Herein, we report on the synthesis and Li-ion storage properties of the 0D–2D nanohybrid consisted of bimetal phosphorus trisulfides nanoneedles（Co_（0.5）Ni_（0.5）PS_3） and graphene nanosheets（denoted as Co_（0....Herein, we report on the synthesis and Li-ion storage properties of the 0D–2D nanohybrid consisted of bimetal phosphorus trisulfides nanoneedles（Co_（0.5）Ni_（0.5）PS_3） and graphene nanosheets（denoted as Co_（0.5）Ni_（0.5）PS_3@G）. By choosing the Co_（0.5）Ni_（0.5）（OH）_2 nanoneedles as precursor, the Co_（0.5）Ni_（0.5）PS_3 derived by a simple solid-state transformation（SST） process was successfully attached onto the graphene surface.The as-prepared nanohybrids showed a superior cycling stability and rate performance for Li-ion storage.After cycling at a current density of 0.5 A g^（-1） for 500 cycles, the capacity are 456 mAh g^（-1）. Particularly,the capacity can reach 302 mAh g^（-1） at a current density of 10 A g^（-1）, which is 66.2% of the capacity at0.5 A g^（-1）. Even cycling at a current density of 50 A g^（-1）, the nanocomposite can still kept a capacity of 153 mAh g^（-1） with a capacity retention of 33.6%.展开更多
基金the financial support from Singapore MOE AcRF Tier 1 under grant Nos.RG113/15 and 2016T1-002-065Singapore EMA project EIRP 12/NRF2015EWTEIRP002-008
文摘Herein, we report on the synthesis and Li-ion storage properties of the 0D–2D nanohybrid consisted of bimetal phosphorus trisulfides nanoneedles（Co_（0.5）Ni_（0.5）PS_3） and graphene nanosheets（denoted as Co_（0.5）Ni_（0.5）PS_3@G）. By choosing the Co_（0.5）Ni_（0.5）（OH）_2 nanoneedles as precursor, the Co_（0.5）Ni_（0.5）PS_3 derived by a simple solid-state transformation（SST） process was successfully attached onto the graphene surface.The as-prepared nanohybrids showed a superior cycling stability and rate performance for Li-ion storage.After cycling at a current density of 0.5 A g^（-1） for 500 cycles, the capacity are 456 mAh g^（-1）. Particularly,the capacity can reach 302 mAh g^（-1） at a current density of 10 A g^（-1）, which is 66.2% of the capacity at0.5 A g^（-1）. Even cycling at a current density of 50 A g^（-1）, the nanocomposite can still kept a capacity of 153 mAh g^（-1） with a capacity retention of 33.6%.