Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxida...Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.展开更多
MCrAlY/TaC metal matrix composite coatings with 10, 20 and 30 wt.% TaC have been successfully produced by electrospark deposition （ESD）. The effects of TaC content on microstructure, hardness and oxidation behavior ...MCrAlY/TaC metal matrix composite coatings with 10, 20 and 30 wt.% TaC have been successfully produced by electrospark deposition （ESD）. The effects of TaC content on microstructure, hardness and oxidation behavior of the composite coatings were studied. The results showed that the composite coatings were composed of superfine 9＇ columnar dendrite and large TaC particles dispersedly distributed. The hardness was enhanced but oxidation resistance of the composite coatings was reduced with increasing TaC contents.展开更多
陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先...陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先使基体与Al2O3结合的复合粉末控制涂层中的Al2O3含量。涂层粉末的微结构在冷喷涂涂层和超音速火焰喷涂涂层中得到了良好的保留,这是因为喷涂粒子未熔化或部分熔化。然而,对于等离子喷涂的涂层,大多数Al2O3颗粒被隔离在层状界面,在条状界面上形成连续的氧化皮。经退火处理后,由元素扩散引起的条状界面的强化使得超音速火焰喷涂和大气等离子喷涂的涂层硬度增大。此外,冷喷涂涂层由于退火后加工硬化效果的消除,硬度增加不像超音速火焰喷涂和等离子喷涂涂层那样明显。展开更多
文摘Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.
基金supported by the National Natural Science Foundation of China(No.50901081)
文摘MCrAlY/TaC metal matrix composite coatings with 10, 20 and 30 wt.% TaC have been successfully produced by electrospark deposition （ESD）. The effects of TaC content on microstructure, hardness and oxidation behavior of the composite coatings were studied. The results showed that the composite coatings were composed of superfine 9＇ columnar dendrite and large TaC particles dispersedly distributed. The hardness was enhanced but oxidation resistance of the composite coatings was reduced with increasing TaC contents.
文摘陶瓷颗粒增强型金属基复合涂层在诸多工业领域都有需求,其中包括炼钢工业。本文中,MCr Al Y-Al2O3复合粉末通过球磨法制备,并且通过等离子喷涂、超音速火焰喷涂和冷喷涂分别制备了MCr Al Y-Al2O3复合涂层。实验结果显示,可以选用不优先使基体与Al2O3结合的复合粉末控制涂层中的Al2O3含量。涂层粉末的微结构在冷喷涂涂层和超音速火焰喷涂涂层中得到了良好的保留,这是因为喷涂粒子未熔化或部分熔化。然而,对于等离子喷涂的涂层,大多数Al2O3颗粒被隔离在层状界面,在条状界面上形成连续的氧化皮。经退火处理后,由元素扩散引起的条状界面的强化使得超音速火焰喷涂和大气等离子喷涂的涂层硬度增大。此外,冷喷涂涂层由于退火后加工硬化效果的消除,硬度增加不像超音速火焰喷涂和等离子喷涂涂层那样明显。