The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,t...The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.展开更多
基金Project(201629) supported by the Scientific Research Foundation for Introduced Talent of Guizhou University,ChinaProjects(20164014,20165654) supported by the Hundred-level Innovative Talents Project of Guizhou Province,ChinaProject(20146013) supported by the Science and Technology of Guizhou Province,China
文摘The effect of strain rate and deformation temperature on theα→βphase transformation in 47Zr-45Ti-5Al-3V alloy with an initial widmanstattenαstructure was investigated.At the deformation temperature of 550°C,the volume fraction ofαphase decreased with increasing strain rate.At 600 and 650°C,the volume fraction ofαphase firstly increased to a maximum value with increasing strain rate from 1×10-3 to 1×10-2 s-1,and then decreased.At 700°C,the microstructure consisted of singleβphase.At a given strain rate,the volume fraction ofαphase decreased with increasing deformation temperature.With decreasing strain rate and increasing deformation temperature,the volume fraction and size of globularαphase increased.At 650°C and 1×10-3 s-1,the lamellarαphase was fully globularized.The variation in the volume fraction and morphology ofαphase with strain rate and deformation temperature significantly affected the hardness of 47Zr-45Ti-5Al-3V alloy.