In order to improve the tribological properties of titanium alloys,the in-situ TiN coatings were prepared by electrospark deposition（ESD） on the surface of TC11 titanium alloy.The effects of nitrogen flux on the mic...In order to improve the tribological properties of titanium alloys,the in-situ TiN coatings were prepared by electrospark deposition（ESD） on the surface of TC11 titanium alloy.The effects of nitrogen flux on the microstructure and tribological properties of TiN coatings were investigated.The results show that the coating is relative thin when the nitrogen flux is small and mainly consists of Ti2N,α-Ti,Ti O and TiN phases,and the metastable phase of Ti2N is developed due to the rapid solidification of ESD.While in excessive nitrogen flux condition,many micro-cracks and holes might be generated in the coating.In moderate nitrogen flux,the coating is mainly composed of TiN phase,and is dense and uniform（50-55 μm）.The average hardness is HV0.2 1165.2,which is 3.4 times that of the TC11 substrate.The TiN coatings prepared in moderate nitrogen flux perform the best wear resistance.The wear loss of the coating is 0.4 mg,which is 2/9 that of the TC11 substrate.The main wear mechanisms of the coatings are micro-cutting wear accompanied by multi-plastic deformation wear.展开更多
C/Mo duplex coating interfacially modified SiC fiber-reinforced γ-TiAl matrix composite （SiCf/C/Mo/γ-TiA1） was prepared by foil-fiber-foil method to investigate its interfacial modification effect. SiCf/C/TiAl com...C/Mo duplex coating interfacially modified SiC fiber-reinforced γ-TiAl matrix composite （SiCf/C/Mo/γ-TiA1） was prepared by foil-fiber-foil method to investigate its interfacial modification effect. SiCf/C/TiAl composites were also prepared under the same processing condition for comparision. Both kinds of the composites were thermally exposed in vacuum at 800 and 900℃ for different durations in order to study thermal stability of the interfacial zone. With the aids of scanning electron microscope （SEM） and energy dispersive spectrometer （EDS）, the interracial microstructures of the composites were investigated. The results reveal that, although adding the Mo coating, the interfacial reaction product of the SiCf/C/Mo/TiAl composite is the same with that of the SiCf/C/TiA1 composite, which is TiC/Ti2AlC between the coating and the matrix. However, C/Mo duplex coating is more efficient in hindering interfacial reaction than C single coating at 900 ℃ and below. In addition, a new layer of interfacial reaction product was found between Ti2AlC and the matrix after 900 ℃, 200 h thermal exposure, which is rich in V and close to the chemical composition of B2 phase.展开更多
A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
A bone-like apatite layer consisting of nano-crystals of apatite phase was prepared on the surface of Ti- 25Nb-2Zr alloy by chemical biomimetic growth method. TiNbZr alloy specimens were first oxidized at 500 ℃ for 2...A bone-like apatite layer consisting of nano-crystals of apatite phase was prepared on the surface of Ti- 25Nb-2Zr alloy by chemical biomimetic growth method. TiNbZr alloy specimens were first oxidized at 500 ℃ for 2 h in the air. Then, they were immersed in 40 ℃ saturated NazHPO4 solution for 15 h and 25 ℃ saturated Ca （OH）2 solution for 8 h in turn for pre-calcification. The pre-calcified specimens were immersed in modified simulated body fluid up to 15 d for biomimetic growth. After common oxidization, amorphous titania and anatase were detected on the specimen surface. Except for the substantial amount of calcium and phosphorus, no new phase appeared on the pre-calcified specimens. After the coating process, it was found that the （002） orientation was the preferred orientation during the growing period of hydroxyapatite. The inorganic composition and structure of the coating are very similar to those of human thigh bone, which will be advantageous for its application as biomedical material.展开更多
TiCx-NiTi2/Ti cermet composite coatings C1 and C2 with gradient TiCx reinforcements were prepared on TC4 titanium alloy by laser cladding method.The microstructure and phase compositions were analyzed by means of scan...TiCx-NiTi2/Ti cermet composite coatings C1 and C2 with gradient TiCx reinforcements were prepared on TC4 titanium alloy by laser cladding method.The microstructure and phase compositions were analyzed by means of scanning electron microscopy(SEM),energy-dispersive spectroscopy(EDS)and X-ray diffraction(XRD)meter.The TiCx exhibited a dendritic microstructure,and homogeneously dispersed in the Ti-based matrix where NiTi2 was embedded.With increasing ingredient supercooling,temperature gradient and cooling temperature,the dendrites displayed a finer morphology with longer primary trunks and intensified side branches in the dilution zone.But the smoothed,coarse columnar ones became dominant in the upper clad layer due to the repeated energy input during multi-track cladding.The Vickers microhardness presented a linear change trend through the cross-sections,which well confirmed the gradient distribution of TiCx.With more TiCx,C1 presented higher hardness than C2.展开更多
The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were i...The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were investigated with a rotating bending fatigue test machine.The basic properties and surface integrity of the coating were investigated by using X-ray diffraction (XRD),surface roughness meter,microscopic hardness tester,scanning electron microscopy (SEM) and X-ray stress test instruments.The results showed that the residual compressive stress could be introduced into the surface of TC21 alloy by GB and SP pretreatment,and that HVOF sprayed WC-17Co coating was compactly bonded with TC21 alloy substrate and it significantly improved the surface hardness of the substrate.However,there was a certain residual tensile stress in the sublayer of the coating.SP could significantly increase fatigue resistance of TC21 alloy due to the surface residual compressive stress.There was no significant effect on fatigue resistance by GB treatment due to the offset between the influence of surface residual compressive stress and the surface notch effect.The fatigue resistance of TC21 alloy was significantly reduced by HVOF WC-17Co coating prepared with GB pretreatment.This could be attributed to the relaxation of surface residual compressive stress during the HVOF heating process,pore defects and residual tensile stress distribution in the WC-17Co coating with low toughness,and the surface notch induced by GB.The fatigue resistance of TC21 alloy was slightly reduced by HVOF WC-17Co coating prepared with SP pretreatment.This was attributed to the offset between the advantage effect by SP and disadvantageous effect of WC-17Co coating and high temperature factor during the HVOF process.展开更多
文摘In order to improve the tribological properties of titanium alloys,the in-situ TiN coatings were prepared by electrospark deposition（ESD） on the surface of TC11 titanium alloy.The effects of nitrogen flux on the microstructure and tribological properties of TiN coatings were investigated.The results show that the coating is relative thin when the nitrogen flux is small and mainly consists of Ti2N,α-Ti,Ti O and TiN phases,and the metastable phase of Ti2N is developed due to the rapid solidification of ESD.While in excessive nitrogen flux condition,many micro-cracks and holes might be generated in the coating.In moderate nitrogen flux,the coating is mainly composed of TiN phase,and is dense and uniform（50-55 μm）.The average hardness is HV0.2 1165.2,which is 3.4 times that of the TC11 substrate.The TiN coatings prepared in moderate nitrogen flux perform the best wear resistance.The wear loss of the coating is 0.4 mg,which is 2/9 that of the TC11 substrate.The main wear mechanisms of the coatings are micro-cutting wear accompanied by multi-plastic deformation wear.
基金Projects(51201134,51271147)supported by the National Natural Science Foundation of ChinaProject(2015JM5181)supported by the Natural Science Foundation of Shaanxi Province,China+1 种基金Project(115-QP-2014)supported by the Research Fund of the State Key Laboratory of Solidification Processing(NWPU),ChinaProject(3102014JCQ01023)supported by the Fundamental Research Funds for the Central Universities,China
文摘C/Mo duplex coating interfacially modified SiC fiber-reinforced γ-TiAl matrix composite （SiCf/C/Mo/γ-TiA1） was prepared by foil-fiber-foil method to investigate its interfacial modification effect. SiCf/C/TiAl composites were also prepared under the same processing condition for comparision. Both kinds of the composites were thermally exposed in vacuum at 800 and 900℃ for different durations in order to study thermal stability of the interfacial zone. With the aids of scanning electron microscope （SEM） and energy dispersive spectrometer （EDS）, the interracial microstructures of the composites were investigated. The results reveal that, although adding the Mo coating, the interfacial reaction product of the SiCf/C/Mo/TiAl composite is the same with that of the SiCf/C/TiA1 composite, which is TiC/Ti2AlC between the coating and the matrix. However, C/Mo duplex coating is more efficient in hindering interfacial reaction than C single coating at 900 ℃ and below. In addition, a new layer of interfacial reaction product was found between Ti2AlC and the matrix after 900 ℃, 200 h thermal exposure, which is rich in V and close to the chemical composition of B2 phase.
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
文摘A bone-like apatite layer consisting of nano-crystals of apatite phase was prepared on the surface of Ti- 25Nb-2Zr alloy by chemical biomimetic growth method. TiNbZr alloy specimens were first oxidized at 500 ℃ for 2 h in the air. Then, they were immersed in 40 ℃ saturated NazHPO4 solution for 15 h and 25 ℃ saturated Ca （OH）2 solution for 8 h in turn for pre-calcification. The pre-calcified specimens were immersed in modified simulated body fluid up to 15 d for biomimetic growth. After common oxidization, amorphous titania and anatase were detected on the specimen surface. Except for the substantial amount of calcium and phosphorus, no new phase appeared on the pre-calcified specimens. After the coating process, it was found that the （002） orientation was the preferred orientation during the growing period of hydroxyapatite. The inorganic composition and structure of the coating are very similar to those of human thigh bone, which will be advantageous for its application as biomedical material.
基金supported by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China(Grant No.2011BAE12B03)the National Natural Science Foundation of China(Grant No.11372110)
文摘TiCx-NiTi2/Ti cermet composite coatings C1 and C2 with gradient TiCx reinforcements were prepared on TC4 titanium alloy by laser cladding method.The microstructure and phase compositions were analyzed by means of scanning electron microscopy(SEM),energy-dispersive spectroscopy(EDS)and X-ray diffraction(XRD)meter.The TiCx exhibited a dendritic microstructure,and homogeneously dispersed in the Ti-based matrix where NiTi2 was embedded.With increasing ingredient supercooling,temperature gradient and cooling temperature,the dendrites displayed a finer morphology with longer primary trunks and intensified side branches in the dilution zone.But the smoothed,coarse columnar ones became dominant in the upper clad layer due to the repeated energy input during multi-track cladding.The Vickers microhardness presented a linear change trend through the cross-sections,which well confirmed the gradient distribution of TiCx.With more TiCx,C1 presented higher hardness than C2.
基金supported by the National Natural Science Foundation of China (Grant Nos. 51171154 and 51101127)
文摘The effects of grit blasting (GB),shot peening (SP) pretreatment and high velocity oxygen fuel(HVOF) sprayed WC-17Co cermet coating on the fatigue properties of the novel ultra-high strength TC21 titanium alloy were investigated with a rotating bending fatigue test machine.The basic properties and surface integrity of the coating were investigated by using X-ray diffraction (XRD),surface roughness meter,microscopic hardness tester,scanning electron microscopy (SEM) and X-ray stress test instruments.The results showed that the residual compressive stress could be introduced into the surface of TC21 alloy by GB and SP pretreatment,and that HVOF sprayed WC-17Co coating was compactly bonded with TC21 alloy substrate and it significantly improved the surface hardness of the substrate.However,there was a certain residual tensile stress in the sublayer of the coating.SP could significantly increase fatigue resistance of TC21 alloy due to the surface residual compressive stress.There was no significant effect on fatigue resistance by GB treatment due to the offset between the influence of surface residual compressive stress and the surface notch effect.The fatigue resistance of TC21 alloy was significantly reduced by HVOF WC-17Co coating prepared with GB pretreatment.This could be attributed to the relaxation of surface residual compressive stress during the HVOF heating process,pore defects and residual tensile stress distribution in the WC-17Co coating with low toughness,and the surface notch induced by GB.The fatigue resistance of TC21 alloy was slightly reduced by HVOF WC-17Co coating prepared with SP pretreatment.This was attributed to the offset between the advantage effect by SP and disadvantageous effect of WC-17Co coating and high temperature factor during the HVOF process.