A series of Fe/HZSM-5 catalysts with different iron loadings were prepared by impregnation method.Characterization was performed by N2 adsorption-desorption,X-ray diffraction（XRD）,NH3 temperature-programmed desorpt...A series of Fe/HZSM-5 catalysts with different iron loadings were prepared by impregnation method.Characterization was performed by N2 adsorption-desorption,X-ray diffraction（XRD）,NH3 temperature-programmed desorption（NH3-TPD）,temperature-programmed reduction （TPR）,temperature-programmed oxidation（TPO）and thermogravimetry（TG）analysis.Iron content in the synthesized samples varied from 1.1 wt%to 20 wt%.The obtained samples have been used for ethanol conversion into light olefins.It was found that the amount of strong acidity at 300 -5 50-C on Fe-modified samples was decreased,going with another new acid site appearance at 550- 600-C and that Fe/HZSM-5 catalysts were highly selective towards light olefins,especially the 9FZ sample.In addition,Fe-modified catalysts suppressed the conversion of ethanol to aromatics and paraffins and enhanced their anti-carbon deposit ability.展开更多
基金supported by the National Natural Science Foundation of China(No.20963010)the Doctor Fund of Science Research(No.070267)
文摘A series of Fe/HZSM-5 catalysts with different iron loadings were prepared by impregnation method.Characterization was performed by N2 adsorption-desorption,X-ray diffraction（XRD）,NH3 temperature-programmed desorption（NH3-TPD）,temperature-programmed reduction （TPR）,temperature-programmed oxidation（TPO）and thermogravimetry（TG）analysis.Iron content in the synthesized samples varied from 1.1 wt%to 20 wt%.The obtained samples have been used for ethanol conversion into light olefins.It was found that the amount of strong acidity at 300 -5 50-C on Fe-modified samples was decreased,going with another new acid site appearance at 550- 600-C and that Fe/HZSM-5 catalysts were highly selective towards light olefins,especially the 9FZ sample.In addition,Fe-modified catalysts suppressed the conversion of ethanol to aromatics and paraffins and enhanced their anti-carbon deposit ability.