Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can r...In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.展开更多
A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts c...A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts calcined at different temperatures were characterized using NH3-TPD, pyridine-FTIR, X-ray diffraction, and Raman techniques. It was found that the calcination process could not only change the structure of these catalysts but also modify the amount of surface acidity on the catalysts. The catalyst calcined at 400 ℃ exhibited the highest conversion of acetylene （94.6%） and highest selectivity to vinyl fluoride （83.4%） and lower coke deposition selectivity （0.72%）. The highest activity was related to the largest amount of surface acidity on the catalyst, and the coke deposition was also related to the total amount of surface acidic sites.展开更多
A series of K-promoted Pt/Al2O3 catalysts were tested for CO oxidation. It was found that the addition of K significantly enhanced the activity. A detailed kinetic study showed that the activation energies of the K-co...A series of K-promoted Pt/Al2O3 catalysts were tested for CO oxidation. It was found that the addition of K significantly enhanced the activity. A detailed kinetic study showed that the activation energies of the K-containing catalysts were lower than those of the K-free ones, particularly for catalysts with high Pt contents （51.6 k）/mol for 0.42K-2.0Pt/Al2O3 and 6：3.6 kJ/mol for 2.0Pt/Al2O3 ）. The CO reaction orders were higher for the K-containing catalysts （about -0.2） than for the K-free ones （about -0.5）, with the former having much lower equilibrium constants for CO adsorption than the latter. In situ Fourier-transform infrared spectroscopy showed that surface CO desorption from the 0.42K-2.0Pt/Al2O3 catalyst was easier than from 2.0Pt/Al2O3. The promoting effect of K was therefore caused by weakening of the interactions between CO and surface Pt atoms. This decreased coverage of the catalyst with CO and facilitated competitive O2 chemisorption on the Pt surface, and significantly lowered the reaction barrier between chemisorbed CO and O2 species.展开更多
separation is an attractive alternative to filtration or centrifugation for separating solid catalysts from a liquid phase, Here, core-shell Fe3O4@UiO-66-NH2 nanohybrids with well-defined structures were constructed b...separation is an attractive alternative to filtration or centrifugation for separating solid catalysts from a liquid phase, Here, core-shell Fe3O4@UiO-66-NH2 nanohybrids with well-defined structures were constructed by dispersing magnets in a dimethylformamide （DMF） solution con- taining two metal-organic framework （MOF） precursors, namely ZrCI4 and 2-aminobenzenetricar- boxylic acid. This method is simpler and more efficient than previously reported step-by-step method in which magnets were consecutively dispersed in DMF solutions each containing one MOF precursor, and the obtained Fe304@UiO-66-NH2 with three assembly cycles has a higher degree of crystallinity and porosiW. The core-shell Fe3O4@UiO-66-NH2 is highly active and selective in Knoevenagel condensations because of the bifunctionality of UiO-66-NH2 and better mass transfer in the nano-sized shells. It also has good recycling stability, and can be recovered magnetically and reused at least four times without significant loss of catalytic activity and framework integrity. The effects of substitution on the reactivity of benzaldehyde and of substrate size were also investigated.展开更多
Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried ...Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried out over coral reef-like Ni/Al2O3 catalysts in a continuous flow type fixed-bed reactor.The structure and properties of the fresh and used catalysts were studied by SEM,N2 adsorption-desorption,XRD,H2-TPR,O2-TPO,TG and ICP-AES techniques.The results showed that the coral reef-like Ni/Al2O3 catalysts exhibited better activity than the conventional Ni/Al2O3-H2O catalysts.The activities of coral reef-like catalysts were in the order of Ni/Al2O3-673Ni/Al2O3-573Ni/Al2O3- 473Ni/Al2O3-773.Ni/Al2O3-673-EG catalyst showed not only good activity and improved stability but also superior resistance to carbon deposition,sintering,and Ni loss.Under the reaction conditions of CO/H2（molar ratio）=1：3,593 K,atmospheric pressure and a GHSV of 2500 h-1,CH4 selectivity was 84.7%,and the CO conversion reached 98.2%.展开更多
The activation of adsorbed CO is an important step in CO hydrogenation. The results from TPSR of pre-adsorbed CO with H2 and syngas suggested that the presence of H2 increased the amount of CO adsorption and accelerat...The activation of adsorbed CO is an important step in CO hydrogenation. The results from TPSR of pre-adsorbed CO with H2 and syngas suggested that the presence of H2 increased the amount of CO adsorption and accelerated CO dissociation. The H2 was adsorbed first, and activated to form H＊ over metal sites, then reacted with carbonaceous species. The oxygen species for CO2 formation in the presence of hydrogen was mostly OH^＊, which reacted with adsorbed CO subsequently via CO^＊＋OH^＊ → CO2^＊＋H^＊; however, the direct CO dissociation was not excluded in CO hydrogenation. The dissociation of C-O bond in the presence of H2 proceeded by a concerted mechanism, which assisted the Boudourd reaction of adsorbed CO on the surface via CO^＊＋2H^＊ → CH^＊＋OH^＊. The formation of the surface species （CH） from adsorbed CO proceeded as indicated with the participation of surface hydrogen, was favored in the initial step of the Fischer-Tropsch synthesis.展开更多
In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for met...In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.展开更多
Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TP...Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TPR and TPO techniques. The results revealed that the deactivation of Cr-Al2O3 catalyst was mainly caused by carbon deposition on its surface. The Cr3＋ ion could not be reduced by hydrogen but could be reduced to Cr2＋ by hydrocarbons and monoxide carbon. The active center for isobutane dehydrogenation could be Cr2＋/Cr3＋ produced from Cr6＋ by the on line reduction of hydrocarbon and carbon monoxide. The binding energy of Al3＋ was strongly affected by the state of chromium cations in the catalysts.展开更多
The applicability of a commercial Pt-Sn/Al2O3 isobutane dehydrogenation catalyst in dehydrogenation of propane was studied. Catalyst performance tests were carded out in a fixed-bed quartz reactor under different oper...The applicability of a commercial Pt-Sn/Al2O3 isobutane dehydrogenation catalyst in dehydrogenation of propane was studied. Catalyst performance tests were carded out in a fixed-bed quartz reactor under different operating conditions. Generally, as the factors improving propane conversion decrease the propylene selectivity, the optimal operating condition to maximize propylene yield is expected. The optimal condition was obtamed by the experimental design method. The investigated parameters were temperature, hydrogen/hydrocarbon （HE/HC） ratio and space velocity, being changed in three levels. Constrains such as the susceptibility of the catalyst components to sintering or phase transformation were also taken into account. Activity, selectivity and stability of the catalyst were considered as the measured response factors, while the space-time-yield （STY） was considered as the variable to be optimized due to its commercial interest. A STY of 16 mol.kg^-1.h^-1 was achieved under the optimal conditions of T= 620 ℃, H2/HC = 0.6 and, weight hourly space velocity （WHSV） = 2.2 h^-1. Single carbon-carbon bond rupture was found to be the main route for the formation of lower hydrocarbon byproducts.展开更多
Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on...Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.展开更多
The selective catalytic hydrogenation of naphthalene to high-value tetralin was systematically investigated.A series of Al2O3 catalysts containing different active metals(Co,Mo,Ni,W)were prepared by incipient wetness ...The selective catalytic hydrogenation of naphthalene to high-value tetralin was systematically investigated.A series of Al2O3 catalysts containing different active metals(Co,Mo,Ni,W)were prepared by incipient wetness impregnation.The effects of different active metals forms(oxidation,reduction,sulfuration)and reaction conditions on naphthalene hydrogenation were investigated and the catalysts were characterized by XRD,XPS,BET,NH3-TPD and SEM.Especially,Ni-Mo/Al2O3 was first used in this reactive system.The results show that the oxidative4%Ni O-20%MoO3/Al2O3 is the best catalyst for the preparation of tetralin.The conversion of naphthalene and the selectivity of tetralin can reach 95.62%and 99.75%respectively at 200℃,8 h and 6 MPa.Compared with reduced and sulfureted 4%Ni O-20%MoO3/Al2O3 catalysts,oxidative 4%Ni O-20%MoO3/Al2O3 has a well dispersed and uniform monolayer of the active metals,larger pore volume and size,and larger total acidity.NiO-MoO3/Al2O3 has a synergistic effect between NiO activity and MoO3 selectivity.展开更多
A series of iron-based Fischer-Tropsch synthesis （FTS） catalysts incorporated with Al2O3 binder were prepared by the combination of co-precipitation and spray drying technology. The catalyst samples were characteriz...A series of iron-based Fischer-Tropsch synthesis （FTS） catalysts incorporated with Al2O3 binder were prepared by the combination of co-precipitation and spray drying technology. The catalyst samples were characterized by using N2 physical adsorption, temperature-programmed reduction/desorption （TPR/TPD） and MSssbauer effect spectroscopy （MES） methods. The characterization results indicated that the BET surface area increases with increasing Al2O3 content and passes through a maximum at the Al2O3/Fe ratio of 10/100 （weight basis）. After the point, it decreases with further increase in Al2O3 content. The incorporation of Al2O3 binder was found to weaken the surface basicity and suppress the reduction and carburization of iron-based catalysts probably due to the strong K-Al2O3 and Fe-Al2O3 interactions. Furthermore, the H2 adsorption ability of the catalysts is enhanced with increasing Al2O3 content. The FTS performances of the catalysts were tested in a slurry-phase continuously stirred tank reactor （CSTR） under the reaction conditions of 260 ℃, 1.5 MPa, 1000 h^-1 and molar ratio of H2/CO 0.67 for 200 h. The results showed that the addition of small amounts of Al2O3 affects the activity of iron-based catalysts to a little extent. However, with further increase of Al2O3 content, the FTS activity and water gas shift reaction （WGS） activity are decreased severely. The addition of appropriate Al2O3 do not affect the product selectivity, but the catalysts incorporated with large amounts of Al2O3 have higher selectivity for light hydrocarbons and lower selectivity for heavy hydrocarbons.展开更多
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.
基金financial support from National Natural Science Foundation of China(Nos.52004102 and 22078125)Postdoctoral Science Foundation of China(No.2021M690068)+2 种基金Fundamental Research Funds for the Central Universities(Nos.JUSRP221018 and JUSRP622038)Key Laboratory of Green Cleaning Technology and Detergent of Zhejiang Province(No.Q202204)Open Project of Key Laboratory of Green Chemical Engineering Process of Ministry of Education(No.GCP202112)。
文摘In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.
基金ACKNOWLEDGMENT This work was supported by the National Natural Science Foundation of China （No.20873125）,
文摘A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts calcined at different temperatures were characterized using NH3-TPD, pyridine-FTIR, X-ray diffraction, and Raman techniques. It was found that the calcination process could not only change the structure of these catalysts but also modify the amount of surface acidity on the catalysts. The catalyst calcined at 400 ℃ exhibited the highest conversion of acetylene （94.6%） and highest selectivity to vinyl fluoride （83.4%） and lower coke deposition selectivity （0.72%）. The highest activity was related to the largest amount of surface acidity on the catalyst, and the coke deposition was also related to the total amount of surface acidic sites.
基金financially supported by the National Natural Science Foundation of China(21173195)~~
文摘A series of K-promoted Pt/Al2O3 catalysts were tested for CO oxidation. It was found that the addition of K significantly enhanced the activity. A detailed kinetic study showed that the activation energies of the K-containing catalysts were lower than those of the K-free ones, particularly for catalysts with high Pt contents （51.6 k）/mol for 0.42K-2.0Pt/Al2O3 and 6：3.6 kJ/mol for 2.0Pt/Al2O3 ）. The CO reaction orders were higher for the K-containing catalysts （about -0.2） than for the K-free ones （about -0.5）, with the former having much lower equilibrium constants for CO adsorption than the latter. In situ Fourier-transform infrared spectroscopy showed that surface CO desorption from the 0.42K-2.0Pt/Al2O3 catalyst was easier than from 2.0Pt/Al2O3. The promoting effect of K was therefore caused by weakening of the interactions between CO and surface Pt atoms. This decreased coverage of the catalyst with CO and facilitated competitive O2 chemisorption on the Pt surface, and significantly lowered the reaction barrier between chemisorbed CO and O2 species.
基金supported by the National Natural Science Foundation of China (21203017)Open Fund of State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences (N-11-3)+1 种基金Program for Liaoning Excellent Talents in University (LNET)the Funda-mental Research Funds for the Central Universities (DC201502020304)~~
文摘separation is an attractive alternative to filtration or centrifugation for separating solid catalysts from a liquid phase, Here, core-shell Fe3O4@UiO-66-NH2 nanohybrids with well-defined structures were constructed by dispersing magnets in a dimethylformamide （DMF） solution con- taining two metal-organic framework （MOF） precursors, namely ZrCI4 and 2-aminobenzenetricar- boxylic acid. This method is simpler and more efficient than previously reported step-by-step method in which magnets were consecutively dispersed in DMF solutions each containing one MOF precursor, and the obtained Fe304@UiO-66-NH2 with three assembly cycles has a higher degree of crystallinity and porosiW. The core-shell Fe3O4@UiO-66-NH2 is highly active and selective in Knoevenagel condensations because of the bifunctionality of UiO-66-NH2 and better mass transfer in the nano-sized shells. It also has good recycling stability, and can be recovered magnetically and reused at least four times without significant loss of catalytic activity and framework integrity. The effects of substitution on the reactivity of benzaldehyde and of substrate size were also investigated.
基金financially supported by Independent Research Subject from Ministry of Science and Technology of China(No.2008BWZ005)
文摘Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried out over coral reef-like Ni/Al2O3 catalysts in a continuous flow type fixed-bed reactor.The structure and properties of the fresh and used catalysts were studied by SEM,N2 adsorption-desorption,XRD,H2-TPR,O2-TPO,TG and ICP-AES techniques.The results showed that the coral reef-like Ni/Al2O3 catalysts exhibited better activity than the conventional Ni/Al2O3-H2O catalysts.The activities of coral reef-like catalysts were in the order of Ni/Al2O3-673Ni/Al2O3-573Ni/Al2O3- 473Ni/Al2O3-773.Ni/Al2O3-673-EG catalyst showed not only good activity and improved stability but also superior resistance to carbon deposition,sintering,and Ni loss.Under the reaction conditions of CO/H2（molar ratio）=1：3,593 K,atmospheric pressure and a GHSV of 2500 h-1,CH4 selectivity was 84.7%,and the CO conversion reached 98.2%.
基金The National Key Project for Basic Research of China(973 Project)(No.2005CB221402)China National Petroleum Corporation
文摘The activation of adsorbed CO is an important step in CO hydrogenation. The results from TPSR of pre-adsorbed CO with H2 and syngas suggested that the presence of H2 increased the amount of CO adsorption and accelerated CO dissociation. The H2 was adsorbed first, and activated to form H＊ over metal sites, then reacted with carbonaceous species. The oxygen species for CO2 formation in the presence of hydrogen was mostly OH^＊, which reacted with adsorbed CO subsequently via CO^＊＋OH^＊ → CO2^＊＋H^＊; however, the direct CO dissociation was not excluded in CO hydrogenation. The dissociation of C-O bond in the presence of H2 proceeded by a concerted mechanism, which assisted the Boudourd reaction of adsorbed CO on the surface via CO^＊＋2H^＊ → CH^＊＋OH^＊. The formation of the surface species （CH） from adsorbed CO proceeded as indicated with the participation of surface hydrogen, was favored in the initial step of the Fischer-Tropsch synthesis.
基金supported by the National Basic Research Program of China(973 Program,2013CB933104)the National Natural Science Foundation of China(Nos.11275258 and 11135008)
文摘In situ quick X-ray absorption spectroscopy(QXAFS) at the Cu and Zn K-edge under operando conditions has been used to unravel the Cu/Zn interaction and identify possible active site of CuO/ZnO/Al_2O_3 catalyst for methanol synthesis. In this work, the catalyst, whose activity increases with the reaction temperature and pressure, was studied at calcined, reduced, and reacted conditions. TEM and EDX images for the calcined and reduced catalysts showed that copper was distributed uniformly at both conditions. TPR profile revealed two reduction peaks at 165 and 195 °C for copper species in the calcined catalyst. QXAFS results demonstrated that the calcined form consisted mainly of a mixed Cu O and Zn O, and it was progressively transformed into Cu metal particles and dispersed Zn O species as the reduction treatment. It was demonstrated that activation of the catalyst precursor occurred via a Cu^+intermediate, and the active catalyst predominantly consisted of metallic Cu and Zn O evenunder higher pressures. Structure of the active catalyst did not change with the temperature or pressure, indicating that the role of the Zn was mainly to improve Cu dispersion.This indicates the potential of QXAFS method in studying the structure evolutions of catalysts in methanol synthesis.
基金supported by the Natural Science Foundation of Shandong Provence of China(ZR2013BM008)
文摘Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TPR and TPO techniques. The results revealed that the deactivation of Cr-Al2O3 catalyst was mainly caused by carbon deposition on its surface. The Cr3＋ ion could not be reduced by hydrogen but could be reduced to Cr2＋ by hydrocarbons and monoxide carbon. The active center for isobutane dehydrogenation could be Cr2＋/Cr3＋ produced from Cr6＋ by the on line reduction of hydrocarbon and carbon monoxide. The binding energy of Al3＋ was strongly affected by the state of chromium cations in the catalysts.
基金Supported by the Petrochemical Research&Technology Co. of National Petrochemical Co.
文摘The applicability of a commercial Pt-Sn/Al2O3 isobutane dehydrogenation catalyst in dehydrogenation of propane was studied. Catalyst performance tests were carded out in a fixed-bed quartz reactor under different operating conditions. Generally, as the factors improving propane conversion decrease the propylene selectivity, the optimal operating condition to maximize propylene yield is expected. The optimal condition was obtamed by the experimental design method. The investigated parameters were temperature, hydrogen/hydrocarbon （HE/HC） ratio and space velocity, being changed in three levels. Constrains such as the susceptibility of the catalyst components to sintering or phase transformation were also taken into account. Activity, selectivity and stability of the catalyst were considered as the measured response factors, while the space-time-yield （STY） was considered as the variable to be optimized due to its commercial interest. A STY of 16 mol.kg^-1.h^-1 was achieved under the optimal conditions of T= 620 ℃, H2/HC = 0.6 and, weight hourly space velocity （WHSV） = 2.2 h^-1. Single carbon-carbon bond rupture was found to be the main route for the formation of lower hydrocarbon byproducts.
基金973 Program (2006CB202500)the National Natural Science Foundation of China (20676096)New Century Excellent Talents in University.9gram (2006CB202500)
文摘Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.
基金supported by the Joint Funds of National Key R&D Program of China(2018YFB0604603)the National Natural Science Foundation of China(21536009,21776229)+2 种基金Science and Technology Plan Projects of Shaanxi Province(2017ZDCXL-GY-10-03,2018ZDXMGY-167)The Young Science and Technology Star Project of Shaanxi Province(2017KJXX-62)Science and Technology Program of Yulin(2018-2-22)。
文摘The selective catalytic hydrogenation of naphthalene to high-value tetralin was systematically investigated.A series of Al2O3 catalysts containing different active metals(Co,Mo,Ni,W)were prepared by incipient wetness impregnation.The effects of different active metals forms(oxidation,reduction,sulfuration)and reaction conditions on naphthalene hydrogenation were investigated and the catalysts were characterized by XRD,XPS,BET,NH3-TPD and SEM.Especially,Ni-Mo/Al2O3 was first used in this reactive system.The results show that the oxidative4%Ni O-20%MoO3/Al2O3 is the best catalyst for the preparation of tetralin.The conversion of naphthalene and the selectivity of tetralin can reach 95.62%and 99.75%respectively at 200℃,8 h and 6 MPa.Compared with reduced and sulfureted 4%Ni O-20%MoO3/Al2O3 catalysts,oxidative 4%Ni O-20%MoO3/Al2O3 has a well dispersed and uniform monolayer of the active metals,larger pore volume and size,and larger total acidity.NiO-MoO3/Al2O3 has a synergistic effect between NiO activity and MoO3 selectivity.
基金The financial support from the National Natural Science Foundation of China (20590361)the National Outstanding Young Scientists Foundation of China (20625620)
文摘A series of iron-based Fischer-Tropsch synthesis （FTS） catalysts incorporated with Al2O3 binder were prepared by the combination of co-precipitation and spray drying technology. The catalyst samples were characterized by using N2 physical adsorption, temperature-programmed reduction/desorption （TPR/TPD） and MSssbauer effect spectroscopy （MES） methods. The characterization results indicated that the BET surface area increases with increasing Al2O3 content and passes through a maximum at the Al2O3/Fe ratio of 10/100 （weight basis）. After the point, it decreases with further increase in Al2O3 content. The incorporation of Al2O3 binder was found to weaken the surface basicity and suppress the reduction and carburization of iron-based catalysts probably due to the strong K-Al2O3 and Fe-Al2O3 interactions. Furthermore, the H2 adsorption ability of the catalysts is enhanced with increasing Al2O3 content. The FTS performances of the catalysts were tested in a slurry-phase continuously stirred tank reactor （CSTR） under the reaction conditions of 260 ℃, 1.5 MPa, 1000 h^-1 and molar ratio of H2/CO 0.67 for 200 h. The results showed that the addition of small amounts of Al2O3 affects the activity of iron-based catalysts to a little extent. However, with further increase of Al2O3 content, the FTS activity and water gas shift reaction （WGS） activity are decreased severely. The addition of appropriate Al2O3 do not affect the product selectivity, but the catalysts incorporated with large amounts of Al2O3 have higher selectivity for light hydrocarbons and lower selectivity for heavy hydrocarbons.