Saturated Ca（OH）2 and AlCl3 solutions were used to synthesize calcium aluminate hydrate precipitates at room temperature; high purity calcium aluminate powders with stable phases were made by calcination of the prec...Saturated Ca（OH）2 and AlCl3 solutions were used to synthesize calcium aluminate hydrate precipitates at room temperature; high purity calcium aluminate powders with stable phases were made by calcination of the precursors at a temperature as low as 1100℃. PSD and BET analysis revealed the particles with sizes ranging from submicrometer to several micrometers and with a specific area of 13 m^2/g. The measurement of hydraulic exotherm revealed that the exothennal rate is in peak for about 2 h. The exothermal quantities are 449.24 J/g at 12 h and 488.38 J/g at 24 h. Its strength development is quick and the 1 day curing strength is almost equal to 100% of the 3 days curing strength in the mortar test.展开更多
基金financially supported by the National Natural Science Foundation of China Key Program (No. 50332010)the National Natural Science Foundation of China (No. 50172007)
文摘Saturated Ca（OH）2 and AlCl3 solutions were used to synthesize calcium aluminate hydrate precipitates at room temperature; high purity calcium aluminate powders with stable phases were made by calcination of the precursors at a temperature as low as 1100℃. PSD and BET analysis revealed the particles with sizes ranging from submicrometer to several micrometers and with a specific area of 13 m^2/g. The measurement of hydraulic exotherm revealed that the exothennal rate is in peak for about 2 h. The exothermal quantities are 449.24 J/g at 12 h and 488.38 J/g at 24 h. Its strength development is quick and the 1 day curing strength is almost equal to 100% of the 3 days curing strength in the mortar test.