A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature...A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.展开更多
Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emu...Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emulsifiers at (78±2) ℃. The effects of different factors, such as the emulsifier, C-1706 monomer and its feeding manner on the properties of acrylate latex modified by C-1706 were investigated. The particle size distribution and the structure, the configuration, the weather durability and stain resistance of copolymer latex were characterized by particle size analyzer, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscope(TEM), scanning electron microscope(SEM) and ultraviolet aging instrument respectively. The results show that SDS to OP-10 as multiple emulsifiers can lead to coordinated efficiency, the optimal emulsifier dosage is 2.4%?3.2%(mass fraction), and the mass ratio of SDS to OP-10 is 1?1? 1?2. The seeded emulsion polymerization can effectively introduce a organic-siloxane bonding in a macromolecule inter polymer, and the obtained acrylate latex modified by organic-siloxane possesses narrow distribution of particle size with mean diameter of 51.8?76.6 nm and has the excellent properties in weather durability and stain-resistance especially.展开更多
基金Ministry of Science and Technology of China for Major State Basic Research Projects (2002AA322020)
文摘A silicone acrylate micro-emulsion of multipolymer was prepared by seed emulsion polymerization. The effects of polymerization process, emulsifier rate and amount, initiator rate and amount, polymerization temperature, functional monomers, titration time on performances of emulsion have been discussed in detail.
基金Project(2003B10506) supported by Science and Technology Department of Guangdong Province, China
文摘Acrylate latex modified by vinyl triisopropoxy silane (C-1706) was synthesized by seeded emulsion polymerization with anionic emulsifier sodium dodecyl sulphonate(SDS) and nonionic emulsifier OP-10 as the multiple emulsifiers at (78±2) ℃. The effects of different factors, such as the emulsifier, C-1706 monomer and its feeding manner on the properties of acrylate latex modified by C-1706 were investigated. The particle size distribution and the structure, the configuration, the weather durability and stain resistance of copolymer latex were characterized by particle size analyzer, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscope(TEM), scanning electron microscope(SEM) and ultraviolet aging instrument respectively. The results show that SDS to OP-10 as multiple emulsifiers can lead to coordinated efficiency, the optimal emulsifier dosage is 2.4%?3.2%(mass fraction), and the mass ratio of SDS to OP-10 is 1?1? 1?2. The seeded emulsion polymerization can effectively introduce a organic-siloxane bonding in a macromolecule inter polymer, and the obtained acrylate latex modified by organic-siloxane possesses narrow distribution of particle size with mean diameter of 51.8?76.6 nm and has the excellent properties in weather durability and stain-resistance especially.