large diameter internal thread of high-strength steel（LDITHSS） manufactured by traditional methods always has the problems of low accuracy and short life. Compared with traditional methods, the cold extrusion proces...large diameter internal thread of high-strength steel（LDITHSS） manufactured by traditional methods always has the problems of low accuracy and short life. Compared with traditional methods, the cold extrusion process is an effective means to realize higher accuracy and longer life. The low-cycle fatigue properties of LDITHSS are obtained by experiments, and the initiation and propagation of fatigue cracks are observed by scanning electron microscope（SEM）. Based on the mechanical properties, surface microstructure and residual stress, the strengthening mechanism of cold extruded large diameter internal thread（LDIT） is discussed. The results show that new grains or sub-grains can be formed on the surface of LDIT due to grain segmentation and grain refinement during cold extrusion. The fibrous structures appear as elongated and streamlined along the normal direction of the tooth surface which leads to residual compressive stress on the extruded surface. The maximum tension stress of LDIT after cold extrusion is found to be 192.55 k N. Under low stress cycling, the yield stress on thread increases, the propagation rate of crack reduces, the fatigue life is thus improved significantly with decreasing surface grain diameter and the average fatigue life increases to 45.539×10~3 cycle when the maximum applied load decreases to 120 k N. The low cycle fatigue and strengthening mechanism of cold extruded LDIT revealed by this research has significant importance to promote application of internal thread by cold extrusion processing.展开更多
The adoption of cold-extrusion forming for internal thread net forming becomes an important component of anti-fatigue processing with the development of internal thread processing towards high performance, low cost an...The adoption of cold-extrusion forming for internal thread net forming becomes an important component of anti-fatigue processing with the development of internal thread processing towards high performance, low cost and low energy consumption. It has vast application foreground in the field of aviation, spaceflight, high speed train and etc. The internal thread processing and anti-fatigue manufacture technology are summarized. In terms of the perspective of processing quality and fatigue serving life, the advantages and disadvantages of the processing methods from are compared. The internal thread cold-extrusion processing technology is investigated for the purpose of improving the anti-fatigue serving life of internal thread. The superiorities of the plastic deformation law and surface integrity of the metal layer in the course of cold extrusion for improving its stability and economy are summed up. The proposed research forecasts the develop- ment tendency of the internal thread anti-fatigue manufacturing technology.展开更多
基金Supported by National Natural Science Foundation of China(Grant No.51372216)Jiangsu Science and Technology Plan Project of China(Grant No.BE2015113)Natural Science Foundation of the Jiangsu Higher Education Institutions of China(Grant No.BKJB460016)
文摘large diameter internal thread of high-strength steel（LDITHSS） manufactured by traditional methods always has the problems of low accuracy and short life. Compared with traditional methods, the cold extrusion process is an effective means to realize higher accuracy and longer life. The low-cycle fatigue properties of LDITHSS are obtained by experiments, and the initiation and propagation of fatigue cracks are observed by scanning electron microscope（SEM）. Based on the mechanical properties, surface microstructure and residual stress, the strengthening mechanism of cold extruded large diameter internal thread（LDIT） is discussed. The results show that new grains or sub-grains can be formed on the surface of LDIT due to grain segmentation and grain refinement during cold extrusion. The fibrous structures appear as elongated and streamlined along the normal direction of the tooth surface which leads to residual compressive stress on the extruded surface. The maximum tension stress of LDIT after cold extrusion is found to be 192.55 k N. Under low stress cycling, the yield stress on thread increases, the propagation rate of crack reduces, the fatigue life is thus improved significantly with decreasing surface grain diameter and the average fatigue life increases to 45.539×10~3 cycle when the maximum applied load decreases to 120 k N. The low cycle fatigue and strengthening mechanism of cold extruded LDIT revealed by this research has significant importance to promote application of internal thread by cold extrusion processing.
基金Supported by National Natural Science Foundation of China(Grant No.51672241)International Cooperation Foundation of Ministry of Agriculture of China(Grant No.20162003)+2 种基金Collaborative Innovation Program of Industry University Research of Jiangsu Province China(Grant No.BE2015113)Young and Middle-aged Academic Leaders of Universities‘‘Qinglan Project’’of Jiangsu Province 2016Foundation of Key Laboratory of Modern Agricultural Equipment Ministry of Agriculture,China(Grant No.201604003)
文摘The adoption of cold-extrusion forming for internal thread net forming becomes an important component of anti-fatigue processing with the development of internal thread processing towards high performance, low cost and low energy consumption. It has vast application foreground in the field of aviation, spaceflight, high speed train and etc. The internal thread processing and anti-fatigue manufacture technology are summarized. In terms of the perspective of processing quality and fatigue serving life, the advantages and disadvantages of the processing methods from are compared. The internal thread cold-extrusion processing technology is investigated for the purpose of improving the anti-fatigue serving life of internal thread. The superiorities of the plastic deformation law and surface integrity of the metal layer in the course of cold extrusion for improving its stability and economy are summed up. The proposed research forecasts the develop- ment tendency of the internal thread anti-fatigue manufacturing technology.