A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were...A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni–P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90°and was not corroded visually after 500 h of neutral salt spray test at 35℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.展开更多
Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were inves...Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were investigated by electron backscatter diffraction characterization, Vickers hardness measurements, and tensile testing. The results showed that liquid CO_(2) coolant significantly reduced the peak temperature and increased the cooling rate, so the rapidly cooled FSW joint exhibited fine grains with a large number of dislocations. The grain refinement mechanism of the FSW A1050 pure aluminum joint was primarily attributed to the combined effects of continuous dynamic recrystallization, grain subdivision, and geometric dynamic recrystallization. Compared with conventional FSW, the yield strength, ultimate tensile strength, and fracture elongation of rapidly cooled FSW joint were significantly enhanced, and the welding efficiency was increased from 80% to 93%. The enhanced mechanical properties and improved synergy of strength and ductility were obtained due to the increased dislocation density and remarkable grain refinement. The wear of the tool can produce several WC particles retained in the joint, and the contribution of second phase strengthening to the enhanced strength should not be ignored.展开更多
Aluminum hypophosphite microspheres(AHP) were synthesized by hydrothermal method using NaH2PO2·H2O and AlCl3·6H2O as raw materials, and then the AHP microspheres were polymerized by surface polymerization of...Aluminum hypophosphite microspheres(AHP) were synthesized by hydrothermal method using NaH2PO2·H2O and AlCl3·6H2O as raw materials, and then the AHP microspheres were polymerized by surface polymerization of micro-nanospheres with cyclic cross-linked poly(cyclotriphosphazene-co-4,4'-sulfonyldiphenol)(PZS). A new organic-inorganic poly(phosphonitrile)-modified aluminum hypophosphite microspheres(PZS-AHP) were synthesized by encapsulation and applied to flame retardant thermoplastic polyurethane(TPU). The microstructure and chemical composition of the PZS-AHP microsphere were characterized by scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy and X-ray spectroscopy. The thermal stability of PZS-AHP microsphere was explored with thermogravimetric analysis. Thermogravimetric data indicate that the PZS-AHP microspheres have excellent thermal stability. The thermal and flame-retarding properties of the TPU composites were evaluated by thermogravimetric(TG), limited oxygen index tests(LOI), and cone calorimeter test(CCT). The TPU composite achieved vertical burning(UL-94) V-0 grade and LOI value reached 29.2% when 10 wt% PZS-AHP was incorporated. Compared with those of pure TPU, the peak heat release rate(pHRR) and total heat release(THR) of TPU/10%PZS-AHP decreased by 82.2% and 42.5%, respectively. The results of CCT indicated that PZS-AHP microsphere could improve the flame retardancy of TPU composites.展开更多
With the large-scale service of lithium-ion batteries(LIBs),their failures have attracted significant attentions.While the decay of active materials is the primary cause for LIB failures,the degradation of auxiliary m...With the large-scale service of lithium-ion batteries(LIBs),their failures have attracted significant attentions.While the decay of active materials is the primary cause for LIB failures,the degradation of auxiliary materials,such as current collector corrosion,should not be disregarded.Therefore,it is necessary to conduct a comprehensive review in this field.In this review,from the perspectives of electrochemistry and materials,we systematically summarize the corrosion behavior of aluminum cathode current collector and propose corresponding countermeasures.Firstly,the corrosion type is clarified based on the properties of passivation layers in different organic electrolyte components.Furthermore,a thoroughgoing analysis is presented to examine the impact of various factors on aluminum corrosion,including lithium salts,organic solvents,water impurities,and operating conditions.Subsequently,strategies for electrolyte and protection layer employed to suppress corrosion are discussed in detail.Lastly and most importantly,we provide insights and recommendations to prevent corrosion of current collectors,facilitate the development of advanced current collectors and the implementation of next-generation high-voltage stable LIBs.展开更多
The evolution of microstructure during hot deformation is key to achieving good mechanical properties in aluminum alloys.We have developed a cellular automaton(CA) based model to simulate the microstructural evolution...The evolution of microstructure during hot deformation is key to achieving good mechanical properties in aluminum alloys.We have developed a cellular automaton(CA) based model to simulate the microstructural evolution in 7075 aluminum alloy during hot deformation.Isothermal compression tests were conducted to obtain material parameters for 7075 aluminum alloy,leading to the establishment of models for dislocation density,nucleation of recrystallized grains,and grain growth.Integrating these aspects with grain topological deformation,our CA model effectively predicts flow stress,dynamic recrystallization(DRX) volume fraction,and average grain size under diverse deformation conditions.A systematic comparison was made between electron back scattered diffraction(EBSD) maps and CA model simulated under different deformation temperatures(573 to 723 K),strain rates(0.001 to 1 s^(-1)),and strain amounts(30% to 70%).These analyses indicate that large strain,high temperature,and low strain rate facilitate dynamic recrystallization and grain refinement.The results from the CA model show good accuracy and predictive capability,with experimental error within 10%.展开更多
The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp...The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.展开更多
Energetic nanofluid fuel has caught the attention of the field of aerospace liquid propellant for its high energy density(HED), but it suffers from the inevitable solid-liquid phase separation problem. To resolve this...Energetic nanofluid fuel has caught the attention of the field of aerospace liquid propellant for its high energy density(HED), but it suffers from the inevitable solid-liquid phase separation problem. To resolve this problem, herein we synthesized the high-Al-/B-containing(up to 30%(mass)) HED gelled fuels, with low-molecular-mass organic gellant Z, which show high net heat of combustion(NHOC), density, storage stability, and thixotropic properties. The characterizations indicate that the application of energetic particles to the gelled fuels obviously destroys their fibrous network structures but can provide the new particle-gellant gelation microstructures, resulting in the comparable stability between 1.0%(mass) Z/JP-10 + 30%(mass) Al or B and pure JP-10 gelled fuel. Moreover, the gelled fuels with high-content Al or B exhibit high shear-thinning property, recovery capability, and mechanical strength, which are favorable for their storage and utilization. Importantly, the prepared 1.0%(mass) Z/JP-10 + 30%(mass) B(or 1.0%(mass) Z/JP-10 + 30%(mass) Al) shows the density and NHOC 1.27 times(1.30) and 1.43 times(1.21)higher than pure JP-10, respectively. This work provides a facile and valid approach to the manufacturing of HED gelled fuels with high content of energetic particles for gel propellants.展开更多
The widespread adoption of aluminumalloy electric buses,known for their energy efficiency and eco-friendliness,faces a challenge due to the aluminum frame’s susceptibility to deformation compared to steel.This issue ...The widespread adoption of aluminumalloy electric buses,known for their energy efficiency and eco-friendliness,faces a challenge due to the aluminum frame’s susceptibility to deformation compared to steel.This issue is further exacerbated by the stringent requirements imposed by the flammability and explosiveness of batteries,necessitating robust frame protection.Our study aims to optimize the connectors of aluminum alloy bus frames,emphasizing durability,energy efficiency,and safety.This research delves into Multi-Objective Coordinated Optimization(MCO)techniques for lightweight design in aluminum alloy bus body connectors.Our goal is to enhance lightweighting,reinforce energy absorption,and improve deformation resistance in connector components.Three typical aluminum alloy connectors were selected and a design optimization platform was built for their MCO using a variety of software and methods.Firstly,through three-point bending experiments and finite element analysis on three types of connector components,we identified optimized design parameters based on deformation patterns.Then,employing Optimal Latin hypercube design(OLHD),parametric modeling,and neural network approximation,we developed high-precision approximate models for the design parameters of each connector component,targeting energy absorption,mass,and logarithmic strain.Lastly,utilizing the Archive-based Micro Genetic Algorithm(AMGA),Multi-Objective Particle Swarm Optimization(MOPSO),and Non-dominated SortingGenetic Algorithm(NSGA2),we explored optimized design solutions for these joint components.Subsequently,we simulated joint assembly buckling during bus rollover crash scenarios to verify and analyze the optimized solutions in three-point bending simulations.Each joint component showcased a remarkable 30%–40%mass reduction while boosting energy absorption.Our design optimization method exhibits high efficiency and costeffectiveness.Leveraging contemporary automation technology,the design optimization platform developed in this study is poised to facilitate intelligent optimization of lightweight metal components in future applications.展开更多
Aluminum (Al) toxicity is a considerable factor limiting crop yield and biomass in acidic soil. Tartary buckwheatgrowing in acidic soil may suffer from Al poisoning. Here, we investigated the influence of Al stress on...Aluminum (Al) toxicity is a considerable factor limiting crop yield and biomass in acidic soil. Tartary buckwheatgrowing in acidic soil may suffer from Al poisoning. Here, we investigated the influence of Al stress on the growthof tartary buckwheat seedling roots, and the alleviation of Al stress by silicon (Si), as has been demonstrated inmany crops. Under Al stress, root growth (total root length, primary root length, root tips, root surface area, androot volume) was significantly inhibited, and Al and malondialdehyde (MDA) accumulated in the root tips. At thesame time, catalase (CAT) and ascorbate peroxidase activities, polyphenols, flavonoids, and 1,1-diphenyl-2-picrylhydrazyl(DPPH) and 2,2′-azinobis-(3-ethylbenzthiazoline-6-sulphonate) (ABTS) free-radical scavenging abilitywere significantly decreased. After the application of Si, root growth, Al accumulation, and oxidative damage wereimproved. Compared to Al-treated seedlings, the contents of ·O2− and MDA decreased by 29.39% and 25.22%,respectively. This was associated with Si-induced increases in peroxidase and CAT enzyme activity, flavonoidcompounds, and free-radical scavenging (DPPH and ABTS). The application of Si therefore has positive effectson Al toxicity in tartary buckwheat roots by reducing Al accumulation in the roots and maintaining oxidationhomeostasis.展开更多
Aiming at improving the properties of magnesia carbon materials,silicon aluminum carbide(Al_(4)SiC_(4))containing materials were prepared using industrial aluminum powder,silicon carbide powder,and graphite as raw mat...Aiming at improving the properties of magnesia carbon materials,silicon aluminum carbide(Al_(4)SiC_(4))containing materials were prepared using industrial aluminum powder,silicon carbide powder,and graphite as raw materials,and activated alumina powder as an additive,mixing thoroughly,pressing into cylinders and then firing at 1200℃for 30 min in a carbon embedded atmosphere by the microwave method.The effects of the aluminum powder addition(20%and 24%,by mass)and activated alumina powder addition(0,3%,5%and 7%,by mass)on the microwave synthesis of Al_(4)SiC_(4) as well as the effect of the obtained Al_(4)SiC_(4) containing material on the properties of magnesia carbon bricks were studied.The results show that:compared with the samples with 20%aluminum powder,those with 24%aluminum powder generate more Al_(4)SiC_(4).With the activated alumina powder addition increasing from 0 to 7%,the amount of Al_(4)SiC_(4) generated increases first and then decreases.Compared with the sample without activated alumina powder,the samples with activated alumina powder show lower bulk density and higher apparent porosity.With the activated alumina powder addition increasing from 3%to 7%,the bulk density of the samples increases first and then decreases,while the apparent porosity of the samples shows an opposite trend.The optimal additions are 24%aluminum powder and 5%activated alumina powder,and Al_(4)SiC_(4) synthesized in this sample has a hexagonal plate structure.With the synthesized Al_(4)SiC_(4) containing material added,the magnesia carbon brick has slightly increased cold modulus of rupture,basically the same modulus of elasticity and improved oxidation resistance.展开更多
The soil chemistry of gallium, indium, and thallium is not well defined, particularly with emerging evidence that these elements have toxic properties and may influence food safety. The purpose of this investigation w...The soil chemistry of gallium, indium, and thallium is not well defined, particularly with emerging evidence that these elements have toxic properties and may influence food safety. The purpose of this investigation was to estimate the soil concentrations of gallium, indium, and thallium and determine if these elements have a soil chemistry like aluminum and therefore demonstrate significant concentration correlations with aluminum. Twenty-seven soil series were selected, and the elemental concentrations were determined using aqua regia digestion with analytical determination performed using inductively coupled plasma emission-mass spectroscopy. The concentrations of gallium, indium, and thallium generally compared with the known literature. Aluminum-gallium and aluminum-thallium exhibited significant concentration correlations across the soil horizons of the sampled soils. Aluminum, gallium, and thallium did demonstrate concentration increases in soil horizons having illuviation of phyllosilicates, implying these phyllosilicates have adsorption and isomorphic substitution behaviors involving these elements.展开更多
This research considered the effect of non-natural aging on the microstructural characteristics and mechanical properties of as-cast aluminum 6063 alloys. The samples were developed through a sand casting process and ...This research considered the effect of non-natural aging on the microstructural characteristics and mechanical properties of as-cast aluminum 6063 alloys. The samples were developed through a sand casting process and machined into tensile and impact test samples before carrying out solution heat treatment at 550?C (0.83 T<sub>m</sub>) on two parts of the samples while retaining one part as the control. The two parts were further divided into sets denoted A and B and were aged at 180?C (0.27 T<sub>m</sub>) and 160?C (0.24 T<sub>m</sub>), respectively, for 12 hours. The results showed that sample A has the optimal yield strength and ultimate tensile strength of 192 and 206 MPa, respectively. Likewise, the sample gave the highest impact strength value of about 9.63 J/mm<sup>2</sup>. The observed results were supported by the optical micrograph, which revealed that the sample has evenly dispersed precipitates in its microstructure. This is deemed responsible for the observed increase in strength of the sample.展开更多
The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coa...The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coating layer inhibits sintering and promotes complete combustion of particles from an atomic view,a comparative study has been done for bare ANP and PTFE coated ANP by using reactive molecular dynamics simulations.The sintering process is quantified by shrinkage ratio and gyration radius.Our results show that,at the same heating rate and combustion temperatures,bare ANPs are sintered together after the temperature exceeds the melting point of aluminum but the decomposition of PTFE coating layer pushes particles away and increases reaction surface area by producing small Al-F clusters.The sintering of ANPs which are heated in PTFE is alleviated compared with particles heated in oxygen,but particles still sinter together due to the lack of intimate contact between PTFE and alumina surface.The effect of temperature on the combustion of PTFE coated ANPs is also studied from 1000 to3500 K.The number density analysis shows the particles will not be sintered at any temperature.Aluminum fluoride prefers diffusing to the external space and the remained particles are mainly composed of Al,C and O.Fast ignition simulations are performed by adopting micro canonical ensemble.With the expansion of aluminum core and the melting of alumina shell,bare ANPs are sintered into a liquid particle directly.For PTFE coated ANPs,the volatilization of gaseous aluminum fluoride products continually endows particles opposite momentum.展开更多
In this research, the ballistic behavior of the ceramic-reinforced aluminum matrix composite plates is investigated to provide an optimal design for protecting against 7.62 mm bullet at the speed of 800 m/s experiment...In this research, the ballistic behavior of the ceramic-reinforced aluminum matrix composite plates is investigated to provide an optimal design for protecting against 7.62 mm bullet at the speed of 800 m/s experimentally and numerically. The target materials are Al5083 alloy as the metal matrix and alumina ceramic balls as the reinforcement. To simulate a 3D numerical model, ABAQUS FE code has been utilized.After validation the numerical model by experiments, the effect of ceramic ball weight percentage include 15%, 30% and 45% and the target thickness 20, 25 and 30 mm is considered on the ballistic results like the kinetic energy, residual velocity and depth of penetration. Finally, it was found that the specimen with 25 mm thickness and 30% alumina is optimum based on existing ballistic protection criteria.展开更多
Aluminum(Al) particles are good fuel additives to improve the energy output performances of explosives. Under detonation environment, reaction delay of Al particles plays a key role in the energy release efficiency. U...Aluminum(Al) particles are good fuel additives to improve the energy output performances of explosives. Under detonation environment, reaction delay of Al particles plays a key role in the energy release efficiency. Up to date, reaction delay of Al particles is still limited by the efficiency of mass and heat transfer from oxidizers to Al particles. To address this issue, a homogeneous fuel-oxidizer assembly has recently become a promising strategy. In this work, oxidizer-activated Al fuel particles(ALG) were prepared with glycidyl azide polymer(GAP) as the oxidizer. The ALG was in uniform spherical shape and core-shell structure with shell layer of around 5 nm which was observed by scanning electron microscope and transmission electron microscope. The localized nanoscale mid-IR measurement detected the uniform distribution of characteristic absorption bond of GAP in the shell layer which confirmed the homogenous fuel-oxidizer structure of ALG. A thermal gravimetric analysis of ALG at ultrafast heating rate of 1000℃/min under argon atmosphere was conducted. The decomposition of GAP finished much earlier than that of GAP at heating rate of 10℃/min. Under ultrafast high laser fluence, the reaction response of ALG was characterized and compared with that of micro-sized Al(μAl). With the increase of laser energy, the propagation distance of the shock wave increased. However, the velocity histories were nearly the same when energies were lower than 299 mJ or higher than 706 mJ. The propagation distance of the shock wave for ALG was 0.5 mm larger than that for μAl at 2.1 μs. The underwater explosion showed the peak pressure and the shock wave energy of the ALG-based explosive were both higher than those of the μAl-based explosive at 2.5 m. This study shows the feasibility to improve the energy release of Al-based explosives via using the oxidizer-activated Al fuel particles with energetic polymer as the oxidizer.展开更多
Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the s...Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the spinning sample.Results showed that the intergranular corrosion resistance of the spinning sample was higher than that of the blank sample.In addition,the electrochemical corrosion resistance of the spinning sample was higher than that of the blank sample.The EDS maps indicated a uniform element distribution pattern of aluminum and magnesium.Moreover,the phase composition and lattice constant of the samples were obtained by XRD analysis.The differences in microstructure between the aluminum alloy subjected to the spinning process and the untreated aluminum alloy were determined by EBSD.The differences were mainly attributed to the complex interactions among grain size,dislocations and grain boundaries.展开更多
The surface composite modification of the 7050 aluminum alloy friction stir-welded joints was performed by shot peening(SP)/multiple rotation rolling(MRR)and MRR/SP,and the fatigue performance of the nugget zone(NZ)wa...The surface composite modification of the 7050 aluminum alloy friction stir-welded joints was performed by shot peening(SP)/multiple rotation rolling(MRR)and MRR/SP,and the fatigue performance of the nugget zone(NZ)was investigated.The results demonstrated that the fatigue life of SP/MRR samples is longer than that of MRR/SP.On the plane 150μm below the surface.The grains with high angle grain boundary account for 71.5%and 34.3%for MRR/SP and SP/MRR samples,respectively.The crack propagation path of the MRR/SP is transgranular and intergranular,and it is intergranular for the MRR/SP.Multitudinous fatigue striations and some voids appeared at the fracture during the stable crack propagation stage.However,fatigue striations for SP/MRR are with smaller spacing,fewer holes,and smaller size under SP/MRR compared with fatigue fracture of MRR/SP.The differences in fatigue properties and fracture characteristics of the NZ are related to the microstructure after the two combined surface modifications.展开更多
Understanding the influence of purities on the electrochemical performance of pure aluminum(Al)in alkaline media for Al–air batteries is significant.Herein,we comprehensively investigate secondary phase precipitate(S...Understanding the influence of purities on the electrochemical performance of pure aluminum(Al)in alkaline media for Al–air batteries is significant.Herein,we comprehensively investigate secondary phase precipitate(SPP)-induced localized corrosion of pure Al in NaOH solution mainly based on quasi-in-situ and cross-section observations under scanning electron microscopy coupled with finite element simulation.The experimental results indicate that Al–Fe SPPs appear as clusters and are coherent with the Al substrate.In alkaline media,Al–Fe SPPs exhibit more positive potentials than the substrate,thus aggravating localized galvanic corrosion as cathodic phases.Moreover,finite element simulation indicates that the irregular geometry coupled with potential difference produces the non-uniform current density distribution inside the SPP cluster,and the current density on the Al substrate gradually decreases with distance.展开更多
Soybean soapstock(SS) is one of the main solid wastes produced in the refinery of edible oil processing. In this study, the co-pyrolysis of SS with iron slag(IS) and aluminum scrap(AS) was carried out in a tubular fur...Soybean soapstock(SS) is one of the main solid wastes produced in the refinery of edible oil processing. In this study, the co-pyrolysis of SS with iron slag(IS) and aluminum scrap(AS) was carried out in a tubular furnace. The gas, liquid and solid products were characterized and the char yield decreased with increasing IS/AS ratio. IS and AS can improve the gas yield, and when the ratio of SS/IS was 1:0.25, the total pyrolysis gas and hydrogen contents were significantly increased. The content of oxygen compounds in pyrolysis oil decreased during co-pyrolysis, while AS promoted the content of polycyclic aromatic hydrocarbons in pyrolysis oil. The co-pyrolysis reaction can be divided into four stages, the mass loss rate reaches the maximum at the third stage(390–575 ℃). The molar ratio of H/C was lower for pyrolysis,indicating good stability of pyrolysis char owing to the high degree of carbonization and aromaticity.The possible co-pyrolysis reaction mechanism was explored.展开更多
With the intensified depletion of high-grade iron ores,the increased aluminum content in iron ore concentrates has become unavoidable,which is detrimental to the pelletization process.Therefore,the effect mechanism of...With the intensified depletion of high-grade iron ores,the increased aluminum content in iron ore concentrates has become unavoidable,which is detrimental to the pelletization process.Therefore,the effect mechanism of aluminum on pellet quality must be identified.In this study,the influence of aluminum occurrence and content on the induration of hematite(H)and magnetite(M)pellets was investigated through the addition of corresponding Al-containing additives,including alumina,alumogoethite,gibbsite,and kaolinite.Systematic mineralogical analysis,combined with the thermodynamic properties of different aluminum occurrences and the quantitative characterization of consolidation behaviors,were conducted to determine the related mechanism.The results showed that the alumina from various aluminum occurrences adversely affected the induration characteristics of pellets,especially at an aluminum content of more than 2.0wt%.The thermal decomposition of gibbsite and kaolinite tends to generate internal stress and fine cracks,which hinder the respective microcrystalline bonding and recrystallization between Fe2O3particles.The adverse effect on the induration characteristics of fired pellets with different aluminum occurrences can be relieved to varying degrees through the formation of liquid phase bonds between the hematite particles.Kaolinite is more beneficial to the induration process than the other three aluminum occurrences because of the formation of more liquid phase,which improves pellet consolidation.The research results can further provide insights into the effect of aluminum occurrence and content in iron ore concentrates on downstream processing and serve as a guide for the utilization of high-alumina iron ore concentrates in pelletization.展开更多
基金financially supported by the National Natural Science Foundation of China (No.52271073)。
文摘A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni–P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90°and was not corroded visually after 500 h of neutral salt spray test at 35℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.
基金Funded by the Natural Science Foundation of Jiangsu Province(No.BK20211067)“Qing Lan” Project of Jiangsu Province。
文摘Two-mm thick A1050 pure aluminum plates were successfully joined by conventional and rapid cooling friction stir welding(FSW), respectively. The microstructure and mechanical properties of the welded joints were investigated by electron backscatter diffraction characterization, Vickers hardness measurements, and tensile testing. The results showed that liquid CO_(2) coolant significantly reduced the peak temperature and increased the cooling rate, so the rapidly cooled FSW joint exhibited fine grains with a large number of dislocations. The grain refinement mechanism of the FSW A1050 pure aluminum joint was primarily attributed to the combined effects of continuous dynamic recrystallization, grain subdivision, and geometric dynamic recrystallization. Compared with conventional FSW, the yield strength, ultimate tensile strength, and fracture elongation of rapidly cooled FSW joint were significantly enhanced, and the welding efficiency was increased from 80% to 93%. The enhanced mechanical properties and improved synergy of strength and ductility were obtained due to the increased dislocation density and remarkable grain refinement. The wear of the tool can produce several WC particles retained in the joint, and the contribution of second phase strengthening to the enhanced strength should not be ignored.
基金Supported by the Opening Project of Hubei Three Gorges Laboratory (No.SK213008)the Innovation Fund of Key Laboratory of Green Chemical Process of Ministry of Education (No.GCXP202109)。
文摘Aluminum hypophosphite microspheres(AHP) were synthesized by hydrothermal method using NaH2PO2·H2O and AlCl3·6H2O as raw materials, and then the AHP microspheres were polymerized by surface polymerization of micro-nanospheres with cyclic cross-linked poly(cyclotriphosphazene-co-4,4'-sulfonyldiphenol)(PZS). A new organic-inorganic poly(phosphonitrile)-modified aluminum hypophosphite microspheres(PZS-AHP) were synthesized by encapsulation and applied to flame retardant thermoplastic polyurethane(TPU). The microstructure and chemical composition of the PZS-AHP microsphere were characterized by scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy and X-ray spectroscopy. The thermal stability of PZS-AHP microsphere was explored with thermogravimetric analysis. Thermogravimetric data indicate that the PZS-AHP microspheres have excellent thermal stability. The thermal and flame-retarding properties of the TPU composites were evaluated by thermogravimetric(TG), limited oxygen index tests(LOI), and cone calorimeter test(CCT). The TPU composite achieved vertical burning(UL-94) V-0 grade and LOI value reached 29.2% when 10 wt% PZS-AHP was incorporated. Compared with those of pure TPU, the peak heat release rate(pHRR) and total heat release(THR) of TPU/10%PZS-AHP decreased by 82.2% and 42.5%, respectively. The results of CCT indicated that PZS-AHP microsphere could improve the flame retardancy of TPU composites.
文摘With the large-scale service of lithium-ion batteries(LIBs),their failures have attracted significant attentions.While the decay of active materials is the primary cause for LIB failures,the degradation of auxiliary materials,such as current collector corrosion,should not be disregarded.Therefore,it is necessary to conduct a comprehensive review in this field.In this review,from the perspectives of electrochemistry and materials,we systematically summarize the corrosion behavior of aluminum cathode current collector and propose corresponding countermeasures.Firstly,the corrosion type is clarified based on the properties of passivation layers in different organic electrolyte components.Furthermore,a thoroughgoing analysis is presented to examine the impact of various factors on aluminum corrosion,including lithium salts,organic solvents,water impurities,and operating conditions.Subsequently,strategies for electrolyte and protection layer employed to suppress corrosion are discussed in detail.Lastly and most importantly,we provide insights and recommendations to prevent corrosion of current collectors,facilitate the development of advanced current collectors and the implementation of next-generation high-voltage stable LIBs.
基金Funded by the Central Government Guides Local Funds for Science and Technology Development(No.YDZJSX20231A045)the Fundamental Research Program of Shanxi Province(Nos.202103021223288 and 202103021224282)。
文摘The evolution of microstructure during hot deformation is key to achieving good mechanical properties in aluminum alloys.We have developed a cellular automaton(CA) based model to simulate the microstructural evolution in 7075 aluminum alloy during hot deformation.Isothermal compression tests were conducted to obtain material parameters for 7075 aluminum alloy,leading to the establishment of models for dislocation density,nucleation of recrystallized grains,and grain growth.Integrating these aspects with grain topological deformation,our CA model effectively predicts flow stress,dynamic recrystallization(DRX) volume fraction,and average grain size under diverse deformation conditions.A systematic comparison was made between electron back scattered diffraction(EBSD) maps and CA model simulated under different deformation temperatures(573 to 723 K),strain rates(0.001 to 1 s^(-1)),and strain amounts(30% to 70%).These analyses indicate that large strain,high temperature,and low strain rate facilitate dynamic recrystallization and grain refinement.The results from the CA model show good accuracy and predictive capability,with experimental error within 10%.
基金the Key Projects of Equipment Pre-research Foundation of the Ministry of Equipment Development of the Central Military Commission of China (No.6140922010201)the Key R&D Plan of Zhenjiang in 2018(No.GY2018021)。
文摘The performance of solid solution aging treatment on aluminum matrix composites prepared by powder metallurgy and reinforced with 6061 aluminum alloy powder as matrix;meanwhile, nano silicon carbide particles(nm Si Cp), submicron silicon carbide particles(1 μm Si Cp) and Ti particles were studied. The Al/Si Cp composite powder was prepared by high-energy ball milling, and then cold-pressed, sintered, hotextruded, and then heat-treated with different solution temperatures and aging times for the extruded composites. Optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy(EDS), X-ray diffractometer(XRD) and extrusion testing were used to analyze and test the microstructure and mechanical properties of aluminum matrix composites. The results show that after the multi-stage solid solution at 530 ℃×2 h+535 ℃×2 h+540 ℃×2 h, the particles are mainly equiaxed grains and uniformly distributed. There is no reinforcement agglomeration, and the surface is dense and the insoluble phase is basically dissolved. In the matrix, the strengthening effect is good, and the hardness and compressive strength are 179.43 HV and 680.42 MPa, respectively. Under this solution process, when the aluminum matrix composites are aged at 170 ℃ for 10 h, the hardness and compressive strength can reach their peaks and increase to 195.82 HV and 721.48 MPa, respectively.
基金support from the National Natural Science Foundation of China (22222808, 21978200)the Haihe Laboratory of Sustainable Chemical Transformations for financial support
文摘Energetic nanofluid fuel has caught the attention of the field of aerospace liquid propellant for its high energy density(HED), but it suffers from the inevitable solid-liquid phase separation problem. To resolve this problem, herein we synthesized the high-Al-/B-containing(up to 30%(mass)) HED gelled fuels, with low-molecular-mass organic gellant Z, which show high net heat of combustion(NHOC), density, storage stability, and thixotropic properties. The characterizations indicate that the application of energetic particles to the gelled fuels obviously destroys their fibrous network structures but can provide the new particle-gellant gelation microstructures, resulting in the comparable stability between 1.0%(mass) Z/JP-10 + 30%(mass) Al or B and pure JP-10 gelled fuel. Moreover, the gelled fuels with high-content Al or B exhibit high shear-thinning property, recovery capability, and mechanical strength, which are favorable for their storage and utilization. Importantly, the prepared 1.0%(mass) Z/JP-10 + 30%(mass) B(or 1.0%(mass) Z/JP-10 + 30%(mass) Al) shows the density and NHOC 1.27 times(1.30) and 1.43 times(1.21)higher than pure JP-10, respectively. This work provides a facile and valid approach to the manufacturing of HED gelled fuels with high content of energetic particles for gel propellants.
基金the National Natural Science Foundation of China(Grant Number 52075553)the Postgraduate Research and Innovation Project of Central South University(School-Enterprise Association)(Grant Number 2021XQLH014).
文摘The widespread adoption of aluminumalloy electric buses,known for their energy efficiency and eco-friendliness,faces a challenge due to the aluminum frame’s susceptibility to deformation compared to steel.This issue is further exacerbated by the stringent requirements imposed by the flammability and explosiveness of batteries,necessitating robust frame protection.Our study aims to optimize the connectors of aluminum alloy bus frames,emphasizing durability,energy efficiency,and safety.This research delves into Multi-Objective Coordinated Optimization(MCO)techniques for lightweight design in aluminum alloy bus body connectors.Our goal is to enhance lightweighting,reinforce energy absorption,and improve deformation resistance in connector components.Three typical aluminum alloy connectors were selected and a design optimization platform was built for their MCO using a variety of software and methods.Firstly,through three-point bending experiments and finite element analysis on three types of connector components,we identified optimized design parameters based on deformation patterns.Then,employing Optimal Latin hypercube design(OLHD),parametric modeling,and neural network approximation,we developed high-precision approximate models for the design parameters of each connector component,targeting energy absorption,mass,and logarithmic strain.Lastly,utilizing the Archive-based Micro Genetic Algorithm(AMGA),Multi-Objective Particle Swarm Optimization(MOPSO),and Non-dominated SortingGenetic Algorithm(NSGA2),we explored optimized design solutions for these joint components.Subsequently,we simulated joint assembly buckling during bus rollover crash scenarios to verify and analyze the optimized solutions in three-point bending simulations.Each joint component showcased a remarkable 30%–40%mass reduction while boosting energy absorption.Our design optimization method exhibits high efficiency and costeffectiveness.Leveraging contemporary automation technology,the design optimization platform developed in this study is poised to facilitate intelligent optimization of lightweight metal components in future applications.
基金Science&Technology Department of Sichuan Province(2022YFQ0041,2022NSFSC1725,2023NSFSC0214)China Agriculture Research System(CARS-07-B-1)+2 种基金The National Natural Science Foundation of China(32160428)Innovative Training Program for College Students(202311079040,S202311079112,CDUCX2023550)Undergraduate Education and Teaching Reform Project of Chengdu University(cdjgb2022186).
文摘Aluminum (Al) toxicity is a considerable factor limiting crop yield and biomass in acidic soil. Tartary buckwheatgrowing in acidic soil may suffer from Al poisoning. Here, we investigated the influence of Al stress on the growthof tartary buckwheat seedling roots, and the alleviation of Al stress by silicon (Si), as has been demonstrated inmany crops. Under Al stress, root growth (total root length, primary root length, root tips, root surface area, androot volume) was significantly inhibited, and Al and malondialdehyde (MDA) accumulated in the root tips. At thesame time, catalase (CAT) and ascorbate peroxidase activities, polyphenols, flavonoids, and 1,1-diphenyl-2-picrylhydrazyl(DPPH) and 2,2′-azinobis-(3-ethylbenzthiazoline-6-sulphonate) (ABTS) free-radical scavenging abilitywere significantly decreased. After the application of Si, root growth, Al accumulation, and oxidative damage wereimproved. Compared to Al-treated seedlings, the contents of ·O2− and MDA decreased by 29.39% and 25.22%,respectively. This was associated with Si-induced increases in peroxidase and CAT enzyme activity, flavonoidcompounds, and free-radical scavenging (DPPH and ABTS). The application of Si therefore has positive effectson Al toxicity in tartary buckwheat roots by reducing Al accumulation in the roots and maintaining oxidationhomeostasis.
基金This work was funded by Luoyang Major Science and Technology Innovation Project(2301009A)Henan Province Key ResearchandDevelopment Project(231111230200).
文摘Aiming at improving the properties of magnesia carbon materials,silicon aluminum carbide(Al_(4)SiC_(4))containing materials were prepared using industrial aluminum powder,silicon carbide powder,and graphite as raw materials,and activated alumina powder as an additive,mixing thoroughly,pressing into cylinders and then firing at 1200℃for 30 min in a carbon embedded atmosphere by the microwave method.The effects of the aluminum powder addition(20%and 24%,by mass)and activated alumina powder addition(0,3%,5%and 7%,by mass)on the microwave synthesis of Al_(4)SiC_(4) as well as the effect of the obtained Al_(4)SiC_(4) containing material on the properties of magnesia carbon bricks were studied.The results show that:compared with the samples with 20%aluminum powder,those with 24%aluminum powder generate more Al_(4)SiC_(4).With the activated alumina powder addition increasing from 0 to 7%,the amount of Al_(4)SiC_(4) generated increases first and then decreases.Compared with the sample without activated alumina powder,the samples with activated alumina powder show lower bulk density and higher apparent porosity.With the activated alumina powder addition increasing from 3%to 7%,the bulk density of the samples increases first and then decreases,while the apparent porosity of the samples shows an opposite trend.The optimal additions are 24%aluminum powder and 5%activated alumina powder,and Al_(4)SiC_(4) synthesized in this sample has a hexagonal plate structure.With the synthesized Al_(4)SiC_(4) containing material added,the magnesia carbon brick has slightly increased cold modulus of rupture,basically the same modulus of elasticity and improved oxidation resistance.
文摘The soil chemistry of gallium, indium, and thallium is not well defined, particularly with emerging evidence that these elements have toxic properties and may influence food safety. The purpose of this investigation was to estimate the soil concentrations of gallium, indium, and thallium and determine if these elements have a soil chemistry like aluminum and therefore demonstrate significant concentration correlations with aluminum. Twenty-seven soil series were selected, and the elemental concentrations were determined using aqua regia digestion with analytical determination performed using inductively coupled plasma emission-mass spectroscopy. The concentrations of gallium, indium, and thallium generally compared with the known literature. Aluminum-gallium and aluminum-thallium exhibited significant concentration correlations across the soil horizons of the sampled soils. Aluminum, gallium, and thallium did demonstrate concentration increases in soil horizons having illuviation of phyllosilicates, implying these phyllosilicates have adsorption and isomorphic substitution behaviors involving these elements.
文摘This research considered the effect of non-natural aging on the microstructural characteristics and mechanical properties of as-cast aluminum 6063 alloys. The samples were developed through a sand casting process and machined into tensile and impact test samples before carrying out solution heat treatment at 550?C (0.83 T<sub>m</sub>) on two parts of the samples while retaining one part as the control. The two parts were further divided into sets denoted A and B and were aged at 180?C (0.27 T<sub>m</sub>) and 160?C (0.24 T<sub>m</sub>), respectively, for 12 hours. The results showed that sample A has the optimal yield strength and ultimate tensile strength of 192 and 206 MPa, respectively. Likewise, the sample gave the highest impact strength value of about 9.63 J/mm<sup>2</sup>. The observed results were supported by the optical micrograph, which revealed that the sample has evenly dispersed precipitates in its microstructure. This is deemed responsible for the observed increase in strength of the sample.
基金supported by the fellowship of China Postdoctoral Science Foundation(Grant No.2021TQ0267)。
文摘The characteristic of easy sintering of aluminum nanoparticle(ANP)limits its application in solid propellants.Coating ANP with fluoropolymer could effectively improve its combustion performance.To find out how the coating layer inhibits sintering and promotes complete combustion of particles from an atomic view,a comparative study has been done for bare ANP and PTFE coated ANP by using reactive molecular dynamics simulations.The sintering process is quantified by shrinkage ratio and gyration radius.Our results show that,at the same heating rate and combustion temperatures,bare ANPs are sintered together after the temperature exceeds the melting point of aluminum but the decomposition of PTFE coating layer pushes particles away and increases reaction surface area by producing small Al-F clusters.The sintering of ANPs which are heated in PTFE is alleviated compared with particles heated in oxygen,but particles still sinter together due to the lack of intimate contact between PTFE and alumina surface.The effect of temperature on the combustion of PTFE coated ANPs is also studied from 1000 to3500 K.The number density analysis shows the particles will not be sintered at any temperature.Aluminum fluoride prefers diffusing to the external space and the remained particles are mainly composed of Al,C and O.Fast ignition simulations are performed by adopting micro canonical ensemble.With the expansion of aluminum core and the melting of alumina shell,bare ANPs are sintered into a liquid particle directly.For PTFE coated ANPs,the volatilization of gaseous aluminum fluoride products continually endows particles opposite momentum.
文摘In this research, the ballistic behavior of the ceramic-reinforced aluminum matrix composite plates is investigated to provide an optimal design for protecting against 7.62 mm bullet at the speed of 800 m/s experimentally and numerically. The target materials are Al5083 alloy as the metal matrix and alumina ceramic balls as the reinforcement. To simulate a 3D numerical model, ABAQUS FE code has been utilized.After validation the numerical model by experiments, the effect of ceramic ball weight percentage include 15%, 30% and 45% and the target thickness 20, 25 and 30 mm is considered on the ballistic results like the kinetic energy, residual velocity and depth of penetration. Finally, it was found that the specimen with 25 mm thickness and 30% alumina is optimum based on existing ballistic protection criteria.
基金National Natural Science Foundation of China(Grant No.11832006,U1530262,21975024).
文摘Aluminum(Al) particles are good fuel additives to improve the energy output performances of explosives. Under detonation environment, reaction delay of Al particles plays a key role in the energy release efficiency. Up to date, reaction delay of Al particles is still limited by the efficiency of mass and heat transfer from oxidizers to Al particles. To address this issue, a homogeneous fuel-oxidizer assembly has recently become a promising strategy. In this work, oxidizer-activated Al fuel particles(ALG) were prepared with glycidyl azide polymer(GAP) as the oxidizer. The ALG was in uniform spherical shape and core-shell structure with shell layer of around 5 nm which was observed by scanning electron microscope and transmission electron microscope. The localized nanoscale mid-IR measurement detected the uniform distribution of characteristic absorption bond of GAP in the shell layer which confirmed the homogenous fuel-oxidizer structure of ALG. A thermal gravimetric analysis of ALG at ultrafast heating rate of 1000℃/min under argon atmosphere was conducted. The decomposition of GAP finished much earlier than that of GAP at heating rate of 10℃/min. Under ultrafast high laser fluence, the reaction response of ALG was characterized and compared with that of micro-sized Al(μAl). With the increase of laser energy, the propagation distance of the shock wave increased. However, the velocity histories were nearly the same when energies were lower than 299 mJ or higher than 706 mJ. The propagation distance of the shock wave for ALG was 0.5 mm larger than that for μAl at 2.1 μs. The underwater explosion showed the peak pressure and the shock wave energy of the ALG-based explosive were both higher than those of the μAl-based explosive at 2.5 m. This study shows the feasibility to improve the energy release of Al-based explosives via using the oxidizer-activated Al fuel particles with energetic polymer as the oxidizer.
基金Funded by the National Natural Science Foundation of China(No.51802189)the Shanghai Lingang Innovation Program(No.SH-LG-GK-2020-28)。
文摘Aluminum alloy tubes were prepared by tube spinning.The intergranular and electrochemical corrosion tests were used to investigate the intergranular corrosion behavior of the 5A06 aluminum alloy blank sample and the spinning sample.Results showed that the intergranular corrosion resistance of the spinning sample was higher than that of the blank sample.In addition,the electrochemical corrosion resistance of the spinning sample was higher than that of the blank sample.The EDS maps indicated a uniform element distribution pattern of aluminum and magnesium.Moreover,the phase composition and lattice constant of the samples were obtained by XRD analysis.The differences in microstructure between the aluminum alloy subjected to the spinning process and the untreated aluminum alloy were determined by EBSD.The differences were mainly attributed to the complex interactions among grain size,dislocations and grain boundaries.
基金supported by the National Natural Science Foundation of China(Grants 51865028)the Gansu Provincial Science and Technology Planning Project(Grant No.20YF8GA056).
文摘The surface composite modification of the 7050 aluminum alloy friction stir-welded joints was performed by shot peening(SP)/multiple rotation rolling(MRR)and MRR/SP,and the fatigue performance of the nugget zone(NZ)was investigated.The results demonstrated that the fatigue life of SP/MRR samples is longer than that of MRR/SP.On the plane 150μm below the surface.The grains with high angle grain boundary account for 71.5%and 34.3%for MRR/SP and SP/MRR samples,respectively.The crack propagation path of the MRR/SP is transgranular and intergranular,and it is intergranular for the MRR/SP.Multitudinous fatigue striations and some voids appeared at the fracture during the stable crack propagation stage.However,fatigue striations for SP/MRR are with smaller spacing,fewer holes,and smaller size under SP/MRR compared with fatigue fracture of MRR/SP.The differences in fatigue properties and fracture characteristics of the NZ are related to the microstructure after the two combined surface modifications.
基金financially supported by the National Natural Science Foundation of China(No.51901018)the Young Elite Scientists Sponsorship Program by the China Association for Science and Technology(YESS,No.2019 QNRC001)+3 种基金the Fundamental Research Funds for the Central Universities,China(No.FRF-AT-20-07,06500119)the Natural Science Foundation of Beijing Municipality,China(No.2212037)the National Science and Technology Resources Investigation Program of China(No.2019FY 101400)the Southwest Institute of Technology and Engineering Cooperation Fund,China(No.HDHDW5902020107)。
文摘Understanding the influence of purities on the electrochemical performance of pure aluminum(Al)in alkaline media for Al–air batteries is significant.Herein,we comprehensively investigate secondary phase precipitate(SPP)-induced localized corrosion of pure Al in NaOH solution mainly based on quasi-in-situ and cross-section observations under scanning electron microscopy coupled with finite element simulation.The experimental results indicate that Al–Fe SPPs appear as clusters and are coherent with the Al substrate.In alkaline media,Al–Fe SPPs exhibit more positive potentials than the substrate,thus aggravating localized galvanic corrosion as cathodic phases.Moreover,finite element simulation indicates that the irregular geometry coupled with potential difference produces the non-uniform current density distribution inside the SPP cluster,and the current density on the Al substrate gradually decreases with distance.
基金supported by China-Central and Eastern Europe Universities Joint Education Project(2021128).
文摘Soybean soapstock(SS) is one of the main solid wastes produced in the refinery of edible oil processing. In this study, the co-pyrolysis of SS with iron slag(IS) and aluminum scrap(AS) was carried out in a tubular furnace. The gas, liquid and solid products were characterized and the char yield decreased with increasing IS/AS ratio. IS and AS can improve the gas yield, and when the ratio of SS/IS was 1:0.25, the total pyrolysis gas and hydrogen contents were significantly increased. The content of oxygen compounds in pyrolysis oil decreased during co-pyrolysis, while AS promoted the content of polycyclic aromatic hydrocarbons in pyrolysis oil. The co-pyrolysis reaction can be divided into four stages, the mass loss rate reaches the maximum at the third stage(390–575 ℃). The molar ratio of H/C was lower for pyrolysis,indicating good stability of pyrolysis char owing to the high degree of carbonization and aromaticity.The possible co-pyrolysis reaction mechanism was explored.
基金financially supported by the National Natural Science Foundation of China(Nos.52004339 and 52174329)the Fundamental Research Funds for the Central Universities,China(No.N2325031)the China Baowu Low Carbon Metallurgy Innovation Foundation(No.BWLCF202216)。
文摘With the intensified depletion of high-grade iron ores,the increased aluminum content in iron ore concentrates has become unavoidable,which is detrimental to the pelletization process.Therefore,the effect mechanism of aluminum on pellet quality must be identified.In this study,the influence of aluminum occurrence and content on the induration of hematite(H)and magnetite(M)pellets was investigated through the addition of corresponding Al-containing additives,including alumina,alumogoethite,gibbsite,and kaolinite.Systematic mineralogical analysis,combined with the thermodynamic properties of different aluminum occurrences and the quantitative characterization of consolidation behaviors,were conducted to determine the related mechanism.The results showed that the alumina from various aluminum occurrences adversely affected the induration characteristics of pellets,especially at an aluminum content of more than 2.0wt%.The thermal decomposition of gibbsite and kaolinite tends to generate internal stress and fine cracks,which hinder the respective microcrystalline bonding and recrystallization between Fe2O3particles.The adverse effect on the induration characteristics of fired pellets with different aluminum occurrences can be relieved to varying degrees through the formation of liquid phase bonds between the hematite particles.Kaolinite is more beneficial to the induration process than the other three aluminum occurrences because of the formation of more liquid phase,which improves pellet consolidation.The research results can further provide insights into the effect of aluminum occurrence and content in iron ore concentrates on downstream processing and serve as a guide for the utilization of high-alumina iron ore concentrates in pelletization.