TiN films were deposited on 2A12 aluminum alloy by arc ion plating (AIP). The Vickers hardness of the films deposited at different bias voltages and different nitrogen gas pressures, and that of the substrate were mea...TiN films were deposited on 2A12 aluminum alloy by arc ion plating (AIP). The Vickers hardness of the films deposited at different bias voltages and different nitrogen gas pressures, and that of the substrate were measured. The surface roughness of the TiN films diposited at –30 V and –80 V respectively and at different nitrogen gas pressure was measured also. The mass loss of TiN films deposited at 0 V, –30 V and –80 V respectively were analyzed in dry sand rubber wheel abrasive wear tests and wet ones in comparison with uncoated Al alloy and austenitic stainless steel (AISI 316L). It is revealed that the highest hardness of the TiN film is obtained at a bias voltage of –30 V and a N2 gas pressure of 0.5 Pa. The surface roughness of the film is larger at –80 V than that at –30 V and reduces as the increase of the N2 gas pressure. The mass loss of TiN-film coated 2A12 aluminum alloy is remarkably less than that of uncoated Al alloy and also that of AISI 316L, which indicates that the abrasive wear rate is greatly reduced by the application of TiN coating. TiN coating deposited by arc ion plating (AIP) technique on aluminum alloy can be a potential coating for machine parts requiring preciseness and lightness.展开更多
文摘TiN films were deposited on 2A12 aluminum alloy by arc ion plating (AIP). The Vickers hardness of the films deposited at different bias voltages and different nitrogen gas pressures, and that of the substrate were measured. The surface roughness of the TiN films diposited at –30 V and –80 V respectively and at different nitrogen gas pressure was measured also. The mass loss of TiN films deposited at 0 V, –30 V and –80 V respectively were analyzed in dry sand rubber wheel abrasive wear tests and wet ones in comparison with uncoated Al alloy and austenitic stainless steel (AISI 316L). It is revealed that the highest hardness of the TiN film is obtained at a bias voltage of –30 V and a N2 gas pressure of 0.5 Pa. The surface roughness of the film is larger at –80 V than that at –30 V and reduces as the increase of the N2 gas pressure. The mass loss of TiN-film coated 2A12 aluminum alloy is remarkably less than that of uncoated Al alloy and also that of AISI 316L, which indicates that the abrasive wear rate is greatly reduced by the application of TiN coating. TiN coating deposited by arc ion plating (AIP) technique on aluminum alloy can be a potential coating for machine parts requiring preciseness and lightness.