Copper wire, serving as a cost-saving alternative to gold wire, has been used in many high-end thermosonic ball bonding applications. In this paper, the bond shear force, bond shear strength, and the ball bond diamete...Copper wire, serving as a cost-saving alternative to gold wire, has been used in many high-end thermosonic ball bonding applications. In this paper, the bond shear force, bond shear strength, and the ball bond diameter are adopted to evaluate the bonding quality. It is concluded that the ef/~cient ultrasonic power is needed to soften the ball to form the copper bonds with high bonding strength. However, excessive ultrasonic power would serve as a fatigue loading to weaken the bonding. Excessive or less bonding force would cause cratering in the silicon.展开更多
A copper vapor laser with active medium length of 60 cm and bore of 16 mm has been operated and optimized using different buffer gases to investigate the effect of the gas flow rates on the output power. It is found t...A copper vapor laser with active medium length of 60 cm and bore of 16 mm has been operated and optimized using different buffer gases to investigate the effect of the gas flow rates on the output power. It is found that there is a special optimum gas flow rate associated with the type of buffer gas.展开更多
[目的]烧结钕铁硼(Nd Fe B)的电镀前处理技术还不够成熟,开发适宜的前处理工艺极其重要。[方法]在电镀铜前,先采用以羟基乙叉二膦酸(HEDP)为主配位剂的溶液对NdFeB进行预浸。预浸液组成和工艺条件为:HEDP 20~30 g/L,氢氧化钾20~25 g/L,...[目的]烧结钕铁硼(Nd Fe B)的电镀前处理技术还不够成熟,开发适宜的前处理工艺极其重要。[方法]在电镀铜前,先采用以羟基乙叉二膦酸(HEDP)为主配位剂的溶液对NdFeB进行预浸。预浸液组成和工艺条件为:HEDP 20~30 g/L,氢氧化钾20~25 g/L,碳酸钾10~15 g/L,葡萄糖酸钾1~2 g/L,乙酸0.5~1.0 g/L,室温,时间60 s。通过电化学测试对比了Nd Fe B基体有无预浸处理时,铜在其表面的电沉积行为,并通过金相显微镜、扫描电镜、能谱仪和荧光光谱测厚仪,对比了有无预浸处理的Nd FeB基体表面Cu镀层的宏观和微观表面形貌、截面形貌、元素分布及厚度分布均匀性。[结果]Nd Fe B基体预浸后表面被活化,静态电位降低。预浸液能够填满基体表面的孔隙并形成一层水薄膜,在后续电镀铜时保护基体不被腐蚀。预浸处理的Nd Fe B基体表面所得Cu镀层均匀、致密,不易氧化发黑,结合力和耐蚀性较好。[结论]对烧结钕铁硼进行预浸处理,能够保证其在后续电镀铜过程不被腐蚀,提高Cu镀层的综合性能。展开更多
The synthetical soft magnetic properties were reported for newly-developed nanocrystalline Fe73.5Cu1Nb0.9 Mo2.1Si13.5B9 and Fe73.5Cu1Nb0.5 Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys ar...The synthetical soft magnetic properties were reported for newly-developed nanocrystalline Fe73.5Cu1Nb0.9 Mo2.1Si13.5B9 and Fe73.5Cu1Nb0.5 Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3, P2/200k=880 and 973kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c4. The dependence of core loss on frequency and amplitude flux density has been analyzed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2kW were reported.展开更多
文摘Copper wire, serving as a cost-saving alternative to gold wire, has been used in many high-end thermosonic ball bonding applications. In this paper, the bond shear force, bond shear strength, and the ball bond diameter are adopted to evaluate the bonding quality. It is concluded that the ef/~cient ultrasonic power is needed to soften the ball to form the copper bonds with high bonding strength. However, excessive ultrasonic power would serve as a fatigue loading to weaken the bonding. Excessive or less bonding force would cause cratering in the silicon.
文摘A copper vapor laser with active medium length of 60 cm and bore of 16 mm has been operated and optimized using different buffer gases to investigate the effect of the gas flow rates on the output power. It is found that there is a special optimum gas flow rate associated with the type of buffer gas.
文摘[目的]烧结钕铁硼(Nd Fe B)的电镀前处理技术还不够成熟,开发适宜的前处理工艺极其重要。[方法]在电镀铜前,先采用以羟基乙叉二膦酸(HEDP)为主配位剂的溶液对NdFeB进行预浸。预浸液组成和工艺条件为:HEDP 20~30 g/L,氢氧化钾20~25 g/L,碳酸钾10~15 g/L,葡萄糖酸钾1~2 g/L,乙酸0.5~1.0 g/L,室温,时间60 s。通过电化学测试对比了Nd Fe B基体有无预浸处理时,铜在其表面的电沉积行为,并通过金相显微镜、扫描电镜、能谱仪和荧光光谱测厚仪,对比了有无预浸处理的Nd FeB基体表面Cu镀层的宏观和微观表面形貌、截面形貌、元素分布及厚度分布均匀性。[结果]Nd Fe B基体预浸后表面被活化,静态电位降低。预浸液能够填满基体表面的孔隙并形成一层水薄膜,在后续电镀铜时保护基体不被腐蚀。预浸处理的Nd Fe B基体表面所得Cu镀层均匀、致密,不易氧化发黑,结合力和耐蚀性较好。[结论]对烧结钕铁硼进行预浸处理,能够保证其在后续电镀铜过程不被腐蚀,提高Cu镀层的综合性能。
文摘The synthetical soft magnetic properties were reported for newly-developed nanocrystalline Fe73.5Cu1Nb0.9 Mo2.1Si13.5B9 and Fe73.5Cu1Nb0.5 Mo2.5Si13.5B9 alloys. The levels of high-frequency losses of the new alloys are P3/100k=612 and 670 kWm-3, P2/200k=880 and 973kWm-3, P2/500k=4300 and 4600 kWm-3, P0.5/1000k=860 and 920 kWm-3, respectively. They are significantly lower than those of the superior power Mn-Zn ferrite H7c4. The dependence of core loss on frequency and amplitude flux density has been analyzed. The practical applications of the new alloys to switching mode power supplies with the output power of 1 and 2kW were reported.