Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were inves...Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were investigated. Results show that the erosion at impingement angle of 30°is more than that of 90°. The erosion resistance of coatings was enhanced uith the inereaase of temperature. Coatings had a better erosion resislance than substrwles. The erosion changed from ductile behariors to brittle behaviors above 450℃ . At high temperature, the erosion resistances were superior to those at low temperwlure and roonl temperwlure. Cowlings had much higher corrosion properties than substrates. The temperature had a little effect on the corrosion resistance of coatings ; The corrosion losing of cowlings increased slowly with the increase of corrosion time. The HVAS-sprayed Fe-Al/Cr3C2 coatings exhibited a high bond strength and hardness.展开更多
Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating propert...Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating properties such as bonding strength, porosity, hardness as well as microstructures were characterized. The results show that the coatings have relatively high heat tremble bond strength, hardness, and typical layer-shaped coatings＇ microstructures. With the rise of temperature, the coating erosion resistance increases too; the impingement angel does effects on erosion properties, and the erosion mechanism changes from ductile to brittle behaviors at 450℃. The coatings have good room temperature wear resistance and relatively good high temperature resistance. The wear mechanism of the coatings is peeling wear behavior. The coatings have excellent high temperature corrosion resistance because of the produce of oxides during corrosion.展开更多
基金Founded by the National Natural Science Foundation of China(Grant No.50235030 ,50005024)
文摘Iron aluminide intermetallic coatings were prepared from Fe-Al/Cr3C2 cored wires using High Velocity Are Spraying （ HVAS ） technology. Erosion and corrosion properties of HVAS sprayed Fe-Al/Cr3C2 coatings were investigated. Results show that the erosion at impingement angle of 30°is more than that of 90°. The erosion resistance of coatings was enhanced uith the inereaase of temperature. Coatings had a better erosion resislance than substrwles. The erosion changed from ductile behariors to brittle behaviors above 450℃ . At high temperature, the erosion resistances were superior to those at low temperwlure and roonl temperwlure. Cowlings had much higher corrosion properties than substrates. The temperature had a little effect on the corrosion resistance of coatings ; The corrosion losing of cowlings increased slowly with the increase of corrosion time. The HVAS-sprayed Fe-Al/Cr3C2 coatings exhibited a high bond strength and hardness.
文摘Fe-Al/Cr3C2 composite coatings were manufactured using high velocity arc spraying （HVAS） technology. The high temperature erosion, wear and corrosion resistance of the coatings were investigated. The coating properties such as bonding strength, porosity, hardness as well as microstructures were characterized. The results show that the coatings have relatively high heat tremble bond strength, hardness, and typical layer-shaped coatings＇ microstructures. With the rise of temperature, the coating erosion resistance increases too; the impingement angel does effects on erosion properties, and the erosion mechanism changes from ductile to brittle behaviors at 450℃. The coatings have good room temperature wear resistance and relatively good high temperature resistance. The wear mechanism of the coatings is peeling wear behavior. The coatings have excellent high temperature corrosion resistance because of the produce of oxides during corrosion.