Significant progress has been made in the development of non-precious metal electrocatalysts （NPMEs） during the past decade. Correspondingly, there is an urgent demand for an appropriate measurement method to be est...Significant progress has been made in the development of non-precious metal electrocatalysts （NPMEs） during the past decade. Correspondingly, there is an urgent demand for an appropriate measurement method to be established for the reliable evaluation of NPMEs. In this study, platinum and graphite counter electrodes were used to investigate the impact of counter electrode material on the accelerated durability testing （ADT） of NPMEs in acidic medium. Platinum used as the coun- ter electrode in a traditional three-electrode electrochemical cell was found to dissolve in acidic medium and re-deposit on NPME coated on the working electrode during ADT. Such re-deposition causes the oxygen reduction reaction （ORR） performance of NPMEs to remarkably improve, and thus will seriously mislead our judgment of NPMEs if we are unaware of it. The phenomenon can be avoided using a graphite counter electrode.展开更多
A new scheme for the preparation of highly dispersed precious metal catalysts is proposed in this work. Samples of LaCol-xPtxO3/SiO2 （x = 0.03, 0.05, 0.07, 0.09, and 0.10） were prepared through a simple method of ci...A new scheme for the preparation of highly dispersed precious metal catalysts is proposed in this work. Samples of LaCol-xPtxO3/SiO2 （x = 0.03, 0.05, 0.07, 0.09, and 0.10） were prepared through a simple method of citrate acid complexa-tion combined with impregnation. In a nanocrystallite of LaCOl-xPtxO3, ions of lanthanum, cobalt, and platinum are evenly mixed at the atomic level and confined within the nanocrystallite. In the reduction process, platinum ions were reduced and migrated onto the surface of the nanocrystallite, and the platinum should be highly dispersed owing to the even mixing of the platinum ions in the precursor. When x = 0.05 or lower, the highest dispersion of Pt could be achieved. The highly dispersed Pt is stable, because of the strong interaction between Pt atoms and the support. The catalysts were characterized by BET surface area, temperature-programmed reduction, X-ray diffraction, transmission electron microscopy, CO temperature-programmed desorption, and turnover frequency. Compared with general precious metal Pt catalysts, the LaCo0.95Pt0.05O3/ SiO2 catalyst exhibited better activity for CO oxidation, and it maintained stability at a high temperature of 400 ℃ for 250 h with complete CO conversion.展开更多
基金supported by the Fundamental Research Funds for the Central Universities(DUT15RC(3)001,DUT15ZD225)the Program for Liao-ning Excellent Talents in University(LR2015014)+1 种基金the Liaoning BaiQianWan Talents Program(201519)Dalian Excellent Young Scientific and Technological Talents(2015R006)
文摘Significant progress has been made in the development of non-precious metal electrocatalysts （NPMEs） during the past decade. Correspondingly, there is an urgent demand for an appropriate measurement method to be established for the reliable evaluation of NPMEs. In this study, platinum and graphite counter electrodes were used to investigate the impact of counter electrode material on the accelerated durability testing （ADT） of NPMEs in acidic medium. Platinum used as the coun- ter electrode in a traditional three-electrode electrochemical cell was found to dissolve in acidic medium and re-deposit on NPME coated on the working electrode during ADT. Such re-deposition causes the oxygen reduction reaction （ORR） performance of NPMEs to remarkably improve, and thus will seriously mislead our judgment of NPMEs if we are unaware of it. The phenomenon can be avoided using a graphite counter electrode.
基金supported by the National Natural Science Foundation of China(Nos.21576192,21776214)
文摘A new scheme for the preparation of highly dispersed precious metal catalysts is proposed in this work. Samples of LaCol-xPtxO3/SiO2 （x = 0.03, 0.05, 0.07, 0.09, and 0.10） were prepared through a simple method of citrate acid complexa-tion combined with impregnation. In a nanocrystallite of LaCOl-xPtxO3, ions of lanthanum, cobalt, and platinum are evenly mixed at the atomic level and confined within the nanocrystallite. In the reduction process, platinum ions were reduced and migrated onto the surface of the nanocrystallite, and the platinum should be highly dispersed owing to the even mixing of the platinum ions in the precursor. When x = 0.05 or lower, the highest dispersion of Pt could be achieved. The highly dispersed Pt is stable, because of the strong interaction between Pt atoms and the support. The catalysts were characterized by BET surface area, temperature-programmed reduction, X-ray diffraction, transmission electron microscopy, CO temperature-programmed desorption, and turnover frequency. Compared with general precious metal Pt catalysts, the LaCo0.95Pt0.05O3/ SiO2 catalyst exhibited better activity for CO oxidation, and it maintained stability at a high temperature of 400 ℃ for 250 h with complete CO conversion.