M-type Al-doped strontium ferrite powders （SrA1xFe2n-xO19, n = 5.9） with nominal Al content of x = 0-2.0 are prepared by traditional ceramic technology. The phase identification of the powders, performed using x-ray...M-type Al-doped strontium ferrite powders （SrA1xFe2n-xO19, n = 5.9） with nominal Al content of x = 0-2.0 are prepared by traditional ceramic technology. The phase identification of the powders, performed using x-ray diffraction, shows the presence of purity hexaferrite structure and absence of any secondary phase. The lattice parameters decrease with increasing x. The average grain size of the powders is about 300 nm-400 nm at Al3＋ ion content x = 0-2.0. The room- temperature hysteresis loops of the powders, measured by using vibrating sample magnetometer, show that the specific saturation magnetization （σs） value continuously decreases while the coercivity （Hc） value increases with increasing x, and He reaches to 9759 Oe （1 Oe = 79.5775 A/m） at x = 2.0. According to the law of approach saturation, Hc value increases with increasing Al3＋ ion content, which is attributed to the saturation magnetization （Ms） decreasing more rapidly than the magnetic anisotropy constant （Kl） obtained by numerical fitting of the hysteresis loops. The distribution of Al3＋ ions in the hexaferrite structure of SrAlxFe2n- xO19 is investigated by using 57Co Mtssbauer spectroscopy. The effect of Al3＋ doping on static magnetic properties contributes to the improvement of magnetic anisotropy field.展开更多
文摘M-type Al-doped strontium ferrite powders （SrA1xFe2n-xO19, n = 5.9） with nominal Al content of x = 0-2.0 are prepared by traditional ceramic technology. The phase identification of the powders, performed using x-ray diffraction, shows the presence of purity hexaferrite structure and absence of any secondary phase. The lattice parameters decrease with increasing x. The average grain size of the powders is about 300 nm-400 nm at Al3＋ ion content x = 0-2.0. The room- temperature hysteresis loops of the powders, measured by using vibrating sample magnetometer, show that the specific saturation magnetization （σs） value continuously decreases while the coercivity （Hc） value increases with increasing x, and He reaches to 9759 Oe （1 Oe = 79.5775 A/m） at x = 2.0. According to the law of approach saturation, Hc value increases with increasing Al3＋ ion content, which is attributed to the saturation magnetization （Ms） decreasing more rapidly than the magnetic anisotropy constant （Kl） obtained by numerical fitting of the hysteresis loops. The distribution of Al3＋ ions in the hexaferrite structure of SrAlxFe2n- xO19 is investigated by using 57Co Mtssbauer spectroscopy. The effect of Al3＋ doping on static magnetic properties contributes to the improvement of magnetic anisotropy field.