The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyse...The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.展开更多
Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is eff...Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.展开更多
CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning ...CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.展开更多
A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence...A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.展开更多
B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells....B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.展开更多
Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effec...Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effect of surface tension/viscosity ratio on flatting time was analyzed.The results demonstrated that LAS glass can polish effectively when polishing at 1 300 ℃ for 8 min,and the optimum flatting and polishing temperature was 1 250-1 300 ℃.展开更多
The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential ther...The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.展开更多
Er^(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_2·(25-x/2)Al_2O_3·xAlF_3·9.1La_2O_3·0.6Er_2O_3·0.3Yb_2O_3(x=4, 8, 12, 20, 30) (mol%) were prepared and...Er^(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_2·(25-x/2)Al_2O_3·xAlF_3·9.1La_2O_3·0.6Er_2O_3·0.3Yb_2O_3(x=4, 8, 12, 20, 30) (mol%) were prepared and their glass transition temperatures and spectroscopic properties were investigated.The Ω_2, Ω_4, and Ω_6 intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass,Ω_2 decreased gradually with the increase of AlF_3 content,but both Ω_4 and Ω_6 did not increase until AlF_3 content increased to 30 mol%.The quantum efficiency of ~4I_(13/2) to ~4I_(15/2) transition of Er^(3+) ions increases with the increase of AlF_3 content in glass.Fluorescent lifetime is longer in glass containing more AlF_3 content.展开更多
Owing to adjustable thermal expansion performance, BaO–CaO–Al_2O_3–B_2O_3–SiO_2(BCABS) glass has a promising commercialization prospect for intermediate temperature-solid oxide fuel cells(IT-SOFCs) sealing. Herein...Owing to adjustable thermal expansion performance, BaO–CaO–Al_2O_3–B_2O_3–SiO_2(BCABS) glass has a promising commercialization prospect for intermediate temperature-solid oxide fuel cells(IT-SOFCs) sealing. Herein, Al_2O_3 with two different contents was added into the same glass formulation, referred to as A and B glass, respectively. In terms of the non-isothermal crystallization kinetic behavior, the effect of Al_2O_3 as the unique intermediate was innovatively studied on the long-term performance of BCABS sealing glass. After the heat treatment at 1023 K for 100 h, the change of the network structure and the expansion coefficient of the glass were characterized. The results showed that the addition of Al_2O_3 as a network forming body could enhance the structure of glass, and increase the activation energy for glass transition, which could effectively inhibit the crystallization ability of sealing glass. Therefore, the B glass with the higher Al_2O_3 content showed the better long-term sealing ability, which was greatly beneficial for IT-SOFCs sealing.展开更多
基金Projects(51264023,51364020,U1202271)supported by the National Natural Science Foundation of ChinaProject(IRT1250)supported by the Program for Innovative Research Team in University of Ministry of Education of ChinaProject(2014HA003)supported by the Science and Technology Leading Talent of Yunnan Province,China
文摘The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.
文摘Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject(BE2010194) supported by Science&Technology Pillar Program of Jiangsu Province, China+1 种基金Project(KF201103) supported by the State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, ChinaProject supported by the Priority Academic Development of Jiangsu Higher Education Institutions, China
文摘CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.
基金supported by the Education Department of Zhejiang Province (20050359)
文摘A near infrared to visible blue, green, and red upconversion luminescence in a Tb^3＋-doped CaO-Al2O3-SiO2 glass was studied, which was excited using 800 nm femtosecond laser irradiation. The upconversion luminescence was attributed to ^5D3→^7F5, ^5D3→^7F4, ^5D3→^7F3, ^5D4→^7F6, ^5D4→^7F5, ^5D4→^7F4, and ^5D4→^7F3 transitions of Tb^3＋. The relationship between upconversion luminescence intensity and the pump power indicated that a three-photon simultaneous absorption process was dominant in this upconversion luminescence. The intense red, green, and blue upconversion luminescence of Tb^3＋-doped CaO-Al2O3-SiO2 glass may be potentially useful in developing three-dimensional display applications.
基金Funded by the Jiangxi Provincial Department of Education(KJLD13008)the National Natural Science Foundation of China(number 51362020)the Research Fund for the Doctoral Program of Higher Education(20123601110006)
文摘B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with different Al_2O_3 contents（1mol%, 3mol%, 5mol%, and 7mol%） was prepared, and it was intended to be used as lead-free and low-melting glass sealants for solid oxide fuel cells. The effects of Al_2O_3 content on the structures, thermal properties, and sintering behaviors of the B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass were investigated in detail. The Al_2O_3 content largely influenced the structures and thermal properties of the glass. When the Al_2O_3 content 5mol%, the transition temperature of the glass decreased with the Al_2O_3 content, while the crystallization temperature increased with the Al_2O_3 content. However, higher Al_2O_3 content degraded the stability of the glass. The B_2O_3-SiO_2-ZnO-BaO-Al_2O_3 glass with 5 mol% Al_2O_3 content exhibits the optimal sintering densification characteristics and can be used as glass sealants for solid oxide fuel cells.
基金Funded partly by the National Key Technology R&D Program in the 11th Five Year Plan of China(No. 2006BAJ02B00)Natural Science Foundation of Hubei Province (No.2008CDA037)
文摘Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effect of surface tension/viscosity ratio on flatting time was analyzed.The results demonstrated that LAS glass can polish effectively when polishing at 1 300 ℃ for 8 min,and the optimum flatting and polishing temperature was 1 250-1 300 ℃.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institution, China
文摘The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.
基金The glass transition temperature of FLAS glasses decreases with the increase of AlF_3 content. The spectroscopic properties of Er~(3+)-doped FLAS glasses, which contain various amounts of AlF_3 content, have been studied by Judd-Ofelt theory and absorpti
文摘Er^(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_2·(25-x/2)Al_2O_3·xAlF_3·9.1La_2O_3·0.6Er_2O_3·0.3Yb_2O_3(x=4, 8, 12, 20, 30) (mol%) were prepared and their glass transition temperatures and spectroscopic properties were investigated.The Ω_2, Ω_4, and Ω_6 intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass,Ω_2 decreased gradually with the increase of AlF_3 content,but both Ω_4 and Ω_6 did not increase until AlF_3 content increased to 30 mol%.The quantum efficiency of ~4I_(13/2) to ~4I_(15/2) transition of Er^(3+) ions increases with the increase of AlF_3 content in glass.Fluorescent lifetime is longer in glass containing more AlF_3 content.
基金financially supported by the research project of National Natural Science Foundation of China (Grant Nos.51662015 and 51462011)
文摘Owing to adjustable thermal expansion performance, BaO–CaO–Al_2O_3–B_2O_3–SiO_2(BCABS) glass has a promising commercialization prospect for intermediate temperature-solid oxide fuel cells(IT-SOFCs) sealing. Herein, Al_2O_3 with two different contents was added into the same glass formulation, referred to as A and B glass, respectively. In terms of the non-isothermal crystallization kinetic behavior, the effect of Al_2O_3 as the unique intermediate was innovatively studied on the long-term performance of BCABS sealing glass. After the heat treatment at 1023 K for 100 h, the change of the network structure and the expansion coefficient of the glass were characterized. The results showed that the addition of Al_2O_3 as a network forming body could enhance the structure of glass, and increase the activation energy for glass transition, which could effectively inhibit the crystallization ability of sealing glass. Therefore, the B glass with the higher Al_2O_3 content showed the better long-term sealing ability, which was greatly beneficial for IT-SOFCs sealing.