We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner ...We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.展开更多
Waste solid propylene oxide sludge （POS） and fly ash were used as main raw material to prepare propylene oxide sludge aggregate （POSA） under the condition of autoclaved （180 ℃,1.0 MPa） curing. Three different t...Waste solid propylene oxide sludge （POS） and fly ash were used as main raw material to prepare propylene oxide sludge aggregate （POSA） under the condition of autoclaved （180 ℃,1.0 MPa） curing. Three different test methods namely cylinder compressive strength （CCS）, individual aggregate compressive strength （IACS） and strength contribution rate （SCR） proposed were used to characterize the mechanical properties of the autoclaved POSA. POS shell-aggregate with SCR of 94% were prepared under the hydrothermal synthesis and autoclaved curing. The experimental results indicate that CCS and IACS have good consistency in characterizing mechanical properties of POSA. It is suggested that SCR not only can characterize the strength of POSA core, but also can reflect the effect of shell on the performance of POSA. By means of least square method, relationships between CCS and IACS, CCS and SCR, IACS and SCR were deduced.展开更多
基金Funded by the"863"National High-tech Research and Development Program of China(No.2012AA06A112)
文摘We experimentally studied the interaction between pozzolanic material（fly ash） and dehydrated autoclaved aerated concrete（DAAC）. The DAAC powder was obtained by grinding aerated concrete waste to particles fi ner than 75μm and was then heated to temperatures up to 900 ℃. New cementitious material was prepared by proportioning fly ash and DAAC, named as AF. X-ray diffraction（XRD） was employed to identify the crystalline phases of DAAC before and after rehydration. The hydration process of AF was analyzed by the heat of hydration and non-evaporable water content（Wn）. The experimental results show that the highest reactivity of DAAC can be obtained by calcining the powder at 700 ℃ and the dehydrated products are mainly β-C2 S and CaO. The cumulative heat of hydration and Wn was found to be strongly dependent on the replacement level of fl y ash, increasing the replacement level of fl y ash lowered them in AF. The strength contribution rates on pozzolanic effect of fl y ash in AF are always negative, showing a contrary tendency of that of cement-fl y ash system.
基金Funded by the National Natural Science Fundation of China(51061015)the scientific Research Program of Jiangsu Economic Information Committee+1 种基金the Program for Postgraduates Research Innovation in University of Jiangsu Province (CX10B_122Z)the Science and Technology Project of Jiangsu Province Construction System (JS2010JH22)
文摘Waste solid propylene oxide sludge （POS） and fly ash were used as main raw material to prepare propylene oxide sludge aggregate （POSA） under the condition of autoclaved （180 ℃,1.0 MPa） curing. Three different test methods namely cylinder compressive strength （CCS）, individual aggregate compressive strength （IACS） and strength contribution rate （SCR） proposed were used to characterize the mechanical properties of the autoclaved POSA. POS shell-aggregate with SCR of 94% were prepared under the hydrothermal synthesis and autoclaved curing. The experimental results indicate that CCS and IACS have good consistency in characterizing mechanical properties of POSA. It is suggested that SCR not only can characterize the strength of POSA core, but also can reflect the effect of shell on the performance of POSA. By means of least square method, relationships between CCS and IACS, CCS and SCR, IACS and SCR were deduced.