activity,atom economy and less side reaction.However,the explosive reaction rate and the use of non-electrolytic am...Thiol-ene click reaction is an intriguing strategy for preparing polymer electrolytes due to its high activity,atom economy and less side reaction.However,the explosive reaction rate and the use of non-electrolytic amine catalyst hamper its application in in-situ batteries.Herein,a nitrogen-containing eutectic solution is designed as both the catalyst of the thiol-ene reaction and the plasticizer to in-situ synthesize the gel polymer electrolytes,realizing a mild in-situ gelation process and the preparation of high-performance gel electrolytes.The obtained gel polymer electrolytes exhibit a high ionic conductivity of 4×10^(−4)S cm^(−1)and lithium-ion transference number(t_(Li)^(+))of 0.51 at 60°C.The as-assembled Li/LiFePO_(4)(LFP)cell delivers a high initial discharge capacity of 155.9 mAh g^(-1),and a favorable cycling stability with the capacity retention of 82%after 800 cycles at 1 C is also obtained.In addition,this eutectic solution significantly improves the rate performance of the LFP cell with high specific capacity of 141.5 and 126.8 mAh g^(-1)at 5 C and 10 C,respectively,and the cell can steadily work at various charge–discharge rate for 200 cycles.This powerful and efficient strategy may provide a novel way for in-situ preparing gel polymer electrolytes with desirable comprehensive performances.展开更多
Conservation programs require rigorous evaluation to ensure the preservation of genetic diversity and viability of conservation populations. In this study, we conducted a comparative analysis of two indigenous Chinese...Conservation programs require rigorous evaluation to ensure the preservation of genetic diversity and viability of conservation populations. In this study, we conducted a comparative analysis of two indigenous Chinese chicken breeds, Gushi and Xichuan black-bone, using whole-genome SNPs to understand their genetic diversity, track changes over time and population structure. The breeds were divided into five conservation populations(GS1, 2010, ex-situ;GS2, 2019, ex-situ;GS3, 2019, in-situ;XB1, 2010, in-situ;and XB2, 2019, in-situ) based on conservation methods and generations. The genetic diversity indices of three conservation populations of Gushi chicken showed consistent trends, with the GS3 population under in-situ strategy having the highest diversity and GS2 under ex-situ strategy having the lowest. The degree of inbreeding of GS2 was higher than that of GS1 and GS3. Conserved populations of Xichuan black-bone chicken showed no obvious changes in genetic diversity between XB1 and XB2. In terms of population structure, the GS3 population were stratified relative to GS1 and GS2. According to the conservation priority, GS3 had the highest contribution to the total gene and allelic diversity in GS breed, whereas the contribution of XB1 and XB2 were similar. We also observed that the genetic diversity of GS2 was lower than GS3, which were from the same generation but under different conservation programs(in-situ and ex-situ). While XB1 and XB2 had similar levels of genetic diversity. Overall, our findings suggested that the conservation programs performed in ex-situ could slow down the occurrence of inbreeding events, but could not entirely prevent the loss of genetic diversity when the conserved population size was small, while in-situ conservation populations with large population size could maintain a relative high level of genetic diversity.展开更多
Revealing the localized corrosion process of Mg alloy is considered as one of the most significant ways for improving its corrosion resistance.The reliable monitor should be high distinguishability and real-time in li...Revealing the localized corrosion process of Mg alloy is considered as one of the most significant ways for improving its corrosion resistance.The reliable monitor should be high distinguishability and real-time in liquid environment.Herein,Mg-9Al-1Fe and Mg-9Al-1Fe-1Gd alloys were designed to highlight the impact of intermetallic on the corrosion behaviour.In-situ AFM with a special electrolyte circulation system and quasi-in-situ SEM observation were used to monitor the corrosion process of the designed alloys.SEM-EDS and TEM-SAED were applied to identify the intermetallic in the designed alloys,and their volta potentials were measured by SKPFM.According to the real-time and real-space in-situ AFM monitor,the corrosion process consisted of dissolution of anodicα-Mg phase,accumulation of corrosion products around cathodic phase and shedding of some fine cathodic phase.Then,the localized corrosion process of Mg alloy was revealed combined with the results of the monitor of corrosion process and Volta potential difference.展开更多
The poor stability of RuO_(2)electrocatalysts has been the primary obstacles for their practical application in polymer electrolyte membrane electrolyzers.To dramatically enhance the durability of RuO_(2)to construct ...The poor stability of RuO_(2)electrocatalysts has been the primary obstacles for their practical application in polymer electrolyte membrane electrolyzers.To dramatically enhance the durability of RuO_(2)to construct activity-stability trade-off model is full of significance but challenging.Herein,a single atom Zn stabilized RuO_(2)with enriched oxygen vacancies(SA Zn-RuO_(2))is developed as a promising alternative to iridium oxide for acidic oxygen evolution reaction(OER).Compared with commercial RuO_(2),the enhanced Ru–O bond strength of SA Zn-RuO_(2)by forming Zn-O-Ru local structure motif is favorable to stabilize surface Ru,while the electrons transferred from Zn single atoms to adjacent Ru atoms protects the Ru active sites from overoxidation.Simultaneously,the optimized surrounding electronic structure of Ru sites in SA ZnRuO_(2)decreases the adsorption energies of OER intermediates to reduce the reaction barrier.As a result,the representative SA Zn-RuO_(2)exhibits a low overpotential of 210 mV to achieve 10 mA cm^(-2)and a greatly enhanced durability than commercial RuO_(2).This work provides a promising dual-engineering strategy by coupling single atom doping and vacancy for the tradeoff of high activity and catalytic stability toward acidic OER.展开更多
The shock-induced reaction mechanism and characteristics of Ni/Al system,considering an Al nanoparticle-embedded Ni single crystal,are investigated through molecular dynamics simulation.For the shock melting of Al nan...The shock-induced reaction mechanism and characteristics of Ni/Al system,considering an Al nanoparticle-embedded Ni single crystal,are investigated through molecular dynamics simulation.For the shock melting of Al nanoparticle,interfacial crystallization and dissolution are the main characteristics.The reaction degree of Al particle first increases linearly and then logarithmically with time driven by rapid mechanical mixing and following dissolution.The reaction rate increases with the decrease of particle diameter,however,the reaction is seriously hindered by interfacial crystallization when the diameter is lower than 9 nm in our simulations.Meanwhile,we found a negative exponential growth in the fraction of crystallized Al atoms,and the crystallinity of B2-NiAl(up to 20%)is positively correlated with the specific surface area of Al particle.This can be attributed to the formation mechanism of B2-NiAl by structural evolution of finite mixing layer near the collapsed interface.For shock melting of both Al particle and Ni matrix,the liquid-liquid phase inter-diffusion is the main reaction mechanism that can be enhanced by the formation of internal jet.In addition,the enhanced diffusion is manifested in the logarithmic growth law of mean square displacement,which results in an almost constant reaction rate similar to the mechanical mixing process.展开更多
High efficiency,cost-effective and durable electrocatalysts are of pivotal importance in energy conversion and storage systems.The electro-oxidation of water to oxygen plays a crucial role in such energy conversion te...High efficiency,cost-effective and durable electrocatalysts are of pivotal importance in energy conversion and storage systems.The electro-oxidation of water to oxygen plays a crucial role in such energy conversion technologies.Herein,we report a robust method for the synthesis of a bimetallic alkoxide for efficient oxygen evolution reaction(OER)for alkaline electrolysis,which yields current density of 10 mA cm^(-2)at an overpotential of 215 mV in 0.1 M KOH electrolyte.The catalyst demonstrates an excellent durability for more than 540 h operation with negligible degradation in activity.Raman spectra revealed that the catalyst underwent structure reconstruction during OER,evolving into oxyhydroxide,which was the active site proceeding OER in alkaline electrolyte.In-situ synchrotron X-ray absorption experiment combined with density functional theory calculation suggests a lattice oxygen involved electrocatalytic reaction mechanism for the in-situ generated nickel–iron bimetal-oxyhydroxide catalyst.This mechanism together with the synergy between nickel and iron are responsible for the enhanced catalytic activity and durability.These findings provide promising strategies for the rational design of nonnoble metal OER catalysts.展开更多
Extensive experimental studies have been performed on the Diels-Alder(DA)reactions in ionic liquids(ILs),which demonstrate that the IL environment can significantly influence the reaction rates and selectivity.However...Extensive experimental studies have been performed on the Diels-Alder(DA)reactions in ionic liquids(ILs),which demonstrate that the IL environment can significantly influence the reaction rates and selectivity.However,the underlying microscopic mechanism remains ambiguous.In this work,the multiscale reaction density functional theory is applied to explore the effect of 1-butyl-3-methylimidazolium hexafluorophosphate([BMIM][PF_(6)])solvent on the reaction of cyclopentadiene(CP)with acrolein,methyl acrylate,or acrylonitrile.By analyzing the free energy landscape during the reaction,it is found that the polarization effect has a relatively small influence,while the solvation effect makes both the activation free energy and reaction free energy decrease.In addition,the rearrangement of local solvent structure shows that the cation spatial distribution responds more evidently to the reaction than the anion,and this indicates that the cation plays a dominant role in the solvation effect and so as to affect the reaction rates and selectivity of the DA reactions.展开更多
Hydrogen production by water reduction reactions has received considerable attention because hydrogen is considered a clean-energy carrier,key for a sustainable energy future.Computational methods have been widely use...Hydrogen production by water reduction reactions has received considerable attention because hydrogen is considered a clean-energy carrier,key for a sustainable energy future.Computational methods have been widely used to study the reaction mechanism of the hydrogen evolution reaction(HER),but the calculation results need to be supported by experimental results and direct evidence to confirm the mechanistic insights.In this review,we discuss the fundamental principles of the in situ spectroscopic strategy and a theoretical model for a mechanistic understanding of the HER.In addition,we investigate recent studies by in situ Fourier transform infrared(FTIR),Raman spectroscopy,and X-ray absorption spectroscopy(XAS) and cover new findings that occur at the catalyst-electrolyte interface during HER.These spectroscopic strategies provide practical ways to elucidate catalyst phase,reaction intermediate,catalyst-electrolyte interface,intermediate binding energy,metal valency state,and coordination environment during HER.展开更多
Sluggish storage kinetics is considered as the main bottleneck of cathode materials for fast-charging aqueous zinc-ion batteries(AZIBs).In this report,we propose a novel in-situ self-etching strategy to unlock the Pal...Sluggish storage kinetics is considered as the main bottleneck of cathode materials for fast-charging aqueous zinc-ion batteries(AZIBs).In this report,we propose a novel in-situ self-etching strategy to unlock the Palm tree-like vanadium oxide/carbon nanofiber membrane(P-VO/C)as a robust freestanding electrode.Comprehensive investigations including the finite element simulation,in-situ X-ray diffraction,and in-situ electrochemical impedance spectroscopy disclosed it an electrochemically induced phase transformation mechanism from VO to layered Zn_(x)V_(2)O_5·nH_(2)O,as well as superior storage kinetics with ultrahigh pseudocapacitive contribution.As demonstrated,such electrode can remain a specific capacity of 285 mA h g^(-1)after 100 cycles at 1 A g^(-1),144.4 mA h g^(-1)after 1500 cycles at 30 A g^(-1),and even 97 mA h g^(-1)after 3000 cycles at 60 A g^(-1),respectively.Unexpectedly,an impressive power density of 78.9 kW kg^(-1)at the super-high current density of 100 A g^(-1)also can be achieved.Such design concept of in-situ self-etching free-standing electrode can provide a brand-new insight into extending the pseudocapacitive storage limit,so as to promote the development of high-power energy storage devices including but not limited to AZIBs.展开更多
Titanium matrix composites reinforced with ceramic particles are considered a promising engineering material due to their combination of high specific strength,low density,and high modulus.In this study,the TA15-based...Titanium matrix composites reinforced with ceramic particles are considered a promising engineering material due to their combination of high specific strength,low density,and high modulus.In this study,the TA15-based composites reinforced with a volume fraction of 10% to 25%(TiB+TiC)were prepared using powder metallurgy and casting technique.Microstructural characterization and phase constitution were examined using optical microscopy(OM),scanning electron microscopy(SEM),and X-ray diffraction(XRD).In addition,the microhardness,room temperature(RT)and high temperature(HT)tensile properties of the composites were evaluated.Results revealed that the reinforcements are distributed uniformly even in the composites with a high volume of TiB and TiC.However,as the volume fraction exceeds 15%,TiB and TiC particles become coarsening and exhibit rod-like and dendritic-like morphology.Microhardness increases gradually from 321.2 HV for the base alloy to a maximum of 473.3 HV as the reinforcement increases to 25vol.%.Tensile test results indicate that a reinforcement volume fraction above 20% is beneficial for enhancing tensile strength and yield strength at high temperatures,but it has an adverse effect on room temperature elongation.Conversely,if the reinforcement volume fraction is below 20%,it can improve high-temperature elongation when the temperature exceeds 600℃.展开更多
Transition metal-nitrogen-carbon(M-N-C)as a promising substitute for the conventional noble metalbased catalyst still suffers from low activity and durability for oxygen reduction reaction(ORR)in proton exchange membr...Transition metal-nitrogen-carbon(M-N-C)as a promising substitute for the conventional noble metalbased catalyst still suffers from low activity and durability for oxygen reduction reaction(ORR)in proton exchange membrane fuel cells(PEMFCs).To tackle the issue,herein,a new type of sulfur-doped ironnitrogen-hard carbon(S-Fe-N-HC)nanosheets with high activity and durability in acid media were developed by using a newly synthesized precursor of amide-based polymer with Fe ions based on copolymerizing two monomers of 2,5-thiophene dicarboxylic acid(TDA)as S source and 1,8-diaminonaphthalene(DAN)as N source via an amination reaction.The as-synthesized S-Fe-N-HC features highly dispersed atomic Fe Nxmoieties embedded into rich thiophene-S doped hard carbon nanosheets filled with highly twisted graphite-like microcrystals,which is distinguished from the majority of M-N-C with soft or graphitic carbon structures.These unique characteristics endow S-Fe-N-HC with high ORR activity and outstanding durability in 0.5 M H_(2)SO_(4).Its initial half-wave potential is 0.80 V and the corresponding loss is only 21 m V after 30,000 cycles.Meanwhile,its practical PEMFC performance is a maximum power output of 628.0 mW cm^(-2)and a slight power density loss is 83.0 m W cm^(-2)after 200-cycle practical operation.Additionally,theoretical calculation shows that the activity of Fe Nxmoieties on ORR can be further enhanced by sulfur doping at meta-site near FeN_(4)C.These results evidently demonstrate that the dual effect of hard carbon substrate and S doping derived from the precursor platform of amid-polymers can effectively enhance the activity and durability of Fe-N-C catalysts,providing a new guidance for developing advanced M-N-C catalysts for ORR.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.U20A20235,52171127)Guangdong East Northwest New R&D Institution Construction(No.2019B090905009)+2 种基金Guangdong Aluminum Strip and Foil Processing Enterprise Research Institute(No.2014B090903012)Development and Electrochemical Performance of Magnesium Alloy Anode Material for Battery(No.2020GDASYL-20200103137)Qingyuan Science and Technology Plan Project(No.2021SJXM030)。
文摘NbC ceramic surface-reinforced steel matrix composites were prepared by an in-situ reaction method at different temperatures(1,050℃,1,100℃and 1,150℃)for different times(1 h,2 h and 3 h).The phase constitution,microstructure and fracture morphology of NbC ceramic surface-reinforced steel matrix composites were analyzed by XRD,SEM and EDS,and the effects of the in-situ reaction temperature and time on the mechanical properties were systematically studied.The results indicate that the NbC reinforcement layer is formed through the reaction between Nb atoms and carbon atoms diffused from the steel matrix to the Nb plate.The thickness of this reinforcement layer increases as the reaction time prolongs.Additionally,an increase in reaction temperature results in a thicker reinforcement layer,although the rate of increase gradually decreases.The relationship among the thickness of the Nb C reinforcement layer,the reaction time and temperature was established by data fitting.The optimal tensile performance is achieved at 1,100℃for 1 h,with a tensile strength of 228 MPa.It is also found that the defects between the reinforcement layer and the steel matrix are related to reaction temperature.At 1,100℃,these defects are minimal.Fracture mostly occurs in the NbC reinforced layer of the composites,and the fracture mode is characterized by typical intergranular brittle fracture.
基金the financial support provided by the National Natural Science Foundation of China(No.11872013)。
文摘Copper azide with high density was successfully synthesized by in-situ reaction of nanoporous copper(NPC)precursor with HN_(3) gaseous.NPC with pore size of about 529 nm has been prepared by electroless plating using polystyrene(PS)as templates.The copper shells thickness of NPC was controlled by adjusting the PS loading amount.The effects of copper shell on the morphology,structure and density of copper azide were investigated.The conversion increased from 87.12%to 95.31%when copper shell thickness decrease from 100 to 50 nm.Meanwhile,the density of copper azide prepared by 529 nm NPC for 24 h was up to 2.38 g/cm^(3).The hollow structure of this NPC was filled by swelling of copper azide which guaranteed enough filling volume for keeping the same shape as well as improving the charge density.Moreover,HNS-IV explosive was successfully initiated by copper azide with minimum charge thickness of 0.55 mm,showing that copper azide prepared has excellent initiation performance,which has more advantages in the application of miniaturized explosive systems.
基金Funded by the National Natural Science Foundation of China(Nos.43190311,43200301,and 631800611)。
文摘The(TiNbTaZrHf)C high entropy carbide(HEC)was successfully synthesized by complete commercial transition metal powders,obtained fine sintered bulks without additives by in-situ reaction element synthesis method.(TiNbTaZrHf)C bulk shows a face centered cubic rock salt structure with homogeneous single-phase FCC structure in composition and structure.The optimum sintering temperature is about 1900℃at which the best mechanical properties are obtained.The mechanical properties of(TiNbTaZrHf)C ceramic block are better than those of binary transition metal carbides,and it has obvious high entropy effect.Adding a small amount of Al as sintering additive,the mechanical properties of(TiNbTaZrHf)C ceramics continue to improve,the bending strength of the samples at each temperature is increased by at least 38%,and the highest is 486 MPa.The elastic modulus and hardness of the sample at 1900℃are also slightly increased by 4%and 14%,respectively.The above conclusions illustrate that the properties of high entropy ceramics are greatly improved by in-situ reaction sintering.
基金the Undergraduate Innovation and Entrepreneurship Training Project (201710057009) for providing funding and support for this research
文摘The potential of carrying out oxidative desulfurization(ODS) using oxygen as an oxidant was explored in this work. n-Octane firstly reacted with oxygen to produce hydroperoxides in-situ, which were then used as oxidants to oxidize the dibenzothiophene(DBT) in the absence of catalysts. The hydroperoxides generated in-situ were effective in oxidizing DBT to its corresponding dibenzothiophene sulfone(DBTO_2) which was characterized by FT-IR and ~1H-NMR. The removal rate of DBT could reached 98.4% under conditions covering a temperaure of 140℃, a rection duration of 4 h, and an oxygen partial pressure of 0.4 MPa. The influences of different hydrocarbon components in diesel on DBT removal were investigated. The results showed that cyclohexane and n-dodecane had no effect on the removal of DBT, but xylene had a slight negative effect on DBT removal. A possible oxidation mechanism was proposed and the concentration of hydroperoxides in both O_2-oxidized octane and model diesel were detected.
文摘ZL202 matrix composite reinforced by Al2 Os particles was prepared by combining in-situ reaction and casting techniques. Particles' size in the composites was from 1 to 5microns in diameter. X-ray diffraction analysis verified that the reinforcing particleswere δ-Al2 O3 which belong to γ-Al2Oa series. The wetting angle between matrix andreinforcement was less than 90°. Energy spectrum analysis indicated that the reactionin bell cover pressing process took place not so completely as in flouring stir process.When the reaction was finished, the matrix was still ZL202 alloy in both processes.
文摘Systematical experiments were done at five temperature levels: （500 ℃,） （630 ℃,） （900 ℃,） （1 000 ℃） and （1 100 ℃） to illuminate the layer structure of the multi-layered metal-intermetallic composites of Ni-Al system that were fabricated by a previously reported simple and cost-effective method. The analysis of back scattering photos and XRD examination of specimens reveal that the look like single compound layer is composed of several different components. The primary phase produced during reaction is Ni2Al3 and there exists a like two-phase field between NiAl3 and Ni2Al3. The high temperature phases like NiAl and Ni3Al are also found at low temperature. The results indicate that the key driving force of in-situ reaction is not temperature, but the atom concentration.
基金the New Century Excellent Youth Fund(NCET-04-0722)
文摘A novel method was used to fabricate AIN coating on graphite substrate.This approach included two steps:firstly,the emulsion composed of BN and anhydrous ethanol was sprayed on the surface of the graphite substrate;secondly,AIN coating was formed through the in-situ reaction of Al with the sprayed BN.The reaction was investigated by thermogravimetric-differential thermal analysis(TG-DTA),and the phase composition in the synthetic process was characterized by X-ray diffraction(XRD).Scanning electronic microscopy(SEM)was used to observe the morphology,and electron probe microanalysis(EPMA)was used to observe the distribution of the elements.The experimental results show that the AIN coating is dense and bonded with graphite tightly.
基金supported by the National Key R&D Program of China(Grant No.2021YFA1600704)the National Natural Science Foundation of China(Grant Nos.52203385 and 52171056)+3 种基金CNNC Science Fund for Talented Young Scholarsthe IMR Innovation Fund(Grant No.2021-ZD02)the Natural Science Foundation of Liaoning Province(Grant No.2022-BS-009)Young Elite Scientists Sponsorship Program by CAST(Grant No.YESS20220225)。
文摘As a classic in-situ reaction, the Al-TiO_(2) reaction is expected to prepare aluminum matrix composites with high thermal stability.In this study, it was found that the preparation method of ensuring sufficient reaction using higher temperatures in previous studies was not conducive to acquiring optimized high-temperature strength. With the increase of hot-pressing temperature and the extension of holding time, the in-situ reaction became more thorough, but the strength of the composites first increased and then decreased. Coarsening of the microstructure at high temperatures would lead to degradation of strength and controlling the in-situ reaction process by the hot-pressing parameters could optimize the mechanical properties of the composites. Strengthening mechanisms at room and high temperatures were studied, and it was found that the load-transfer and Orowan strengthening mechanisms are the main strengthening effects at room temperature, while the pinning effect of fine particles became more crucial at elevated temperatures. As a result, the coarsening of the reinforcing phases was more detrimental to the hightemperature strength. Therefore, an insufficient in-situ reaction led to more excellent mechanical properties, and the composite hot-pressed at 605℃ and held for 2 h exhibited the highest strength, which was 367 MPa at room temperature and 170 MPa at 350℃.
基金the National Natural Science Foundation of China(Grant no.51973073)the Fel owship of China Postdoctoral Science Foundation(2021M701303)the analytical and testing assistance from the Analysis and Testing Center of HUST for support of this work
文摘Thiol-ene click reaction is an intriguing strategy for preparing polymer electrolytes due to its high activity,atom economy and less side reaction.However,the explosive reaction rate and the use of non-electrolytic amine catalyst hamper its application in in-situ batteries.Herein,a nitrogen-containing eutectic solution is designed as both the catalyst of the thiol-ene reaction and the plasticizer to in-situ synthesize the gel polymer electrolytes,realizing a mild in-situ gelation process and the preparation of high-performance gel electrolytes.The obtained gel polymer electrolytes exhibit a high ionic conductivity of 4×10^(−4)S cm^(−1)and lithium-ion transference number(t_(Li)^(+))of 0.51 at 60°C.The as-assembled Li/LiFePO_(4)(LFP)cell delivers a high initial discharge capacity of 155.9 mAh g^(-1),and a favorable cycling stability with the capacity retention of 82%after 800 cycles at 1 C is also obtained.In addition,this eutectic solution significantly improves the rate performance of the LFP cell with high specific capacity of 141.5 and 126.8 mAh g^(-1)at 5 C and 10 C,respectively,and the cell can steadily work at various charge–discharge rate for 200 cycles.This powerful and efficient strategy may provide a novel way for in-situ preparing gel polymer electrolytes with desirable comprehensive performances.
基金supported by the Key Research Project of the Shennong Laboratory,Henan Province,China(SN012022-05)the National Natural Science Foundation of China(32272866)+1 种基金the Young Elite Scientists Sponsorship Program by CAST(2021QNRC001)the Starting Foundation for Outstanding Young Scientists of Henan Agricultural University,China(30500664&30501280)。
文摘Conservation programs require rigorous evaluation to ensure the preservation of genetic diversity and viability of conservation populations. In this study, we conducted a comparative analysis of two indigenous Chinese chicken breeds, Gushi and Xichuan black-bone, using whole-genome SNPs to understand their genetic diversity, track changes over time and population structure. The breeds were divided into five conservation populations(GS1, 2010, ex-situ;GS2, 2019, ex-situ;GS3, 2019, in-situ;XB1, 2010, in-situ;and XB2, 2019, in-situ) based on conservation methods and generations. The genetic diversity indices of three conservation populations of Gushi chicken showed consistent trends, with the GS3 population under in-situ strategy having the highest diversity and GS2 under ex-situ strategy having the lowest. The degree of inbreeding of GS2 was higher than that of GS1 and GS3. Conserved populations of Xichuan black-bone chicken showed no obvious changes in genetic diversity between XB1 and XB2. In terms of population structure, the GS3 population were stratified relative to GS1 and GS2. According to the conservation priority, GS3 had the highest contribution to the total gene and allelic diversity in GS breed, whereas the contribution of XB1 and XB2 were similar. We also observed that the genetic diversity of GS2 was lower than GS3, which were from the same generation but under different conservation programs(in-situ and ex-situ). While XB1 and XB2 had similar levels of genetic diversity. Overall, our findings suggested that the conservation programs performed in ex-situ could slow down the occurrence of inbreeding events, but could not entirely prevent the loss of genetic diversity when the conserved population size was small, while in-situ conservation populations with large population size could maintain a relative high level of genetic diversity.
基金support by the National Natural Science Foundation of China(51961026)the Interdisciplinary Innovation Fund of Nanchang University(Project No.2019-9166-27060003).
文摘Revealing the localized corrosion process of Mg alloy is considered as one of the most significant ways for improving its corrosion resistance.The reliable monitor should be high distinguishability and real-time in liquid environment.Herein,Mg-9Al-1Fe and Mg-9Al-1Fe-1Gd alloys were designed to highlight the impact of intermetallic on the corrosion behaviour.In-situ AFM with a special electrolyte circulation system and quasi-in-situ SEM observation were used to monitor the corrosion process of the designed alloys.SEM-EDS and TEM-SAED were applied to identify the intermetallic in the designed alloys,and their volta potentials were measured by SKPFM.According to the real-time and real-space in-situ AFM monitor,the corrosion process consisted of dissolution of anodicα-Mg phase,accumulation of corrosion products around cathodic phase and shedding of some fine cathodic phase.Then,the localized corrosion process of Mg alloy was revealed combined with the results of the monitor of corrosion process and Volta potential difference.
基金supported by the Taishan Scholar Program of Shandong Province,China (tsqn202211162)the National Natural Science Foundation of China (22102079)the Natural Science Foundation of Shandong Province of China (ZR2021YQ10,ZR2022QB163)。
文摘The poor stability of RuO_(2)electrocatalysts has been the primary obstacles for their practical application in polymer electrolyte membrane electrolyzers.To dramatically enhance the durability of RuO_(2)to construct activity-stability trade-off model is full of significance but challenging.Herein,a single atom Zn stabilized RuO_(2)with enriched oxygen vacancies(SA Zn-RuO_(2))is developed as a promising alternative to iridium oxide for acidic oxygen evolution reaction(OER).Compared with commercial RuO_(2),the enhanced Ru–O bond strength of SA Zn-RuO_(2)by forming Zn-O-Ru local structure motif is favorable to stabilize surface Ru,while the electrons transferred from Zn single atoms to adjacent Ru atoms protects the Ru active sites from overoxidation.Simultaneously,the optimized surrounding electronic structure of Ru sites in SA ZnRuO_(2)decreases the adsorption energies of OER intermediates to reduce the reaction barrier.As a result,the representative SA Zn-RuO_(2)exhibits a low overpotential of 210 mV to achieve 10 mA cm^(-2)and a greatly enhanced durability than commercial RuO_(2).This work provides a promising dual-engineering strategy by coupling single atom doping and vacancy for the tradeoff of high activity and catalytic stability toward acidic OER.
基金supported by the State Key Program of National Natural Science Foundation of China(Grant No.12132003)State Key Laboratory of Explosion Science and Technology(Grant No.QNKT20-07)。
文摘The shock-induced reaction mechanism and characteristics of Ni/Al system,considering an Al nanoparticle-embedded Ni single crystal,are investigated through molecular dynamics simulation.For the shock melting of Al nanoparticle,interfacial crystallization and dissolution are the main characteristics.The reaction degree of Al particle first increases linearly and then logarithmically with time driven by rapid mechanical mixing and following dissolution.The reaction rate increases with the decrease of particle diameter,however,the reaction is seriously hindered by interfacial crystallization when the diameter is lower than 9 nm in our simulations.Meanwhile,we found a negative exponential growth in the fraction of crystallized Al atoms,and the crystallinity of B2-NiAl(up to 20%)is positively correlated with the specific surface area of Al particle.This can be attributed to the formation mechanism of B2-NiAl by structural evolution of finite mixing layer near the collapsed interface.For shock melting of both Al particle and Ni matrix,the liquid-liquid phase inter-diffusion is the main reaction mechanism that can be enhanced by the formation of internal jet.In addition,the enhanced diffusion is manifested in the logarithmic growth law of mean square displacement,which results in an almost constant reaction rate similar to the mechanical mixing process.
基金the staff at Beamline (BL08U1-A and BL11B)of the Shanghai Synchrotron Radiation Facility (SSRF)the support from the National Key Research&Development Program of China (2022YFB3803700)+2 种基金the National Natural Science Foundation of China (52171186)the support through the Overseas Outstanding Youth Fund and Shanghai Pujiang Talent Project (21PJ1408500)the financial support from the Center of Hydrogen Science,Shanghai Jiao Tong University。
文摘High efficiency,cost-effective and durable electrocatalysts are of pivotal importance in energy conversion and storage systems.The electro-oxidation of water to oxygen plays a crucial role in such energy conversion technologies.Herein,we report a robust method for the synthesis of a bimetallic alkoxide for efficient oxygen evolution reaction(OER)for alkaline electrolysis,which yields current density of 10 mA cm^(-2)at an overpotential of 215 mV in 0.1 M KOH electrolyte.The catalyst demonstrates an excellent durability for more than 540 h operation with negligible degradation in activity.Raman spectra revealed that the catalyst underwent structure reconstruction during OER,evolving into oxyhydroxide,which was the active site proceeding OER in alkaline electrolyte.In-situ synchrotron X-ray absorption experiment combined with density functional theory calculation suggests a lattice oxygen involved electrocatalytic reaction mechanism for the in-situ generated nickel–iron bimetal-oxyhydroxide catalyst.This mechanism together with the synergy between nickel and iron are responsible for the enhanced catalytic activity and durability.These findings provide promising strategies for the rational design of nonnoble metal OER catalysts.
基金supported by the National Natural Science Foundation of China(22168002,22108070,21878078)the Natural Science Foundation of Guangxi Province(2020GXNSFAA159119)+2 种基金the Dean Project of Guangxi Key Laboratory of Petrochemical Resource Processing and Process Intensification Technology(2021Z012)the Open Fund of the State Key Laboratory of Molecular Reaction Dynamics in DICP(SKLMRD-K202106)the Young Elite Scientists Sponsorship Program by CAST(2022QNRC001)。
文摘Extensive experimental studies have been performed on the Diels-Alder(DA)reactions in ionic liquids(ILs),which demonstrate that the IL environment can significantly influence the reaction rates and selectivity.However,the underlying microscopic mechanism remains ambiguous.In this work,the multiscale reaction density functional theory is applied to explore the effect of 1-butyl-3-methylimidazolium hexafluorophosphate([BMIM][PF_(6)])solvent on the reaction of cyclopentadiene(CP)with acrolein,methyl acrylate,or acrylonitrile.By analyzing the free energy landscape during the reaction,it is found that the polarization effect has a relatively small influence,while the solvation effect makes both the activation free energy and reaction free energy decrease.In addition,the rearrangement of local solvent structure shows that the cation spatial distribution responds more evidently to the reaction than the anion,and this indicates that the cation plays a dominant role in the solvation effect and so as to affect the reaction rates and selectivity of the DA reactions.
基金the immense support provided by the National Research Foundation of Korea(NRF)Grant funded by the Korean Government(MSIT)(RS-2023–00210114)the National R&D Program through the National Research Foundation of Korea(NRF)funded by Ministry of Science and ICT(2021M3D1A2051636)。
文摘Hydrogen production by water reduction reactions has received considerable attention because hydrogen is considered a clean-energy carrier,key for a sustainable energy future.Computational methods have been widely used to study the reaction mechanism of the hydrogen evolution reaction(HER),but the calculation results need to be supported by experimental results and direct evidence to confirm the mechanistic insights.In this review,we discuss the fundamental principles of the in situ spectroscopic strategy and a theoretical model for a mechanistic understanding of the HER.In addition,we investigate recent studies by in situ Fourier transform infrared(FTIR),Raman spectroscopy,and X-ray absorption spectroscopy(XAS) and cover new findings that occur at the catalyst-electrolyte interface during HER.These spectroscopic strategies provide practical ways to elucidate catalyst phase,reaction intermediate,catalyst-electrolyte interface,intermediate binding energy,metal valency state,and coordination environment during HER.
基金financially supported by the Shenzhen Science and Technology Program (JCYJ20200109105805902,JCYJ20220818095805012)the National Natural Science Foundation of China (22208221,22178221,42377487)+2 种基金the Scientific and Technological Plan of Guangdong Province (2019B090905005,2019B090911004)the Natural Science Foundation of Guangdong Province (2021A1515110751)the Guangdong Basic and Applied Basic Research Foundation (2022A1515110477,2021B1515120004)。
文摘Sluggish storage kinetics is considered as the main bottleneck of cathode materials for fast-charging aqueous zinc-ion batteries(AZIBs).In this report,we propose a novel in-situ self-etching strategy to unlock the Palm tree-like vanadium oxide/carbon nanofiber membrane(P-VO/C)as a robust freestanding electrode.Comprehensive investigations including the finite element simulation,in-situ X-ray diffraction,and in-situ electrochemical impedance spectroscopy disclosed it an electrochemically induced phase transformation mechanism from VO to layered Zn_(x)V_(2)O_5·nH_(2)O,as well as superior storage kinetics with ultrahigh pseudocapacitive contribution.As demonstrated,such electrode can remain a specific capacity of 285 mA h g^(-1)after 100 cycles at 1 A g^(-1),144.4 mA h g^(-1)after 1500 cycles at 30 A g^(-1),and even 97 mA h g^(-1)after 3000 cycles at 60 A g^(-1),respectively.Unexpectedly,an impressive power density of 78.9 kW kg^(-1)at the super-high current density of 100 A g^(-1)also can be achieved.Such design concept of in-situ self-etching free-standing electrode can provide a brand-new insight into extending the pseudocapacitive storage limit,so as to promote the development of high-power energy storage devices including but not limited to AZIBs.
基金financially supported by the National Key Research&Development Program of China(Nos.2020YFB2008300,2020YFB2008303)。
文摘Titanium matrix composites reinforced with ceramic particles are considered a promising engineering material due to their combination of high specific strength,low density,and high modulus.In this study,the TA15-based composites reinforced with a volume fraction of 10% to 25%(TiB+TiC)were prepared using powder metallurgy and casting technique.Microstructural characterization and phase constitution were examined using optical microscopy(OM),scanning electron microscopy(SEM),and X-ray diffraction(XRD).In addition,the microhardness,room temperature(RT)and high temperature(HT)tensile properties of the composites were evaluated.Results revealed that the reinforcements are distributed uniformly even in the composites with a high volume of TiB and TiC.However,as the volume fraction exceeds 15%,TiB and TiC particles become coarsening and exhibit rod-like and dendritic-like morphology.Microhardness increases gradually from 321.2 HV for the base alloy to a maximum of 473.3 HV as the reinforcement increases to 25vol.%.Tensile test results indicate that a reinforcement volume fraction above 20% is beneficial for enhancing tensile strength and yield strength at high temperatures,but it has an adverse effect on room temperature elongation.Conversely,if the reinforcement volume fraction is below 20%,it can improve high-temperature elongation when the temperature exceeds 600℃.
基金finically supported by the National Natural Science Foundation of China(22075055)the Guangxi Science and Technology Project(AB16380030)。
文摘Transition metal-nitrogen-carbon(M-N-C)as a promising substitute for the conventional noble metalbased catalyst still suffers from low activity and durability for oxygen reduction reaction(ORR)in proton exchange membrane fuel cells(PEMFCs).To tackle the issue,herein,a new type of sulfur-doped ironnitrogen-hard carbon(S-Fe-N-HC)nanosheets with high activity and durability in acid media were developed by using a newly synthesized precursor of amide-based polymer with Fe ions based on copolymerizing two monomers of 2,5-thiophene dicarboxylic acid(TDA)as S source and 1,8-diaminonaphthalene(DAN)as N source via an amination reaction.The as-synthesized S-Fe-N-HC features highly dispersed atomic Fe Nxmoieties embedded into rich thiophene-S doped hard carbon nanosheets filled with highly twisted graphite-like microcrystals,which is distinguished from the majority of M-N-C with soft or graphitic carbon structures.These unique characteristics endow S-Fe-N-HC with high ORR activity and outstanding durability in 0.5 M H_(2)SO_(4).Its initial half-wave potential is 0.80 V and the corresponding loss is only 21 m V after 30,000 cycles.Meanwhile,its practical PEMFC performance is a maximum power output of 628.0 mW cm^(-2)and a slight power density loss is 83.0 m W cm^(-2)after 200-cycle practical operation.Additionally,theoretical calculation shows that the activity of Fe Nxmoieties on ORR can be further enhanced by sulfur doping at meta-site near FeN_(4)C.These results evidently demonstrate that the dual effect of hard carbon substrate and S doping derived from the precursor platform of amid-polymers can effectively enhance the activity and durability of Fe-N-C catalysts,providing a new guidance for developing advanced M-N-C catalysts for ORR.