Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%,5%,10%,15%,20%,25%,30%,35%,40%,45%,50%Cu-coated Fe were prepared in mesh belt sintering furnace.Microscopic pore morphology of materials was observe...Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%,5%,10%,15%,20%,25%,30%,35%,40%,45%,50%Cu-coated Fe were prepared in mesh belt sintering furnace.Microscopic pore morphology of materials was observed,bending strength was tested.Results show that,There is a good bonding between Cu-coated Fe and CuSn10,with the increase of Cu-coated Fe content from 0%to 50%,bending strength of bilayer composite materials increases.展开更多
Copper, iron and cobalt based pre-alloyed powders for diamond tools were prepared by ultrahigh pressure water atomization（UPWA） process. Pre-alloyed powders prepared by different processes including UPWA, convention...Copper, iron and cobalt based pre-alloyed powders for diamond tools were prepared by ultrahigh pressure water atomization（UPWA） process. Pre-alloyed powders prepared by different processes including UPWA, conventional water atomization （CWA） and elemental metal mechanical mixing （EMMM） were sintered to segments and then compared in mechanical properties, holding force between matrix and diamond, fracture morphology of blank and sintering diamond section containing matrix. The results showed that the pre-alloyed powder prepared by UPWA exhibits the best mechanical properties including the relative density, the hardness and the bending strength of matrix sinteredsegment. Sintered segments fractography of UPWA pre-alloyed powder indicatesmechanical mosaic strength and chemical bonding force between the pre-alloyed powder and the diamond, leading to the great increase in the holding force between matrix and diamond. The mechanical performance andthe service life of diamond tools were greatly improved by UPWA pre-alloyed powders.展开更多
基金Research project of Heyuan polytechnic(2022ky05,2022ky06)2019 Provincial Science and Technology Special Fund("Big project"+"Task List")project(2019005,2019004).
文摘Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%,5%,10%,15%,20%,25%,30%,35%,40%,45%,50%Cu-coated Fe were prepared in mesh belt sintering furnace.Microscopic pore morphology of materials was observed,bending strength was tested.Results show that,There is a good bonding between Cu-coated Fe and CuSn10,with the increase of Cu-coated Fe content from 0%to 50%,bending strength of bilayer composite materials increases.
基金Projects(2010SK3172,2015JC3005)supported by the Key Program of Science and Technology Project of Hunan Province,China
文摘Copper, iron and cobalt based pre-alloyed powders for diamond tools were prepared by ultrahigh pressure water atomization（UPWA） process. Pre-alloyed powders prepared by different processes including UPWA, conventional water atomization （CWA） and elemental metal mechanical mixing （EMMM） were sintered to segments and then compared in mechanical properties, holding force between matrix and diamond, fracture morphology of blank and sintering diamond section containing matrix. The results showed that the pre-alloyed powder prepared by UPWA exhibits the best mechanical properties including the relative density, the hardness and the bending strength of matrix sinteredsegment. Sintered segments fractography of UPWA pre-alloyed powder indicatesmechanical mosaic strength and chemical bonding force between the pre-alloyed powder and the diamond, leading to the great increase in the holding force between matrix and diamond. The mechanical performance andthe service life of diamond tools were greatly improved by UPWA pre-alloyed powders.