Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by...Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by scanning electronic microscopy, X-ray diffraction and energy dispersive spectroscopy. The results indicate thatthe 20 μm alloyed layer is homogeneous and compact. The alloyed elements exhibit a gradient distribution along the cross section. Microhardness and nanoindentation tests imply that the surface hardness of the alloyed layer reaches HV 580, which is almost 2.8 times that of the substrate. Compared with the substrate, the alloyed layer has a much smaller displacement and a larger elastic modulus. According to the friction and wear tests at room temperature, the? FeAl?Cr?Nb alloyed layer has lower friction coefficient and less wear mass, implying that the Fe?Al?Cr?Nb alloyed layer can effectively improve the surface hardness and wear resistance of the substrate.展开更多
基金Project(51371097)supported by the National Natural Science Foundation of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Double glow plasma surface metallurgy technique was used to fabricate a Fe?Al?Cr?Nb alloyed layer onto the surface of the 45 steel. The microstructures and composition of th?eA Fl?eCr?Nb alloyed layer were analyzed by scanning electronic microscopy, X-ray diffraction and energy dispersive spectroscopy. The results indicate thatthe 20 μm alloyed layer is homogeneous and compact. The alloyed elements exhibit a gradient distribution along the cross section. Microhardness and nanoindentation tests imply that the surface hardness of the alloyed layer reaches HV 580, which is almost 2.8 times that of the substrate. Compared with the substrate, the alloyed layer has a much smaller displacement and a larger elastic modulus. According to the friction and wear tests at room temperature, the? FeAl?Cr?Nb alloyed layer has lower friction coefficient and less wear mass, implying that the Fe?Al?Cr?Nb alloyed layer can effectively improve the surface hardness and wear resistance of the substrate.