The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^＋-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties ...The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^＋-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties were investigated.A distinct bipolar resistive switching behavior of the devices was observed at room temperature.The resistance ratio R_（HRS）/RLRS of high resistance state and low resistance state is as large as four orders of magnitude with a readout voltage of 2.0 V.The dominant conduction mechanism of the device is trap-controlled space charge limited current（SCLC）.The devices exhibit good durability under 1×10^3cycles and the degradation is invisible for more than 10^6 s.展开更多
基金Funded by the National Natural Science Foundation of China(No.51262003)the Guangxi Key Laboratory of Information Materials(Guilin University of Electronic Technology),China(No.1110908-10-Z)
文摘The Ag/Mg0.2Zn0.8O/ZnMn2O4/p^＋-Si heterostructure devices were fabricated by sol-gel spin coating technique and the resistive switching behavior,conduction mechanism,endurance characteristic,and retention properties were investigated.A distinct bipolar resistive switching behavior of the devices was observed at room temperature.The resistance ratio R_（HRS）/RLRS of high resistance state and low resistance state is as large as four orders of magnitude with a readout voltage of 2.0 V.The dominant conduction mechanism of the device is trap-controlled space charge limited current（SCLC）.The devices exhibit good durability under 1×10^3cycles and the degradation is invisible for more than 10^6 s.