Ca_(12)Al_(14)O_(33)(C12A7)and Y_(0.02)Ca_(11.98)Al_(14)O_(33)(Y-C12A7)single crystals were grown by using the traveling-solvent floating zone(TSFZ)method.The temperature was increased to avoid the bubbles and cracks ...Ca_(12)Al_(14)O_(33)(C12A7)and Y_(0.02)Ca_(11.98)Al_(14)O_(33)(Y-C12A7)single crystals were grown by using the traveling-solvent floating zone(TSFZ)method.The temperature was increased to avoid the bubbles and cracks which may be formed during the preparation of the ingot material.We have started with the flux higher than the normal to avoid the bubbles and make good treatment for the solid-liquid interface.The structures of both Ca_(12)Al_(14)O_(33)(C12A7)and Y_(0.02)Ca_(11.98)Al_(14)O_(33)(Y-C12A7)were studied by using x-ray diffraction(XRD).Optical properties for C12A7 and Y-C12A7 single crystals have been studied in order to determine the optical parameters such as optical energy gap(Eg),refractive index n,oscillating energy(Eo),dispersion energy(Ed),volume energy loss function(VELF),and surface energy loss function(SELF).Finally,a new result for these samples is that the third-order nonlinear optical susceptibility(χ(3))was determined.The results have been discussed with effect of Y-doping on the C12A7 single crystals for optical and industrial applications.展开更多
文摘Ca_(12)Al_(14)O_(33)(C12A7)and Y_(0.02)Ca_(11.98)Al_(14)O_(33)(Y-C12A7)single crystals were grown by using the traveling-solvent floating zone(TSFZ)method.The temperature was increased to avoid the bubbles and cracks which may be formed during the preparation of the ingot material.We have started with the flux higher than the normal to avoid the bubbles and make good treatment for the solid-liquid interface.The structures of both Ca_(12)Al_(14)O_(33)(C12A7)and Y_(0.02)Ca_(11.98)Al_(14)O_(33)(Y-C12A7)were studied by using x-ray diffraction(XRD).Optical properties for C12A7 and Y-C12A7 single crystals have been studied in order to determine the optical parameters such as optical energy gap(Eg),refractive index n,oscillating energy(Eo),dispersion energy(Ed),volume energy loss function(VELF),and surface energy loss function(SELF).Finally,a new result for these samples is that the third-order nonlinear optical susceptibility(χ(3))was determined.The results have been discussed with effect of Y-doping on the C12A7 single crystals for optical and industrial applications.