Raman scattering measurements of K_2 Sr（MoO_4）2 were performed in the temperature range of 25–750？C. The Raman spectrum of the low-temperature phase α-K_2 Sr（MoO_4）2 that was obtained by first-principle calcula...Raman scattering measurements of K_2 Sr（MoO_4）2 were performed in the temperature range of 25–750？C. The Raman spectrum of the low-temperature phase α-K_2 Sr（MoO_4）2 that was obtained by first-principle calculations indicated that the Raman bands in the wavenumber region of 250–500 cm-1 are related to Mo–O bending vibrations in MoO4 tetrahedra,while the Raman bands in the wavenumber region of 650–950 cm-1 are attributed to stretching vibrations of Mo–O bonds.The temperature-dependent Raman spectra reveal that K_2 Sr（MoO_4）2 exhibits two sets of modifications in the Raman spectra at ～ 150？C and ～ 475？C, attributed to structural phase transitions. The large change of the Raman spectra in the temperature range of 150？C to 475？C suggests structural instability of the medium-temperature phase β-K_2 Sr（MoO_4）2.展开更多
Flower-like NaY（MoO4）2 particles were synthesized through a microwave-assisted hydrother- mal process followed by a subsequent calcination process. The products were characterized by X-ray diffraction, X-ray photoel...Flower-like NaY（MoO4）2 particles were synthesized through a microwave-assisted hydrother- mal process followed by a subsequent calcination process. The products were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron mi- croscopy. The possible formation mechanism of the flower-like NaY（MoO4）2 precursor was proposed. The NaY（MoO4）2：Eu3＋ phosphors were also prepared and their luminescence properties showed the NaY（MoO4）2：Eu^3＋ materials with the emission peak at 612 nm had potential application as a red phosphor for white light-emitting diodes. Furthermore, the microwave-assisted hydrothermal process followed by a subsequent calcination process could be extended to prepare the other lanthanide molybdates with the flower-like morphology.展开更多
基金Project supported by the Natural Science Foundation of Anhui Province,China(Grant Nos.KJ2018A0588 and KJ2017A625)
文摘Raman scattering measurements of K_2 Sr（MoO_4）2 were performed in the temperature range of 25–750？C. The Raman spectrum of the low-temperature phase α-K_2 Sr（MoO_4）2 that was obtained by first-principle calculations indicated that the Raman bands in the wavenumber region of 250–500 cm-1 are related to Mo–O bending vibrations in MoO4 tetrahedra,while the Raman bands in the wavenumber region of 650–950 cm-1 are attributed to stretching vibrations of Mo–O bonds.The temperature-dependent Raman spectra reveal that K_2 Sr（MoO_4）2 exhibits two sets of modifications in the Raman spectra at ～ 150？C and ～ 475？C, attributed to structural phase transitions. The large change of the Raman spectra in the temperature range of 150？C to 475？C suggests structural instability of the medium-temperature phase β-K_2 Sr（MoO_4）2.
文摘采用高温固相法制备了KLa(Mo O4)2∶Sm3+红色荧光粉,利用X射线衍射对晶体结构进行表征,发现不同浓度Sm3+掺杂的样品均为单斜相结构。测量了样品的激发和发射光谱,观察到样品在紫外区及可见蓝绿区均有强的激发带,在404 nm激发下存在4个发射峰。测量了不同温度下样品的发射光谱和荧光衰减曲线,对样品的荧光温度猝灭进行了分析,确定了样品发光的温度猝灭是由横向穿越所导致的,采用Arrhennius模型对实验数据进行拟合,确定激活能约为0.48 e V,表明荧光粉具有良好的热稳定性。
文摘Flower-like NaY（MoO4）2 particles were synthesized through a microwave-assisted hydrother- mal process followed by a subsequent calcination process. The products were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, field-emission scanning electron mi- croscopy. The possible formation mechanism of the flower-like NaY（MoO4）2 precursor was proposed. The NaY（MoO4）2：Eu3＋ phosphors were also prepared and their luminescence properties showed the NaY（MoO4）2：Eu^3＋ materials with the emission peak at 612 nm had potential application as a red phosphor for white light-emitting diodes. Furthermore, the microwave-assisted hydrothermal process followed by a subsequent calcination process could be extended to prepare the other lanthanide molybdates with the flower-like morphology.