In this paper, Ni-based alloy composite coating reinforced by Ti （C, N） particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means ...In this paper, Ni-based alloy composite coating reinforced by Ti （C, N） particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means of optical microscopy （OM）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The wear resistance test of the coating was evaluated using an M-2000 tester. The results showed that the Ni-based composite coating had an ability of rapid solidification to form dendritic crystals microstructure consisting of Ti （ C, N） particulates uniformly distributed in the matrix. It was found that some Ti（ C,N） particles are similar to be round in shape, and the others are irregular. Laser cladding layer reinforced by Ti（ C, N） particulates was found to possess good wear resistance property.展开更多
A series of CoCrFeNb_xNi（x values in molar ratio, x = 0, 0.25, 0.45, 0.5, 0.75, 1.0 and 1.2） high entropy alloys（HEAs） was prepared to investigate the alloying effect of Nb on the microstructures and mechanical pr...A series of CoCrFeNb_xNi（x values in molar ratio, x = 0, 0.25, 0.45, 0.5, 0.75, 1.0 and 1.2） high entropy alloys（HEAs） was prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties. The results indicate that the prepared CoCrFeNb_xNi（x 〉 0） HEAs consist of a simple FCC solid solution phase and a Laves phase. The microstructures of the alloys change from an initial single-phase FCC solid solution structure（x = 0） to a hypoeutectic microstructure（x = 0.25）, then to a full eutectic microstructure（x = 0.45） and finally to a hypereutectic microstructure（0.5 〈 x 〈 1.2）. The compressive test results show that the Nb0.45（x = 0.45） alloy with a full eutectic microstructure possesses the highest compressive fracture strength of 2558 MPa and a fracture strain of 27.9%. The CoCrFeNi alloy exhibits an excellent compressive ductility, which can reach 50% height reduction without fracture. The Nb0.25 alloy with a hypoeutectic structure exhibits a larger plastic strain of 34.8%. With the increase of Nb content, increased hard/brittle Laves phase leads to a decrease of the plasticity and increases of the Vickers hardness and the wear resistance. The wear mass loss, width and depth of wear scar of the Nb1.2（x = 1.2） alloy with a hypereutectic structure are the lowest among all alloy systems, indicating that the wear resistance of the Nb1.2 alloy is the best one.展开更多
文摘In this paper, Ni-based alloy composite coating reinforced by Ti （C, N） particles was fabricated on the mild steel through laser cladding technology. The microstrncture of laser cladding layer was analyzed by means of optical microscopy （OM）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The wear resistance test of the coating was evaluated using an M-2000 tester. The results showed that the Ni-based composite coating had an ability of rapid solidification to form dendritic crystals microstructure consisting of Ti （ C, N） particulates uniformly distributed in the matrix. It was found that some Ti（ C,N） particles are similar to be round in shape, and the others are irregular. Laser cladding layer reinforced by Ti（ C, N） particulates was found to possess good wear resistance property.
基金supported by the National Natural Science Foundation of China (Nos. 51134013, and 51471044)funds for the central universities, key laboratory of basic research projects of Liaoning Province Department of Education (No. LZ2014007)the Natural Science Foundation of Liaoning Province (No. 2014028013)
文摘A series of CoCrFeNb_xNi（x values in molar ratio, x = 0, 0.25, 0.45, 0.5, 0.75, 1.0 and 1.2） high entropy alloys（HEAs） was prepared to investigate the alloying effect of Nb on the microstructures and mechanical properties. The results indicate that the prepared CoCrFeNb_xNi（x 〉 0） HEAs consist of a simple FCC solid solution phase and a Laves phase. The microstructures of the alloys change from an initial single-phase FCC solid solution structure（x = 0） to a hypoeutectic microstructure（x = 0.25）, then to a full eutectic microstructure（x = 0.45） and finally to a hypereutectic microstructure（0.5 〈 x 〈 1.2）. The compressive test results show that the Nb0.45（x = 0.45） alloy with a full eutectic microstructure possesses the highest compressive fracture strength of 2558 MPa and a fracture strain of 27.9%. The CoCrFeNi alloy exhibits an excellent compressive ductility, which can reach 50% height reduction without fracture. The Nb0.25 alloy with a hypoeutectic structure exhibits a larger plastic strain of 34.8%. With the increase of Nb content, increased hard/brittle Laves phase leads to a decrease of the plasticity and increases of the Vickers hardness and the wear resistance. The wear mass loss, width and depth of wear scar of the Nb1.2（x = 1.2） alloy with a hypereutectic structure are the lowest among all alloy systems, indicating that the wear resistance of the Nb1.2 alloy is the best one.