The strain hardening behaviors of 32Mn-TCr-1Mo-0.3N austenitic steel were characterized by a simple and effective method. The results show that Hollomon relationship is not applicable during total uniform deformation ...The strain hardening behaviors of 32Mn-TCr-1Mo-0.3N austenitic steel were characterized by a simple and effective method. The results show that Hollomon relationship is not applicable during total uniform deformation stage. The flow equation was proposed, Inσ=αexp（lnε/b）＋c. The variation rates of strain hardening exponents with true strain at 77 K are obviously higher than that at other temperatures and the value of d^2σ/dε^2 becomes positive during high strain stage. The characters of this variation are principal reasons for increasing elongation at 77 K. The forming of mechanical twin as well as ε-martensite leads to a high elongation at 77 K.展开更多
基金This work was supported by the National Natural Science Foundation of China No. 59771001Natural Science Foundation of Hebei Province under grant No. E200400197.
文摘The strain hardening behaviors of 32Mn-TCr-1Mo-0.3N austenitic steel were characterized by a simple and effective method. The results show that Hollomon relationship is not applicable during total uniform deformation stage. The flow equation was proposed, Inσ=αexp（lnε/b）＋c. The variation rates of strain hardening exponents with true strain at 77 K are obviously higher than that at other temperatures and the value of d^2σ/dε^2 becomes positive during high strain stage. The characters of this variation are principal reasons for increasing elongation at 77 K. The forming of mechanical twin as well as ε-martensite leads to a high elongation at 77 K.