The distinctive intrinsic heat treatment(IHT)originating from cyclic reheating in the laser-directed energy deposition(LDED) has attracted growing attention in recent years.In this investigation,simulations and experi...The distinctive intrinsic heat treatment(IHT)originating from cyclic reheating in the laser-directed energy deposition(LDED) has attracted growing attention in recent years.In this investigation,simulations and experimental characterizations were performed to examine the impact of IHT on the micros true ture and mechanical properties of LDED-fabricated CrCoNi medium-entropy alloy(MEA).The results show that the intensity of the IHT is proportional to the utilized laser energy density(LED).As the LED increased,significant dynamic recrystallization and grain refinement occurred within the alloy due to the enhanced intensity of IHT.However,the high LED leads to severe hot cracking within the as-built MEA,resulting in inferior ductility.By decreasing LED,the hot cracking was effectively eliminated.Meanwhile,low LED weakened the intensity of IHT and consequently inhibited kinetic conditions of dynamic recrystallization,resulting in a heterogeneous grain structure characterized by multi-scale-sized grains.This structure provides significant hetero-deformation-induced hardening during plastic deformation,enabling the alloy to have a sustainable work-hardening capacity.We expect that this work will have implications in taking full advantage of the unique IHT of the LDED process to fabricate ME As with excellent metallurgical quality and mechanical performance.展开更多
Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposit...Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposited samples was systematically studied.The results indicate that refining the W particle size could refine theγ-Ni grains and subgrains,thin the(Ni,Cr)_(4)W interface layer,and increase the disloca-tion density of the intergranular matrix,thus improving the tensile strength and elongation of the L-DED samples.As W particle size decreased from 75 to 150μm to 6.5-12μm,the tensile strength and elonga-tion of the deposited samples increased by 150 MPa and 2.9 times to 1347.6±15.7 MPa and 17.5±0.4%,respectively.Based on the properties of the interface(Ni,Cr)_(4)W,a load-transfer efficiency factor suitable for this composite was proposed and the load-transfer strengthening formula was optimized.A quanti-tative analysis of the strengthening mechanisms was established considering load-transfer strengthening,Hall-Petch strengthening,thermal-mismatch strengthening,and solid-solution strengthening.The calcu-lated contribution of each strengthening mechanism to the yield strength and theoretical calculations were in good agreement with the experimental data.The article breaks the bottleneck of poor plasticity of W particle-reinforced Ni-based composites prepared by L-DED and provides a theoretical basis for the construction design of W particle-reinforced Ni-based composites with excellent mechanical properties.展开更多
美国定向能机动近程防空(directed energy maneuver-short range air defense,DE M-SHORAD)计划通过击伤、摧毁或压制旋转翼无人机、固定翼无人机以及火箭弹、火炮炮弹、迫击炮弹(rockets,artillery and mortar,RAM)等威胁目标,为机动...美国定向能机动近程防空(directed energy maneuver-short range air defense,DE M-SHORAD)计划通过击伤、摧毁或压制旋转翼无人机、固定翼无人机以及火箭弹、火炮炮弹、迫击炮弹(rockets,artillery and mortar,RAM)等威胁目标,为机动部队提供伴随防空,对抗新兴威胁,属于美国陆军防空反导现代化的优先项目之一。首先介绍了DE M-SHORAD研制计划;其次详细分析了系统结构,并由系统参数评估了系统的作战性能;最后梳理了系统的研制进展。通过综合分析可知,DE M-SHORAD系统采用最佳组件,通过快速原型方法实现激光武器系统在装甲车上的集成;为降低技术风险,该计划在发展方式上分为两个阶段,首先集成、测试2 kW~5 kW机动实验型高能激光器(mobile experimental high-energy laser,MEHEL),然后再研制50 kW级的多任务高能激光器(multi-mission high-energy laser,MMHEL)。经计算可得:MEHEL和MMHEL对无人机的最大射程分别约为0.77 km、4.8 km。展开更多
基金financially supported by the funding from Guangdong Province Basic and Applied Research Key Projects (No.2020B0301030001)National Key R&D Programme,Ministry of Science and Technology of China (Nos. 2018YFB1105200 and 2019YFA0209904)the National Natural Science Foundation of China (Nos.52371106 and 52371025)。
文摘The distinctive intrinsic heat treatment(IHT)originating from cyclic reheating in the laser-directed energy deposition(LDED) has attracted growing attention in recent years.In this investigation,simulations and experimental characterizations were performed to examine the impact of IHT on the micros true ture and mechanical properties of LDED-fabricated CrCoNi medium-entropy alloy(MEA).The results show that the intensity of the IHT is proportional to the utilized laser energy density(LED).As the LED increased,significant dynamic recrystallization and grain refinement occurred within the alloy due to the enhanced intensity of IHT.However,the high LED leads to severe hot cracking within the as-built MEA,resulting in inferior ductility.By decreasing LED,the hot cracking was effectively eliminated.Meanwhile,low LED weakened the intensity of IHT and consequently inhibited kinetic conditions of dynamic recrystallization,resulting in a heterogeneous grain structure characterized by multi-scale-sized grains.This structure provides significant hetero-deformation-induced hardening during plastic deformation,enabling the alloy to have a sustainable work-hardening capacity.We expect that this work will have implications in taking full advantage of the unique IHT of the LDED process to fabricate ME As with excellent metallurgical quality and mechanical performance.
基金supported by the Key Projects of the National Natural Science Foundation of China(Nos.92066201 and 92266101)the Jiangxi Provincial Key R&D Programme Projects(No.20212BBE51011).
文摘Tungsten(W)particle-reinforced nickel(Ni)-based composites were fabricated via laser-direct energy de-position(L-DED).The influence of the W particle size on the microstructure and mechanical properties of the deposited samples was systematically studied.The results indicate that refining the W particle size could refine theγ-Ni grains and subgrains,thin the(Ni,Cr)_(4)W interface layer,and increase the disloca-tion density of the intergranular matrix,thus improving the tensile strength and elongation of the L-DED samples.As W particle size decreased from 75 to 150μm to 6.5-12μm,the tensile strength and elonga-tion of the deposited samples increased by 150 MPa and 2.9 times to 1347.6±15.7 MPa and 17.5±0.4%,respectively.Based on the properties of the interface(Ni,Cr)_(4)W,a load-transfer efficiency factor suitable for this composite was proposed and the load-transfer strengthening formula was optimized.A quanti-tative analysis of the strengthening mechanisms was established considering load-transfer strengthening,Hall-Petch strengthening,thermal-mismatch strengthening,and solid-solution strengthening.The calcu-lated contribution of each strengthening mechanism to the yield strength and theoretical calculations were in good agreement with the experimental data.The article breaks the bottleneck of poor plasticity of W particle-reinforced Ni-based composites prepared by L-DED and provides a theoretical basis for the construction design of W particle-reinforced Ni-based composites with excellent mechanical properties.