CH3NH3PbI3 perovskite solar cells with 2TPA-n-DP （TPA = 4,4＇-（（1E, I＇E,3E,3＇E）- [1,1＇-biphenyl]4,4＇-diylbis（buta-1,3-diene-4,1-diyl））; DP = bis（N,N-di-p-tolylaniline）; n = 1, 2, 3, 4） as hole-transporti...CH3NH3PbI3 perovskite solar cells with 2TPA-n-DP （TPA = 4,4＇-（（1E, I＇E,3E,3＇E）- [1,1＇-biphenyl]4,4＇-diylbis（buta-1,3-diene-4,1-diyl））; DP = bis（N,N-di-p-tolylaniline）; n = 1, 2, 3, 4） as hole-transporting materials （HTMs） have been fabricated. After optimization of the mesoporous TiO2 film thickness, devices based on 2TPA- 2-DP with power conversion efficiencies （PCEs） of up to 12.96% have been achieved, comparable to those of devices with （2,2＇,7,7＇-tetrakis（N,N-di-p- methoxyphenylamine）-9,9＇-spirobifluorene） （spiro-OMeTAD） as HTM under similar conditions. Further time-resolved photoluminescence （PL） measurements showed a fast charge transfer process at the perovskite/2TPA-2-DP interface. With the aid of electrochemical impedance spectra, a study of the electron blocking ability of 2TPA-2-DP in the device reveals that the presence of 2TPA-2-DP can greatly increase charge transfer resistance at the HTM/Au interface in the device, thus reducing the recombination. Furthermore, the perovskite solar cells based on these four HTMs exhibit ~ood stability after testin~ for one month.展开更多
文摘CH3NH3PbI3 perovskite solar cells with 2TPA-n-DP （TPA = 4,4＇-（（1E, I＇E,3E,3＇E）- [1,1＇-biphenyl]4,4＇-diylbis（buta-1,3-diene-4,1-diyl））; DP = bis（N,N-di-p-tolylaniline）; n = 1, 2, 3, 4） as hole-transporting materials （HTMs） have been fabricated. After optimization of the mesoporous TiO2 film thickness, devices based on 2TPA- 2-DP with power conversion efficiencies （PCEs） of up to 12.96% have been achieved, comparable to those of devices with （2,2＇,7,7＇-tetrakis（N,N-di-p- methoxyphenylamine）-9,9＇-spirobifluorene） （spiro-OMeTAD） as HTM under similar conditions. Further time-resolved photoluminescence （PL） measurements showed a fast charge transfer process at the perovskite/2TPA-2-DP interface. With the aid of electrochemical impedance spectra, a study of the electron blocking ability of 2TPA-2-DP in the device reveals that the presence of 2TPA-2-DP can greatly increase charge transfer resistance at the HTM/Au interface in the device, thus reducing the recombination. Furthermore, the perovskite solar cells based on these four HTMs exhibit ~ood stability after testin~ for one month.