Ultrasonic treatment has great contributions on modifying the morphology,dimension and distribution of constituent phases during solidification,which serve as dominate factors influencing the hydrogen storage performa...Ultrasonic treatment has great contributions on modifying the morphology,dimension and distribution of constituent phases during solidification,which serve as dominate factors influencing the hydrogen storage performance of Mg-based alloys.In this research,ultrasonic treatment is utilized as a novel method to enhance the de-/hydriding properties of Mg-2Ni(at.%)alloy.Due to ultrasonic treatment,the microstructure of as-cast alloy is significantly refined and homogenized.Ascribing to the increased eutectic boundaries and shortened distance insideα-Mg for hydrogen atoms diffusion,the hydrogen uptake capacities and isothermal de-/hydriding rates improve effectively,especially at lower temperature.The peak desorption temperature reduces from 392.99°C to 345.56°C,and the dehydriding activation energy decreases from 101.93 k J mol^(-1)to 88.65 k J mol^(-1).Weakened hysteresis of plateau pressures and slightly optimized thermodynamics are determined from the pressure-composition isotherms.Owing to the refined primary Mg,a larger amount of hydrogen with the higher hydriding proportion is absorbed in the first stage when hydrides nucleate in eutectic region and grow on primary Mg periphery subsequently before MgH2colonies impinging,resulting in the enhancement of hydrogenation rates and capacities.展开更多
In this work,La-doped Mg-Ni multiphase alloys were prepared by resistance melting furnace(RMF)and then modified by high-energy ball milling(HEBM).The hydrolysis H_(2) generation kinetics/thermodynamics of prepared all...In this work,La-doped Mg-Ni multiphase alloys were prepared by resistance melting furnace(RMF)and then modified by high-energy ball milling(HEBM).The hydrolysis H_(2) generation kinetics/thermodynamics of prepared alloys in Na Cl solutions have been investigated with the help of nonlinear and linear fitting by Avrami-Erofeev and Arrhenius equations.Combining the microstructure information before and after hydrolysis and thermodynamics fitting results,the hydrolysis H_(2) generation mechanism based on nucleation&growth has been elaborated.The final H_(2) generation capacities of 0La,5La,10La and 15 La alloys are 677,653,641 and 770 m L·g^(-1)H_(2) in 240 min at291 K,respectively.While,the final H_(2) generation capacities of HEBM 0La,5La,10La and 15 La alloys are 632,824,611 and 653 m L·g^(-1)H_(2) in 20 min at 291 K,respectively.The as-cast 15La alloy and HEMB 5La alloy present the best H_(2) production rates and final H_(2) production capacities,especially the HEBM 5La can rapidly achieve high H_(2) generation capacity(670 and 824 m L·g^(-1)H_(2) )at low temperature(291 K)within short time(5 and 20 min).The difference between the H_(2) generation capacities is mainly originated from the initial nucleation rate of Mg(OH)_(2) and the subsequent processes affected by the microstructures and phase compositions of the hydrolysis alloys.Relative low initial nucleation rate and fully growth of Mg(OH)_(2) nucleus are the premise of high H_(2) generation capacity due to the hydrolysis H_(2) generation process consisted by the nucleation,growth and contacting of Mg(OH)_(2) nucleus.To utilization H_(2) by designing solid state H_(2) generators using optimized Mg-based alloys is expected to be a feasible H_(2) generation strategy at the moment.展开更多
基金supported by National Key Research and Development Program of China(2017YFA0403804)National Natural Science Foundation of China(51825401)
文摘Ultrasonic treatment has great contributions on modifying the morphology,dimension and distribution of constituent phases during solidification,which serve as dominate factors influencing the hydrogen storage performance of Mg-based alloys.In this research,ultrasonic treatment is utilized as a novel method to enhance the de-/hydriding properties of Mg-2Ni(at.%)alloy.Due to ultrasonic treatment,the microstructure of as-cast alloy is significantly refined and homogenized.Ascribing to the increased eutectic boundaries and shortened distance insideα-Mg for hydrogen atoms diffusion,the hydrogen uptake capacities and isothermal de-/hydriding rates improve effectively,especially at lower temperature.The peak desorption temperature reduces from 392.99°C to 345.56°C,and the dehydriding activation energy decreases from 101.93 k J mol^(-1)to 88.65 k J mol^(-1).Weakened hysteresis of plateau pressures and slightly optimized thermodynamics are determined from the pressure-composition isotherms.Owing to the refined primary Mg,a larger amount of hydrogen with the higher hydriding proportion is absorbed in the first stage when hydrides nucleate in eutectic region and grow on primary Mg periphery subsequently before MgH2colonies impinging,resulting in the enhancement of hydrogenation rates and capacities.
基金financially supported by the National Natural Science Foundation of China(Grant Nos.51704188,51702199,61705125,51802181)the State Key Laboratory of Solidification Processing in NWPU(Grant No.SKLSP201809)+2 种基金Natural Science Foundation of Shaanxi Province(Grant No.2019JQ-099)Research Starting Foundation from Shaanxi University of Science and Technology(Grant No.2016GBJ-04)the financial support of China Scholarship Council(Grant No.201808610089)。
文摘In this work,La-doped Mg-Ni multiphase alloys were prepared by resistance melting furnace(RMF)and then modified by high-energy ball milling(HEBM).The hydrolysis H_(2) generation kinetics/thermodynamics of prepared alloys in Na Cl solutions have been investigated with the help of nonlinear and linear fitting by Avrami-Erofeev and Arrhenius equations.Combining the microstructure information before and after hydrolysis and thermodynamics fitting results,the hydrolysis H_(2) generation mechanism based on nucleation&growth has been elaborated.The final H_(2) generation capacities of 0La,5La,10La and 15 La alloys are 677,653,641 and 770 m L·g^(-1)H_(2) in 240 min at291 K,respectively.While,the final H_(2) generation capacities of HEBM 0La,5La,10La and 15 La alloys are 632,824,611 and 653 m L·g^(-1)H_(2) in 20 min at 291 K,respectively.The as-cast 15La alloy and HEMB 5La alloy present the best H_(2) production rates and final H_(2) production capacities,especially the HEBM 5La can rapidly achieve high H_(2) generation capacity(670 and 824 m L·g^(-1)H_(2) )at low temperature(291 K)within short time(5 and 20 min).The difference between the H_(2) generation capacities is mainly originated from the initial nucleation rate of Mg(OH)_(2) and the subsequent processes affected by the microstructures and phase compositions of the hydrolysis alloys.Relative low initial nucleation rate and fully growth of Mg(OH)_(2) nucleus are the premise of high H_(2) generation capacity due to the hydrolysis H_(2) generation process consisted by the nucleation,growth and contacting of Mg(OH)_(2) nucleus.To utilization H_(2) by designing solid state H_(2) generators using optimized Mg-based alloys is expected to be a feasible H_(2) generation strategy at the moment.