Laser alloying was used for production of thick layers on surface of Nimonic 80A-alloy.For laser surface modification,three types of pre-coated pastes were applied:with amorphous boron,with amorphous boron and molybde...Laser alloying was used for production of thick layers on surface of Nimonic 80A-alloy.For laser surface modification,three types of pre-coated pastes were applied:with amorphous boron,with amorphous boron and molybdenum as well as with amorphous boron and niobium.The microstructure,hardness and wear resistance of produced layers were studied in details.The presence of different types of borides in re-melted zone depended on the paste composition and caused an increase in hardness up to about HV 1000.The wear resistance was evaluated by calculation of mass wear intensity factor Imw and relative mass loss of specimen and counter-specimen.The wear behavior of the tested frictional pairs was determined by 3D interference microscopy,scanning electron microscopy equipped with EDS microanalyzer.The significant increase in abrasive wear resistance was observed in comparison to untreated Nimonic 80A-alloy.The lowest mass loss intensity factor was characteristic of laser-alloyed Nimonic 80A-alloy with boron and niobium(Imw=1.234 mg/(cm2?h)).Laser alloyed-layers indicated abrasive wear mechanism with clearly visible grooves.Laser alloying with boron and niobium resulted in the additional oxidative wear mechanism.In this case,EDS patterns revealed presence of oxygen on the worn surface of specimen.展开更多
基金financially supported within the project "Engineer of the Future.Improving the didactic potential of the Poznan University of Technology"-POKL.04.03.00-00-259/12,implemented within the Human Capital Operational Programme,co-financed by the European Union within the European Social Fundby Ministry of Science and Higher Education in Poland as a part of the 02/24/DSPB project
文摘Laser alloying was used for production of thick layers on surface of Nimonic 80A-alloy.For laser surface modification,three types of pre-coated pastes were applied:with amorphous boron,with amorphous boron and molybdenum as well as with amorphous boron and niobium.The microstructure,hardness and wear resistance of produced layers were studied in details.The presence of different types of borides in re-melted zone depended on the paste composition and caused an increase in hardness up to about HV 1000.The wear resistance was evaluated by calculation of mass wear intensity factor Imw and relative mass loss of specimen and counter-specimen.The wear behavior of the tested frictional pairs was determined by 3D interference microscopy,scanning electron microscopy equipped with EDS microanalyzer.The significant increase in abrasive wear resistance was observed in comparison to untreated Nimonic 80A-alloy.The lowest mass loss intensity factor was characteristic of laser-alloyed Nimonic 80A-alloy with boron and niobium(Imw=1.234 mg/(cm2?h)).Laser alloyed-layers indicated abrasive wear mechanism with clearly visible grooves.Laser alloying with boron and niobium resulted in the additional oxidative wear mechanism.In this case,EDS patterns revealed presence of oxygen on the worn surface of specimen.