By making use of the diagrammatic techniques in perturbation theory,we have investigated the Hall effect in a quasi-two-dimensional disordered electron system.In the weakly localized regime,the analytical expression f...By making use of the diagrammatic techniques in perturbation theory,we have investigated the Hall effect in a quasi-two-dimensional disordered electron system.In the weakly localized regime,the analytical expression for quantum correction to Hall conductivity has been obtained using the Kubo formalism and quasiclassical approximation.The relevant dimensional crossover behavior from three dimensions to two dimensions with decreasing the interlayer hopping energy is discussed.The quantum interference effect is shown to have a vanishing correction t,o the Hall coefficient.展开更多
Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room tem...Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room temperature,a mechanically mixed layer(MML)was formed to protect the surface of the samples.Under 80 N of load at room temperature,the milled Al5083 and the Al5083−5wt.%B4C samples showed evidence of abrasion with limited volume loss.In this case,the wear rates were 5.8×10−7 and 4.4×10−7 mm3/(m·N),respectively.At 200°C and under 80 N of applied load,severe wear occurred in the milled Al5083 sample,and wear rate reached 10.8×10−7 mm3/(m·N)while the Al5083−5wt.%B4C sample showed mild wear with local 3-body abrasion and the wear rate reached 5.3×10−7 mm3/(m·N).Strengthening mechanisms such as dislocation pinning and the Hall−Petch theory,high hardness and the load transfer effect were crucial in determining the wear behavior of the Al5083−5wt.%B4C composite.On the other hand,the milled Al5083 sample represented a relatively high wear rate at 200°C,which seemed to be related to the local grain growth and a drop in its hardness.展开更多
文摘By making use of the diagrammatic techniques in perturbation theory,we have investigated the Hall effect in a quasi-two-dimensional disordered electron system.In the weakly localized regime,the analytical expression for quantum correction to Hall conductivity has been obtained using the Kubo formalism and quasiclassical approximation.The relevant dimensional crossover behavior from three dimensions to two dimensions with decreasing the interlayer hopping energy is discussed.The quantum interference effect is shown to have a vanishing correction t,o the Hall coefficient.
基金Authors would like to appreciate the former chief of Faculty of Materials&Manufacturing Processes of the Malek-Ashtar University of Technology,Professor EHSANI and the chief of the Composite Department,Dr.POURHOSSEINI along with the Razi and Kimiazi SEM labs and mechanical properties and SEM labs of Iran University of Science and Technology.Furthermore,the authors would like to thank Professor REZAEI,Ms.HAMIDI,and Ms.DAYYANI,Mr.SA'ADAT,and Mr.ATAEI from Iran University of Science and Technology.Special thanks to Mrs.KESHAVARZ,Ms.HAMEDANIZADEH,Ms.SHABANI,Ms.SHOJAEI and Mr.GANDOMKAR for their help and support.
文摘Tribological behavior and wear mechanisms of mechanically milled Al5083 alloy and Al5083−5wt.%B4C composite at room temperature and 200°C were discussed.Results revealed that due to the oxidative wear at room temperature,a mechanically mixed layer(MML)was formed to protect the surface of the samples.Under 80 N of load at room temperature,the milled Al5083 and the Al5083−5wt.%B4C samples showed evidence of abrasion with limited volume loss.In this case,the wear rates were 5.8×10−7 and 4.4×10−7 mm3/(m·N),respectively.At 200°C and under 80 N of applied load,severe wear occurred in the milled Al5083 sample,and wear rate reached 10.8×10−7 mm3/(m·N)while the Al5083−5wt.%B4C sample showed mild wear with local 3-body abrasion and the wear rate reached 5.3×10−7 mm3/(m·N).Strengthening mechanisms such as dislocation pinning and the Hall−Petch theory,high hardness and the load transfer effect were crucial in determining the wear behavior of the Al5083−5wt.%B4C composite.On the other hand,the milled Al5083 sample represented a relatively high wear rate at 200°C,which seemed to be related to the local grain growth and a drop in its hardness.