An integrated low-temperature nitriding process was carried out for Ti6Al4V to investigateitseffect on microstructure and properties.The process was designed to enhance the nitriding kinetics in low-temperature（500℃...An integrated low-temperature nitriding process was carried out for Ti6Al4V to investigateitseffect on microstructure and properties.The process was designed to enhance the nitriding kinetics in low-temperature（500℃） nitriding by deformation, and to strengthen Ti6Al4V alloybydispersionat the same time. Specimens of Ti6Al4V alloyweretreated through the process of solid solutionstrengthening-cold deformation-nitriding at 500℃. The white nitriding layeris formed after some time and then kept stable, changing little withthedeformationdegreeand time. The effect of aging on substrate is significant. Surface hardness and substrate hardnessincrease with deformation increasing. The construction was investigated by XRD.The surface nitridesare TiN, Ti2N, Ti4N3-Xand Ti3N1.29,and thenitridesin cross-section are Ti3N1.29and TiN0.3. The wear tests of specimens after nitriding, aging and deformation were carried out,andthetest data show that the nitrided pieces have the best wear resistance.展开更多
基金Projects(51275105,51375106)supported by the National Natural Science Foundation of China
文摘An integrated low-temperature nitriding process was carried out for Ti6Al4V to investigateitseffect on microstructure and properties.The process was designed to enhance the nitriding kinetics in low-temperature（500℃） nitriding by deformation, and to strengthen Ti6Al4V alloybydispersionat the same time. Specimens of Ti6Al4V alloyweretreated through the process of solid solutionstrengthening-cold deformation-nitriding at 500℃. The white nitriding layeris formed after some time and then kept stable, changing little withthedeformationdegreeand time. The effect of aging on substrate is significant. Surface hardness and substrate hardnessincrease with deformation increasing. The construction was investigated by XRD.The surface nitridesare TiN, Ti2N, Ti4N3-Xand Ti3N1.29,and thenitridesin cross-section are Ti3N1.29and TiN0.3. The wear tests of specimens after nitriding, aging and deformation were carried out,andthetest data show that the nitrided pieces have the best wear resistance.