基于耦合模理论利用传输矩阵法研究级联长周期光纤光栅(Cascaded Long Period Fiber Gratings, CLPG)的光谱特性。结果表明:选用两个参数相近的长周期光纤光栅(Long Period Fiber Gratings, LPG)级联可以获得更明显的透射谱。周期的增...基于耦合模理论利用传输矩阵法研究级联长周期光纤光栅(Cascaded Long Period Fiber Gratings, CLPG)的光谱特性。结果表明:选用两个参数相近的长周期光纤光栅(Long Period Fiber Gratings, LPG)级联可以获得更明显的透射谱。周期的增加导致损耗峰向长波方向线性漂移,可据此实现对特定波长的损耗。长度和折射率调制深度主要影响损耗峰深度,可以用于调控损耗峰出现极深值点。得到当两个级联LPG的周期为500 μm、长度为3 cm,折射率调制深度为0.00014时存在窄而深的最优CLPG损耗峰。该研究结论为分析级联长周期光纤光栅理论和改进传感器件设计应用提供了依据。展开更多
There are an absorption peak at 485 nm and a synchronous fluorescence peak at 510 nm for fluorescein in the medium of 3.4×10 -3 mol/L tri-sodium citrate. The gold nanoparticle system exhibits a characterization r...There are an absorption peak at 485 nm and a synchronous fluorescence peak at 510 nm for fluorescein in the medium of 3.4×10 -3 mol/L tri-sodium citrate. The gold nanoparticle system exhibits a characterization resonance scattering peak at 580 nm. In the coexisting system of gold nanoparticle and fluorescein, there are a synchronous fluorescence peak at 510 nm and a resonance scattering peak at 580 nm. It has been found that the fluorescence peak may be quenched by gold nanoparticle. When the concentration of fluorescein is higher, the A 470 nm affects the I 470 nm of gold nanoparticle. The I 470 nm decreases exponentially with the concentration of fluorescein.展开更多
文摘基于耦合模理论利用传输矩阵法研究级联长周期光纤光栅(Cascaded Long Period Fiber Gratings, CLPG)的光谱特性。结果表明:选用两个参数相近的长周期光纤光栅(Long Period Fiber Gratings, LPG)级联可以获得更明显的透射谱。周期的增加导致损耗峰向长波方向线性漂移,可据此实现对特定波长的损耗。长度和折射率调制深度主要影响损耗峰深度,可以用于调控损耗峰出现极深值点。得到当两个级联LPG的周期为500 μm、长度为3 cm,折射率调制深度为0.00014时存在窄而深的最优CLPG损耗峰。该研究结论为分析级联长周期光纤光栅理论和改进传感器件设计应用提供了依据。
文摘There are an absorption peak at 485 nm and a synchronous fluorescence peak at 510 nm for fluorescein in the medium of 3.4×10 -3 mol/L tri-sodium citrate. The gold nanoparticle system exhibits a characterization resonance scattering peak at 580 nm. In the coexisting system of gold nanoparticle and fluorescein, there are a synchronous fluorescence peak at 510 nm and a resonance scattering peak at 580 nm. It has been found that the fluorescence peak may be quenched by gold nanoparticle. When the concentration of fluorescein is higher, the A 470 nm affects the I 470 nm of gold nanoparticle. The I 470 nm decreases exponentially with the concentration of fluorescein.