Four typical theories on the formation of thermal tears:strength,liquid film,intergranular bridging,and solidifica-tion shrinkage compensation theories.From these theories,a number of criteria have been derived for pr...Four typical theories on the formation of thermal tears:strength,liquid film,intergranular bridging,and solidifica-tion shrinkage compensation theories.From these theories,a number of criteria have been derived for predicting the formation of thermal cracks,such as the stress-based Niyama,Clyne,and RDG(Rapaz-Dreiser-Grimaud)criteria.In this paper,a mathematical model of horizontal centrifugal casting was established,and numerical simulation analysis was conducted for the centrifugal casting process of cylindrical Al-Cu alloy castings to investigate the effect of the centrifugal casting process conditions on the microstructure and hot tearing sensitivity of alloy castings by using the modified RDG hot tearing criterion.Results show that increasing the centrifugal rotation and pouring speeds can refine the microstructure of the alloy but increasing the pouring and mold preheating temperatures can lead to an increase in grain size.The grain size gradually transitions from fine grain on the outer layer to coarse grain on the inner layer.Meanwhile,combined with the modified RDG hot tearing criterion,the overall distribution of the castings’hot tearing sensitivity was analyzed.The analysis results indicate that the porosity in the middle region of the casting was large,and hot tearing defects were prone to occur.The hot tearing tendency on the inner side of the casting was greater than that on the outer side.The effects of centrifugal rotation speed,pouring temperature,and preheating temperature on the thermal sensitivity of Al-Cu alloy castings are summarized in this paper.This study revealed that the tendency of alloy hot cracking decreases with the increase of the centrifugal speed,and the maximum porosity of castings decreases first and then increases with the pouring temperature.As the preheating temperature increases,the overall maximum porosity of castings shows a decreasing trend.展开更多
In this work the influence of the density of the molten metal on the emergence of the raining phenomenon in the horizontal centrifugal casting process is numerically studied. Transient 2D numerical simulations were ca...In this work the influence of the density of the molten metal on the emergence of the raining phenomenon in the horizontal centrifugal casting process is numerically studied. Transient 2D numerical simulations were carried out using Computational Fluid Dynamics software. Three molten metals with different density, namely aluminum, iron and lead, and three angular frequencies, namely 50, 66 and 77 rad/s were considered. It is found that the density of the molten metal significantly affects the emergence, transient or permanent, of the rain phenomenon. However, the magnitude and duration of the rain phenomenon depend on the angular frequency of the rotating mold. Likewise, since gravitational forces affect the metal according to its density, the value of the critical rotation speed of the mold is also affected.展开更多
Compound casting is an efficient method for bonding dissimilar metals,in which a dramatic reaction can occur between the melt and solid.The centrifugal casting process,a type of compound casting,was applied to cast Al...Compound casting is an efficient method for bonding dissimilar metals,in which a dramatic reaction can occur between the melt and solid.The centrifugal casting process,a type of compound casting,was applied to cast Al/Mg dissimilar bimetals.Magnesium melt was poured at 700 °C,with melt-to-solid volume ratios(Vm/Vs) of 1.5 and 3,into a preheated hollow aluminum cylinder.The preheating temperatures of the solid part were 320,400,and 450 °C,and the constant rotational speed was 1,600 rpm.The cast parts were kept inside the casting machine until reaching the cooling temperature of 150 °C.The result showed that an increase in preheating temperature from 320 to 450 °C led to an enhanced reaction layer thickness.In addition,an increase in the Vm/Vs from 1.5 to 3 resulted in raising the interface thickness from 1.2 to 1.8 mm.Moreover,the interface was not continuously formed when a Vm/Vs of 3 was selected.In this case,the force of contraction overcame the resultant acting force on the interface.An interface formed at the volume ratio of 1.5 was examined using scanning electron microscopy(SEM) equipped with energy-dispersive X-ray spectroscopy(EDS),and the results demonstrated the formation of Al_(3)Mg_(2),Al_(12)Mg_(17) and(δ+Al_(12)Mg_(17)) eutectic structures in the interface.展开更多
An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on ...An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on fracture behavior of the composite were investigated. The results show that the average fraction of primary Si and Mg2Si particles in the composites is as high as 38%, and ultimate tensile strengths （UTS） of the composites first increase then decrease with the increase of test temperature. Microstructures of broken specimens show that both the particle fracture and the interface debonding affect the fracture behavior of the composites, and the interface debonding becomes the dominant fracture mechanism with increasing test temperature. Comparative results indicate that rich particles in the composites and excellent interface strength play great roles in enhancing tensile property by preventing the movement of dislocations.展开更多
By means of similar physical simulation, liquid metal filling flow pattern in the microscale during the centrifugal casting process was studied. It was found that, in microscale, the flow channel with the maximum cros...By means of similar physical simulation, liquid metal filling flow pattern in the microscale during the centrifugal casting process was studied. It was found that, in microscale, the flow channel with the maximum cross-sectional area was filled first, and the micro flow channels with 0.1 mm in diameter were filled when the rotational speed was increased to 964 r/min. The total fluid energy remained constant during the mould filling, and the changes of cross-sectional area only occurred in the microflow channels with 0.3 mm in diameter. Filling velocity increased with processing time, and a peak value was achieved rapidly, followed by a gentle increase as the process proceeded further. The time required to achieve the peak filling rate decreased dramatically with increase of rotational speed.展开更多
Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed an...Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed and the effects of the used process factors on these characteristics were analyzed. The results of observations shows that, in thickness, the components possess microstructures accumulating lots of Mg2Si particles and a portion of primary silicon particles in the inner layer, a little MgzSi and primary silicon particles in the outer layer, and without any Mg2Si and primary silicon particle in the middle layer. The results of the analysis indicate that the rotation rate of centrifugal casting, mould temperature, and melt pouring temperature have evidently affected the accumulation of the second phase particles. Also, the higher the centrifugal rotation rate, mould temperature, and melt pouring temperature are, the more evident in the inner layer the degree of accumulation of Mg2Si and primary silicon particles is.展开更多
Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structura...Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structural and mechanical characters were compared.It is found that the composite reinforced with primary Si particles takes a characteristic of particles distribution both in the inner and outer layers.However,composite reinforced with primary Si/Mg2Si particles jointly takes a characteristic of particles distribution only in the inner layer and shows a sudden change of particles distribution across the section of inner and outer layers.The hardness and wear resistance of Al-19Si-5Mg tube in the inner layer are greatly higher than that in the other layers of Al-19Si-5Mg tube and Al-19Si tube.Theoretical analysis reveals that the existence of Mg2Si particles is the key factor to form this sudden change of gradient distribution of two kinds of particles.Because Mg2Si particles with a lower density have a higher centripetal moving velocity than primary Si particles,in a field of centrifugal force,they would collide with primary Si particles and then impel the later to move together forward to the inner layer of the tube.展开更多
High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost ...High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.展开更多
A ring-shaped Mg?8.5 Gd?4 Y?1 Zn?0.4 Zr(wt%) alloy was manufactured via centrifugal casting and ring-rolling process. The effects of accumulative ring-rolling reduction amount on the microstructure, texture, and tensi...A ring-shaped Mg?8.5 Gd?4 Y?1 Zn?0.4 Zr(wt%) alloy was manufactured via centrifugal casting and ring-rolling process. The effects of accumulative ring-rolling reduction amount on the microstructure, texture, and tensile properties of the alloy were investigated. The results indicate that the microstructure of centrifugal cast alloy consists of equiaxed grains and network-like eutectic structure present at grain boundaries. The ring-rolled alloy exhibits a characteristic bimodal microstructure composed of fine dynamic recrystallized(DRXed) grains with weak basal texture and coarse un-DRXed grains with strong basal texture, along with the presence of LPSO phase. With increasing amount of accumulative ring-rolling reduction, the coarse un-DRXed grains are refined via the formation of increasing amount of fine DRXed grains. Meanwhile, the dynamic precipitation of Mg5 RE phase occurs, generating a dispersion strengthening effect. A superior combination of strength and ductility is achieved in the ring-rolled alloy after an accumulative rolling reduction of 80%. The tensile strength of this ring-rolled alloy after peak aging is further enhanced, reaching 511 MPa, while keeping a reasonable ductility. The salient strengthening mechanisms identified include the grain boundary strengthening of fine DRXed grains, dispersion strengthening of dynamic precipitated Mg;RE phase, short fiber strengthening of LPSO lamellae/rods, and precipitation strengthening of nano-sized prismatic β precipitates and basal γ precipitates.展开更多
The solidified structure of the thin-walled and complicated Ti-6AI-4V castings produced by the vertical centrifugal casting process was studied in the present work. The results show that the wall thickness of the sect...The solidified structure of the thin-walled and complicated Ti-6AI-4V castings produced by the vertical centrifugal casting process was studied in the present work. The results show that the wall thickness of the section is featured with homogeneously distributed fine equiaxial grains, compared with the microstructure of the thick-walled section. The grain size of the castings has a tendency to decrease gradually with the increasing of the centrifugal radius. The inter-lamellar space in thick-walled casting parts is bigger than that of the thin-walled parts, and the profile of inter-lamellar space is not susceptible to the centrifugal radius.展开更多
Functionally graded Al/B_4C, Al/Si C, Al/Al_2O_3 and Al/TiB_2 composites with constant 12%(mass fraction) of reinforcement were fabricated by centrifugal casting and hollow cylindrical components were obtained. Micros...Functionally graded Al/B_4C, Al/Si C, Al/Al_2O_3 and Al/TiB_2 composites with constant 12%(mass fraction) of reinforcement were fabricated by centrifugal casting and hollow cylindrical components were obtained. Microstructural characteristics were investigated at outer surface of all composites and segregation of reinforcement particles was observed. Graded property of the composites with different reinforcements was investigated through hardness and tensile measurements. Results revealed that the outer peripheries of all composites exhibit higher hardness except in Al/B_4C composite and the outer zones of all composites show higher tensile strength. Abrasive wear test was conducted on the outer peripheries of all composites and Al/TiB_2 composite exhibits less wear rate.展开更多
Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, ...Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, some technologies were invented, such as mounting high Ni cast iron ring around the first ring groove in Al alloy piston body and thermal resistant steel on piston top surface, and fabricating Al composite pistons by squeeze casting for enhancing the whole or local piston performance. In this paper, composite pistons locally reinforced with in situ primary Si and primary Mg2Si particles are fabricated by centrifugal casting. The microstructure characteristics, hardness and wear resistance of the composite piston are investigated and the motion characteristic of the in situ particles in centrifugal field is analyzed. The results of the experiments show that primary Si and Mg2Si particles mix up with each other in melt and segregate at the regions of piston top and piston ring grooves under the effect of centrifugal force. Particulate reinforced regions have a higher hardness and better wear resistance compared with the unreinforced regions and this performance increases after heat treatment. The analysis result of particle movement shows that, primary Si and primary Mg2Si particles move at approximately the same velocity in the centrifugal field, because of the growth of primary Si and fusion after colliding between primary Si particles, which compromised the velocity difference of primary Si and primary Mg2Si particles caused by the difference of their densities. Research results have some theory significance and applicative value of project in development of new aluminum matrix composites piston products.展开更多
The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were inv...The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were investigated. Structurally, the composites are divided into two zones： a reinforced zone with the high volume fraction of primary Si and Mg2Si particles and an unreinforced zone with no or a few particles. In the reinforced zone, the primary particles are evenly distributed, with the sizes of the primary Si particles 80-120 μm, and that of primary Mg2Si particles 20-50 μm. The properties test results show the reinforced zone has higher Rockwell hardness and better wear resistance than the unreinforced zone, due to the complementary reinforcement relationship between the primary Si and Mg2Si particles and their high volume fraction.展开更多
A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathemat...A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathematical model of the filling process is established and the forming mechanism of internal gaseous defect is summarized. The results of calculation show that the melt fills the mould with varying cross-section area and inclined angle. The filling speed of the cross-section is a function of filling time. The cross-section area is directly proportional to the filling speed and the inclined angle is inversely proportional to the filling speed at a given rotating speed of the platform. Both of them changes more obvious near the mould entrance. The gaseous defect can be formed in several ways and the centrifugal field has an important influence on the formation of the defect. In addition, the filling process in centrifugal field has been verified by wax experiments and the theoretical analysis are consistent with experimental results.展开更多
Ti6Al4V hip joint was foundered and the filling process of the melt poured in permanent mould during the centrifugal casting process was analyzed and the mathematical model of the filling process was established. Furt...Ti6Al4V hip joint was foundered and the filling process of the melt poured in permanent mould during the centrifugal casting process was analyzed and the mathematical model of the filling process was established. Furthermore, the mathematical model was validated with a wax model experiment. Calculating results show that the centrifugal field has an important influence on the filling process and the melt fills the mould with variational cross sectional area and inclined angle. The cross sectional area is in inverse proportion to the filling speed and its decreasing speed becomes fast with increasing rotating speed. The tangential value of the melt cross sectional free surface inclined angle is in direct proportion to the filling speed and the inclined angle increases with the filling length. Change curves of the cross sectional inclined angle and area were obtained by the wax model experiment when the rotating speeds were 60, 90 and 120 r/min respectively, which shows that the mathematical model is consistent with the experimental results. [展开更多
Navier-Stokes equation and Lorentz force equation are used to calculate the fluid field of liquid metal of electromagnetic centrifugal casting (EMCC) in this paper. A field equation is given, which shows the azimuthal...Navier-Stokes equation and Lorentz force equation are used to calculate the fluid field of liquid metal of electromagnetic centrifugal casting (EMCC) in this paper. A field equation is given, which shows the azimuthal velocity closely relates to electrical conductivity, magnetic density, viscosity of liquid metal and radius of casting. The results show that the stationary magnetic field can effectively restrain the fluid flow and the relative velocity between liquid metal and casting mould and the velocity gradient at solid / liquid interface increases with rising magnetic density, which has a great effect on the solidification of liquid metal and crystal growth characteristics.展开更多
A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects ...A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects which normally occur in the overlaid welding process. In this study, the effects of Ni on the microstructure and mechanical properties of martensitic stainless steel were investigated. The results show that the addition of Ni resulted in a decrease in the volume fraction of delta ferrite and an increase in the volume fraction of the retained austenite, respectively. Moreover, a tensile strength of 1600 MPa with an elongation of 4% were obtained after tempering at 500℃ for 2 h. These values were higher than those obtained by using the conventional overlaid process.展开更多
The bubble migration in liquid titanium alloy melt during vertical centrifugal casting process has been predicted. The effects of different parameters, such as the initial bubble location, the mold rotational speed an...The bubble migration in liquid titanium alloy melt during vertical centrifugal casting process has been predicted. The effects of different parameters, such as the initial bubble location, the mold rotational speed and the mold rotational direction on the bubble in the migration process are investigated. The results show that the bubble migration can be divided into the radial movement to the mould rotation axis and the circular movement to the mould wall opposite to rotational direction of the casting mould. The casting mould wall has an impeditive effect on the circular movement of the bubble during its migration process. And the bubble finally migrates like a straight line along the mould wall located at the opposite direction of the rotational casting mould whether it rotates clockwise or anti-clockwise. The bubbles at the position near the mould wall located at the opposite direction of the rotational casting mould are much easier to migrate in a straight line. The instantaneous speed of the gas bubble increases with the increment of the mould rotational speed. However the mould rotational speed is high or low, the moving speed of the gas bubble increases slightly at the primary stage, and then decreases gradually like a ladder.展开更多
A complicated Cu-Ni based alloy was developed to fabricate wear-resisting bush for high temperature application.The concern focuses on the control of equiaxed grains in the developed alloy ingot prepared by centrifuga...A complicated Cu-Ni based alloy was developed to fabricate wear-resisting bush for high temperature application.The concern focuses on the control of equiaxed grains in the developed alloy ingot prepared by centrifugal casting.The results show that the equiaxed grains are determined by the pouring temperature of the melt,the cooling rate and the rotation speed of the mold.With the decrease in pouring temperature,the fraction of the equiaxed grains in the transverse section of the ingot increases and the average length of columnar grain decreases.When the pouring temperature is confined below 1,250℃,complete equiaxed grains can be obtained.Based on the optimal centrifugal casting processing,the tensile strength of the developed alloy ingot with complete equiaxed grains reaches to 810 MPa and 435 MPa at room temperature and 500℃,respectively,which is 14% and 110% higher than that of common commercial QAl10-4-4 alloy.The wear rate of the developed alloy is 7.0 × 10-8 and 3.8 × 10-7 mm3?N-1?mm-1 at room temperature and 500℃,respectively,which is 5 times and 39 times lower than that of QAl10-4-4 alloy.展开更多
The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was f...The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.展开更多
文摘Four typical theories on the formation of thermal tears:strength,liquid film,intergranular bridging,and solidifica-tion shrinkage compensation theories.From these theories,a number of criteria have been derived for predicting the formation of thermal cracks,such as the stress-based Niyama,Clyne,and RDG(Rapaz-Dreiser-Grimaud)criteria.In this paper,a mathematical model of horizontal centrifugal casting was established,and numerical simulation analysis was conducted for the centrifugal casting process of cylindrical Al-Cu alloy castings to investigate the effect of the centrifugal casting process conditions on the microstructure and hot tearing sensitivity of alloy castings by using the modified RDG hot tearing criterion.Results show that increasing the centrifugal rotation and pouring speeds can refine the microstructure of the alloy but increasing the pouring and mold preheating temperatures can lead to an increase in grain size.The grain size gradually transitions from fine grain on the outer layer to coarse grain on the inner layer.Meanwhile,combined with the modified RDG hot tearing criterion,the overall distribution of the castings’hot tearing sensitivity was analyzed.The analysis results indicate that the porosity in the middle region of the casting was large,and hot tearing defects were prone to occur.The hot tearing tendency on the inner side of the casting was greater than that on the outer side.The effects of centrifugal rotation speed,pouring temperature,and preheating temperature on the thermal sensitivity of Al-Cu alloy castings are summarized in this paper.This study revealed that the tendency of alloy hot cracking decreases with the increase of the centrifugal speed,and the maximum porosity of castings decreases first and then increases with the pouring temperature.As the preheating temperature increases,the overall maximum porosity of castings shows a decreasing trend.
文摘In this work the influence of the density of the molten metal on the emergence of the raining phenomenon in the horizontal centrifugal casting process is numerically studied. Transient 2D numerical simulations were carried out using Computational Fluid Dynamics software. Three molten metals with different density, namely aluminum, iron and lead, and three angular frequencies, namely 50, 66 and 77 rad/s were considered. It is found that the density of the molten metal significantly affects the emergence, transient or permanent, of the rain phenomenon. However, the magnitude and duration of the rain phenomenon depend on the angular frequency of the rotating mold. Likewise, since gravitational forces affect the metal according to its density, the value of the critical rotation speed of the mold is also affected.
文摘Compound casting is an efficient method for bonding dissimilar metals,in which a dramatic reaction can occur between the melt and solid.The centrifugal casting process,a type of compound casting,was applied to cast Al/Mg dissimilar bimetals.Magnesium melt was poured at 700 °C,with melt-to-solid volume ratios(Vm/Vs) of 1.5 and 3,into a preheated hollow aluminum cylinder.The preheating temperatures of the solid part were 320,400,and 450 °C,and the constant rotational speed was 1,600 rpm.The cast parts were kept inside the casting machine until reaching the cooling temperature of 150 °C.The result showed that an increase in preheating temperature from 320 to 450 °C led to an enhanced reaction layer thickness.In addition,an increase in the Vm/Vs from 1.5 to 3 resulted in raising the interface thickness from 1.2 to 1.8 mm.Moreover,the interface was not continuously formed when a Vm/Vs of 3 was selected.In this case,the force of contraction overcame the resultant acting force on the interface.An interface formed at the volume ratio of 1.5 was examined using scanning electron microscopy(SEM) equipped with energy-dispersive X-ray spectroscopy(EDS),and the results demonstrated the formation of Al_(3)Mg_(2),Al_(12)Mg_(17) and(δ+Al_(12)Mg_(17)) eutectic structures in the interface.
基金Project(51174244) supported by the National Natural Science Foundation of ChinaProject(CDJZR11130005) supported by the Fundamental Research Funds for the Central Universities,China
文摘An aluminum-based in-situ composites reinforced with Mg2Si and Si particles were produced by centrifugal casting A1-20Si-5Mg alloy. The microstructure of the composites was examined, and the effects of temperature on fracture behavior of the composite were investigated. The results show that the average fraction of primary Si and Mg2Si particles in the composites is as high as 38%, and ultimate tensile strengths （UTS） of the composites first increase then decrease with the increase of test temperature. Microstructures of broken specimens show that both the particle fracture and the interface debonding affect the fracture behavior of the composites, and the interface debonding becomes the dominant fracture mechanism with increasing test temperature. Comparative results indicate that rich particles in the composites and excellent interface strength play great roles in enhancing tensile property by preventing the movement of dislocations.
基金Project (51005053) supported by the National Science Foundation for Young Scientists of China
文摘By means of similar physical simulation, liquid metal filling flow pattern in the microscale during the centrifugal casting process was studied. It was found that, in microscale, the flow channel with the maximum cross-sectional area was filled first, and the micro flow channels with 0.1 mm in diameter were filled when the rotational speed was increased to 964 r/min. The total fluid energy remained constant during the mould filling, and the changes of cross-sectional area only occurred in the microflow channels with 0.3 mm in diameter. Filling velocity increased with processing time, and a peak value was achieved rapidly, followed by a gentle increase as the process proceeded further. The time required to achieve the peak filling rate decreased dramatically with increase of rotational speed.
文摘Cylindrical components of in situ functionally gradient composite materials of Al-19Si-5Mg alloy were manufactured by centrifugal casting. Microstructure characteristics of the manufactured components were observed and the effects of the used process factors on these characteristics were analyzed. The results of observations shows that, in thickness, the components possess microstructures accumulating lots of Mg2Si particles and a portion of primary silicon particles in the inner layer, a little MgzSi and primary silicon particles in the outer layer, and without any Mg2Si and primary silicon particle in the middle layer. The results of the analysis indicate that the rotation rate of centrifugal casting, mould temperature, and melt pouring temperature have evidently affected the accumulation of the second phase particles. Also, the higher the centrifugal rotation rate, mould temperature, and melt pouring temperature are, the more evident in the inner layer the degree of accumulation of Mg2Si and primary silicon particles is.
基金Project(2008BB4177) supported by the Natural Science Foundation of Chongqing,China
文摘Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structural and mechanical characters were compared.It is found that the composite reinforced with primary Si particles takes a characteristic of particles distribution both in the inner and outer layers.However,composite reinforced with primary Si/Mg2Si particles jointly takes a characteristic of particles distribution only in the inner layer and shows a sudden change of particles distribution across the section of inner and outer layers.The hardness and wear resistance of Al-19Si-5Mg tube in the inner layer are greatly higher than that in the other layers of Al-19Si-5Mg tube and Al-19Si tube.Theoretical analysis reveals that the existence of Mg2Si particles is the key factor to form this sudden change of gradient distribution of two kinds of particles.Because Mg2Si particles with a lower density have a higher centripetal moving velocity than primary Si particles,in a field of centrifugal force,they would collide with primary Si particles and then impel the later to move together forward to the inner layer of the tube.
文摘High speed steel (HSS) rolls can replace traditional rolls such as alloyed cast iron rolls and powder metallurgical (PM) hard alloy rolls. The main reasons for the replacement are that the wear resistance of low-cost alloyed cast iron rolls is poor and the cost of high-quality PM hard alloy rolls is very high. By means of centrifugal casting, HSS rolls having excellent wear resistance have been manufactured. The hardness of the HSS roll is 6.5~67 HRC, the range of variation is smaller than 2 HRC and its impact toughness is 15 J/cm^2. The wear rate of HSS rolls used in the pre-finishing stands of high-speed hot wire-rod rolling mill reaches 2.5×10^(-4)mm per ton steel. Furthermore, the manufacturing cost of HSS rolls is significantly lower than that of PM hard alloy rolls; it is only 30 percent of that of PM hard alloy rolls.
基金financial support by Fundamental Research Funds for the National Key Research and Development Program of China(Project No.2016YFB0700403)the Venture&Innovation Support Program for Chongqing Overseas Returnees(Project No.cx2018057)+1 种基金the Chongqing Research Program of Basic Research and Frontier Technology(Project Nos.cstc2019jcyjmsxm0548 and cstc2019jcyj-msxm X0306)the Fundamental Research Funds for the Central Universities(Project No.2021CDJJMRH-001)。
文摘A ring-shaped Mg?8.5 Gd?4 Y?1 Zn?0.4 Zr(wt%) alloy was manufactured via centrifugal casting and ring-rolling process. The effects of accumulative ring-rolling reduction amount on the microstructure, texture, and tensile properties of the alloy were investigated. The results indicate that the microstructure of centrifugal cast alloy consists of equiaxed grains and network-like eutectic structure present at grain boundaries. The ring-rolled alloy exhibits a characteristic bimodal microstructure composed of fine dynamic recrystallized(DRXed) grains with weak basal texture and coarse un-DRXed grains with strong basal texture, along with the presence of LPSO phase. With increasing amount of accumulative ring-rolling reduction, the coarse un-DRXed grains are refined via the formation of increasing amount of fine DRXed grains. Meanwhile, the dynamic precipitation of Mg5 RE phase occurs, generating a dispersion strengthening effect. A superior combination of strength and ductility is achieved in the ring-rolled alloy after an accumulative rolling reduction of 80%. The tensile strength of this ring-rolled alloy after peak aging is further enhanced, reaching 511 MPa, while keeping a reasonable ductility. The salient strengthening mechanisms identified include the grain boundary strengthening of fine DRXed grains, dispersion strengthening of dynamic precipitated Mg;RE phase, short fiber strengthening of LPSO lamellae/rods, and precipitation strengthening of nano-sized prismatic β precipitates and basal γ precipitates.
基金by the National Natural Science Foundation of China under grant No. 50775050the State Key Laboratory of Solidif ication Processing in NWPU (200702)
文摘The solidified structure of the thin-walled and complicated Ti-6AI-4V castings produced by the vertical centrifugal casting process was studied in the present work. The results show that the wall thickness of the section is featured with homogeneously distributed fine equiaxial grains, compared with the microstructure of the thick-walled section. The grain size of the castings has a tendency to decrease gradually with the increasing of the centrifugal radius. The inter-lamellar space in thick-walled casting parts is bigger than that of the thin-walled parts, and the profile of inter-lamellar space is not susceptible to the centrifugal radius.
基金Department of Science and Technology (India) for the financial support (Grant No.SR/S3/MERC/0116/2012)
文摘Functionally graded Al/B_4C, Al/Si C, Al/Al_2O_3 and Al/TiB_2 composites with constant 12%(mass fraction) of reinforcement were fabricated by centrifugal casting and hollow cylindrical components were obtained. Microstructural characteristics were investigated at outer surface of all composites and segregation of reinforcement particles was observed. Graded property of the composites with different reinforcements was investigated through hardness and tensile measurements. Results revealed that the outer peripheries of all composites exhibit higher hardness except in Al/B_4C composite and the outer zones of all composites show higher tensile strength. Abrasive wear test was conducted on the outer peripheries of all composites and Al/TiB_2 composite exhibits less wear rate.
文摘Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, some technologies were invented, such as mounting high Ni cast iron ring around the first ring groove in Al alloy piston body and thermal resistant steel on piston top surface, and fabricating Al composite pistons by squeeze casting for enhancing the whole or local piston performance. In this paper, composite pistons locally reinforced with in situ primary Si and primary Mg2Si particles are fabricated by centrifugal casting. The microstructure characteristics, hardness and wear resistance of the composite piston are investigated and the motion characteristic of the in situ particles in centrifugal field is analyzed. The results of the experiments show that primary Si and Mg2Si particles mix up with each other in melt and segregate at the regions of piston top and piston ring grooves under the effect of centrifugal force. Particulate reinforced regions have a higher hardness and better wear resistance compared with the unreinforced regions and this performance increases after heat treatment. The analysis result of particle movement shows that, primary Si and primary Mg2Si particles move at approximately the same velocity in the centrifugal field, because of the growth of primary Si and fusion after colliding between primary Si particles, which compromised the velocity difference of primary Si and primary Mg2Si particles caused by the difference of their densities. Research results have some theory significance and applicative value of project in development of new aluminum matrix composites piston products.
基金Funded by the National Natural Science Foundation of China(No.51201140)the Fundamental Research Funds for the Central Universities(No.XDJK2010C007)
文摘The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were investigated. Structurally, the composites are divided into two zones： a reinforced zone with the high volume fraction of primary Si and Mg2Si particles and an unreinforced zone with no or a few particles. In the reinforced zone, the primary particles are evenly distributed, with the sizes of the primary Si particles 80-120 μm, and that of primary Mg2Si particles 20-50 μm. The properties test results show the reinforced zone has higher Rockwell hardness and better wear resistance than the unreinforced zone, due to the complementary reinforcement relationship between the primary Si and Mg2Si particles and their high volume fraction.
文摘A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48A1-2Cr-2Nb alloy melt poured in a permanent mould during the centrifugal casting process has been analyzed. A mathematical model of the filling process is established and the forming mechanism of internal gaseous defect is summarized. The results of calculation show that the melt fills the mould with varying cross-section area and inclined angle. The filling speed of the cross-section is a function of filling time. The cross-section area is directly proportional to the filling speed and the inclined angle is inversely proportional to the filling speed at a given rotating speed of the platform. Both of them changes more obvious near the mould entrance. The gaseous defect can be formed in several ways and the centrifugal field has an important influence on the formation of the defect. In addition, the filling process in centrifugal field has been verified by wax experiments and the theoretical analysis are consistent with experimental results.
文摘Ti6Al4V hip joint was foundered and the filling process of the melt poured in permanent mould during the centrifugal casting process was analyzed and the mathematical model of the filling process was established. Furthermore, the mathematical model was validated with a wax model experiment. Calculating results show that the centrifugal field has an important influence on the filling process and the melt fills the mould with variational cross sectional area and inclined angle. The cross sectional area is in inverse proportion to the filling speed and its decreasing speed becomes fast with increasing rotating speed. The tangential value of the melt cross sectional free surface inclined angle is in direct proportion to the filling speed and the inclined angle increases with the filling length. Change curves of the cross sectional inclined angle and area were obtained by the wax model experiment when the rotating speeds were 60, 90 and 120 r/min respectively, which shows that the mathematical model is consistent with the experimental results. [
文摘Navier-Stokes equation and Lorentz force equation are used to calculate the fluid field of liquid metal of electromagnetic centrifugal casting (EMCC) in this paper. A field equation is given, which shows the azimuthal velocity closely relates to electrical conductivity, magnetic density, viscosity of liquid metal and radius of casting. The results show that the stationary magnetic field can effectively restrain the fluid flow and the relative velocity between liquid metal and casting mould and the velocity gradient at solid / liquid interface increases with rising magnetic density, which has a great effect on the solidification of liquid metal and crystal growth characteristics.
文摘A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects which normally occur in the overlaid welding process. In this study, the effects of Ni on the microstructure and mechanical properties of martensitic stainless steel were investigated. The results show that the addition of Ni resulted in a decrease in the volume fraction of delta ferrite and an increase in the volume fraction of the retained austenite, respectively. Moreover, a tensile strength of 1600 MPa with an elongation of 4% were obtained after tempering at 500℃ for 2 h. These values were higher than those obtained by using the conventional overlaid process.
基金Sponsored by the National Natural Science Foundation of China(Grant No.U1604254)the Initial Scientific Research Fund of Young Teachers in Henan University of Technology(Grant No.2013BS050)
文摘The bubble migration in liquid titanium alloy melt during vertical centrifugal casting process has been predicted. The effects of different parameters, such as the initial bubble location, the mold rotational speed and the mold rotational direction on the bubble in the migration process are investigated. The results show that the bubble migration can be divided into the radial movement to the mould rotation axis and the circular movement to the mould wall opposite to rotational direction of the casting mould. The casting mould wall has an impeditive effect on the circular movement of the bubble during its migration process. And the bubble finally migrates like a straight line along the mould wall located at the opposite direction of the rotational casting mould whether it rotates clockwise or anti-clockwise. The bubbles at the position near the mould wall located at the opposite direction of the rotational casting mould are much easier to migrate in a straight line. The instantaneous speed of the gas bubble increases with the increment of the mould rotational speed. However the mould rotational speed is high or low, the moving speed of the gas bubble increases slightly at the primary stage, and then decreases gradually like a ladder.
文摘A complicated Cu-Ni based alloy was developed to fabricate wear-resisting bush for high temperature application.The concern focuses on the control of equiaxed grains in the developed alloy ingot prepared by centrifugal casting.The results show that the equiaxed grains are determined by the pouring temperature of the melt,the cooling rate and the rotation speed of the mold.With the decrease in pouring temperature,the fraction of the equiaxed grains in the transverse section of the ingot increases and the average length of columnar grain decreases.When the pouring temperature is confined below 1,250℃,complete equiaxed grains can be obtained.Based on the optimal centrifugal casting processing,the tensile strength of the developed alloy ingot with complete equiaxed grains reaches to 810 MPa and 435 MPa at room temperature and 500℃,respectively,which is 14% and 110% higher than that of common commercial QAl10-4-4 alloy.The wear rate of the developed alloy is 7.0 × 10-8 and 3.8 × 10-7 mm3?N-1?mm-1 at room temperature and 500℃,respectively,which is 5 times and 39 times lower than that of QAl10-4-4 alloy.
文摘The present study aims at developing the high speed steel (HSS) as rollmaterials to replace the traditional roll materials such as the alloy cast iron and powdermetallurgical (PM) hard alloy. The HSS roll billet was formed by centrifugal casting, and the billetwas rough machined alter soften annealing heat treatment, then it was quenched and tempered to getsuitable hardness and toughness. After that the HSS roll was finish machined to the final dimensionof phi 285 mm in the outer diameter, phi 160 mm in the inner diameter and 120 mm in width and itssurface hardness was tested. Finally the HSS roll was used in high speed wire rod mill. The testresults show that a high and homogeneous hardness can obtain on the work surface of HSS rolls, thesurface hardness is 63-65HRC and its variation is smaller than 2HRC. The impact toughness of thiskind of HSS is about 16 J/cm^2. The results of on-line service investigation in high speed wire rodmill indicate that the HSS rolls have excellent wear resistance, the steel rolling quantity per mmof HSS rolls is 3120 t, the service life-span of HSS rolls is 4 times longer than that of highchromium cast iron rolls and it is close to that of the PM hard alloy rolls. The manufacturingburden of HSS rolls is obviously lower than that of the PM hard alloy rolls, it is only 25 percentof that of the PM hard alloy rolls.