In situ study on columnar-equiaxed transition and anaxial columnar dendrite growth of Al-15%Cu alloy by synchrotron radiography 被引量:3
1
作者 李发国 东青 +5 位作者 张佼 戴永兵 付亚楠 谢红兰 尹付成 孙宝德 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2014年第7期2112-2116,共5页
Directional solidification of Al-15% (mass fraction) Cu alloy was investigated by in situ and real time radiography which was performed by Shanghai synchrotron radiation facility (SSRF). The imaging results reveal... Directional solidification of Al-15% (mass fraction) Cu alloy was investigated by in situ and real time radiography which was performed by Shanghai synchrotron radiation facility (SSRF). The imaging results reveal that columnar to equiaxed transition (CET) is provoked by external thermal disturbance. The detaching and floating of fragments of dendrite arms are the prelude of the transition when the solute boundary layer in front of the solid-liquid interface is thin. And the dendrite triangular tip is the fracture sensitive zone. When the conditions are suitable, new dendrites can sprout and grow up. This kind of dendrite has no obvious stem and is named anaxial columnar dendrites. 展开更多
关键词 al-15%Cu alloy directional solidification columnar to equiaxed transition synchrotron X-ray radiography
下载PDF
石墨和硅对偏晶Al-15Pb合金组织和耐磨性能的影响
2
作者 王振玲 张宏芳 +2 位作者 江宇红 王佳杰 李莉 《佳木斯大学学报(自然科学版)》 CAS 2010年第5期732-735,共4页
采用金相显微镜、X射线衍射仪和摩擦磨损试验机对A l-15Pb、A l-15b-5Si-0.2RE和A l-15Pb-5Si-2G-0.2RE合金的组织和耐磨性能进行了研究.试验结果表明:将合金液浇注到金属型中后,其凝固组织中,铅相呈粒状分布于铝基体中;加入硅后,硅相... 采用金相显微镜、X射线衍射仪和摩擦磨损试验机对A l-15Pb、A l-15b-5Si-0.2RE和A l-15Pb-5Si-2G-0.2RE合金的组织和耐磨性能进行了研究.试验结果表明:将合金液浇注到金属型中后,其凝固组织中,铅相呈粒状分布于铝基体中;加入硅后,硅相沿晶界偏聚;同时加入硅和石墨后,铅相、硅相均呈颗粒状分布,且Si相均匀分布,无偏聚.在三组合金中,随着硅和石墨的加入,摩擦系数逐渐减小,磨损失重逐渐减小,A l-15Pb-5Si-2G-0.2RE合金表现出较佳的耐磨性能. 展开更多
关键词 al-15pb合金 石墨 显微组织 耐磨性能
下载PDF
Microstructure and Wear Characteristics of Al-4.5Cu-5Pb Alloy
3
作者 Om Prakas Pandey(School of Basic and Applied Sciences, Thapar Institute of Engineering & Technology, Patiala-147001, India) 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 1998年第2期125-131,共7页
Al-4. 5Cu-5Pb alloy was prepared by sand and chill casting. The same alloy was also spray deposited at a gas pressure of 1.6 MPa. The microstructural features exhibit a coarse to fine dendritic morphology for sand ... Al-4. 5Cu-5Pb alloy was prepared by sand and chill casting. The same alloy was also spray deposited at a gas pressure of 1.6 MPa. The microstructural features exhibit a coarse to fine dendritic morphology for sand and chill cast alloys. Equiaxed grains were observed for spray formed alloys. Wear testing employing a pin-on-disc type set-up, reveals considerably lower wear of spray deposited alloy compared to that of chill and sand cast alloys. The morphological features of wear track on specimen and debris indicated a mixed oxidative-cum-adhesive wear mechanisms for these alloys tested in the present investigation. (Edited author abstract) 36 Refs. 展开更多
关键词 AL CU Microstructure and Wear Characteristics of al-4.5Cu-5pb alloy pb
全文增补中
电脉冲处理对Sn-15%Pb合金凝固组织中枝晶形态的影响 被引量:6
4
作者 王静松 薛庆国 +3 位作者 石向东 范方国 许建国 苍大强 《北京科技大学学报》 EI CAS CSCD 北大核心 2005年第2期193-196,共4页
研究了电脉冲处理对Sn-15%Pb合金凝固组织的影响.通过对Sn-15%Pb合金熔体 施加电脉冲处理,其凝固组织发生了由原始的树枝晶向球状组织的转化,同时晶粒发生明显 细化.分析认为,由于电脉冲处理作用,合金熔体结构发生了改变,使熔体中Pb... 研究了电脉冲处理对Sn-15%Pb合金凝固组织的影响.通过对Sn-15%Pb合金熔体 施加电脉冲处理,其凝固组织发生了由原始的树枝晶向球状组织的转化,同时晶粒发生明显 细化.分析认为,由于电脉冲处理作用,合金熔体结构发生了改变,使熔体中Pb的活度提高, 进而引起溶质平衡分配系数的变化,导致凝固前沿的溶质富集减轻,溶质分布情况发生改变, 促使树枝晶向球状组织转化,并且使凝固组织发生细化. 展开更多
关键词 Sn-15%pb合金 电脉冲 熔体结构 凝固组织 活度
下载PDF
振动冷却通道对Sn-15%Pb合金凝固组织的影响 被引量:2
5
作者 刘文锋 王猛 +1 位作者 林鑫 黄卫东 《铸造技术》 CAS 北大核心 2007年第3期359-362,共4页
对传统冷却斜板铸造法进行了改进,在冷却通道上设置振动源对Sn-15wt%Pb熔体施加机械振动,并以表观晶粒形态和尺度来描述凝固组织特征,研究工艺参数对凝固组织的影响。结果显示:对冷却通道施加振动可以改变表观晶粒形态和特征尺度;较高... 对传统冷却斜板铸造法进行了改进,在冷却通道上设置振动源对Sn-15wt%Pb熔体施加机械振动,并以表观晶粒形态和尺度来描述凝固组织特征,研究工艺参数对凝固组织的影响。结果显示:对冷却通道施加振动可以改变表观晶粒形态和特征尺度;较高的振动加速度有助于表观晶粒细化;较高的冷却速率有助于减小表观晶粒特征尺度,但其形态圆整度降低。 展开更多
关键词 半固态 振动 激冷导流管 Sn-15%pb合金
下载PDF
Al-15Pb合金高压下凝固及热处理后的组织与耐磨性 被引量:1
6
作者 王振玲 于玉城 +2 位作者 霍树斌 尹冬松 魏尊杰 《特种铸造及有色合金》 CAS CSCD 北大核心 2014年第4期353-356,共4页
采用高压六面顶在4GPa下制备了Al-15Pb合金并在该压力下进行了热处理。通过扫描电镜(SEM)、能谱仪(EDX)、X射线衍射仪(XRD)、摩擦磨损试验机对制备的Al-15Pb合金进行了微观组织和耐磨性能的研究。结果表明,常压和高压下,Al-15Pb合金均由... 采用高压六面顶在4GPa下制备了Al-15Pb合金并在该压力下进行了热处理。通过扫描电镜(SEM)、能谱仪(EDX)、X射线衍射仪(XRD)、摩擦磨损试验机对制备的Al-15Pb合金进行了微观组织和耐磨性能的研究。结果表明,常压和高压下,Al-15Pb合金均由α-Al相和Pb粒子相组成,但是常压凝固时大量Pb粒子分布于Al基体上,而高压凝固后,Pb粒子数量减少,尺寸减小;高压热处理时,分布于Al基体上的Pb粒子相数量极少,且尺寸很大。常压凝固时,Pb在α-Al相中固溶度为0,高压凝固和高压热处理时,Pb在α-Al相中均有一定的固溶度。高压凝固Al-15Pb合金中α-Al相的硬度比常压时大很多,增大39%,高压热处理态时α-Al相硬度也增大,增大了19%。高压条件制备的Al-15Pb合金的抗磨性能改善,但减摩性能变差。 展开更多
关键词 al-15pb合金 高压凝固 高压热处理 显微组织