Dissimilar friction stir welding between AZ31-O Mg and 6061-T6 Al alloys was investigated. 3 mm thick plates of aluminum and magnesium were used. Friction stir welding operations were performed at different rotation a...Dissimilar friction stir welding between AZ31-O Mg and 6061-T6 Al alloys was investigated. 3 mm thick plates of aluminum and magnesium were used. Friction stir welding operations were performed at different rotation and travel speeds. The rotation speeds varied from 600 to 1400 r/min, and the travel speed varied from 20 to 60 mm/min. Defect-free weld was obtained with a rotation speed of 1000 r/min and travel speed of 40 mm/min. Metallographic studies showed that the grain size in the stir zone is much finer than that in the base metals. Complex flow pattern was formed in the stir zone. Microhardness measurement revealed an uneven distribution in the stir zone. Tensile test results indicated that the tensile strength of the welded specimen is about 76% of AZ31 Mg alloy and 60% of the 6061 Al alloy in tensile strength. SEM fracture surface image of the welded specimen indicated that the welded specimen failed through brittle-mode fracture.展开更多
6061 aluminum alloy T-joints were welded by double-pulsed MIG welding process. Then, the post-weld heat treatment was performed on the welded T-joints. The weld microstructure under different aging temperature and tim...6061 aluminum alloy T-joints were welded by double-pulsed MIG welding process. Then, the post-weld heat treatment was performed on the welded T-joints. The weld microstructure under different aging temperature and time was investigated by transmission electron microscopy and scanning electron microscopy. The mechanical properties were examined by hardness test and tensile test. The results showed that the micro-hardness was sensitive to heat treatment temperature and time. Increasing temperature was beneficial to the shortening of peak aging time. There were a large number of dislocations and few precipitates in the welded joints. With the increase of post-weld heat treatment temperature and time, the density of dislocation decreased. Meanwhile, the strengthening phase precipitated and grew up gradually. When the post-weld heat treatment temperature increased up to 200℃, large Q' phases were observed. And they were responsible for the peak value of the micro-hardness in the welded joints.展开更多
30-50 wt.%graphite nanoflakes(GNFs)/6061Al matrix composites were fabricated via spark plasma sintering(SPS)at 610℃.The effects of the sintering pressure and GNF content on the microstructure and properties of the co...30-50 wt.%graphite nanoflakes(GNFs)/6061Al matrix composites were fabricated via spark plasma sintering(SPS)at 610℃.The effects of the sintering pressure and GNF content on the microstructure and properties of the composites were investigated.The results indicated that interfacial reactions were inhibited during SPS because no Al4C3 was detected.Moreover,the agglomeration of the GNFs increased,and the distribution orientation of the GNFs decreased with increasing the GNF content.The relative density,bending strength,and coefficient of thermal expansion(CTE)of the composites decreased,while the thermal conductivity(TC)in the X−Y direction increased.As the sintering pressure increased,the GNFs deagglomerated and were distributed preferentially in the X−Y direction,which increased the relative density,bending strength and TC,and decreased the CTE of the composites.The 50wt.%GNFs/6061Al matrix composite sintered at 610℃ under 55 MPa demonstrated the best performance,i.e.,bending strength of 72 MPa,TC and CTE(RT−100℃)of 254 W/(m·K)and 8.5×10^(−6)K^(−1)in the X−Y direction,and 55 W/(m·K)and 9.7×10^(−6)K^(−1)in the Z direction,respectively.展开更多
文摘Dissimilar friction stir welding between AZ31-O Mg and 6061-T6 Al alloys was investigated. 3 mm thick plates of aluminum and magnesium were used. Friction stir welding operations were performed at different rotation and travel speeds. The rotation speeds varied from 600 to 1400 r/min, and the travel speed varied from 20 to 60 mm/min. Defect-free weld was obtained with a rotation speed of 1000 r/min and travel speed of 40 mm/min. Metallographic studies showed that the grain size in the stir zone is much finer than that in the base metals. Complex flow pattern was formed in the stir zone. Microhardness measurement revealed an uneven distribution in the stir zone. Tensile test results indicated that the tensile strength of the welded specimen is about 76% of AZ31 Mg alloy and 60% of the 6061 Al alloy in tensile strength. SEM fracture surface image of the welded specimen indicated that the welded specimen failed through brittle-mode fracture.
基金Projects(2019JJ70077,2019JJ50510) supported by the National Science Foundation of Hunan Province,ChinaProject(31665004) supported by Open Fund of State Key Laboratory of Advanced Design and Manufacture for Vehicle Body,ChinaProjects(18B552,18B285) supported by Scientific Research Fund of Hunan Provincial Education Department,China
文摘6061 aluminum alloy T-joints were welded by double-pulsed MIG welding process. Then, the post-weld heat treatment was performed on the welded T-joints. The weld microstructure under different aging temperature and time was investigated by transmission electron microscopy and scanning electron microscopy. The mechanical properties were examined by hardness test and tensile test. The results showed that the micro-hardness was sensitive to heat treatment temperature and time. Increasing temperature was beneficial to the shortening of peak aging time. There were a large number of dislocations and few precipitates in the welded joints. With the increase of post-weld heat treatment temperature and time, the density of dislocation decreased. Meanwhile, the strengthening phase precipitated and grew up gradually. When the post-weld heat treatment temperature increased up to 200℃, large Q' phases were observed. And they were responsible for the peak value of the micro-hardness in the welded joints.
基金financial support from the International Science&Technology Cooperation Program of China(No.2014DFA50860)。
文摘30-50 wt.%graphite nanoflakes(GNFs)/6061Al matrix composites were fabricated via spark plasma sintering(SPS)at 610℃.The effects of the sintering pressure and GNF content on the microstructure and properties of the composites were investigated.The results indicated that interfacial reactions were inhibited during SPS because no Al4C3 was detected.Moreover,the agglomeration of the GNFs increased,and the distribution orientation of the GNFs decreased with increasing the GNF content.The relative density,bending strength,and coefficient of thermal expansion(CTE)of the composites decreased,while the thermal conductivity(TC)in the X−Y direction increased.As the sintering pressure increased,the GNFs deagglomerated and were distributed preferentially in the X−Y direction,which increased the relative density,bending strength and TC,and decreased the CTE of the composites.The 50wt.%GNFs/6061Al matrix composite sintered at 610℃ under 55 MPa demonstrated the best performance,i.e.,bending strength of 72 MPa,TC and CTE(RT−100℃)of 254 W/(m·K)and 8.5×10^(−6)K^(−1)in the X−Y direction,and 55 W/(m·K)and 9.7×10^(−6)K^(−1)in the Z direction,respectively.