A novel process of composite roasting with CaO/MgO and subsequent acid leaching was proposed to improve the recovery rate of vanadium from Linz–Donawiz(LD)converter vanadium slag.The effects of the MgO/(CaO+MgO)molar...A novel process of composite roasting with CaO/MgO and subsequent acid leaching was proposed to improve the recovery rate of vanadium from Linz–Donawiz(LD)converter vanadium slag.The effects of the MgO/(CaO+MgO)molar ratio and the roasting and leaching parameters on the recovery of vanadium were studied.The results showed that the leaching efficiency of vanadium decreased from 88%to 81%when CaO was replaced completely by MgO;however,it could be improved by roasting with the composite of CaO/MgO.The maximum vanadium leaching efficiency of 94%was achieved under the optimum MgO/(CaO+MgO)mole ratio of 0.5:1.The results from X-ray diffractometry(XRD)and scanning electron microscopy with energy-dispersive X-ray spectroscopy(SEM−EDS)confirm that the formation rate of acid-soluble vanadates can be enhanced during roasting with the composite of CaO/MgO and that the leaching kinetics can be accelerated owing to the suppression of calcium sulfate precipitation.展开更多
基金Project(2018M640898)supported by the China Postdoctoral Science FoundationProject(cstc2019jcyj-bshX0068)supported by the Natural Science Foundation of Chongqing,China+1 种基金Project(52004044)supported by the National Natural Science Foundation of ChinaProject(2018YFC1900500)supported by the National Key Research and Development Program of China。
文摘A novel process of composite roasting with CaO/MgO and subsequent acid leaching was proposed to improve the recovery rate of vanadium from Linz–Donawiz(LD)converter vanadium slag.The effects of the MgO/(CaO+MgO)molar ratio and the roasting and leaching parameters on the recovery of vanadium were studied.The results showed that the leaching efficiency of vanadium decreased from 88%to 81%when CaO was replaced completely by MgO;however,it could be improved by roasting with the composite of CaO/MgO.The maximum vanadium leaching efficiency of 94%was achieved under the optimum MgO/(CaO+MgO)mole ratio of 0.5:1.The results from X-ray diffractometry(XRD)and scanning electron microscopy with energy-dispersive X-ray spectroscopy(SEM−EDS)confirm that the formation rate of acid-soluble vanadates can be enhanced during roasting with the composite of CaO/MgO and that the leaching kinetics can be accelerated owing to the suppression of calcium sulfate precipitation.