In this paper a preliminary investigation of a novel optoelectronic polymer, poly (p-phenylene N-4-n-butylphenyl-N,N-bis- 4-vinylenephenylamine) (PNB), is reported. A single layer structure of ITO/PNB/Al was prepared ...In this paper a preliminary investigation of a novel optoelectronic polymer, poly (p-phenylene N-4-n-butylphenyl-N,N-bis- 4-vinylenephenylamine) (PNB), is reported. A single layer structure of ITO/PNB/Al was prepared via spin-coating of PNB solution as a thin film on the top of an ITO substrate, while aluminum top electrode was vacuum evaporated. Dark current- voltage characteristics of this device showed a typical rectifying behaviour. Photovoltaic response under a monochromatic illumination at 420 nm was observed, with an open circuit voltage of 0.3 V and fill factor of 0.21. Spectral response and optical absorption were found to be matched well. It was also discovered that the device showed a green electroluminescent emission at a forward bias. Turn-on voltage of the device was about 6 V and light output about 22.6 nW at a forward bias of 10 V. The work demonstrated that the PNB material might possess dual exciton sites resulting in a competition for excitons to be either separated or recombined. Both effects were associated with each other, which limited the photovoltaic or electroluminescence to some degrees.展开更多
Polystyrene N-hydroxyl sulfonamide resin 1 was prepared and used to catalyze the esterification of n-butanol and acetic anhydride. The mechanism of catalytic esterification proved by IR spectra of the resins was found...Polystyrene N-hydroxyl sulfonamide resin 1 was prepared and used to catalyze the esterification of n-butanol and acetic anhydride. The mechanism of catalytic esterification proved by IR spectra of the resins was found that O-H and N-H of the N-hydroxyl sulfonamide resin reacted with the acetic anhydride respectively to form the active intermediate polystyrene N,O-diacetyl sulfonamate which was cleaved by n-butanol to produce butyl acetate. The catalytic esterification by resin 1 was in good agreement with the kinetic model of 揵i-bi-ping-pong?mechanism.展开更多
基金This work is supported by National Natural Science Foundationof China(20344002,10434030) State Key Program forBasic research of China (2003CB314707)
文摘In this paper a preliminary investigation of a novel optoelectronic polymer, poly (p-phenylene N-4-n-butylphenyl-N,N-bis- 4-vinylenephenylamine) (PNB), is reported. A single layer structure of ITO/PNB/Al was prepared via spin-coating of PNB solution as a thin film on the top of an ITO substrate, while aluminum top electrode was vacuum evaporated. Dark current- voltage characteristics of this device showed a typical rectifying behaviour. Photovoltaic response under a monochromatic illumination at 420 nm was observed, with an open circuit voltage of 0.3 V and fill factor of 0.21. Spectral response and optical absorption were found to be matched well. It was also discovered that the device showed a green electroluminescent emission at a forward bias. Turn-on voltage of the device was about 6 V and light output about 22.6 nW at a forward bias of 10 V. The work demonstrated that the PNB material might possess dual exciton sites resulting in a competition for excitons to be either separated or recombined. Both effects were associated with each other, which limited the photovoltaic or electroluminescence to some degrees.
基金Natural Science Foundation of China (Project number: 20074017)
文摘Polystyrene N-hydroxyl sulfonamide resin 1 was prepared and used to catalyze the esterification of n-butanol and acetic anhydride. The mechanism of catalytic esterification proved by IR spectra of the resins was found that O-H and N-H of the N-hydroxyl sulfonamide resin reacted with the acetic anhydride respectively to form the active intermediate polystyrene N,O-diacetyl sulfonamate which was cleaved by n-butanol to produce butyl acetate. The catalytic esterification by resin 1 was in good agreement with the kinetic model of 揵i-bi-ping-pong?mechanism.