Mixed mesophilic and extreme thermophilic bioleaching were evaluated to remove copper from the molybdenite concentrate.Bioleaching tests were carried out in shake flasks and in a 50-L bioreactor.The shake flask tests ...Mixed mesophilic and extreme thermophilic bioleaching were evaluated to remove copper from the molybdenite concentrate.Bioleaching tests were carried out in shake flasks and in a 50-L bioreactor.The shake flask tests were performed with different inoculum size,solids density,pH.and temperature in order to identify optimum conditions.The highest amount of copper elimination,75%was obtained with extreme thermophilic microorganisms(at 12%inoculation,10%solids,65℃and a pH of 1.5).The highest copper elimination by mesophilic microorganisms was 55%(at 12%inoculation,5%solids,30℃at pH 2).The optimum conditions in shake flask tests were applied to 7 days batch tests in a50-L bioreactor.Extreme thermophilic experiment gave the best copper elimination of 60%(at 12%inoculation,10%solids,65℃and pH 1.5).Mesophilic test removed 50%of the copper(at 12%inoculation,10%solids,35℃at pH 2).展开更多
Dielectric properties were measured using cavity perturbation method. The temperature rising behaviors of molybdenite concentrate were investigated in the field of microwave. This process was conducted to show the mic...Dielectric properties were measured using cavity perturbation method. The temperature rising behaviors of molybdenite concentrate were investigated in the field of microwave. This process was conducted to show the microwave absorption properties of molybdenite concentrate and the feasibility of microwave roasting molybdenite concentrate to prepare high purity M_OO_3. The dielectric constant,dielectric loss,and loss tangent increase from 3. 51 to 5. 04,0. 22 to 0. 51 and 0. 065 to 0. 102 respectively. They are proportional to the apparent density of molybdenite concentrate in the range of 0. 9-1. 4 g/cm3. The results show that the molybdenite concentrate has good microwave absorption capacity in the conventional density range. The temperature rising curves show that the apparent heating rate of the molybdenite concentrate increases with the increase in microwave power and decreases with the increase in the sample mass and thickness. The temperature of concentrate sample of 100 g reaches approximately 800 ℃ after 5 min of microwave treatment at 0. 5 kW of power. Our findings show that it is feasible to prepare high-purity M_OO_3 from molybdenite concentrate by microwave roasting.展开更多
基金supported by the National Iranian Copper Industry Co.
文摘Mixed mesophilic and extreme thermophilic bioleaching were evaluated to remove copper from the molybdenite concentrate.Bioleaching tests were carried out in shake flasks and in a 50-L bioreactor.The shake flask tests were performed with different inoculum size,solids density,pH.and temperature in order to identify optimum conditions.The highest amount of copper elimination,75%was obtained with extreme thermophilic microorganisms(at 12%inoculation,10%solids,65℃and a pH of 1.5).The highest copper elimination by mesophilic microorganisms was 55%(at 12%inoculation,5%solids,30℃at pH 2).The optimum conditions in shake flask tests were applied to 7 days batch tests in a50-L bioreactor.Extreme thermophilic experiment gave the best copper elimination of 60%(at 12%inoculation,10%solids,65℃and pH 1.5).Mesophilic test removed 50%of the copper(at 12%inoculation,10%solids,35℃at pH 2).
基金Supported by the National Natural Science Foundation-Yunnan Joint Fund Project of China(U1402274)the National Natural Science Foundation of China(51564033)Yunnan Applied Basic Research Project(2016FA023)
文摘Dielectric properties were measured using cavity perturbation method. The temperature rising behaviors of molybdenite concentrate were investigated in the field of microwave. This process was conducted to show the microwave absorption properties of molybdenite concentrate and the feasibility of microwave roasting molybdenite concentrate to prepare high purity M_OO_3. The dielectric constant,dielectric loss,and loss tangent increase from 3. 51 to 5. 04,0. 22 to 0. 51 and 0. 065 to 0. 102 respectively. They are proportional to the apparent density of molybdenite concentrate in the range of 0. 9-1. 4 g/cm3. The results show that the molybdenite concentrate has good microwave absorption capacity in the conventional density range. The temperature rising curves show that the apparent heating rate of the molybdenite concentrate increases with the increase in microwave power and decreases with the increase in the sample mass and thickness. The temperature of concentrate sample of 100 g reaches approximately 800 ℃ after 5 min of microwave treatment at 0. 5 kW of power. Our findings show that it is feasible to prepare high-purity M_OO_3 from molybdenite concentrate by microwave roasting.