A solid-solution-phase Ba1.75Ca1.25MgSi2O8： Eu2＋, Mn2＋ phosphor in the photosynthetic action spectrum with dual band emissions at 438 nm and 660 nm is fabricated. X-ray diffraction （XRD） confirms the presence of ...A solid-solution-phase Ba1.75Ca1.25MgSi2O8： Eu2＋, Mn2＋ phosphor in the photosynthetic action spectrum with dual band emissions at 438 nm and 660 nm is fabricated. X-ray diffraction （XRD） confirms the presence of the solid-solution phase. With the supporting information from the diffuse reflection spectrum, a feasible way to obtain higher energy-transfer （ET） efficiency is attained, and the ET efficiency of Eu2＋-Mn2＋ is enhanced to 76%. The mechanism of this enhancement is owing to variation of the solid solution composition of Ca3MgSi208 and Ba3MgSi2Os, which contributes to the extension of the critical distance. Temperature-dependent results show an en- hancement which is attributed to Ca. These enhancements show great promise for improving coo-lighting devices.展开更多
基金supported by the National Natural Science Foundation of China(No.21076161)
文摘A solid-solution-phase Ba1.75Ca1.25MgSi2O8： Eu2＋, Mn2＋ phosphor in the photosynthetic action spectrum with dual band emissions at 438 nm and 660 nm is fabricated. X-ray diffraction （XRD） confirms the presence of the solid-solution phase. With the supporting information from the diffuse reflection spectrum, a feasible way to obtain higher energy-transfer （ET） efficiency is attained, and the ET efficiency of Eu2＋-Mn2＋ is enhanced to 76%. The mechanism of this enhancement is owing to variation of the solid solution composition of Ca3MgSi208 and Ba3MgSi2Os, which contributes to the extension of the critical distance. Temperature-dependent results show an en- hancement which is attributed to Ca. These enhancements show great promise for improving coo-lighting devices.