Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimen...Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.展开更多
Urea holds promise as an alternative water-oxidation substrate in electrolytic cells.High-valence nickelbased spinel,especially after heteroatom doping,excels in urea oxidation reactions(UOR).However,traditional spine...Urea holds promise as an alternative water-oxidation substrate in electrolytic cells.High-valence nickelbased spinel,especially after heteroatom doping,excels in urea oxidation reactions(UOR).However,traditional spinel synthesis methods with prolonged high-temperature reactions lack kinetic precision,hindering the balance between controlled doping and highly active two-dimensional(2D)porous structures design.This significantly impedes the identification of electron configuration-dependent active sites in doped 2D nickel-based spinels.Herein,we present a microwave shock method for the preparation of 2D porous NiCo_(2)O_(4)spinel.Utilizing the transient on-off property of microwave pulses for precise heteroatom doping and 2D porous structural design,non-metal doping(boron,phosphorus,and sulfur)with distinct extranuclear electron disparities serves as straightforward examples for investigation.Precise tuning of lattice parameter reveals the impact of covalent bond strength on NiCo_(2)O_(4)structural stability.The introduced defect levels induce unpaired d-electrons in transition metals,enhancing the adsorption of electron-donating amino groups in urea molecules.Simultaneously,Bode plots confirm the impact mechanism of rapid electron migration caused by reduced band gaps on UOR activity.The prepared phosphorus-doped 2D porous NiCo_(2)O_(4),with optimal electron configuration control,outperforms most reported spinels.This controlled modification strategy advances understanding theoretical structure-activity mechanisms of high-performance 2D spinels in UOR.展开更多
Augite-based glass ceramics were synthesised using ZnO,FeO,and Fe_(2)O_(3)as additives,and the spinel formation,matrix structure,crystallisation thermodynamics,and physicochemical properties were investigated.The resu...Augite-based glass ceramics were synthesised using ZnO,FeO,and Fe_(2)O_(3)as additives,and the spinel formation,matrix structure,crystallisation thermodynamics,and physicochemical properties were investigated.The results showed that oxides resulted in numerous preliminary spinels in the glass matrix.FeO,ZnO,and Fe_(2)O_(3)influenced the formation of spinel,while FeO simplified the glass network.FeO and ZnO promoted bulk crystallisation of the parent glass.After adding oxides,the grains of augite phase were refined,and the relative quantities of augite crystal planes were also influenced.All samples displayed good mechanical properties and chemical stability.The 2wt%ZnO-doping sample displayed the maximum flexural strength(170.3 MPa).Chromium leaching amount values of all the samples were less than the national standard(1.5 mg/L),confirming the safety of the materials.In conclusion,an appropriate amount of zinc-containing raw material is beneficial for the preparation of augite-based glass ceramics.展开更多
Spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),a 5 V class high voltage cathode,has been regarded as an attractive candidate to further improve the energy density of lithium-ion battery.The issue simultaneously enabling side st...Spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),a 5 V class high voltage cathode,has been regarded as an attractive candidate to further improve the energy density of lithium-ion battery.The issue simultaneously enabling side stability and maintaining high interfacial kinetics,however,has not yet been resolved.Herein,we design a coherent Li_(1.3)A_(l0.3)Ti_(1.7)(PO)_(4)(LATP)layer that is crystally connected to the spinel LNMO host lattices,which offers fast lithium ions transportation as well as enhances the mechanical stability that prevents the particle fracture.Furthermore,the inactive Li_(3)BO_(3)(LBO)coating layer inhibits the corrosion of transition metals and continuous side reactions.Consequently,the coherent-engineered LNMO-LATPLBO cathode material exhibits superior electrochemical cycling stability in a window of 3.0–5.0 V,for example a high-capacity retention that is 89.7%after 500 cycles at 200 m A g-1obtained and enhanced rate performance(85.1 m A h g^(-1)at 800 m A g^(-1))when tested with a LiPF6-based carbonate electrolyte.Our work presents a new approach of engineering 5 V class spinel oxide cathode that combines interfacial coherent crystal lattice design and surface coating.展开更多
Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants co...Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants cold-start capable.In the present study,performance of Co and Ba doped CuCr_2O_4 nanocatalysts prepared by hydrothermal method was evaluated on the decomposition of aqueous ADN solution and ADN liquid monopropellant(LMP103X).The catalysts were characterized by PXRD(Powder X-ray Diffraction),FTIR(Fourier Transform Infrared spectroscopy),SEM(Scanning Electron Microscopy),TEM(Transmission Electron Microscopy),EDS(Energy Dispersive X-ray Spectroscopy),and XPS(X-ray Photoelectron Spectroscopy).The nanosize was confirmed by SEM and TEM,while the nanoflake morphology was confirmed by the SEM analysis.Further,we obtained the elemental composition from the EDS analysis.We investigated the catalytic activity of the catalysts by thermogravimetric(TG)analysis and the developed catalysts lowered the decomposition temperature of ADN monopropellant by about 55℃.The XPS analysis confirmed the presence of metal ions with different chemical states.Apparently,increase in the surface area of the catalysts and the mixed active sites as well as the development of oxygen vacancy on the catalyst surface introduced by metal doping are influencing the decomposition temperature of ADN samples.展开更多
The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable struct...The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable structure and capacity.The LNMO,LiNi_(0.45)Al_(0.05)Mn_(1.5)O_(4)(LNAMO)and LiNi_(0.45)Co_(0.05)Mn_(1.5)O_(4)(LNCMO)were synthesized by calcination at 900℃ for 8 h,which was called as solid-phase method and applied universally in industry.XRD,FT-IR and CV test results showed the synthesized samples have cation disordering Fd-3m space group structures.Moreover,the incorporation of Al and Co increased the cation disordering of LNMO,thereby increasing the transfer rate of Li+.The SEM results showed that the doped samples performed more regular and ortho-octahedral.The EDS elemental analysis confirmed the uniform distribution of each metal element in the samples.Moreover,the doped samples showed better electrochemical properties than undoped LNMO.The LNAMO and LNCMO samples were discharged with specific capacities of 116.3 mA·h·g^(-1)and 122.8 mA·h·g^(-1)at 1 C charge/discharge rate with good capacity retention of 95.8% and 94.8% after 200 cycles at room temperature,respectively.The capacity fading phenomenon of the doped samples at 50℃ and 1 C rate was significantly improved.Further,cations doping also enhanced the rate performance,especially for the LNCMO,the discharge specific capacity of 117.9 mA·h·g^(-1)can be obtained at a rate of 5 C.展开更多
Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(whe...Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(when Al powder addition is 4%,Si powder addition varies:1%and 2%,by mass)as additives.The effects of the Al powder and Si powder additions on the properties and microstructure of the refractories heat treated at different temperatures(1000,1400,and 1600℃for 3 h)were studied.The results show that the Al powder addition can greatly enhance the cold modulus of rupture of the samples fired at 1000 or 1400℃,and meanwhile AlN reinforcement phase forms in the matrix,which greatly improves the hot modulus of rupture of the samples at 1400℃;however,the heat treatment at 1600℃has little influence on the strength;the addition of Al powder and Si powder results in the formation of low melting point phases,greatly reducing the hot modulus of rupture.However,the low melting point phases promote sintering,which enhances the density and the cold modulus of rupture,and decreases the volume change during heating.The samples added with Al and Si all have higher cold modulus of rupture than those added with Al powder only.展开更多
Detailed mineralogical and gemological records were conducted on 340 unheated spinels from the Horana, Eheliyagoda, Ratnapura, and Okkampatiya mining areas in Sri Lanka. The color of Sri Lankan spinel varies greatly: ...Detailed mineralogical and gemological records were conducted on 340 unheated spinels from the Horana, Eheliyagoda, Ratnapura, and Okkampatiya mining areas in Sri Lanka. The color of Sri Lankan spinel varies greatly: in addition to the mainstream pink to purple pink, green and blue can also be seen. Compared with spinel from other regions such as Myanmar, Vietnam, and Tanzania, Sri Lanka's spinel has more abundant inclusions: several mining areas generally have inclusions such as dolomite, apatite, zircon, and chondrodite. Minerals such as graphite and forsterite are also found in spinel produced in the Horana region;graphite and rutile have been found in spinel produced in the Okkamptiya region. Partially healed fissures are most common in spinel in the Okkampatiya mining area;Unlike Vietnamese spinel, dislocations and growth structures are almost absent in Sri Lankan spinel. The LA-ICP-MS analysis results showed that there were no significant differences among the mining areas. LA-ICP-MS analysis of 5 Sri Lankan cobalt blue spinels showed a variation of 11 to 120 ppm in this chromogenic element. The UV visible absorption spectrum results show that Sri Lankan spinel has a combination spectra with variable ratios of the spectral components Cr 3+ , V 3+ and Fe 2+ from pink to red, orange, purple to purple, and blue-green. The results of infrared spectroscopy and laser Raman spectroscopy analysis showed that all samples showed no indications for heat treatment.展开更多
In order to clarify the effect of ultrafine spinel sources on slag resistance and microstructure of alumina-spinel castables,using tabular alumina and spinel as coarse aggregates, tabular alumina powders, spinel powde...In order to clarify the effect of ultrafine spinel sources on slag resistance and microstructure of alumina-spinel castables,using tabular alumina and spinel as coarse aggregates, tabular alumina powders, spinel powders,calcium aluminate cement,spinel containing cement,spinel micro-powder and reactive alumina ultrafines as matrix,alumina-spinel castables used for RH snorkels were prepared by changing the particle size and sources of preformed spinel. The effects of different ultrafine spinel sources( CMA72,spinel micro-powder) on the properties of alumina-spinel castables were investigated. Thermal shock resistance and slag resistance of specimens were compared by the residual strength rate( 1 100 ℃,air cooling 1 cycle) and static crucible method. The microstructure and the slag corrosion resistance mechanism of the specimens were analyzed by SEM and EDS. The result shows that slag resistance of alumina-spinel castables can be improved by adding ultrafine preformed spinel,such as CMA72,and spinel micro-powder. The introduction of ultra-fine preformed spinel has little effect on HMOR of alumina-spinel castables,but has negative effect on TSR. ultra-fine and dispersive preformed spinel in the matrix and fine microstructure are the main reasons for the improvement of slag resistance of castables.展开更多
The feasibility of aluminum recovery from secondary aluminum dross by extraction with NaOH solution and the subsequent synthesis of MgAl_2O_4 spinel by sintering the extracted slag were studied. The extraction percent...The feasibility of aluminum recovery from secondary aluminum dross by extraction with NaOH solution and the subsequent synthesis of MgAl_2O_4 spinel by sintering the extracted slag were studied. The extraction percentage of soluble aluminum from the dross reached 80% at a temperature of 353 K, liquid-to-solid ratio of 12 mL·g^(-1), stirring speed of 300 r·min^(-1), and an extraction time of 15 min; the hydrolysis percentage of AlN reached 40% with an extraction time of 30 min. The activation energies of the soluble aluminum and AlN extracted from the dross were 7.15 and 8.98 kJ·mol^(-1), respectively, indicating that their kinetics were controlled by outer diffusion without a product layer. The extracted slag was sintered in the temperature range 1373–1773 K; MgAl_2O_4 spinel with a compressive strength as high as 69.4 MPa was produced in the sample sintered at 1673 K for 3 h. This value exceeds the threshold(40 MPa) prescribed by the National Standard for the Magnesia and Magnesia-alumina Refractory Bricks of China(GB/T 2275-2007). These results establish the effectiveness of aluminum recovery from secondary aluminum dross and subsequent MgAl_2O_4 spinel synthesis.展开更多
The slag-resistance and microstructural changes after the slag tests of MgAlON spinel containing different amount of nitrogenwere studied by means of crucible slag-resistant experiment, SEM and EDS in the work. The re...The slag-resistance and microstructural changes after the slag tests of MgAlON spinel containing different amount of nitrogenwere studied by means of crucible slag-resistant experiment, SEM and EDS in the work. The results show that the slag-resistance ofMgAlON is dependent on the nitrogen content, and the optimum amount is 2.88%. The strUcture is not changed although the grains havebeen permeated by some silicon, calcium and iron. A glass phase which contained nitrogen formed in the metaInorphic layeL The glasscan driprove the ability of the slag-resistance of MgAlON because of its higher viscosity.展开更多
The stability of chromium in stainless steel slag can be enhanced by increasing the spinel crystal size. The effect of Fe2O3 on the size of spinel crystals in the CaO–SiO2–MgO–Al2O3–Cr2O3 system was investigated u...The stability of chromium in stainless steel slag can be enhanced by increasing the spinel crystal size. The effect of Fe2O3 on the size of spinel crystals in the CaO–SiO2–MgO–Al2O3–Cr2O3 system was investigated using lab experiments carried out in a carbon tube fur-nace. Scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM–EDS) and X-ray diffraction (XRD) were used to ana-lyze the microstructure, components, and the mineral phases of synthetic slags. FactSage 7.1 was used to calculate the crystallization process of the molten slag. The results showed that the addition of Fe2O3 promoted the precipitation of spinel crystals and inhibited the formation of dicalcium silicate. The size of spinel crystals increased from 2.74 to 8.10μm and the contents of chromium and iron in the spinel varied as the Fe2O3 addition was increased from 0 to 20wt%. Fe2O3 thermodynamically provided the spinel-forming components to enhance the for-mation of FeCr2O4, MgFe2O4, and Fe3O4. The addition of Fe2O3 increased the fraction of liquid phase in a certain temperature range and promoted diffusion by decreasing the slag's viscosity. Therefore, Fe2O3 is beneficial to the growth of spinel crystals in stainless steel slag.展开更多
NiCr_2O_4(NCO)spinel composites with different Mn/Ni atomic ratios(Mn/Ni=0.05,0.10,0.15,and 0.20)were synthesized via solid state reaction method.Phase compositions and microstructure of samples were characterized by ...NiCr_2O_4(NCO)spinel composites with different Mn/Ni atomic ratios(Mn/Ni=0.05,0.10,0.15,and 0.20)were synthesized via solid state reaction method.Phase compositions and microstructure of samples were characterized by X-ray diffraction(XRD)and X-ray photoelectron spectroscopy(XPS).The TG-DSC curves showed that the appropriate baking temperature for Mn-doped NCO spinel preparation was approximately 1 320℃.X-ray diffraction patterns exhibited the formation of NCO spinel with Fd-3m space group.Valence state of the Mn ions was determined from 2p and 3s X-ray photoelectron spectra.Manganese ions were mostly in divalent and trivalent states,and the ratio of Mn^(2+)/Mn^(3+)was 0.78-0.98.Fourier transform infrared spectroscopy(FTIR)was used to analyze the spectral emissivity of Mn doped NCO spinel.It was revealed that the infrared emissivity of Mn-doped NCO spinel in 1.8-5μm could be significantly enhanced with increasing content of Mn^(2+),reaching as high as 0.9398.Mn-doped NCO spinel showed excellent radiation performance and good prospect in high emissivity applications in the temperature range of 800-1 200℃.展开更多
The demand for efficient and environmentally-benign electrocatalysts that help availably harness the renewable energy resources is growing rapidly. In recent years, increasing insights into the design of water electro...The demand for efficient and environmentally-benign electrocatalysts that help availably harness the renewable energy resources is growing rapidly. In recent years, increasing insights into the design of water electrolysers, fuel cells, and metal–air batteries emerge in response to the need for developing sustainable energy carriers, in which the oxygen evolution reaction and the oxygen reduction reaction play key roles. However, both reactions suffer from sluggish kinetics that restricts the reactivity. Therefore, it is vital to probe into the structure of the catalysts to exploit high-performance bifunctional oxygen electrocatalysts. Spinel-type catalysts are a class of materials with advantages of versatility, low toxicity, low expense, high abundance, flexible ion arrangement, and multivalence structure. In this review, we afford a basic overview of spinel-type materials and then introduce the relevant theoretical principles for electrocatalytic activity, following that we shed light on the structure–property relationship strategies for spinel-type catalysts including electronic structure, microstructure, phase and composition regulation,and coupling with electrically conductive supports. We elaborate the relationship between structure and property, in order to provide some insights into the design of spinel-type bifunctional oxygen electrocatalysts.展开更多
LiMn_2O_4 and LiNi_xAlyMn_(2-x-y)O_4(x= 0.50;y = 0.05-0.50) powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical charact...LiMn_2O_4 and LiNi_xAlyMn_(2-x-y)O_4(x= 0.50;y = 0.05-0.50) powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis(TG/DTA),X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FT-IR),field-emission scanning electron microscopy(FESEM),transmission electron microscopy(TEM) and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy(EIS) and differential capacity curves(dQ/dE).Finger print XRD patterns of LiMn_2O_4 and LiNi_xAl_yMn_(2-x-y)O_4 fortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth(50nm) with ice-cube surface morphology.TEM images of the spinel LiMn_2O_4 shows the uniform spherical morphology with particle size of(100 nm) while low level of Al-doping spinel(LiNio.5Alo.05Mn1.45O4) displaying cloudy particles with agglomerated particles of(50nm).The LiMn_2O_4 samples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNi_(0.5)Al_(0.05)Mn_(1.45)O_4 delivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle(capacity retention of 92%) over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMn_2O_4 and LiNi_(0.5)Al_(0.05)Mn_(1.45)O_4 depict the high and low real polarization of 1562 and 1100 Ω.展开更多
A PAA sol-gel method, which is based on the chelate effect of PAA polymer, was developed for the synthesis of the spinel LiMn 2O 4 material. The pyrolysis process of the PAA-nitrate mixture precursor was investigated ...A PAA sol-gel method, which is based on the chelate effect of PAA polymer, was developed for the synthesis of the spinel LiMn 2O 4 material. The pyrolysis process of the PAA-nitrate mixture precursor was investigated by TG and DTA analysis. It is found that the structure and electrochemical properties of the material are sensitive to the atmosphere employed in the synthesis process. Preliminary results show that the material thus prepared has a good electrochemical performance even at high charge and discharge current.展开更多
基金the National Natural Science Foundation of China(Nos.52074078 and 52374327)the Applied Fundamental Research Program of Liaoning Province(No.2023JH2/101600002)+2 种基金the Shenyang Young Middle-Aged Scientific and Technological Innovation Talent Support Program(No.RC220491)the Liaoning Province Steel Industry-University-Research Innovation Alliance Cooperation Project of Bensteel Group(No.KJBLM202202)the Fundamental Research Funds for the Central Universities(Nos.N2201023 and N2325009).
文摘Chromium plays a vital role in stainless steel due to its ability to improve the corrosion resistance of the latter.However,the re-lease of chromium from stainless steel slag(SSS)during SSS stockpiling causes detrimental environmental issues.To prevent chromium pollution,the effects of iron oxide on crystallization behavior and spatial distribution of spinel were investigated in this work.The results revealed that FeO was more conducive to the growth of spinels compared with Fe2O3 and Fe3O4.Spinels were found to be mainly distrib-uted at the top and bottom of slag.The amount of spinel phase at the bottom decreased with the increasing FeO content,while that at the top increased.The average particle size of spinel in the slag with 18wt%FeO content was 12.8μm.Meanwhile,no notable structural changes were observed with a further increase in FeO content.In other words,the spatial distribution of spinel changed when the content of iron oxide varied in the range of 8wt%to 18wt%.Finally,less spinel was found at the bottom of slag with a FeO content of 23wt%.
基金financial support from the National Natural Science Foundation of China(52203070)the Open Fund of State Key Laboratory of New Textile Materials and Advanced Processing Technologies(FZ2022005)+2 种基金the Open Fund of Hubei Key Laboratory of Biomass Fiber and Ecological Dyeing and Finishing(STRZ202203)the financial support provided by the China Scholarship Council(CSC)Visiting Scholar Programfinancial support from Institute for Sustainability,Energy and Resources,The University of Adelaide,Future Making Fellowship。
文摘Urea holds promise as an alternative water-oxidation substrate in electrolytic cells.High-valence nickelbased spinel,especially after heteroatom doping,excels in urea oxidation reactions(UOR).However,traditional spinel synthesis methods with prolonged high-temperature reactions lack kinetic precision,hindering the balance between controlled doping and highly active two-dimensional(2D)porous structures design.This significantly impedes the identification of electron configuration-dependent active sites in doped 2D nickel-based spinels.Herein,we present a microwave shock method for the preparation of 2D porous NiCo_(2)O_(4)spinel.Utilizing the transient on-off property of microwave pulses for precise heteroatom doping and 2D porous structural design,non-metal doping(boron,phosphorus,and sulfur)with distinct extranuclear electron disparities serves as straightforward examples for investigation.Precise tuning of lattice parameter reveals the impact of covalent bond strength on NiCo_(2)O_(4)structural stability.The introduced defect levels induce unpaired d-electrons in transition metals,enhancing the adsorption of electron-donating amino groups in urea molecules.Simultaneously,Bode plots confirm the impact mechanism of rapid electron migration caused by reduced band gaps on UOR activity.The prepared phosphorus-doped 2D porous NiCo_(2)O_(4),with optimal electron configuration control,outperforms most reported spinels.This controlled modification strategy advances understanding theoretical structure-activity mechanisms of high-performance 2D spinels in UOR.
基金supported by the National Key R&D Program of China(No.2019YFC1905701)the National Natural Science Foundation of China(Nos.U1960201 and 52204336)the China Postdoctoral Science Foundation(No.2022M710359).
文摘Augite-based glass ceramics were synthesised using ZnO,FeO,and Fe_(2)O_(3)as additives,and the spinel formation,matrix structure,crystallisation thermodynamics,and physicochemical properties were investigated.The results showed that oxides resulted in numerous preliminary spinels in the glass matrix.FeO,ZnO,and Fe_(2)O_(3)influenced the formation of spinel,while FeO simplified the glass network.FeO and ZnO promoted bulk crystallisation of the parent glass.After adding oxides,the grains of augite phase were refined,and the relative quantities of augite crystal planes were also influenced.All samples displayed good mechanical properties and chemical stability.The 2wt%ZnO-doping sample displayed the maximum flexural strength(170.3 MPa).Chromium leaching amount values of all the samples were less than the national standard(1.5 mg/L),confirming the safety of the materials.In conclusion,an appropriate amount of zinc-containing raw material is beneficial for the preparation of augite-based glass ceramics.
基金supported by the Natural Science Foundation of Jiangsu Province(BK20200800)the National Natural Science Foundation of China(22209075,51902165,12004145)+1 种基金the Natural Science Foundation of Jiangxi Province(20212BAB214032,20192ACBL20048)the Key Science and Technology Plan Project of Ji’an City(20211-015311)。
文摘Spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),a 5 V class high voltage cathode,has been regarded as an attractive candidate to further improve the energy density of lithium-ion battery.The issue simultaneously enabling side stability and maintaining high interfacial kinetics,however,has not yet been resolved.Herein,we design a coherent Li_(1.3)A_(l0.3)Ti_(1.7)(PO)_(4)(LATP)layer that is crystally connected to the spinel LNMO host lattices,which offers fast lithium ions transportation as well as enhances the mechanical stability that prevents the particle fracture.Furthermore,the inactive Li_(3)BO_(3)(LBO)coating layer inhibits the corrosion of transition metals and continuous side reactions.Consequently,the coherent-engineered LNMO-LATPLBO cathode material exhibits superior electrochemical cycling stability in a window of 3.0–5.0 V,for example a high-capacity retention that is 89.7%after 500 cycles at 200 m A g-1obtained and enhanced rate performance(85.1 m A h g^(-1)at 800 m A g^(-1))when tested with a LiPF6-based carbonate electrolyte.Our work presents a new approach of engineering 5 V class spinel oxide cathode that combines interfacial coherent crystal lattice design and surface coating.
基金financial support by DST-SERB (Grant No.SRG/2021/001182)DRDO (Grant No.ARMREB/HEM/2021/241)is gratefully acknowledged。
文摘Ammonium dinitramide(ADN)based liquid monopropellants have been identified as environmentally benign substitutes for hydrazine monopropellant.However,new catalysts are to be developed for making ADN monopropellants cold-start capable.In the present study,performance of Co and Ba doped CuCr_2O_4 nanocatalysts prepared by hydrothermal method was evaluated on the decomposition of aqueous ADN solution and ADN liquid monopropellant(LMP103X).The catalysts were characterized by PXRD(Powder X-ray Diffraction),FTIR(Fourier Transform Infrared spectroscopy),SEM(Scanning Electron Microscopy),TEM(Transmission Electron Microscopy),EDS(Energy Dispersive X-ray Spectroscopy),and XPS(X-ray Photoelectron Spectroscopy).The nanosize was confirmed by SEM and TEM,while the nanoflake morphology was confirmed by the SEM analysis.Further,we obtained the elemental composition from the EDS analysis.We investigated the catalytic activity of the catalysts by thermogravimetric(TG)analysis and the developed catalysts lowered the decomposition temperature of ADN monopropellant by about 55℃.The XPS analysis confirmed the presence of metal ions with different chemical states.Apparently,increase in the surface area of the catalysts and the mixed active sites as well as the development of oxygen vacancy on the catalyst surface introduced by metal doping are influencing the decomposition temperature of ADN samples.
基金supported by the National Natural Science Foundation of China(52022109 and 51834008)Beijing Municipal Natural Science Foundation(2202047)+1 种基金National Key Research and Development Program of China(2021YFC2901100)Science Foundation of China University of Petroleum,Beijing(2462021QNX2010,2462020YXZZ019,2462020YXZZ016,and 2462022QZDX008)。
文摘The poor structural stability and capacity retention of the high-voltage spinel-type LiNi_(0.5)Mn_(1.5)O_(4)(LNMO)limits their further application.Herein,Al and Co were doped in LNMO materials for a more stable structure and capacity.The LNMO,LiNi_(0.45)Al_(0.05)Mn_(1.5)O_(4)(LNAMO)and LiNi_(0.45)Co_(0.05)Mn_(1.5)O_(4)(LNCMO)were synthesized by calcination at 900℃ for 8 h,which was called as solid-phase method and applied universally in industry.XRD,FT-IR and CV test results showed the synthesized samples have cation disordering Fd-3m space group structures.Moreover,the incorporation of Al and Co increased the cation disordering of LNMO,thereby increasing the transfer rate of Li+.The SEM results showed that the doped samples performed more regular and ortho-octahedral.The EDS elemental analysis confirmed the uniform distribution of each metal element in the samples.Moreover,the doped samples showed better electrochemical properties than undoped LNMO.The LNAMO and LNCMO samples were discharged with specific capacities of 116.3 mA·h·g^(-1)and 122.8 mA·h·g^(-1)at 1 C charge/discharge rate with good capacity retention of 95.8% and 94.8% after 200 cycles at room temperature,respectively.The capacity fading phenomenon of the doped samples at 50℃ and 1 C rate was significantly improved.Further,cations doping also enhanced the rate performance,especially for the LNCMO,the discharge specific capacity of 117.9 mA·h·g^(-1)can be obtained at a rate of 5 C.
文摘Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(when Al powder addition is 4%,Si powder addition varies:1%and 2%,by mass)as additives.The effects of the Al powder and Si powder additions on the properties and microstructure of the refractories heat treated at different temperatures(1000,1400,and 1600℃for 3 h)were studied.The results show that the Al powder addition can greatly enhance the cold modulus of rupture of the samples fired at 1000 or 1400℃,and meanwhile AlN reinforcement phase forms in the matrix,which greatly improves the hot modulus of rupture of the samples at 1400℃;however,the heat treatment at 1600℃has little influence on the strength;the addition of Al powder and Si powder results in the formation of low melting point phases,greatly reducing the hot modulus of rupture.However,the low melting point phases promote sintering,which enhances the density and the cold modulus of rupture,and decreases the volume change during heating.The samples added with Al and Si all have higher cold modulus of rupture than those added with Al powder only.
文摘Detailed mineralogical and gemological records were conducted on 340 unheated spinels from the Horana, Eheliyagoda, Ratnapura, and Okkampatiya mining areas in Sri Lanka. The color of Sri Lankan spinel varies greatly: in addition to the mainstream pink to purple pink, green and blue can also be seen. Compared with spinel from other regions such as Myanmar, Vietnam, and Tanzania, Sri Lanka's spinel has more abundant inclusions: several mining areas generally have inclusions such as dolomite, apatite, zircon, and chondrodite. Minerals such as graphite and forsterite are also found in spinel produced in the Horana region;graphite and rutile have been found in spinel produced in the Okkamptiya region. Partially healed fissures are most common in spinel in the Okkampatiya mining area;Unlike Vietnamese spinel, dislocations and growth structures are almost absent in Sri Lankan spinel. The LA-ICP-MS analysis results showed that there were no significant differences among the mining areas. LA-ICP-MS analysis of 5 Sri Lankan cobalt blue spinels showed a variation of 11 to 120 ppm in this chromogenic element. The UV visible absorption spectrum results show that Sri Lankan spinel has a combination spectra with variable ratios of the spectral components Cr 3+ , V 3+ and Fe 2+ from pink to red, orange, purple to purple, and blue-green. The results of infrared spectroscopy and laser Raman spectroscopy analysis showed that all samples showed no indications for heat treatment.
基金the financial support from the National Natural Science Foundation of China(Grant no.51402089)the Science and Technology Research Planning Project of Henan Province(Project No.162102210206)the Plan of Young-backbone Teachers of Colleges and Universities in Henan Province(Project No.2015GGJS-045)
文摘In order to clarify the effect of ultrafine spinel sources on slag resistance and microstructure of alumina-spinel castables,using tabular alumina and spinel as coarse aggregates, tabular alumina powders, spinel powders,calcium aluminate cement,spinel containing cement,spinel micro-powder and reactive alumina ultrafines as matrix,alumina-spinel castables used for RH snorkels were prepared by changing the particle size and sources of preformed spinel. The effects of different ultrafine spinel sources( CMA72,spinel micro-powder) on the properties of alumina-spinel castables were investigated. Thermal shock resistance and slag resistance of specimens were compared by the residual strength rate( 1 100 ℃,air cooling 1 cycle) and static crucible method. The microstructure and the slag corrosion resistance mechanism of the specimens were analyzed by SEM and EDS. The result shows that slag resistance of alumina-spinel castables can be improved by adding ultrafine preformed spinel,such as CMA72,and spinel micro-powder. The introduction of ultra-fine preformed spinel has little effect on HMOR of alumina-spinel castables,but has negative effect on TSR. ultra-fine and dispersive preformed spinel in the matrix and fine microstructure are the main reasons for the improvement of slag resistance of castables.
基金financially supported by the National Natural Science Foundation of China (No. 21577176)the Environment Protection Scientific Research Project of Hunan Province, China (No. [2016]59-3)
文摘The feasibility of aluminum recovery from secondary aluminum dross by extraction with NaOH solution and the subsequent synthesis of MgAl_2O_4 spinel by sintering the extracted slag were studied. The extraction percentage of soluble aluminum from the dross reached 80% at a temperature of 353 K, liquid-to-solid ratio of 12 mL·g^(-1), stirring speed of 300 r·min^(-1), and an extraction time of 15 min; the hydrolysis percentage of AlN reached 40% with an extraction time of 30 min. The activation energies of the soluble aluminum and AlN extracted from the dross were 7.15 and 8.98 kJ·mol^(-1), respectively, indicating that their kinetics were controlled by outer diffusion without a product layer. The extracted slag was sintered in the temperature range 1373–1773 K; MgAl_2O_4 spinel with a compressive strength as high as 69.4 MPa was produced in the sample sintered at 1673 K for 3 h. This value exceeds the threshold(40 MPa) prescribed by the National Standard for the Magnesia and Magnesia-alumina Refractory Bricks of China(GB/T 2275-2007). These results establish the effectiveness of aluminum recovery from secondary aluminum dross and subsequent MgAl_2O_4 spinel synthesis.
文摘The slag-resistance and microstructural changes after the slag tests of MgAlON spinel containing different amount of nitrogenwere studied by means of crucible slag-resistant experiment, SEM and EDS in the work. The results show that the slag-resistance ofMgAlON is dependent on the nitrogen content, and the optimum amount is 2.88%. The strUcture is not changed although the grains havebeen permeated by some silicon, calcium and iron. A glass phase which contained nitrogen formed in the metaInorphic layeL The glasscan driprove the ability of the slag-resistance of MgAlON because of its higher viscosity.
基金financially supported by the National Natural Science Foundation of China (No. 51404173)Hubei Provincial Natural Science Foundation (No. 2016CFB579)+1 种基金China Postdoctoral Science Foundation (No. 2014M562073)State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology
文摘The stability of chromium in stainless steel slag can be enhanced by increasing the spinel crystal size. The effect of Fe2O3 on the size of spinel crystals in the CaO–SiO2–MgO–Al2O3–Cr2O3 system was investigated using lab experiments carried out in a carbon tube fur-nace. Scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM–EDS) and X-ray diffraction (XRD) were used to ana-lyze the microstructure, components, and the mineral phases of synthetic slags. FactSage 7.1 was used to calculate the crystallization process of the molten slag. The results showed that the addition of Fe2O3 promoted the precipitation of spinel crystals and inhibited the formation of dicalcium silicate. The size of spinel crystals increased from 2.74 to 8.10μm and the contents of chromium and iron in the spinel varied as the Fe2O3 addition was increased from 0 to 20wt%. Fe2O3 thermodynamically provided the spinel-forming components to enhance the for-mation of FeCr2O4, MgFe2O4, and Fe3O4. The addition of Fe2O3 increased the fraction of liquid phase in a certain temperature range and promoted diffusion by decreasing the slag's viscosity. Therefore, Fe2O3 is beneficial to the growth of spinel crystals in stainless steel slag.
基金Funded by the Scientific and Technological Research Projects for Education Department of Hubei Province(Q20161407)
文摘NiCr_2O_4(NCO)spinel composites with different Mn/Ni atomic ratios(Mn/Ni=0.05,0.10,0.15,and 0.20)were synthesized via solid state reaction method.Phase compositions and microstructure of samples were characterized by X-ray diffraction(XRD)and X-ray photoelectron spectroscopy(XPS).The TG-DSC curves showed that the appropriate baking temperature for Mn-doped NCO spinel preparation was approximately 1 320℃.X-ray diffraction patterns exhibited the formation of NCO spinel with Fd-3m space group.Valence state of the Mn ions was determined from 2p and 3s X-ray photoelectron spectra.Manganese ions were mostly in divalent and trivalent states,and the ratio of Mn^(2+)/Mn^(3+)was 0.78-0.98.Fourier transform infrared spectroscopy(FTIR)was used to analyze the spectral emissivity of Mn doped NCO spinel.It was revealed that the infrared emissivity of Mn-doped NCO spinel in 1.8-5μm could be significantly enhanced with increasing content of Mn^(2+),reaching as high as 0.9398.Mn-doped NCO spinel showed excellent radiation performance and good prospect in high emissivity applications in the temperature range of 800-1 200℃.
基金supported by the Natural Scientific Foundation of China (21825501)National Key Research and Development Program (2016YFA0202500 and 2016YFA0200102)+1 种基金Australian Research Council (DP160103107, FT170100224)Tsinghua University Initiative Scientific Research Program。
文摘The demand for efficient and environmentally-benign electrocatalysts that help availably harness the renewable energy resources is growing rapidly. In recent years, increasing insights into the design of water electrolysers, fuel cells, and metal–air batteries emerge in response to the need for developing sustainable energy carriers, in which the oxygen evolution reaction and the oxygen reduction reaction play key roles. However, both reactions suffer from sluggish kinetics that restricts the reactivity. Therefore, it is vital to probe into the structure of the catalysts to exploit high-performance bifunctional oxygen electrocatalysts. Spinel-type catalysts are a class of materials with advantages of versatility, low toxicity, low expense, high abundance, flexible ion arrangement, and multivalence structure. In this review, we afford a basic overview of spinel-type materials and then introduce the relevant theoretical principles for electrocatalytic activity, following that we shed light on the structure–property relationship strategies for spinel-type catalysts including electronic structure, microstructure, phase and composition regulation,and coupling with electrically conductive supports. We elaborate the relationship between structure and property, in order to provide some insights into the design of spinel-type bifunctional oxygen electrocatalysts.
基金support given under the "Brain Pool Program of the Korean Federation of Science and Technology Societies" (KOFST), Republic of South Koreasupported by the Human Resources Development Program (No. 20124010203270) of the Korea Institute of Energy Technology EvaluationPlanning (KETEP) grant funded by the Korea Government Ministry of Trade, Industry and Energy
文摘LiMn_2O_4 and LiNi_xAlyMn_(2-x-y)O_4(x= 0.50;y = 0.05-0.50) powders have been synthesized via facile solgel method using Behenic acid as active cheiating agent.The synthesized samples are subjected to physical characterizations such as thermo gravimetric analysis(TG/DTA),X-ray diffraction(XRD),Fourier transform infrared spectroscopy(FT-IR),field-emission scanning electron microscopy(FESEM),transmission electron microscopy(TEM) and electrochemical studies viz.,galvanostatic cycling properties,electrochemical impedance spectroscopy(EIS) and differential capacity curves(dQ/dE).Finger print XRD patterns of LiMn_2O_4 and LiNi_xAl_yMn_(2-x-y)O_4 fortify the high degree of crystallinity with better phase purity.FESEM images of the undoped pristine spinel illustrate uniform spherical grains surface morphology with an average particle size of 0.5 μm while Ni doped particles depict the spherical grains growth(50nm) with ice-cube surface morphology.TEM images of the spinel LiMn_2O_4 shows the uniform spherical morphology with particle size of(100 nm) while low level of Al-doping spinel(LiNio.5Alo.05Mn1.45O4) displaying cloudy particles with agglomerated particles of(50nm).The LiMn_2O_4 samples calcined at 850℃ deliver the discharge capacity of 130 mAh/g in the first cycle corresponds to 94%coiumbic efficiency with capacity fade of 1.5 mAh/g/cycle over the investigated 10 cycles.Among all four dopant compositions investigated,LiNi_(0.5)Al_(0.05)Mn_(1.45)O_4 delivers the maximum discharge capacity of 126 mAh/g during the first cycle and shows the stable cycling performance with low capacity fade of 1 mAh/g/cycle(capacity retention of 92%) over the investigated 10 cycles.Electrochemical impedance studies of spinel LiMn_2O_4 and LiNi_(0.5)Al_(0.05)Mn_(1.45)O_4 depict the high and low real polarization of 1562 and 1100 Ω.
基金Supported by the National Science Foundation of China( No.2 98330 90 )
文摘A PAA sol-gel method, which is based on the chelate effect of PAA polymer, was developed for the synthesis of the spinel LiMn 2O 4 material. The pyrolysis process of the PAA-nitrate mixture precursor was investigated by TG and DTA analysis. It is found that the structure and electrochemical properties of the material are sensitive to the atmosphere employed in the synthesis process. Preliminary results show that the material thus prepared has a good electrochemical performance even at high charge and discharge current.