In the present work,seven Mg-Zn-Ag alloys with the nominal composition of Mg_(96-x)Zn_(x)Ag_(4)(x=17,20,23,26,29,32,35 in at.%)were prepared by induction melting and single-roller melt-spinning.The X-ray diffraction(X...In the present work,seven Mg-Zn-Ag alloys with the nominal composition of Mg_(96-x)Zn_(x)Ag_(4)(x=17,20,23,26,29,32,35 in at.%)were prepared by induction melting and single-roller melt-spinning.The X-ray diffraction(XRD)analyses indicate the metallic glasses with three composition of Mg_(73)Zn_(23)Ag_(4),Mg_(70)Zn_(26)Ag_(4),and Mg_(67)Zn_(29)Ag_(4)were obtained successfully.The differential scanning calorimetry(DSC)measurement was used to obtain the characteristic temperature of Mg-Zn-Ag metallic glasses for the glass-forming ability analysis.The maximum glass transition temperature(Trg)was found to be 0.525 with a composition close to Mg_(67)Zn_(29)Ag_(4),which results in the best glass-forming ability.Moreover,the immersion test in simulated body fluid(SBF)demonstrate the relative homogeneous corrosion behavior of the Mg-Zn-Ag metallic glasses.The corrosion rate of Mg-Zn-Ag metallic glasses in SBF solution decreases with the increase of Zn content.The sample Mg_(67)Zn_(29)Ag_(4)has the lowest corrosion rate of 0.19mm/yr,which could meet the clinical application requirement well.The in vitro cell experiments show that the Madin-Darby canine kidney(MDCK)cells cultured in sample Mg_(67)Zn_(29)Ag_(4)and its extraction medium have higher activity.However,the Mg-Zn-Ag metallic glasses exhibit obvious inhibitory effect on human rhabdomyosarcoma(RD)tumor cells.The present investigations on the glass-forming ability,corrosion behavior,cytocompatibility and tumor inhibition function of the Mg-Zn-Ag based metallic glass could reveal their biomedical application possibility.展开更多
Zirconium-based metallic glasses(Zr-MGs)are demonstrated to exhibit high mechanical strength,low elastic modulus and excellent biocompatibility,making them promising materials for endosseous implants.Meanwhile,tantalu...Zirconium-based metallic glasses(Zr-MGs)are demonstrated to exhibit high mechanical strength,low elastic modulus and excellent biocompatibility,making them promising materials for endosseous implants.Meanwhile,tantalum(Ta)is also well known for its ideal corrosion resistance and biological effects.However,the metal has an elastic modulus as high as 186 GPa which is not comparable to the natural bone(10–30 GPa),and it also has a relative high cost.Here,to fully exploit the advantages of Ta as endosseous implants,a small amount of Ta(as low as 3 at.%)was successfully added into a Zr-MG to generate an advanced functional endosseous implant,Zr58Cu25Al14Ta3 MG,with superior comprehensive properties.Upon carefully dissecting the atomic structure and surface chemistry,the results show that amorphization of Ta enables the uniform distribution in material surface,leading to a significantly improved chemical stability and extensive material-cell contact regulation.Systematical analyses on the immunological,angiogenesis and osteogenesis capability of the material are carried out utilizing the next-generation sequencing,revealing that Zr_(58)Cu_(25)Al_(14)Ta_(3)MG can regulate angiogenesis through VEGF signaling pathway and osteogenesis via BMP signaling pathway.Animal experiment further confirms a sound osseointegration of Zr_(58)Cu_(25)Al_(14)Ta_(3)MG in achieving better bone-implant-contact and inducing faster periimplant bone formation.展开更多
Amorphous solids exhibit scale-free avalanches,even under small external loading,and thus can work as suitable systems to study critical behavior and universality classes.The abundance of scale-free avalanches in the ...Amorphous solids exhibit scale-free avalanches,even under small external loading,and thus can work as suitable systems to study critical behavior and universality classes.The abundance of scale-free avalanches in the entire elastic tension regime of bulk metallic glass(BMG)samples has been experimentally observed using acoustic emission(AE)measurements.In this work,we compare the statistics of avalanches with those of earthquakes,and find that they both follow the Gutenberg–Richter law in the statistics of energies and Omori’s law of aftershock rates,and share the same characteristics in the distribution of recurrence times.These resemblances encourage us to propose the term“glass-quake”to describe avalanches in elastically loaded BMGs.Furthermore,our work echoes the potential universality of critical behavior in disordered physical systems from atomic to planetary scales,and motivates the use of elastic loaded BMGs as valuable laboratory simulators of seismic dynamics.展开更多
The alteration in surface color of metallic glasses(MGs)holds great significance in the context of microstructuredesign and commercial utility.It is essential to accurately describe the structures that are formed duri...The alteration in surface color of metallic glasses(MGs)holds great significance in the context of microstructuredesign and commercial utility.It is essential to accurately describe the structures that are formed during the laser and colorseparation processes in order to develop practical laser coloring applications.Due to the high oxidation sensitivity of Labasedmetallic glass,it can broaden the color range but make it more complex.Structure coloring by laser processing on thesurface of La-based metallic glass can be conducted after thermoplastic forming.It is particularly important to clarify therole of structure and composition in the surface coloring process.The aim is to study the relationship between amorphoussurface structural color,surface geometry,and oxide formation by laser processing in metallic glasses.The findings revealedthat the periodic structure primarily determines the surface color at laser energy densities below 1.0 J/mm^(2).In contrast,thesurface color predominantly depends on the proportion of oxides that are formed when energy densities exceed 1.0 J/mm^(2).Consequently,this study provides a novel concept for the fundamental investigation of laser coloring and establishes a newavenue for practical application.展开更多
Melt treatment is well known to have an important influence on the properties of metallic glasses(MGs).However,for the MGs quenched from different melt temperatures with a quartz tube,the underlying physical origin re...Melt treatment is well known to have an important influence on the properties of metallic glasses(MGs).However,for the MGs quenched from different melt temperatures with a quartz tube,the underlying physical origin responsible for the variation of properties remains poorly understood.In the present work,we systematically studied the influence of melt treatment on the thermal properties of a Zr50Cu36Al14 glass-forming alloy and unveiled the microscopic origins.Specifically,we quenched the melt at different temperatures ranging from 1.1Tl to 1.5Tl(Tl is the liquidus temperature)to obtain melt-spun MG ribbons and investigated the variation of thermal properties of the MGs upon heating.We found that glass transition temperature,Tg,increases by as much as 36 K,and the supercooled liquid region disappears in the curve of differential scanning calorimetry when the melt is quenched at a high temperature up to 1.5Tl.The careful chemical analyses indicate that the change in glass transition behavior originates from the incorporation of oxygen and silicon in the molten alloys.The incorporated oxygen and silicon can both enhance the interactions between atoms,which renders the cooperative rearrangements of atoms difficult,and thus enhances the kinetic stability of the MGs.展开更多
The early stage evolution of local atomic structures in a multicomponent metallic glass during its crystallization process has been investigated via molecular dynamics simulation.It is found that the initial thermal s...The early stage evolution of local atomic structures in a multicomponent metallic glass during its crystallization process has been investigated via molecular dynamics simulation.It is found that the initial thermal stability and earliest stage evolution of the local atomic clusters show no strong correlation with their initial short-range orders,and this leads to an observation of a novel symmetry convergence phenomenon,which can be understood as an atomic structure manifestation of the ergodicity.Furthermore,in our system we have quantitatively proved that the crucial factor for the thermal stability against crystallization exhibited by the metallic glass is not the total amount of icosahedral clusters,but the degree of global connectivity among them.展开更多
In order to develop the Mg-Zn-Ag metallic glasses(MGs)for biodegradable implant applications,the glass formation ability(GFA)and biocompatibility of Mg-Zn-Ag alloys were investigated using a combination of the calcula...In order to develop the Mg-Zn-Ag metallic glasses(MGs)for biodegradable implant applications,the glass formation ability(GFA)and biocompatibility of Mg-Zn-Ag alloys were investigated using a combination of the calculation of phase diagrams(CALPHAD)and experimental measurements.High GFA potentiality of two alloy series,specifically Mg_(96-x)Zn_xAg_(4)and Mg_(94-x)Zn_xAg_6(x=17,20,23,26,29,32,35),was predicted theoretically and then substantiated through experimental testing.X-ray diffraction(XRD)and differential scanning calorimetry(DSC)techniques were used to evaluate the crystallinity,GFA,and crystallization characteristics of these alloys.The results showed that compositions between Mg_(73)Zn_(23)Ag_(4)and Mg_(64)Zn_(32)Ag_(4)for Mg_(96-x)Zn_xAg_4,Mg_(66)Zn_(28)Ag_(6)and Mg_(63)Zn_(31)Ag_(6for)Mg_(94-x)Zn_xAg_(6)displayed a superior GFA.Notably,the GFA of the Mg_(96-x)Zn_xAg_(4)series was better than that of the Mg_(94-x)Zn_xAg_(6)series.Furthermore,the Mg_(70)Zn_(26)Ag_4,Mg_(74)Zn_(20)Ag_6,and Mg_(71)Zn_(23)Ag_(6)alloys showed acceptable corrosion rates,good cytocompatibility,and positive effects on cell proliferation.These characteristics make them suitable for applications in medical settings,potentially materials as biodegradable implants.展开更多
In this paper,high-energy Ne ions were used to irradiate Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) metallic glass(MG)and crystalline W to investigate their difference in mechanical response after irradiation.The results showed t...In this paper,high-energy Ne ions were used to irradiate Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) metallic glass(MG)and crystalline W to investigate their difference in mechanical response after irradiation.The results showed that with the irradiation dose increased,the tensile micro-strain increased,nano-hardness increased from 7.11 GPa to 7.90 GPa and 8.62 GPa,Young’s modulus increased,and H3/E2 increased which indicating that the plastic deformability decreased in crystalline W.Under the same irradiation conditions,the Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG still maintained the amorphous structure and became more disordered despite the longer range and stronger displacement damage of Ne ions in Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG than in crystalline W.Unlike the irradiation hardening and embrittlement behavior of crystalline W,Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG showed the gradual decrease in hardness from 6.02 GPa to 5.89 GPa and 5.50 GPa,the decrease in modulus and the increase in plastic deformability with the increasing dose.Possibly,the irradiation softening and toughening phenomenon of Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG could provide new ideas for the design of nuclear materials.展开更多
Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_...Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.展开更多
In this work, a quaternary Ni-Cu-Nb-Ta system has been designed to obtain composite microstructure with sphericalcrystalline Cu-rich particles embedded in amorphous Ni-rich matrix. The alloy samples were prepared by u...In this work, a quaternary Ni-Cu-Nb-Ta system has been designed to obtain composite microstructure with sphericalcrystalline Cu-rich particles embedded in amorphous Ni-rich matrix. The alloy samples were prepared by using single-roller melting-spinning method. The microstructure and thermal properties of the as-quenched alloy samples were char-acterized by X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, anddifferential scanning calorimetry. It shows that the spherical crystalline Cu-rich particles are embedded in the amorphousNi-rich matrix. The average size of the Cu-rich particles is strongly dependent upon the Cu content. The effect of the alloycomposition on the behavior of liquid-liquid phase separation and microstructure evolution was discussed. The phaseformation in the Ni-based metallic glass matrix composite was analyzed.展开更多
The effects of microstructure change on the corrosion behaviours of Ni55Nb20Ti10Zr8Co7 bulk glass-forming alloy were investigated in 1 mol/L HCl and 0.5 mol/L H2SO4 solutions. Different microstructures of the Ni-based...The effects of microstructure change on the corrosion behaviours of Ni55Nb20Ti10Zr8Co7 bulk glass-forming alloy were investigated in 1 mol/L HCl and 0.5 mol/L H2SO4 solutions. Different microstructures of the Ni-based alloy were achieved by annealing the bulk glassy rod prepared by copper mould casting. The microstructure, grain size, grain distribution, and phase composition were characterized. Electrochemical behaviours of the Ni-based alloy were revealed by static immersion and anodic potentiodynamic polarization tests. It is indicated that the corrosion behaviours of the Ni-based bulk glass-forming alloy are related to its microstructures, while the fully crystallized alloy exhibits a relatively lower corrosion resistance than those of the amorphous states.展开更多
Inspired by research into the association between icosahedral local orders and the plasticity of metallic glasses(MGs),beryllium(Be) is added to the icosahedral quasi-crystal forming alloy Zr40Ti40Ni20. In this way, b...Inspired by research into the association between icosahedral local orders and the plasticity of metallic glasses(MGs),beryllium(Be) is added to the icosahedral quasi-crystal forming alloy Zr40Ti40Ni20. In this way, bulk metallic glasses(BMGs) with favorable compressive plasticity are fabricated. Therein, the icosahedral quasi-crystalline phase is the main competing phase of amorphous phases and icosahedral local orders are the main local atomic motifs in amorphous phases.The alloys of(Zr40Ti40Ni20)76Be24and (Zr40Ti40Ni20)72Be28with their greater plastic strain capacity show similar characteristics to highly plastic amorphous systems: The serrated flow of compression curves always follows a near-exponential distribution. The primary and secondary shear bands intersect each other, bifurcate, and bend. Typical vein patterns are densely distributed on the fracture surfaces. The relaxation enthalpy of four MGs is linearly correlated with the plastic strain, that is, the greater the relaxation enthalpy, the larger the plastic strain.展开更多
We systematically investigate the structures of Cu–Zr metallic glass(MG) by varying the Cu concentration in classic molecular-dynamics simulation. From the pair distribution functions(PDFs), it is found that the near...We systematically investigate the structures of Cu–Zr metallic glass(MG) by varying the Cu concentration in classic molecular-dynamics simulation. From the pair distribution functions(PDFs), it is found that the nearest atomic distance between Zr atom and Zr atom increases significantly after adding Cu, which is related to the composition-dependent coordination behavior between Cu atom and Zr atom in the nearest neighbors. The portion of PDF related to the nearest connection is decomposed into the contributions from quadrilateral structure, pentagonal structure, hexagonal structure,and heptagonal bipyramid structure. Although the population of denser structures, i.e. 5-, 6-, and 7-number sharing ones,increases with Cu addition increasing, the connection distances between the central atoms in all these bipyramids increase for Zr–Zr pairs, leading to the expansion of Zr–Zr nearest atomic distance. These results unveil the effect of the interplay between chemical interaction and geometric packing on the atomic-level structure in Cu–Zr metallic glasses.展开更多
A novel Ni-based metallic glass, i.e., Ni68.6W17.9B13.5（mole fraction, %）, was prepared using melt spinning method. The results showed that the element B has much effect on the glass forming ability of the Ni-W-B me...A novel Ni-based metallic glass, i.e., Ni68.6W17.9B13.5（mole fraction, %）, was prepared using melt spinning method. The results showed that the element B has much effect on the glass forming ability of the Ni-W-B metallic glass. Ni-W-B metallic glass could not be fabricated with lower content of B, whereas a higher content of 13.5% B could easily lead to the fully amorphous structure. The glass transition temperature and the onset temperature of crystallization are as high as 768 K and 781.5 K, respectively, and the crystallization activation energy calculated by Ozawa model is（637±60） k J/mol, which showed strong thermal stability of Ni68.6W17.9B13.5 metallic glass. This novel Ni-based metallic glass also exhibited good mechanical properties with the tensile strength of about 2331 MPa. The results indicate that this metallic glass should have a promising application in high strength material.展开更多
A metallic glass coating with the composition of Fe51.33Cr14.9Mo25.67Y3.4C3.44B1.26 （mole fraction, %） on the Q235 stainless steel was developed by the detonation gun （D-gun） spraying process. The microstructure a...A metallic glass coating with the composition of Fe51.33Cr14.9Mo25.67Y3.4C3.44B1.26 （mole fraction, %） on the Q235 stainless steel was developed by the detonation gun （D-gun） spraying process. The microstructure and the phase aggregate were analyzed by scanning electron microscopy and X-ray diffractometry, respectively. Microhardness, wear resistance and corrosion behavior were assessed using a Vickers microhardness tester, a ball-on-disk wear testing machine and the electrochemical measurement method, respectively. Microstructural studies show that the coatings possess a densely layered structure with the porosity less than 2.1%. The tribological behavior of the coatings examined under dry conditions shows that their relative wear resistance is five times higher than that of the substrate material. Both adhesive wear and abrasive wear contribute to the friction, but the former is the dominant wear mechanism of the metallic glass coatings. The coatings exhibit low passive current density and extremely wide passive region in 3.5% NaCl solution, thus indicating excellent corrosion resistance.展开更多
An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition w...An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition when the larger specimens were machined into smaller specimens through removing the cast-softening surface layer by layer. After compression tests, the as-machined small specimens, owing to the absence of the cast-softening surface, displayed highly dense and intersecting shear bands, and extensive plastic deformation. This is in contrast to the catastrophic failure and low deformability in the as-cast large specimens. More free volume was detected in the smaller as-fractured specimens, by differential scanning calorimetry, which may be attributed to the occurrence of strain softening and increased plasticity. Compared with the relatively smooth fracture surface in the smaller specimens, the larger specimens showed more diverse features on the fracture surface due to their graded structures.展开更多
The（Zr_（0.55）Al_（0.1）Ni_（0.05）Cu_（0.3））_（100-x）Ti_x alloys were prepared using an in-situ suck-casting method in a copper mold. The effects of Ti addition on the microstructure, mechanical and corrosion pr...The（Zr_（0.55）Al_（0.1）Ni_（0.05）Cu_（0.3））_（100-x）Ti_x alloys were prepared using an in-situ suck-casting method in a copper mold. The effects of Ti addition on the microstructure, mechanical and corrosion properties of the（Zr_（0.55）Al_（0.1）Ni_（0.05）Cu_（0.3））_（100-x）Ti_x alloys were investigated by X-ray diffraction, scanning electron microscopy, compressive tests and corrosion tests. It has been found that the addition of Ti higher than 4%（mole fraction） causes the formation of many crystalline phases in the alloy. The alloys with 1%-3% Ti display an obvious yield stage on their compressive stress-strain curves. An appropriate addition of Ti can improve the strength and ductility of the alloys. All the alloys have high corrosion resistance in 1 mol/L Na OH solution, and are corroded in 1 mol/L HCl solution. However, the appropriate addition of Ti can significantly improve the corrosion resistance of the alloys in HCl solution.展开更多
A series of rod samples with diameter of 3 mm（Zr0.55Al0.10Ni0.05Cu0.30）100-xFex（x=0,1,2,3,4） were prepared by magnetic suspend melting and copper mold suction casting method.The effects of a small amount of Fe on ...A series of rod samples with diameter of 3 mm（Zr0.55Al0.10Ni0.05Cu0.30）100-xFex（x=0,1,2,3,4） were prepared by magnetic suspend melting and copper mold suction casting method.The effects of a small amount of Fe on glass forming ability（GFA） and mechanical properties of Zr55Al10Ni5Cu30 bulk metallic glass（BMG） were investigated.The results show that the addition of an appropriate amount（less than 3%,mole fraction） of Fe enhances GFA,as indicated by the increase in the reduced glass transition temperature Trg（=Tg/Tl） and the parameter γ（=Tx/（Tg＋Tl）） with increasing Fe content,and GFA gets deteriorated by further Fe addition（4%）.The addition of Fe also effectively improves the compressive plasticity and increases the compressive fracture strength in these Zr-based BMGs.Compressive tests on BMG sample with 3 mm in diameter and 6 mm in length reveal work-hardening and a certain plastic strain in the alloy containing 2% Fe.The BMG composite containing 4% Fe also exhibits a high fracture strength along with significant plasticity.展开更多
The room temperature compressive plasticity of Fe75MosP10Cs.3B1.7 bulk metallic glass （BMG） was improved from 0.5% to 1.8% by increasing the sample diameter from 1.5 mm to 2.0 mm. With increasing the sample diameter...The room temperature compressive plasticity of Fe75MosP10Cs.3B1.7 bulk metallic glass （BMG） was improved from 0.5% to 1.8% by increasing the sample diameter from 1.5 mm to 2.0 mm. With increasing the sample diameter to 2.0 mm, a heterogeneous microstructure with in-situ formed a-Fe dendrite sparsely distributed in the amorphous matrix can be attained. This heterogeneous mierostructure is conceived to be highly responsible for the enhanced global plasticity in this marginal Fe-based BMG.展开更多
The glassy rods were successfully fabricated in the Cu-Zr-Ti-In alloy system by casting into a copper mold. The value of ATx reaches a maximum of 66 K for the BMG CusoZraTTi8In5 alloy. The reasons for enhancing glass ...The glassy rods were successfully fabricated in the Cu-Zr-Ti-In alloy system by casting into a copper mold. The value of ATx reaches a maximum of 66 K for the BMG CusoZraTTi8In5 alloy. The reasons for enhancing glass forming ability of Cu-based BMGs with the addition of indium were discussed from atomic size and thermodynamics. Alternatively, the BMG Cu52Zra7Ti8In3 exhibits the highest compressive strength （1981 MPa） and the best plasticity among glassy Cu55-xZra7TisInx （x_〈5）. The total plastic deformation of Cu52Zr37TisIn3 before fracture approaches 1.2%.展开更多
基金National Key Research and Development Program of China(2018YFC1106702)Guangdong Basic and Applied Basic Research Foundation(2020A1515011301,2019A1515110067 and 2020A1515110055)+1 种基金Shenzhen Basic Research Project(JCYJ20210324120001003,JCYJ20200109144608205 and JCYJ20200109144604020)IER Foundation(HT-JDCXY-201902 and HT-JD-CXY-201907)for financial support.
文摘In the present work,seven Mg-Zn-Ag alloys with the nominal composition of Mg_(96-x)Zn_(x)Ag_(4)(x=17,20,23,26,29,32,35 in at.%)were prepared by induction melting and single-roller melt-spinning.The X-ray diffraction(XRD)analyses indicate the metallic glasses with three composition of Mg_(73)Zn_(23)Ag_(4),Mg_(70)Zn_(26)Ag_(4),and Mg_(67)Zn_(29)Ag_(4)were obtained successfully.The differential scanning calorimetry(DSC)measurement was used to obtain the characteristic temperature of Mg-Zn-Ag metallic glasses for the glass-forming ability analysis.The maximum glass transition temperature(Trg)was found to be 0.525 with a composition close to Mg_(67)Zn_(29)Ag_(4),which results in the best glass-forming ability.Moreover,the immersion test in simulated body fluid(SBF)demonstrate the relative homogeneous corrosion behavior of the Mg-Zn-Ag metallic glasses.The corrosion rate of Mg-Zn-Ag metallic glasses in SBF solution decreases with the increase of Zn content.The sample Mg_(67)Zn_(29)Ag_(4)has the lowest corrosion rate of 0.19mm/yr,which could meet the clinical application requirement well.The in vitro cell experiments show that the Madin-Darby canine kidney(MDCK)cells cultured in sample Mg_(67)Zn_(29)Ag_(4)and its extraction medium have higher activity.However,the Mg-Zn-Ag metallic glasses exhibit obvious inhibitory effect on human rhabdomyosarcoma(RD)tumor cells.The present investigations on the glass-forming ability,corrosion behavior,cytocompatibility and tumor inhibition function of the Mg-Zn-Ag based metallic glass could reveal their biomedical application possibility.
基金supported by the National Natural Science Foundation of China(52035001)National Key R&D Program of China(2019YFB1706904)+3 种基金Beijing Training Project for the Leading Talents in S&T(Z191100006119022)National Key Research and Development Plan(2018YFA0703603)National Science 535 Foundation of China(52192602)Youth Fund of the National Natural Science Foundation of China(82201125).
文摘Zirconium-based metallic glasses(Zr-MGs)are demonstrated to exhibit high mechanical strength,low elastic modulus and excellent biocompatibility,making them promising materials for endosseous implants.Meanwhile,tantalum(Ta)is also well known for its ideal corrosion resistance and biological effects.However,the metal has an elastic modulus as high as 186 GPa which is not comparable to the natural bone(10–30 GPa),and it also has a relative high cost.Here,to fully exploit the advantages of Ta as endosseous implants,a small amount of Ta(as low as 3 at.%)was successfully added into a Zr-MG to generate an advanced functional endosseous implant,Zr58Cu25Al14Ta3 MG,with superior comprehensive properties.Upon carefully dissecting the atomic structure and surface chemistry,the results show that amorphization of Ta enables the uniform distribution in material surface,leading to a significantly improved chemical stability and extensive material-cell contact regulation.Systematical analyses on the immunological,angiogenesis and osteogenesis capability of the material are carried out utilizing the next-generation sequencing,revealing that Zr_(58)Cu_(25)Al_(14)Ta_(3)MG can regulate angiogenesis through VEGF signaling pathway and osteogenesis via BMP signaling pathway.Animal experiment further confirms a sound osseointegration of Zr_(58)Cu_(25)Al_(14)Ta_(3)MG in achieving better bone-implant-contact and inducing faster periimplant bone formation.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51801122 and 52071210)the Science Challenge Project(Grant No.TZ2018001)the Science and Technology Commission of Shanghai(Grant No.21ZR1430800).
文摘Amorphous solids exhibit scale-free avalanches,even under small external loading,and thus can work as suitable systems to study critical behavior and universality classes.The abundance of scale-free avalanches in the entire elastic tension regime of bulk metallic glass(BMG)samples has been experimentally observed using acoustic emission(AE)measurements.In this work,we compare the statistics of avalanches with those of earthquakes,and find that they both follow the Gutenberg–Richter law in the statistics of energies and Omori’s law of aftershock rates,and share the same characteristics in the distribution of recurrence times.These resemblances encourage us to propose the term“glass-quake”to describe avalanches in elastically loaded BMGs.Furthermore,our work echoes the potential universality of critical behavior in disordered physical systems from atomic to planetary scales,and motivates the use of elastic loaded BMGs as valuable laboratory simulators of seismic dynamics.
基金supported by the National Natural Science Foundation of China(Grant Nos.52071222 and 52471180)Guangdong Major Project of Basic and Applied Basic Research,China(Grant No.2019B030302010)+2 种基金Guangdong Basic and Applied Basic Research,China(Grant No.2020B1515130007)the National Key Research and Development Program of China(Grant No.2021YFA0716302)the Strategic Priority Research Program of the Chinese Academy of Sciences(Grant No.XDB30000000).
文摘The alteration in surface color of metallic glasses(MGs)holds great significance in the context of microstructuredesign and commercial utility.It is essential to accurately describe the structures that are formed during the laser and colorseparation processes in order to develop practical laser coloring applications.Due to the high oxidation sensitivity of Labasedmetallic glass,it can broaden the color range but make it more complex.Structure coloring by laser processing on thesurface of La-based metallic glass can be conducted after thermoplastic forming.It is particularly important to clarify therole of structure and composition in the surface coloring process.The aim is to study the relationship between amorphoussurface structural color,surface geometry,and oxide formation by laser processing in metallic glasses.The findings revealedthat the periodic structure primarily determines the surface color at laser energy densities below 1.0 J/mm^(2).In contrast,thesurface color predominantly depends on the proportion of oxides that are formed when energy densities exceed 1.0 J/mm^(2).Consequently,this study provides a novel concept for the fundamental investigation of laser coloring and establishes a newavenue for practical application.
基金The work was financially supported by the National Key Research and Development Program of China(Grant Nos.2018YFA0703600,2021YFA0716302,and 2021YFA0718703)the National Natural Science Foundation of China(Grant Nos.51825104 and 52192602)China Postdoctoral Science Foundation(Grant No.2022T150691).
文摘Melt treatment is well known to have an important influence on the properties of metallic glasses(MGs).However,for the MGs quenched from different melt temperatures with a quartz tube,the underlying physical origin responsible for the variation of properties remains poorly understood.In the present work,we systematically studied the influence of melt treatment on the thermal properties of a Zr50Cu36Al14 glass-forming alloy and unveiled the microscopic origins.Specifically,we quenched the melt at different temperatures ranging from 1.1Tl to 1.5Tl(Tl is the liquidus temperature)to obtain melt-spun MG ribbons and investigated the variation of thermal properties of the MGs upon heating.We found that glass transition temperature,Tg,increases by as much as 36 K,and the supercooled liquid region disappears in the curve of differential scanning calorimetry when the melt is quenched at a high temperature up to 1.5Tl.The careful chemical analyses indicate that the change in glass transition behavior originates from the incorporation of oxygen and silicon in the molten alloys.The incorporated oxygen and silicon can both enhance the interactions between atoms,which renders the cooperative rearrangements of atoms difficult,and thus enhances the kinetic stability of the MGs.
基金supported by the National Natural Science Foundation of China (Grant Nos. 52031016 and 11804027)the China Scholarship Council for financial support during part of this work
文摘The early stage evolution of local atomic structures in a multicomponent metallic glass during its crystallization process has been investigated via molecular dynamics simulation.It is found that the initial thermal stability and earliest stage evolution of the local atomic clusters show no strong correlation with their initial short-range orders,and this leads to an observation of a novel symmetry convergence phenomenon,which can be understood as an atomic structure manifestation of the ergodicity.Furthermore,in our system we have quantitatively proved that the crucial factor for the thermal stability against crystallization exhibited by the metallic glass is not the total amount of icosahedral clusters,but the degree of global connectivity among them.
基金the financial supports from the Shenzhen Basic Research Project,China(No.JCYJ20170815153210359)the National Natural Science Foundation of China(No.12174210)。
文摘In order to develop the Mg-Zn-Ag metallic glasses(MGs)for biodegradable implant applications,the glass formation ability(GFA)and biocompatibility of Mg-Zn-Ag alloys were investigated using a combination of the calculation of phase diagrams(CALPHAD)and experimental measurements.High GFA potentiality of two alloy series,specifically Mg_(96-x)Zn_xAg_(4)and Mg_(94-x)Zn_xAg_6(x=17,20,23,26,29,32,35),was predicted theoretically and then substantiated through experimental testing.X-ray diffraction(XRD)and differential scanning calorimetry(DSC)techniques were used to evaluate the crystallinity,GFA,and crystallization characteristics of these alloys.The results showed that compositions between Mg_(73)Zn_(23)Ag_(4)and Mg_(64)Zn_(32)Ag_(4)for Mg_(96-x)Zn_xAg_4,Mg_(66)Zn_(28)Ag_(6)and Mg_(63)Zn_(31)Ag_(6for)Mg_(94-x)Zn_xAg_(6)displayed a superior GFA.Notably,the GFA of the Mg_(96-x)Zn_xAg_(4)series was better than that of the Mg_(94-x)Zn_xAg_(6)series.Furthermore,the Mg_(70)Zn_(26)Ag_4,Mg_(74)Zn_(20)Ag_6,and Mg_(71)Zn_(23)Ag_(6)alloys showed acceptable corrosion rates,good cytocompatibility,and positive effects on cell proliferation.These characteristics make them suitable for applications in medical settings,potentially materials as biodegradable implants.
基金supported by National Natural Science Foundation of China(Nos.12305224,U23B2099 and 11975065)the Natural Science Foundation of Liaoning Province(No.2021-BS-223)+1 种基金the Liaoning Provincial Department of Education Youth Fund Project(No.LJKQZ20222309)supports from the National Laboratory of Heavy-ion Research Facility(HIRFL)in the Institute of Modern Physics in Lanzhou,China.
文摘In this paper,high-energy Ne ions were used to irradiate Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) metallic glass(MG)and crystalline W to investigate their difference in mechanical response after irradiation.The results showed that with the irradiation dose increased,the tensile micro-strain increased,nano-hardness increased from 7.11 GPa to 7.90 GPa and 8.62 GPa,Young’s modulus increased,and H3/E2 increased which indicating that the plastic deformability decreased in crystalline W.Under the same irradiation conditions,the Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG still maintained the amorphous structure and became more disordered despite the longer range and stronger displacement damage of Ne ions in Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG than in crystalline W.Unlike the irradiation hardening and embrittlement behavior of crystalline W,Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG showed the gradual decrease in hardness from 6.02 GPa to 5.89 GPa and 5.50 GPa,the decrease in modulus and the increase in plastic deformability with the increasing dose.Possibly,the irradiation softening and toughening phenomenon of Zr_(63.5)Cu_(23)Al_(9)Fe_(4.5) MG could provide new ideas for the design of nuclear materials.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.52371203 and 52271192)the Ministry of Science and Technology of China(Grant No.2021YFB3501201)。
文摘Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass exhibited excellent magnetic refrigeration material with a wide temperature range and high refrigeration capacity(RC)was reported.Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass was observed with typical spin glass behavior around 15.5 K.In addition,we find that the magnetic entropy change(-△S_(M))originates from the sample undergoing a ferromagnetic(FM)to paramagnetic(PM)transition around 20 K.Under a field change from 0 T to 7 T,the value of maximum magnetic entropy change(-△S_(M)^(max))reaches 12.5 J/kg·K,and the corresponding value of RC reaches 487.7 J/kg in the temperature range from 6 K to 60 K.The large RC and wide temperature range make the Er_(20)Ho_(20)Dy_(20)Cu_(20)Ni_(20)high-entropy metallic glass be a promising material for application in magnetic refrigerators.
基金supported by the National Natural Science Foundation of China(Grant Nos.51774264,51574216 and 51374194)the Natural Science Foundation of Liaoning Province of China(Grant No.2015020172)
文摘In this work, a quaternary Ni-Cu-Nb-Ta system has been designed to obtain composite microstructure with sphericalcrystalline Cu-rich particles embedded in amorphous Ni-rich matrix. The alloy samples were prepared by using single-roller melting-spinning method. The microstructure and thermal properties of the as-quenched alloy samples were char-acterized by X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy, anddifferential scanning calorimetry. It shows that the spherical crystalline Cu-rich particles are embedded in the amorphousNi-rich matrix. The average size of the Cu-rich particles is strongly dependent upon the Cu content. The effect of the alloycomposition on the behavior of liquid-liquid phase separation and microstructure evolution was discussed. The phaseformation in the Ni-based metallic glass matrix composite was analyzed.
基金supported by the National Natural Science Foundation of China (Nos.50631010 and 50771005)the National Basic Research Priorities Program of China (No.2007CB613900)the Program for New Century Excellent Talents in Chinese Universities (No.NCET-07-0041)
文摘The effects of microstructure change on the corrosion behaviours of Ni55Nb20Ti10Zr8Co7 bulk glass-forming alloy were investigated in 1 mol/L HCl and 0.5 mol/L H2SO4 solutions. Different microstructures of the Ni-based alloy were achieved by annealing the bulk glassy rod prepared by copper mould casting. The microstructure, grain size, grain distribution, and phase composition were characterized. Electrochemical behaviours of the Ni-based alloy were revealed by static immersion and anodic potentiodynamic polarization tests. It is indicated that the corrosion behaviours of the Ni-based bulk glass-forming alloy are related to its microstructures, while the fully crystallized alloy exhibits a relatively lower corrosion resistance than those of the amorphous states.
基金supported by the National Key R&D Program of China (Grant No. 2018YFA0703602)the National Natural Science Foundation of China (Grant Nos. 51871193, 52271155 and 52271154)+2 种基金the Natural Science Foundation for Excellent Young Scholars of Hebei Province (Grant No. E2021203050)the Hundred Talent Program of Hebei Province (Grant No. E2020050018)the Hebei Province Innovation Ability Promotion Project (Grant No. 22567609H)。
文摘Inspired by research into the association between icosahedral local orders and the plasticity of metallic glasses(MGs),beryllium(Be) is added to the icosahedral quasi-crystal forming alloy Zr40Ti40Ni20. In this way, bulk metallic glasses(BMGs) with favorable compressive plasticity are fabricated. Therein, the icosahedral quasi-crystalline phase is the main competing phase of amorphous phases and icosahedral local orders are the main local atomic motifs in amorphous phases.The alloys of(Zr40Ti40Ni20)76Be24and (Zr40Ti40Ni20)72Be28with their greater plastic strain capacity show similar characteristics to highly plastic amorphous systems: The serrated flow of compression curves always follows a near-exponential distribution. The primary and secondary shear bands intersect each other, bifurcate, and bend. Typical vein patterns are densely distributed on the fracture surfaces. The relaxation enthalpy of four MGs is linearly correlated with the plastic strain, that is, the greater the relaxation enthalpy, the larger the plastic strain.
基金Project supported by the Open Research Fund of Songshan Lake Materials Laboratory, China (Grant No. 2022SLABFN14)。
文摘We systematically investigate the structures of Cu–Zr metallic glass(MG) by varying the Cu concentration in classic molecular-dynamics simulation. From the pair distribution functions(PDFs), it is found that the nearest atomic distance between Zr atom and Zr atom increases significantly after adding Cu, which is related to the composition-dependent coordination behavior between Cu atom and Zr atom in the nearest neighbors. The portion of PDF related to the nearest connection is decomposed into the contributions from quadrilateral structure, pentagonal structure, hexagonal structure,and heptagonal bipyramid structure. Although the population of denser structures, i.e. 5-, 6-, and 7-number sharing ones,increases with Cu addition increasing, the connection distances between the central atoms in all these bipyramids increase for Zr–Zr pairs, leading to the expansion of Zr–Zr nearest atomic distance. These results unveil the effect of the interplay between chemical interaction and geometric packing on the atomic-level structure in Cu–Zr metallic glasses.
基金Project(50774098)supported by the National Natural Science Foundation of ChinaProject(50721003)supported by Creative Research Group of the National Natural Science Foundation of ChinaProject(CX2013B054)supported by the Innovative Research Project for Postgraduates in Hunan Province,China
文摘A novel Ni-based metallic glass, i.e., Ni68.6W17.9B13.5（mole fraction, %）, was prepared using melt spinning method. The results showed that the element B has much effect on the glass forming ability of the Ni-W-B metallic glass. Ni-W-B metallic glass could not be fabricated with lower content of B, whereas a higher content of 13.5% B could easily lead to the fully amorphous structure. The glass transition temperature and the onset temperature of crystallization are as high as 768 K and 781.5 K, respectively, and the crystallization activation energy calculated by Ozawa model is（637±60） k J/mol, which showed strong thermal stability of Ni68.6W17.9B13.5 metallic glass. This novel Ni-based metallic glass also exhibited good mechanical properties with the tensile strength of about 2331 MPa. The results indicate that this metallic glass should have a promising application in high strength material.
基金Project(51301205)supported by the National Natural Science Foundation of ChinaProject(20130162120001)supported by the Doctoral Program of Higher Education of China+2 种基金Project(K1502003-11)supported by the Changsha Municipal Major Science and Technology Program,ChinaProject(K1406012-11)supported by the Changsha Municipal Science and Technology Plan,ChinaProject(2016CX003)supported by the Innovation-driven Plan in Central South University,China
文摘A metallic glass coating with the composition of Fe51.33Cr14.9Mo25.67Y3.4C3.44B1.26 （mole fraction, %） on the Q235 stainless steel was developed by the detonation gun （D-gun） spraying process. The microstructure and the phase aggregate were analyzed by scanning electron microscopy and X-ray diffractometry, respectively. Microhardness, wear resistance and corrosion behavior were assessed using a Vickers microhardness tester, a ball-on-disk wear testing machine and the electrochemical measurement method, respectively. Microstructural studies show that the coatings possess a densely layered structure with the porosity less than 2.1%. The tribological behavior of the coatings examined under dry conditions shows that their relative wear resistance is five times higher than that of the substrate material. Both adhesive wear and abrasive wear contribute to the friction, but the former is the dominant wear mechanism of the metallic glass coatings. The coatings exhibit low passive current density and extremely wide passive region in 3.5% NaCl solution, thus indicating excellent corrosion resistance.
基金Project(2012M511401)supported by China Postdoctoral Science FoundationProject(12JJ5018)supported by Hunan Provincial Natural Science Foundation of China+1 种基金Project(2012RS4006)supported by Hunan Provincial Science and Technology Plan of ChinaProject(CSUZC2012028)supported by the Open-End Fund for the Valuable and Precision Instruments of Central South University,China
文摘An interesting phenomenon of cooling-rate induced brittleness in Zr52.5Cu17.9Ni14.6Al10Ti5 bulk metallic glass （BMG） was reported. It was found that the as-cast BMG specimens exhibited a brittle-ductile transition when the larger specimens were machined into smaller specimens through removing the cast-softening surface layer by layer. After compression tests, the as-machined small specimens, owing to the absence of the cast-softening surface, displayed highly dense and intersecting shear bands, and extensive plastic deformation. This is in contrast to the catastrophic failure and low deformability in the as-cast large specimens. More free volume was detected in the smaller as-fractured specimens, by differential scanning calorimetry, which may be attributed to the occurrence of strain softening and increased plasticity. Compared with the relatively smooth fracture surface in the smaller specimens, the larger specimens showed more diverse features on the fracture surface due to their graded structures.
基金Projects(51171041,51104047) supported by the National Natural Science Foundation of ChinaProject(N100409001) supported by the Fundamental Research Funds for the Central Universities,China
文摘The（Zr_（0.55）Al_（0.1）Ni_（0.05）Cu_（0.3））_（100-x）Ti_x alloys were prepared using an in-situ suck-casting method in a copper mold. The effects of Ti addition on the microstructure, mechanical and corrosion properties of the（Zr_（0.55）Al_（0.1）Ni_（0.05）Cu_（0.3））_（100-x）Ti_x alloys were investigated by X-ray diffraction, scanning electron microscopy, compressive tests and corrosion tests. It has been found that the addition of Ti higher than 4%（mole fraction） causes the formation of many crystalline phases in the alloy. The alloys with 1%-3% Ti display an obvious yield stage on their compressive stress-strain curves. An appropriate addition of Ti can improve the strength and ductility of the alloys. All the alloys have high corrosion resistance in 1 mol/L Na OH solution, and are corroded in 1 mol/L HCl solution. However, the appropriate addition of Ti can significantly improve the corrosion resistance of the alloys in HCl solution.
基金Project(50371016) supported by the National Natural Science Foundation of ChinaProject(50611130629) supported by the International Cooperation and Exchange of the National Natural Science Foundation of China
文摘A series of rod samples with diameter of 3 mm（Zr0.55Al0.10Ni0.05Cu0.30）100-xFex（x=0,1,2,3,4） were prepared by magnetic suspend melting and copper mold suction casting method.The effects of a small amount of Fe on glass forming ability（GFA） and mechanical properties of Zr55Al10Ni5Cu30 bulk metallic glass（BMG） were investigated.The results show that the addition of an appropriate amount（less than 3%,mole fraction） of Fe enhances GFA,as indicated by the increase in the reduced glass transition temperature Trg（=Tg/Tl） and the parameter γ（=Tx/（Tg＋Tl）） with increasing Fe content,and GFA gets deteriorated by further Fe addition（4%）.The addition of Fe also effectively improves the compressive plasticity and increases the compressive fracture strength in these Zr-based BMGs.Compressive tests on BMG sample with 3 mm in diameter and 6 mm in length reveal work-hardening and a certain plastic strain in the alloy containing 2% Fe.The BMG composite containing 4% Fe also exhibits a high fracture strength along with significant plasticity.
基金Foundation item: Project (SWU110046) supported by the Startup Foundation for Doctors of Southwest University, ChinaProjects (XDJK2012C017,CDJXS11132228, CDJZR10130012) supported by the Fundamental Research Funds for the Central Universities, China+1 种基金Project (CSTS2006AA4012) supported by the Chongqing Science and Technology Commission, ChinaProject (T201112) supported by Shenzhen Key Laboratory of Special Functional Materials,Shenzhen University,China
文摘The room temperature compressive plasticity of Fe75MosP10Cs.3B1.7 bulk metallic glass （BMG） was improved from 0.5% to 1.8% by increasing the sample diameter from 1.5 mm to 2.0 mm. With increasing the sample diameter to 2.0 mm, a heterogeneous microstructure with in-situ formed a-Fe dendrite sparsely distributed in the amorphous matrix can be attained. This heterogeneous mierostructure is conceived to be highly responsible for the enhanced global plasticity in this marginal Fe-based BMG.
基金Project(50971041)support by the National Natural Science Foundation of China
文摘The glassy rods were successfully fabricated in the Cu-Zr-Ti-In alloy system by casting into a copper mold. The value of ATx reaches a maximum of 66 K for the BMG CusoZraTTi8In5 alloy. The reasons for enhancing glass forming ability of Cu-based BMGs with the addition of indium were discussed from atomic size and thermodynamics. Alternatively, the BMG Cu52Zra7Ti8In3 exhibits the highest compressive strength （1981 MPa） and the best plasticity among glassy Cu55-xZra7TisInx （x_〈5）. The total plastic deformation of Cu52Zr37TisIn3 before fracture approaches 1.2%.