The microstructure in vacuum-assisted high-pressure die casting(HPDC) Mg-4Al-4RE(AE44) alloy was studied. Special attention was paid to the characteristics of defect bands and their formation mechanisms. Since double ...The microstructure in vacuum-assisted high-pressure die casting(HPDC) Mg-4Al-4RE(AE44) alloy was studied. Special attention was paid to the characteristics of defect bands and their formation mechanisms. Since double defect bands are commonly observed, the cross section of die cast samples is divided into five parts with different grain morphologies and size distributions. The inner defect band is much wider than the outer one. Both the defect bands are solute segregation bands, resulting in a higher area fraction of Al;RE;phase than that in the adjacent regions. No obvious aggregation of porosities is observed in the defect bands of AE44 alloy. This may be due to a narrow solidification temperature range of AE44 alloy and a large amount of latent heat released during the precipitation of intermetallic phases. The formation of the defect bands is related to the shear stress acting upon the partially solidified alloy, which can lead to collapse of the grain network. However, the generation mechanisms of shear stress in the outer and inner defect bands are quite different.展开更多
The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC proces...The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC process and casting structure on the distribution of defect bands.Results show that the defect bands are solute segregation bands with the enrichment of Al,Ce and La elements,which are basically in the form of Al_(11)RE_(3) phase.There is no obvious aggregation of porosities in the defect bands.The width of the inner defect band is 4-8 times larger than that of the outer one.The variation trends of the distribution of the inner and outer defect bands are not consistent under different process parameters and at different locations of castings.This is due to the discrepancy between the formation mechanisms of double defect bands.The filling and solidification behavior of the melt near the chilling layer is very complicated,which finally leads to a fluctuation of the width and location of the outer defect band.By affecting the content and aggregation degree of externally solidified crystals(ESCs)in the cross section of die castings,the process parameters and casting structure have a great influence on the distribution of the inner defect band.展开更多
The interaction between a molten magnesium alloy AE44 and a SiC?Al2O3?SiO2 ceramics and the resulting reaction products were studied. The samples were investigated using optical and electron microscopy, energy dispers...The interaction between a molten magnesium alloy AE44 and a SiC?Al2O3?SiO2 ceramics and the resulting reaction products were studied. The samples were investigated using optical and electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction. SiO2was predominantly reduced by Mg during the contact of the magnesium-rich melt with the ceramics. The main reaction product was MgO, whilst Si dissolved in the melt. Two novel tetragonal phases formed at the interface: AlSiRE and AlMgSiRE, having a specific mutual crystallographic orientation relationship. The interactions resulted in strongly connected interfaces between the metal and ceramics after short interaction time; however, interactions lead to disintegration of the ceramics after longer contact time.展开更多
基金the financial supports from the the National Natural Science Foundation of China (No. 51805389)the Natural Science Foundation of Hubei Province, China (No. 2018CFB210)the “111” Project, China (No. B17034)
文摘The microstructure in vacuum-assisted high-pressure die casting(HPDC) Mg-4Al-4RE(AE44) alloy was studied. Special attention was paid to the characteristics of defect bands and their formation mechanisms. Since double defect bands are commonly observed, the cross section of die cast samples is divided into five parts with different grain morphologies and size distributions. The inner defect band is much wider than the outer one. Both the defect bands are solute segregation bands, resulting in a higher area fraction of Al;RE;phase than that in the adjacent regions. No obvious aggregation of porosities is observed in the defect bands of AE44 alloy. This may be due to a narrow solidification temperature range of AE44 alloy and a large amount of latent heat released during the precipitation of intermetallic phases. The formation of the defect bands is related to the shear stress acting upon the partially solidified alloy, which can lead to collapse of the grain network. However, the generation mechanisms of shear stress in the outer and inner defect bands are quite different.
基金the National Natural Science Foundation of China(No.51805389)the Key R&D Program of Hubei Province,China(No.2021BAA048)+1 种基金the 111 Project(No.B17034)the fund of the Hubei Key Laboratory of Advanced Technology for Automotive Components,Wuhan University of Technology(No.XDQCKF2021011).
文摘The characteristics of defect bands in the microstructure of high pressure die casting(HPDC)AE44 magnesium alloy were investigated.Special attention was paid to the effects of process parameters during the HPDC process and casting structure on the distribution of defect bands.Results show that the defect bands are solute segregation bands with the enrichment of Al,Ce and La elements,which are basically in the form of Al_(11)RE_(3) phase.There is no obvious aggregation of porosities in the defect bands.The width of the inner defect band is 4-8 times larger than that of the outer one.The variation trends of the distribution of the inner and outer defect bands are not consistent under different process parameters and at different locations of castings.This is due to the discrepancy between the formation mechanisms of double defect bands.The filling and solidification behavior of the melt near the chilling layer is very complicated,which finally leads to a fluctuation of the width and location of the outer defect band.By affecting the content and aggregation degree of externally solidified crystals(ESCs)in the cross section of die castings,the process parameters and casting structure have a great influence on the distribution of the inner defect band.
基金financed by the Slovenian Research Agency (ARRS), projects 1000-09-310152 and L2-2269
文摘The interaction between a molten magnesium alloy AE44 and a SiC?Al2O3?SiO2 ceramics and the resulting reaction products were studied. The samples were investigated using optical and electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction. SiO2was predominantly reduced by Mg during the contact of the magnesium-rich melt with the ceramics. The main reaction product was MgO, whilst Si dissolved in the melt. Two novel tetragonal phases formed at the interface: AlSiRE and AlMgSiRE, having a specific mutual crystallographic orientation relationship. The interactions resulted in strongly connected interfaces between the metal and ceramics after short interaction time; however, interactions lead to disintegration of the ceramics after longer contact time.