A novel Cu?6.5Ni?1Al?1Si?0.15Mg?0.15Ce alloy with super-high strength was designed and its corrosion behavior in3.5%NaCl solution at25°C was investigated by the means of SEM observation,TEM observation and XPS an...A novel Cu?6.5Ni?1Al?1Si?0.15Mg?0.15Ce alloy with super-high strength was designed and its corrosion behavior in3.5%NaCl solution at25°C was investigated by the means of SEM observation,TEM observation and XPS analysis.The alloy after solution treatment,80%cold rolling and aging at450°C for1h had the best comprehensive properties with hardness of HV314,electrical conductivity of19.4%IACS,tensile strength of1017MPa,and average annual corrosion rate of0.028mm/a.The oxides and chloride products formed at first,followed by the formation of dyroxides products.The alloy showed super-high strength,good electrical conductivity and corrosion resistant because Ni2Si hindered the precipitation of large NiAl at the grain boundary and the denickelefication of the alloy.展开更多
基金Project(51271203)supported by the National Natural Science Foundation of China
文摘A novel Cu?6.5Ni?1Al?1Si?0.15Mg?0.15Ce alloy with super-high strength was designed and its corrosion behavior in3.5%NaCl solution at25°C was investigated by the means of SEM observation,TEM observation and XPS analysis.The alloy after solution treatment,80%cold rolling and aging at450°C for1h had the best comprehensive properties with hardness of HV314,electrical conductivity of19.4%IACS,tensile strength of1017MPa,and average annual corrosion rate of0.028mm/a.The oxides and chloride products formed at first,followed by the formation of dyroxides products.The alloy showed super-high strength,good electrical conductivity and corrosion resistant because Ni2Si hindered the precipitation of large NiAl at the grain boundary and the denickelefication of the alloy.