Cavity perturbation method was used to determine the dielectric properties （ε′,ε″, and tanδ） of zinc oxide dust in different apparent densities. The process was conducted to study the microwave-absorption prope...Cavity perturbation method was used to determine the dielectric properties （ε′,ε″, and tanδ） of zinc oxide dust in different apparent densities. The process was conducted to study the microwave-absorption properties of zinc oxide dust and the feasibility of microwave roasting zinc oxide dust to remove fluorine and chlorine. The dielectric constant, dielectric loss, and loss tangent were proportional to the apparent density of zinc oxide dust. The effects of sample mass and microwave power on the temperature increase characteristics under the microwave field were also studied. The results show that the apparent heating rate of the zinc oxide dust increases with the increase in microwave roasting power and decreases with the increase in the sample mass. The temperature of the samples reaches approximately 800 ＆#176;C after microwave treatment for 8 min, which indicates that the zinc oxide dust has strong microwave-absorption ability.展开更多
基金Project(51104073)supported by the National Natural Science Foundation of ChinaProject(2014CB643404)supported by the National Basic Research Program of China+1 种基金Project(2013AA064003)supported by the Hi-tech Research and Development Program of ChinaProject(2012HB008)supported by the Yunnan Provincial Young Academic Technology Leader Reserve Talents,China
文摘Cavity perturbation method was used to determine the dielectric properties （ε′,ε″, and tanδ） of zinc oxide dust in different apparent densities. The process was conducted to study the microwave-absorption properties of zinc oxide dust and the feasibility of microwave roasting zinc oxide dust to remove fluorine and chlorine. The dielectric constant, dielectric loss, and loss tangent were proportional to the apparent density of zinc oxide dust. The effects of sample mass and microwave power on the temperature increase characteristics under the microwave field were also studied. The results show that the apparent heating rate of the zinc oxide dust increases with the increase in microwave roasting power and decreases with the increase in the sample mass. The temperature of the samples reaches approximately 800 ＆#176;C after microwave treatment for 8 min, which indicates that the zinc oxide dust has strong microwave-absorption ability.