Fe3Al alloys with nearly full density were fabricated by plasma activated sintering（PAS） and hot pressing（HP） from mechanical alloyed Fe-28%Al（mole fraction） powders,respectively.It is found that A2-type Fe3Al a...Fe3Al alloys with nearly full density were fabricated by plasma activated sintering（PAS） and hot pressing（HP） from mechanical alloyed Fe-28%Al（mole fraction） powders,respectively.It is found that A2-type Fe3Al alloys were obtained by PAS,and they had a heterogeneous grain size distribution,most areas had a grain size smaller than 500 nm,and other areas had a grain size of about 1 μm.Different to PAS,D03-type Fe3Al alloys with a grain size of of 1-2 μm were obtained by HP.The compression testing results show that yield strength values of Fe3Al alloys fabricated by PAS and HP are almost equal at an elevated temperature,and the compression yield strength was about 100 MPa for all at 800 ℃.The room temperature compression ductility of Fe3Al alloys by PAS was about 20%,which was superior to that of Fe3Al alloys prepared by HP and casting.展开更多
Hydrogen-induced cracking (HIC) of Fe3Al alloy was studied by in situ transmission electron microscope (TEM). Electron transparent specimens were mounted onto a constant displacement device. Stress was applied to the ...Hydrogen-induced cracking (HIC) of Fe3Al alloy was studied by in situ transmission electron microscope (TEM). Electron transparent specimens were mounted onto a constant displacement device. Stress was applied to the specimen by using a bolt through the device. The results showed that hydrogen enhanced the dislocation emission and motion in Fe3Al alloy. A dislocation free zone (DFZ) was formed following the dislocation emission. Microcrack initiated in the DFZ or at the main crack tip when the emission reached a critical extension. Hydrogen played an important role in the process of brittle fracture of Fe3Al alloy.展开更多
Coating structural materials with Fe 3Al based intermetallics may rapidly lead to industrial application of their environment and wear resistant features. In the present study, high velocity arc spraying (HVAS) was u...Coating structural materials with Fe 3Al based intermetallics may rapidly lead to industrial application of their environment and wear resistant features. In the present study, high velocity arc spraying (HVAS) was used to in situ synthesize Fe 3Al intermetallic coating. The microstructural characterization and properties of the coating have been investigated. The microstructure was found to consist of Fe 3Al based intermetallic (D0 3 and B2) and α Fe regions together with fine oxide (α Al 2O 3) layers. TEM images of coating show that the solidified lamellae are polycrystalline and have a grain size of the order of about 150 nm , and there also exists amorphous state in some areas. It can be concluded that a very high cooling rate has been obtained during HVAS process. Moreover, the coating has relatively higher adhesion strength and microhardness, as well as lower density and porosity.展开更多
Phase structure characteristics near the interface of Fe3Al/Q235 diffusion bonding are investigated by means of X raydiffraction (XRD), transmission electronic microscope (TEM) and electron diffraction, etc. The test ...Phase structure characteristics near the interface of Fe3Al/Q235 diffusion bonding are investigated by means of X raydiffraction (XRD), transmission electronic microscope (TEM) and electron diffraction, etc. The test results indicatedthat obviously a diffusion transition zone forms near the interface of Fe3Al/Q235 under the condition of heatingtemperature 1050~1100℃, holding time 60 min and pressure 9.8 MPa, which indicated that the diffusion interfaceof Fe3Al/Q235 was combined well. The diffusion transition zone consisted of Fe3Al and a-Fe(Al) solid solution.Microhardness near the diffusion transition zone was HM 480~540. There was not brittle phase of high hardness inthe interface transition zone. This is favorable to enhance toughness of Fe3Al/Q235 diffusion joint.展开更多
Fe3Al and Crl8-Ni8 steel were bonded in vacuum and an interface was formed between Fe3Al and Crl8-Ni8 steel. Stress distribution at the diffusion-bonded interface was researched by numerical simulation and finite elem...Fe3Al and Crl8-Ni8 steel were bonded in vacuum and an interface was formed between Fe3Al and Crl8-Ni8 steel. Stress distribution at the diffusion-bonded interface was researched by numerical simulation and finite element method （FEM）. The results indicated that the peak stress appeared at the interface near Cr18-Ni8 steel side. This is the key factor to induce crack at this position. With the enhancement of heating temperature, the peak stress at the bonded interface increases. When the temperature is 1 100 22, the peak stress is up to 65.9 MPa, which is bigger than that at 1 000 22 by 9. 4%. In addition, the peak stress becomes bigger with the increase of the thickness of base metal from 1 mm to 8 ram. While the thickness is more than 8 ram, the peak stress varies slightly with the change of the thickness.展开更多
基金Project (50871084) supported by the National Natural Science Foundation of ChinaProject (2009AA032601) supported by the National High Technology Research and Development Program of China
文摘Fe3Al alloys with nearly full density were fabricated by plasma activated sintering（PAS） and hot pressing（HP） from mechanical alloyed Fe-28%Al（mole fraction） powders,respectively.It is found that A2-type Fe3Al alloys were obtained by PAS,and they had a heterogeneous grain size distribution,most areas had a grain size smaller than 500 nm,and other areas had a grain size of about 1 μm.Different to PAS,D03-type Fe3Al alloys with a grain size of of 1-2 μm were obtained by HP.The compression testing results show that yield strength values of Fe3Al alloys fabricated by PAS and HP are almost equal at an elevated temperature,and the compression yield strength was about 100 MPa for all at 800 ℃.The room temperature compression ductility of Fe3Al alloys by PAS was about 20%,which was superior to that of Fe3Al alloys prepared by HP and casting.
文摘Hydrogen-induced cracking (HIC) of Fe3Al alloy was studied by in situ transmission electron microscope (TEM). Electron transparent specimens were mounted onto a constant displacement device. Stress was applied to the specimen by using a bolt through the device. The results showed that hydrogen enhanced the dislocation emission and motion in Fe3Al alloy. A dislocation free zone (DFZ) was formed following the dislocation emission. Microcrack initiated in the DFZ or at the main crack tip when the emission reached a critical extension. Hydrogen played an important role in the process of brittle fracture of Fe3Al alloy.
文摘Coating structural materials with Fe 3Al based intermetallics may rapidly lead to industrial application of their environment and wear resistant features. In the present study, high velocity arc spraying (HVAS) was used to in situ synthesize Fe 3Al intermetallic coating. The microstructural characterization and properties of the coating have been investigated. The microstructure was found to consist of Fe 3Al based intermetallic (D0 3 and B2) and α Fe regions together with fine oxide (α Al 2O 3) layers. TEM images of coating show that the solidified lamellae are polycrystalline and have a grain size of the order of about 150 nm , and there also exists amorphous state in some areas. It can be concluded that a very high cooling rate has been obtained during HVAS process. Moreover, the coating has relatively higher adhesion strength and microhardness, as well as lower density and porosity.
基金The work was supported by the Visiting Scholar Foundation of National Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, People's Republic of China.
文摘Phase structure characteristics near the interface of Fe3Al/Q235 diffusion bonding are investigated by means of X raydiffraction (XRD), transmission electronic microscope (TEM) and electron diffraction, etc. The test results indicatedthat obviously a diffusion transition zone forms near the interface of Fe3Al/Q235 under the condition of heatingtemperature 1050~1100℃, holding time 60 min and pressure 9.8 MPa, which indicated that the diffusion interfaceof Fe3Al/Q235 was combined well. The diffusion transition zone consisted of Fe3Al and a-Fe(Al) solid solution.Microhardness near the diffusion transition zone was HM 480~540. There was not brittle phase of high hardness inthe interface transition zone. This is favorable to enhance toughness of Fe3Al/Q235 diffusion joint.
基金the Doctoral Foundation of Shandong Province (2006BS04004)National Natural Science Foundation of China (50375088)
文摘Fe3Al and Crl8-Ni8 steel were bonded in vacuum and an interface was formed between Fe3Al and Crl8-Ni8 steel. Stress distribution at the diffusion-bonded interface was researched by numerical simulation and finite element method （FEM）. The results indicated that the peak stress appeared at the interface near Cr18-Ni8 steel side. This is the key factor to induce crack at this position. With the enhancement of heating temperature, the peak stress at the bonded interface increases. When the temperature is 1 100 22, the peak stress is up to 65.9 MPa, which is bigger than that at 1 000 22 by 9. 4%. In addition, the peak stress becomes bigger with the increase of the thickness of base metal from 1 mm to 8 ram. While the thickness is more than 8 ram, the peak stress varies slightly with the change of the thickness.