This work proposed a strategy of indirectly inducing uniform microarc discharge by controlling the content and distribution ofβ-Mg_(17)Al_(12)phase in AZ91D Mg alloy.Two kinds of nano-particles(ZrO_(2)and TiO_(2))wer...This work proposed a strategy of indirectly inducing uniform microarc discharge by controlling the content and distribution ofβ-Mg_(17)Al_(12)phase in AZ91D Mg alloy.Two kinds of nano-particles(ZrO_(2)and TiO_(2))were designed to be added into the substrate of Mg alloy by friction stir processing(FSP).Then,Mg alloy sample designed with different precipitated morphology ofβ-Mg_(17)Al_(12)phase was treated by microarc oxidation(MAO)in Na_(3)PO_(4)/Na2SiO3electrolyte.The characteristics and performance of the MAO coating was analyzed using scanning electron microscopy(SEM),energy dispersive spectrometer(EDS),X-ray diffraction(XRD),X-ray photoelectron spectroscopy(XPS),contact angle meter,and potentiodynamic polarization.It was found that the coarseα-Mg grains in extruded AZ91D Mg alloy were refined by FSP,and theβ-Mg_(17)Al_(12)phase with reticular structure was broken and dispersed.The nano-ZrO_(2)particles were pinned at the grain boundary by FSP,which refined theα-Mg grain and promoted the precipitation ofβ-Mg_(17)Al_(12)phase in grains.It effectively inhibited the“cascade”phenomenon of microarcs,which induced the uniform distribution of discharge pores.The MAO coating on Zr-FSP sample had good wettability and corrosion resistance.However,TiO_(2)particles were hardly detected in the coating on TiFSP sample.展开更多
The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese scr...The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.展开更多
AZ31-4.6% Mg2Si （mass fraction） composite was prepared by conventional casting method. Repetitive upsetting （RU） was applied to severely deforming the as-cast composite at 400 ℃ for 1, 3, and 5 passes. Finite ele...AZ31-4.6% Mg2Si （mass fraction） composite was prepared by conventional casting method. Repetitive upsetting （RU） was applied to severely deforming the as-cast composite at 400 ℃ for 1, 3, and 5 passes. Finite element analysis of the material flow indicates that deformation concentrates in the bottom region of the sample after 1 pass, and much more uniform deformation is obtained after 5 passes. During multi-pass RU process, both dendritic and Chinese script type Mg2Si phases are broken up into smaller particles owing to the shear stress forced by the matrix. With the increasing number of RU passes, finer grain size and more homogeneous distribution of Mg2Si particles are obtained along with significant enhancement in both strength and ductility. AZ31-4.6%Mg2Si composite exhibits tensile strength of 284 MPa and elongation of 9.8%after 5 RU passes at 400 ℃ compared with the initial 128 MPa and 5.4%of original AZ31-4.6%Mg2Si composite.展开更多
The effect of Sr on modification and refinement of the Mg 2 Si phase in an AZ61-0.7Si magnesium alloy has been investigated and analyzed.The results indicate that Sr can effectively modify and refine the Chinese-scrip...The effect of Sr on modification and refinement of the Mg 2 Si phase in an AZ61-0.7Si magnesium alloy has been investigated and analyzed.The results indicate that Sr can effectively modify and refine the Chinese-script shaped Mg2Si phase in the AZ61-0.7Si alloy.By adding 0.06wt.%-0.12wt.%Sr to AZ61-0.7Si alloy,the Mg2Si phase in the alloy can be changed from the initial coarse Chinese-script shape to fine granule and/or irregular polygonal shapes.Accordingly,the Sr-containing AZ61-0.7Si alloy exhibits higher tensile and creep properties than the AZ61-0.7Si alloy without Sr modification.The mechanism on modification and refinement of the Mg2Si phase in Sr-containing AZ61-0.7Si alloy is possibly related to the following two aspects:(1)adding Sr may form the Al4Sr phase which can serve as the heterogeneous nucleus for the Mg2Si particles and/or(2)adding Sr may lower the onset crystallizing temperature and increase the undercooling level.展开更多
In-situ ZrB2/AZ91D magnesium matrix composite was successfully synthesized with AI/K2ZrF6＋NH4BF4 by means of Direct Melt Reaction. The fabricated ZrB2/AZ91D magnesium matrix composite through direct melt mixing metho...In-situ ZrB2/AZ91D magnesium matrix composite was successfully synthesized with AI/K2ZrF6＋NH4BF4 by means of Direct Melt Reaction. The fabricated ZrB2/AZ91D magnesium matrix composite through direct melt mixing method was investigated. Results from X-ray diffraction （XRD） and energy dispersive X-ray spectroscopy （EDS） confirmed the existence of ZrB2 particles in the AZ91D alloy, and most ZrB2 particles were in the size range of just several microns, some even to 100 nm. The cast specimens were studied through corrosion testing and heat treatment. The average grain size of AZ91D decreased markedly from about 250 pm to 50 IJm. In addition, the shape and size of the ,β-MglTAI12 phase as well as the morphologies of primary a-Mg in the magnesium matrix composite were greatly changed. The network structure of the β-MglTAI12 phase was broken into small blocks and the size of a-Mg decreased significantly.展开更多
基金funded by China Postdoctoral Science Foundation(No.2021M700569)Chongqing Postdoctoral Science Foundation(No.7 cstc2021jcyj-bshX0087)。
文摘This work proposed a strategy of indirectly inducing uniform microarc discharge by controlling the content and distribution ofβ-Mg_(17)Al_(12)phase in AZ91D Mg alloy.Two kinds of nano-particles(ZrO_(2)and TiO_(2))were designed to be added into the substrate of Mg alloy by friction stir processing(FSP).Then,Mg alloy sample designed with different precipitated morphology ofβ-Mg_(17)Al_(12)phase was treated by microarc oxidation(MAO)in Na_(3)PO_(4)/Na2SiO3electrolyte.The characteristics and performance of the MAO coating was analyzed using scanning electron microscopy(SEM),energy dispersive spectrometer(EDS),X-ray diffraction(XRD),X-ray photoelectron spectroscopy(XPS),contact angle meter,and potentiodynamic polarization.It was found that the coarseα-Mg grains in extruded AZ91D Mg alloy were refined by FSP,and theβ-Mg_(17)Al_(12)phase with reticular structure was broken and dispersed.The nano-ZrO_(2)particles were pinned at the grain boundary by FSP,which refined theα-Mg grain and promoted the precipitation ofβ-Mg_(17)Al_(12)phase in grains.It effectively inhibited the“cascade”phenomenon of microarcs,which induced the uniform distribution of discharge pores.The MAO coating on Zr-FSP sample had good wettability and corrosion resistance.However,TiO_(2)particles were hardly detected in the coating on TiFSP sample.
基金Project (BG2007030) supported by High-tech Research Program of Jiangsu Province, ChinaProject (07KJA43008) supported by the Natural Science Foundation of Jiangsu Province, ChinaProject (20070299004) supported by the Specialized Research Fund for the Doctoral Program of Higher Education of China
文摘The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.
基金Projects(51074106,51374145)supported by the National Natural Science Foundation of ChinaProject(09JC1408200)supported by the Science and Technology Commission of Shanghai Municipality,China+1 种基金Project(2014M561466)supported by China Postdoctoral Science FoundationProject(14R21411000)supported by Shanghai Postdoctoral Scientific Program,China
文摘AZ31-4.6% Mg2Si （mass fraction） composite was prepared by conventional casting method. Repetitive upsetting （RU） was applied to severely deforming the as-cast composite at 400 ℃ for 1, 3, and 5 passes. Finite element analysis of the material flow indicates that deformation concentrates in the bottom region of the sample after 1 pass, and much more uniform deformation is obtained after 5 passes. During multi-pass RU process, both dendritic and Chinese script type Mg2Si phases are broken up into smaller particles owing to the shear stress forced by the matrix. With the increasing number of RU passes, finer grain size and more homogeneous distribution of Mg2Si particles are obtained along with significant enhancement in both strength and ductility. AZ31-4.6%Mg2Si composite exhibits tensile strength of 284 MPa and elongation of 9.8%after 5 RU passes at 400 ℃ compared with the initial 128 MPa and 5.4%of original AZ31-4.6%Mg2Si composite.
基金supported by the National Natural Science Funds for Distinguished Young Scholar in China(No.50725413)the Major State Basic Research Development Program of China(973)(No.2007CB613704)+1 种基金the Natural Science Foundation Project of CQ CSTC(No.2007BB4400)Chongqing Science and Technology Commission in China(No.2006AA4012-9-6).
文摘The effect of Sr on modification and refinement of the Mg 2 Si phase in an AZ61-0.7Si magnesium alloy has been investigated and analyzed.The results indicate that Sr can effectively modify and refine the Chinese-script shaped Mg2Si phase in the AZ61-0.7Si alloy.By adding 0.06wt.%-0.12wt.%Sr to AZ61-0.7Si alloy,the Mg2Si phase in the alloy can be changed from the initial coarse Chinese-script shape to fine granule and/or irregular polygonal shapes.Accordingly,the Sr-containing AZ61-0.7Si alloy exhibits higher tensile and creep properties than the AZ61-0.7Si alloy without Sr modification.The mechanism on modification and refinement of the Mg2Si phase in Sr-containing AZ61-0.7Si alloy is possibly related to the following two aspects:(1)adding Sr may form the Al4Sr phase which can serve as the heterogeneous nucleus for the Mg2Si particles and/or(2)adding Sr may lower the onset crystallizing temperature and increase the undercooling level.
基金financially supported by the Specialized Research Fund Project for the Doctoral Program of Higher Education of China (No.20070299004)the Jiangsu Higher Education Institutions Natural Science Foundation Research Program (No.10KJD430003)+2 种基金the Jiangsu University Outstanding Talents Building Project (No.1213000004)the Jiangsu University Undergraduate Practice-Innovation Training Project (No.1201220038)Doctoral Foundation of Jiangsu University (No.1281220014)
文摘In-situ ZrB2/AZ91D magnesium matrix composite was successfully synthesized with AI/K2ZrF6＋NH4BF4 by means of Direct Melt Reaction. The fabricated ZrB2/AZ91D magnesium matrix composite through direct melt mixing method was investigated. Results from X-ray diffraction （XRD） and energy dispersive X-ray spectroscopy （EDS） confirmed the existence of ZrB2 particles in the AZ91D alloy, and most ZrB2 particles were in the size range of just several microns, some even to 100 nm. The cast specimens were studied through corrosion testing and heat treatment. The average grain size of AZ91D decreased markedly from about 250 pm to 50 IJm. In addition, the shape and size of the ,β-MglTAI12 phase as well as the morphologies of primary a-Mg in the magnesium matrix composite were greatly changed. The network structure of the β-MglTAI12 phase was broken into small blocks and the size of a-Mg decreased significantly.